Effect of grain constraint on the field requirements for magnetocaloric effect in Ni45Co5Mn40Sn10 melt-spun ribbons.

ABSTRACT: The influence of grain constraint on the magnetic field levels required to complete the isothermal martensitic transformation in magnetic shape memory alloys has been demonstrated for a NiCoMnSn alloy, and the magnetocaloric performance of an optimally heat treated alloy was quantified. Ni45CoxMn45-xSn10 melt spun ribbons with x = 2, 4, 5, and 6 were characterized. The x = 5 sample was determined to exhibit the lowest transformation thermal hysteresis (7 K) and transformation temperature range during transformation from paramagnetic austenite to nonmagnetic martensite, as well as a large latent heat of transformation (45 J kg-1 K-1). For this composition, it was found that increasing the grain size to thickness ratio of the ribbons from 0.2 to 1.2, through select heat treatments, resulted in a decrease in the magnetic field required to induce the martensitic transformation by about 3 T due to the corresponding reduction in the martensitic transformation temperature range. This decrease in the field requirement ultimately led to a larger magnetocaloric entropy change achieved under relatively smaller magnetic field levels. The giant inverse magnetocaloric effect of the optimized alloy was measured and showed that up to 25 J kg-1 K-1 was generated by driving the martensitic transition with magnetic fields up to 7 T.

SUBMITTER: Bruno NM

PROVIDER: S-EPMC5543997 | biostudies-other | 2016 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Magnetocaloric effect and magnetic cooling near a field-induced quantum-critical point

Project description:The presence of a quantum-critical point (QCP) can significantly affect the thermodynamic properties of a material at finite temperatures T. This is reflected, e.g., in the entropy landscape S(T,r) in the vicinity of a QCP, yielding particularly strong variations for varying the tuning parameter r such as pressure or magnetic field B. Here we report on the determination of the critical enhancement of ?S/?B near a B-induced QCP via absolute measurements of the magnetocaloric effect (MCE), (?T/?B)S and demonstrate that the accumulation of entropy around the QCP can be used for efficient low-temperature magnetic cooling. Our proof of principle is based on measurements and theoretical calculations of the MCE and the cooling performance for a Cu2+-containing coordination polymer, which is a very good realization of a spin-½ antiferromagnetic Heisenberg chain—one of the simplest quantum-critical systems.

| S-EPMC3084140 | biostudies-literature

First Order Reversal Curve Study of SmFe₂ Melt-Spun Ribbons.

Project description:First-order reversal curves (FORC) and the FORC distribution provide a detailed characterization of the relative proportions of reversible and irreversible components of the magnetization of a material, revealing the dominant interactions in the system. Alloys with the nominal composition SmFe₂ were obtained by melt-spinning with a cooper wheel velocity of 30 m/s. X-ray powder diffraction analysis showed a greater part consisting of an amorphous phase and a very small amount of SmFe₂ crystalline phase with an average crystallite size of 8 nm. A constant acceleration Mössbauer spectrum, measured at room temperature in transmission mode, was fitted to a continuous distribution of effective fields at the nucleus of the amorphous phase (about 84% of the total area), plus two sextets for the non-equivalent sites of Fe in the SmFe₂ crystalline phase. 91 first-order reversal curves were collected in a Quantum Design PPMS-VSM with reversal fields from ⁻800 mT to +800 mT and using a calibration field of 850 mT. The obtained FORC diagrams showed a combined effect of a local interaction field and a mean interaction field, and showed that the reversible magnetization is a function of both, the applied magnetic field and the irreversible magnetization.

| S-EPMC6212980 | biostudies-literature

Role of disorder when upscaling magnetocaloric Ni-Co-Mn-Al Heusler alloys from thin films to ribbons.

