Comparative Evaluation of shear Bond Strength of universal Dental Adhesives -An in vitro study.

ABSTRACT: Patient demand for tooth colored restorations and desire for minimally invasive restorations have made composites an indispensable part of the restorative process. An important factor affecting the intra-oral performance of composite restorations is bonding.Ninty six freshly extracted molar teeth were collected and occlusal 3mm is removed using a diamond disc to expose dentine. Following with samples were divided in to two main groups (self-etch & total etch). Each main group is again sub divided in to three groups each according to bonding agent used (Tetric N- Bond Universal, Single Bond Universal, Tetric N Bond Total etch in total etch group and Clear Fill SE in self etch group). Following which bonding protocol is followed according to manufacture instructions, a composite buildup of 2x3 mm is done on each specimen and then specimen were subjected to shear bond test under universal testing machine. All the readings were noted and subjected to statistical analysis using One way ANOVA and Tukey's posthoc test.It showed that there is no significant difference among the groups in both self-etch and total etch modes.It can be concluded that application of an etching step prior to Universal Adhesives significantly improves their dentine penetration pattern, although this does not affect their mean SBS. The bond strength values of the TBU regardless of application mode were comparable to SBU making them reliable for working under different clinical conditions. Key words:Dentine bonding agents, self-etch mode, total etch mode, shear bond strength.

SUBMITTER: Jayasheel A

PROVIDER: S-EPMC5549587 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Currently, the availability of a wide variety of universal adhesives makes it difficult for clinicians to choose the correct system for specific bonding situations to dentin substrate. This study aimed to determine whether there are any alternative techniques or additional strategies available to enhance the bond strength of universal adhesives to dentin through a systematic review and meta-analysis. Two reviewers executed a literature search up to September 2020 in four electronic databases: PubMed, ISI Web of Science, Scopus, and EMBASE. Only in vitro studies that reported the dentin bond strength of universal adhesives using additional strategies were included. An analysis was carried out using Review Manager Software version 5.3.5 (The Nordic Cochrane Centre, The Cochrane Collaboration, Copenhagen, Denmark). The methodological quality of each in vitro study was assessed according to the parameters of a previous systematic. A total of 5671 potentially relevant studies were identified. After title and abstract examination, 74 studies remained in systematic review. From these, a total of 61 studies were included in the meta-analysis. The bond strength of universal adhesives to dentin was improved by the use of one of the following techniques: Previous application of matrix metalloproteinases (MMP) inhibitors (p < 0.001), prolonged application time (p = 0.007), scrubbing technique (p < 0.001), selective dentin etching (p < 0.001), non-atmospheric plasma (p = 0.01), ethanol-wet bonding (p < 0.01), prolonged blowing time (p = 0.02), multiple layer application (p = 0.005), prolonged curing time (p = 0.006), and hydrophobic layer coating (p < 0.001). On the other hand, the use of a shortened application time (p = 0.006), and dentin desensitizers (p = 0.01) impaired the bond strength of universal adhesives to dentin. Most of the analyses performed showed a high heterogenicity. The in vitro evidence suggests that the application of universal adhesives using some alternative techniques or additional strategies may be beneficial for improving their bonding performance to dentin. This research received no external funding. Considering that this systematic review was carried out only with in vitro studies, registration was not performed.

Project description:Based on the frequent application of composite resins as tooth-colored fillings, this method is considered a viable alternative to dental amalgam. However, this method has the low bond strength of the composite to dentin. To solve this issue, various dental adhesive systems with different characteristics have been developed by dentistry experts.To assess the effect of an additional layer of unfilled resin in self-etch and total-etch dentin adhesives on the shear bond strength (SBS) of composite to dentin. Moreover, we assessed the effects of sample storage in artificial saliva on the SBS of composite to dentin.Methods: This experimental study was conducted on 160 freshly extracted human first or second premolar teeth, which were randomly divided into 16 groups. The teeth were prepared from Mashhad University of Medical Sciences, Mashhad, Iran (2008-2009). Scotchbond Multi-purpose (SBMP), single bond (SB), Clearfil SE Bond, and Clearfil S3 Bond were applied to dentin surface with or without the placement of hydrophobic resin (Margin Bond) in accordance with the instructions of the manufacturers. To expose the coronal dentin, the teeth were abraded with 600 grit SiC paper. Immediately after restoration, half of the samples were tested in terms of SBS, while the other samples were evaluated in terms of SBS after three months of storage in artificial saliva. SBS rates of dental composites evaluated by universal testing machine and samples were studied by optical stereomicroscopy to verify the failure type. Data analysis was performed in SPSS V.16 using Kolmogorov-Smirnov test, independent-samples t-test, ANOVA, and Duncan's logistic regression test.In this study, a significant reduction was observed in the SBS rates of SB and S3 bond adhesive systems after storage with and without hydrophobic resin (p>0.000). Without storage in normal saline, a significant increase was observed in the SBS rate of the SE bond (p=0.013). In addition, SBS rate of SBMP significantly increased after storage with hydrophobic resin (p=0.001). Finally, the highest and lowest rates of SBS were observed in the SE and S3 bonds in all the experimental groups, respectively.The effects of using a hydrophobic resin layer on shear bond strength values seem to be effective. The mild self-etch adhesive exhibited the best resin-dentine bond strength after aging.

Dataset Information

Comparative Evaluation of shear Bond Strength of universal Dental Adhesives -An in vitro study.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets