Flow and fracture behavior of aluminum alloy 6082-T6 at different tensile strain rates and triaxialities.

ABSTRACT: This study aims to investigate the flow and fracture behavior of aluminum alloy 6082-T6 (AA6082-T6) at different strain rates and triaxialities. Two groups of Charpy impact tests were carried out to further investigate its dynamic impact fracture property. A series of tensile tests and numerical simulations based on finite element analysis (FEA) were performed. Experimental data on smooth specimens under various strain rates ranging from 0.0001~3400 s-1 shows that AA6082-T6 is rather insensitive to strain rates in general. However, clear rate sensitivity was observed in the range of 0.001~1 s-1 while such a characteristic is counteracted by the adiabatic heating of specimens under high strain rates. A Johnson-Cook constitutive model was proposed based on tensile tests at different strain rates. In this study, the average stress triaxiality and equivalent plastic strain at facture obtained from numerical simulations were used for the calibration of J-C fracture model. Both of the J-C constitutive model and fracture model were employed in numerical simulations and the results was compared with experimental results. The calibrated J-C fracture model exhibits higher accuracy than the J-C fracture model obtained by the common method in predicting the fracture behavior of AA6082-T6. Finally, the Scanning Electron Microscope (SEM) of fractured specimens with different initial stress triaxialities were analyzed. The magnified fractographs indicate that high initial stress triaxiality likely results in dimple fracture.

SUBMITTER: Chen X

PROVIDER: S-EPMC5536279 | biostudies-other | 2017

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Fatigue life analysis for 6061-T6 aluminum alloy based on surface roughness.

Project description:Surface condition is one of the dominant factors affecting fatigue life. Considering the complexity of surface condition, a relatively efficient and economic approach based on surface reconstruction and interpolation method was proposed. The effect of surface roughness on the fatigue life of 6061-T6 aluminum alloy is studied to analyze the fatigue life by surface roughness parameters. Surface topography was simplified into a series of elliptic micro notches, and empirical formula for stress concentration factor is established based on simulation work. Then the extraction method of surface curve is proposed to effectively represent the real surface roughness through 3D model reconstruction. Experiment of surface roughness verified the correctness of the model. The relationship between surface roughness and fatigue life is established and the calculated value of the fatigue life is compared with the test results. The maximum error is 15.65%, indicating that the formula established is reasonable and effective.

| S-EPMC8244873 | biostudies-literature

Tensile Properties and Fracture Behavior of Aluminum Alloy Foam Fabricated from Die Castings without Using Blowing Agent by Friction Stir Processing Route.

Project description:Al foam has been used in a wide range of applications owing to its light weight, high energy absorption and high sound insulation. One of the promising processes for fabricating Al foam involves the use of a foamable precursor. In this study, ADC12 Al foams with porosities of 67%-78% were fabricated from Al alloy die castings without using a blowing agent by the friction stir processing route. The pore structure and tensile properties of the ADC12 foams were investigated and compared with those of commercially available ALPORAS. From X-ray computed tomography (X-ray CT) observations of the pore structure of ADC12 foams, it was found that they have smaller pores with a narrower distribution than those in ALPORAS. Tensile tests on the ADC12 foams indicated that as their porosity increased, the tensile strength and tensile strain decreased, with strong relation between the porosity, tensile strength, and tensile strain. ADC12 foams exhibited brittle fracture, whereas ALPORAS exhibited ductile fracture, which is due to the nature of the Al alloy used as the base material of the foams. By image-based finite element (FE) analysis using X-ray CT images corresponding to the tensile tests on ADC12 foams, it was shown that the fracture path of ADC12 foams observed in tensile tests and the regions of high stress obtained from FE analysis correspond to each other. Therefore, it is considered that the fracture behavior of ADC12 foams in relation to their pore structure distribution can be investigated by image-based FE analysis.

| S-EPMC5453280 | biostudies-other

Welding Characteristics Analysis and Application on Spacecraft of Friction Stir Welded 2A14-T6 Aluminum Alloy.