Project description:Research in functional magnetic materials often employs thin films as model systems for finding new chemical compositions with promising properties. However, the scale-up of thin films towards bulk-like structures is challenging, since the material synthesis conditions are entirely different for thin films and e.g. rapid quenching methods. As one of the consequences, the type and degree of order in thin films and melt-spun ribbons are usually different, leading to different magnetic properties. In this work, using the example of magnetocaloric Ni-Co-Mn-Al melt-spun ribbons and thin films, we show that the excellent functional properties of the films can be reproduced also in ribbons, if an appropriate heat treatment is applied, that installs the right degree of order in the ribbons. We show that some chemical disorder is needed to get a pronounced and sharp martensitic transition. Increasing the order with annealing improves the magnetic properties only up to a point where selected types of disorder survive, which in turn compromise the magnetic properties. These findings allow us to understand the impact of the type and degree of disorder on the functional properties, paving the way for a faster transfer of combinatorial thin film research towards bulk-like materials for magnetic Heusler alloys.

| S-EPMC6002362 | biostudies-literature

Non-hysteretic first-order phase transition with large latent heat and giant low-field magnetocaloric effect.

Project description:First-order magnetic transitions (FOMTs) with a large discontinuity in magnetization are highly sought in the development of advanced functional magnetic materials. Isosymmetric magnetoelastic FOMTs that do not perturb crystal symmetry are especially rare, and only a handful of material families, almost exclusively transition metal-based, are known to exhibit them. Yet, here we report a surprising isosymmetric FOMT in a rare-earth intermetallic, Eu2In. What makes this transition in Eu2In even more remarkable is that it is associated with a large latent heat and an exceptionally high magnetocaloric effect in low magnetic fields, but with tiny lattice discontinuities and negligible hysteresis. An active role of the Eu-5d and In-4p states and a rather unique electronic structure borne by In to Eu charge transfer, altogether result in an unusual exchange mechanism that both sets the transition in motion and unveils an approach toward developing specific magnetic functionalities ad libitum.

| S-EPMC6062548 | biostudies-literature

Tunable Magnetocaloric Effect in Ni-Mn-Ga Microwires.

Project description:Magnetic refrigeration is of great interest due to its high energy efficiency, environmental friendliness and low cost. However, undesired hysteresis losses, concentrated working temperature interval (WTI) and poor mechanical stability are vital drawbacks that hinder its practical application. Off-stoichiometric Ni-Mn-Ga Heusler alloys are capable of giant magnetocaloric effect (MCE) and tunable transformation temperatures. Here, by creating Ni-Mn-Ga microwires with diameter of 35-80 ?m using a melt-extraction technique, negligible hysteresis and relatively good mechanical stability are found due to the high specific surface area (SSA) that reduces incompatibility between neighboring grains. The high SSA also favors the element evaporation at high temperatures so that the transformation temperatures can be feasibly adjusted. Tunable magnetocaloric effect owing to different magneto-structural coupling states is realized by (i) composition design and subsequent tuning, which adjusts the temperature difference between the martensite transformation (MT) and the magnetic transition, and (ii) creation of gradient composition distribution state, which manipulates the MT range. Magnetic entropy change ?Sm ~-18.5?J?kg-1 K-1 with relatively concentrated WTI and WTI up to ~60?K with net refrigeration capacity ~240?J?kg-1 at 50?kOe are demonstrated in the present Ni-Mn-Ga microwires. This criterion is also applicable for other small-sized materials.

| S-EPMC6224590 | biostudies-literature

Large magnetocaloric effect and adiabatic demagnetization refrigeration with YbPt2Sn.

Project description:Adiabatic demagnetization is currently gaining strong interest in searching for alternatives to (3)He-based refrigeration techniques for achieving temperatures below 2?K. The main reasons for that are the recent shortage and high price of the rare helium isotope (3)He. Here we report the discovery of a large magnetocaloric effect in the intermetallic compound YbPt2Sn, which allows adiabatic demagnetization cooling from 2?K down to 0.2?K. We demonstrate this with a home-made refrigerator. Other materials, for example, paramagnetic salts, are commonly used for the same purpose but none of them is metallic, a severe limitation for low-temperature applications. YbPt2Sn is a good metal with an extremely rare weak magnetic coupling between the Yb atoms, which prevents them from ordering above 0.25?K, leaving enough entropy free for use in adiabatic demagnetization cooling. The large volumetric entropy capacity of YbPt2Sn guarantees also a good cooling power.

| S-EPMC4846311 | biostudies-literature

The physical mechanism of magnetic field controlled magnetocaloric effect and magnetoresistance in bulk PrGa compound.

Project description:The PrGa compound shows excellent performance on the magnetocaloric effect (MCE) and magnetoresistance (MR). The physical mechanism of MCE and MR in PrGa compound was investigated and elaborated in detail on the basis of magnetic measurement, heat capacity measurement and neutron powder diffraction (NPD) experiment. New types of magnetic structure and magnetic transition are found. The results of the NPD along with the saturation magnetic moment (MS) and magnetic entropy (SM) indicate that the magnetic moments are randomly distributed within the equivalent conical surface in the ferromagnetic (FM) temperature range. PrGa compound undergoes an FM to FM transition and an FM to paramagnetic (PM) transition as temperature increases. The magnetizing process was discussed in detail and the physical mechanism of the magnetic field controlled magnetocaloric effect (MCE) and the magnetoresistance (MR) was studied. The formation of the plateau on MCE curve was explained and MR was calculated in detail on the basis of the magnetic structure and the analysis of the magnetizing process. The experimental results are in excellent agreement with the calculations. Finally, the expression of MR = β(T)X(2) and its application conditions were discussed, where X is M(H)/Meff, and Meff is the paramagnetic effective moment.

| S-EPMC4601143 | biostudies-other

A first constraint on basal melt-water production of the Greenland ice sheet.

Project description:The Greenland ice sheet has been one of the largest sources of sea-level rise since the early 2000s. However, basal melt has not been included explicitly in assessments of ice-sheet mass loss so far. Here, we present the first estimate of the total and regional basal melt produced by the ice sheet and the recent change in basal melt through time. We find that the ice sheet's present basal melt production is 21.4 +4.4/-4.0 Gt per year, and that melt generated by basal friction is responsible for about half of this volume. We estimate that basal melting has increased by 2.9 ± 5.2 Gt during the first decade of the 2000s. As the Arctic warms, we anticipate that basal melt will continue to increase due to faster ice flow and more surface melting thus compounding current mass loss trends, enhancing solid ice discharge, and modifying fjord circulation.

| S-EPMC8187594 | biostudies-literature

Criticality-Enhanced Magnetocaloric Effect in Quantum Spin Chain Material Copper Nitrate.

Project description:In this work, a systematic study of Cu(NO3)2·2.5 H2O (copper nitrate hemipentahydrate, CN), an alternating Heisenberg antiferromagnetic chain model material, is performed with multi-technique approach including thermal tensor network (TTN) simulations, first-principles calculations, as well as magnetization measurements. Employing a cutting-edge TTN method developed in the present work, we verify the couplings J = 5.13 K, α = 0.23(1) and Landé factors g∥= 2.31, g⊥ = 2.14 in CN, with which the magnetothermal properties have been fitted strikingly well. Based on first-principles calculations, we reveal explicitly the spin chain scenario in CN by displaying the calculated electron density distributions, from which the distinct superexchange paths are visualized. On top of that, we investigated the magnetocaloric effect (MCE) in CN by calculating its isentropes and magnetic Grüneisen parameter. Prominent quantum criticality-enhanced MCE was uncovered near both critical fields of intermediate strengths as 2.87 and 4.08 T, respectively. We propose that CN is potentially a very promising quantum critical coolant.

| S-EPMC5353727 | biostudies-literature

The rotating magnetocaloric effect as a potential mechanism for natural magnetic senses.

Project description:Many animals are able to sense the earth's magnetic field, including varieties of arthropods and members of all major vertebrate groups. While the existence of this magnetic sense is widely accepted, the mechanism of action remains unknown. Building from recent work on synthetic magnetoreceptors, we propose a new model for natural magnetosensation based on the rotating magnetocaloric effect (RME), which predicts that heat generated by magnetic nanoparticles may allow animals to detect features of the earth's magnetic field. Using this model, we identify the conditions for the RME to produce physiological signals in response to the earth's magnetic field and suggest experiments to distinguish between candidate mechanisms of magnetoreception.

| S-EPMC6773214 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data