Project description:According to the actual size parameters, the finite element model (FEM) of friction stir welding (FSW) was established, and the FEM was updated by experiments. The FSW of the 2A14-T6 high-strength aluminum alloy was simulated under a reasonable welding process parameter range, and the welding process parameters with good simulation effect were determined. The test was carried out under the same parameters, and the axial force of the FSW tool and temperature of the workpiece measuring point were collected. The comparison between the simulated data and the experimental data is reasonable, indicating the correctness of the FEM. The microstructure analysis of the welded joint shows that the grain size in the upper part of the weld nugget was smaller than that in the middle and lower parts, and there are obvious boundaries of grain size in each region of the joint. The hardness of the joint in the upper layer is higher than that in the middle and lower layers, and the minimum Vickers hardness value of the joint appears near the interface between the thermo-mechanically affected zone and the heat-affected zone on both sides of the weld. Tensile testing shows that the strength coefficient of the joint reaches 82.5% under this process parameter, and the sample breaks at the intersection of the material flow during stretching. After analyzing the final mechanical properties of the joint, we found that a degree of aerospace application can be achieved. Under this parameter, the welding test was carried out on the top cover of the rocket fuel tank. Firstly, melon valve welding, which is relatively difficult in welding conditions, was carried out, and a high-quality joint with good surface and no defects was obtained.

| S-EPMC6384982 | biostudies-literature

The Microstructure Evolution and Electrochemical Corrosion Behavior of 7A46 Aluminum Alloy in Different Quenching Conditions.

Project description:The quenching condition of aluminum alloy can affect the mechanical property and corrosion resistance of the profile. This paper is aimed at the low quench sensitivity of aluminum alloys. Scanning electron microscopy and transmission electron microscopy were used to analyze precipitate behaviors of the 7A46 aluminum alloy under different isothermal cooling conditions and microstructure evolutions of quench-induced precipitations. The effect of the different isothermal time on the corrosion resistance of the alloy, and the relationship between microstructure and corrosion resistance after quenching were revealed through electrochemical impedance spectroscopy and potentiodynamic polarization tests. Results show that corrosion sensitivity of the quenching-aged alloy is much higher than that of the double-aged (DA) alloy, and the corrosion resistance of the quenched alloy decreases firstly and then increases. Due to the high density of the matrix precipitates, the increased content of the impurity element, the discontinuity of the grain boundary precipitates and the widening of the precipitates free zone, the most serious degree of corrosion performance among the quenched alloys is 295 °C at 800 s, and the self-corrosion potential and self-current density is -0.919 V and 2.371 μA/cm2, respectively.

| S-EPMC8777919 | biostudies-literature

Microstructure and Mechanical Properties of Butt Joints between Stainless Steel SUS304L and Aluminum Alloy A6061-T6 by TIG Welding.

Project description:The tungsten inert gas (TIG) welding method most commonly used to weld ferrous metals, nonferrous metals, and other metals since it is simple, easily implemented, and achieves consistent high-quality welds. In this study, butt joints produced between aluminum alloy A6061-T6 and stainless steel SUS304L have been achieved by using TIG welding with ER4047 filler metal. The macrostructure and microstructure of the resulting specimens were analyzed by means of an optical microscope (OM), a scanning electron microscope (SEM), and an energy dispersive X-ray spectrometer (EDS). A uniform intermetallic layer was found at the interface between the stainless steel and the weld seam having a thickness of 2 µm, and the intermetallic compound (IMC) includes Fe?Al13, Fe?Al?, and FeAl? phases. The micro-hardness and tensile strength of the weld joints were also investigated. Due to Si content in the compensating metal, there was a prevention of iron diffusion into the aluminum, thus hindering the development of the IMC layer and reducing its thickness in such a way that the weld joint strength increases. The analyzed results show that the average micro-hardness of the stainless steel, weld seam, aluminum alloys, and IMC layer were 218 HV, 88.3 HV, 63.3 HV, and 411 HV, respectively. The fracture occurred at the brazed interface, and the ultimate tensile strength value reached 225 MPa.

| S-EPMC6073269 | biostudies-literature

Fabrication and Mechanical Properties of Tungsten Inert Gas Welding Ring Welded Joint of 7A05-T6/5A06-O Dissimilar Aluminum Alloy.

Project description:In this paper, Tungsten Inert Gas Welding (TIG) and single-sided welding and double-sided forming have been used to weld the 7A05-T6/5A06-O dissimilar aluminum alloy circular welded joint of a ring-stiffened closed cylindrical sandwich shell. Microstructural characterization and mechanical properties of welded joints were investigated by use of scanning electron microscopy (SEM), backscatter electron diffraction (EBSD) and transmission electron microscopy (TEM), respectively. Hardness distribution and tensile properties of the welded joints were examined. The results showed the failure of the welded joints produced in the fusion zone (FZ). The tensile strength and yield strength of the welded joints were, respectively, 78.87% and 97.24% of the 5A06-O base metal (BM), and the elongation reached 84.29% of 7A05-T6 base metal. Welding high heat input led to the coarse grain size in the fusion zone, and the long-term similar quenching effect can lead to the full dissolution of the strengthening zone of the fusion zone resulting in the reductions of strength and hardness. Around 7A05 heat-affected zone (HAZ), there is an obvious hardening zone and softening zone, the solid solution precipitates into the Rayleigh brilliant η′ (MgZn₂) phase, which results in natural aging strengthening, thus obtaining high hardness. η′ (MgZn₂) enhanced phase dissolved fully and the dislocation density decreased rapidly in the HAZ region resulted in a softening zone with a lower hardness at about (10⁻18) mm from the center of the weld center.

| S-EPMC6073191 | biostudies-literature

Dynamic Recrystallization Behavior and Processing Map of the 6082 Aluminum Alloy.

Project description:Multiple hot-compression tests were carried out on the 6082 aluminum (Al) alloy using a Gleeble-1500 thermal simulation testing machine. Data on flow stresses of the 6082 Al alloy at deformation temperatures of 623 to 773 K and strain rates from 0.01 to 5 s-1 were attained. Utilizing electron backscatter diffraction (EBSD) and a transmission electron microscope (TEM), the dynamic recrystallization behaviors of the 6082 Al alloy during hot compression in isothermal conditions were explored. With the test data, a hot-working processing map for the 6082 Al alloy (based on dynamic material modeling (DMM)) was drawn. Using the work-hardening rate, the initial critical strain causing dynamic recrystallization was determined, and an equation for the critical strain was constructed. A dynamic model for the dynamic recrystallization of the 6082 Al alloy was established using analyses and test results from the EBSD. The results showed that the safe processing zone (with a high efficiency of power dissipation) mainly corresponded to a zone with deformation temperatures of 703 to 763 K and strain rates of 0.1 to 0.3 s-1. The alloy was mainly subjected to continuous dynamic recrystallization in the formation of the zone. According to the hot-working processing map and an analysis of the microstructures, it is advised that the following technological parameters be selected for the 6082 Al alloy during hot-forming: a range of temperatures between 713 and 753 K and strain rates between 0.1 and 0.2 s-1.

| S-EPMC7084686 | biostudies-literature

Tensile deformation behavior of twist grain boundaries in CoCrFeMnNi high entropy alloy bicrystals.

Project description:High entropy alloys (HEA) are a class of materials that consist of multiple elemental species in similar concentrations. The use of elements in far from dilute concentrations introduces a multi-dimensional composition design space by which the properties of metallic systems can be tailored. While the mechanical behavior of HEAs has been the subject of active research recently, the role of grain boundaries (GBs) in their deformation behavior remains poorly understood. Motivated by recent experiments on HEAs demonstrating that GBs act as nucleation sites for deformation twins, herein, we leverage atomistic simulations to construct a series of equiatomic CoCrFeMnNi HEA bicrystals with [Formula: see text] and [Formula: see text] symmetric twist GBs and examine their tensile behavior and underlying deformation mechanisms at 77 K. Simulation results reveal that plastic deformation proceeds by the nucleation of partial dislocations from GBs, which then grow with further loading by bowing into the bulk crystals leaving behind stacking faults. Variations in the nucleation stress exist as function of GB character, defined in this work by the twist angle. Our results provide future avenues to explore GBs as a microstructure design tool to develop HEAs with tailored properties.

| S-EPMC7801446 | biostudies-literature

Anomalous tensile response of bacterial cellulose nanopaper at intermediate strain rates.

Project description:Nanocellulose network in the form of cellulose nanopaper is an important material structure and its time-dependent mechanical response is crucial in many of its potential applications. In this work, we report the influences of grammage and strain rate on the tensile response of bacterial cellulose (BC) nanopaper. BC nanopaper with grammages of 20, 40, 60 and 80 g m-2 were tested in tension at strain rates ranging from 0.1% s-1 to 50% s-1. At strain rates [Formula: see text] 2.5% s-1, both the tensile modulus and strength of the BC nanopapers stayed constant at ~ 14 GPa and ~ 120 MPa, respectively. At higher strain rates of 25% s-1 and 50% s-1 however, the tensile properties of the BC nanopapers decreased significantly. This observed anomalous tensile response of BC nanopaper is attributed to inertial effect, in which some of the curled BC nanofibres within the nanopaper structure do not have enough time to uncurl before failure at such high strain rates. Our measurements further showed that BC nanopaper showed little deformation under creep, with a secondary creep rate of only ~ 10-6 s-1. This stems from the highly crystalline nature of BC, as well as the large number of contact or physical crosslinking points between adjacent BC nanofibres, further reducing the mobility of the BC nanofibres in the nanopaper structure.

| S-EPMC7498453 | biostudies-literature