Microstructural Analysis and Wear Performance of Carbon-Fiber-Reinforced SiC Composite for Brake Pads.

ABSTRACT: Carbon-fiber-reinforced silicon carbide (C/C-SiC) composite is widely used as a friction material owing to its good performance, even though it is more expensive than metallic materials. The light C/C-SiC composite is an ideal candidate for weight reduction of frictional parts. In this study, the friction and wear behavior of C/C-SiC composite was assessed using a ball-on-disk friction tester under dry reciprocating sliding conditions at different temperatures of 25, 100, and 200 °C. The disk specimens were made of C/C-SiC composite, while the mating counterpart pins were made of bearing steel. The microstructure and wear track of the specimens were characterized using a scanning electron microscopy (SEM) and Raman spectroscopy. The microstructural analysis of the wear track revealed that the wear mechanism was abrasive. The friction coefficient and wear behavior of the specimens was dependent on the temperature, where the friction coefficients and wear rate increased with increasing temperature.

SUBMITTER: Byeong-Choon G

PROVIDER: S-EPMC5551744 | biostudies-other | 2017 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Liquid-Phase Assisted Engineering of Highly Strong SiC Composite Reinforced by Multiwalled Carbon Nanotubes.

Project description:Despite the ultrahigh intrinsic strength of multiwalled carbon nanotube (MWCNT), the strengthening effect on ceramic matrix composite remains far from expectation mainly due to the weak load transfer between the reinforcement and ceramic matrix. With the assistance of the in situ pullout test, it is revealed that the liquid-phase sintering (LPS) can serve as a novel strategy to achieve effective load transfer in MWCNT reinforced ceramic matrix composites. The YAlO3 formed liquid phase during spark plasma sintering of SiC composite greatly facilitates radical elastic deformation of MWCNT, leading to highly increased interfacial shear strength (IFSS) as well as interlayer shear resistance (ISR) of nested walls. The liquid phase with superior wettability can even penetrate into the defects of MWCNT, which further increases the ISR of MWCNT. Moreover, the first-principles calculation indicates that the oxygen terminated YAlO3 phase displays much stronger bonding compared with SiC matrix, which is also responsible for the large IFSS in the composite. As a result, as high as 30% improvement of bending strength is achieved in the composite with only 3 wt% MWCNT in comparison to the monolithic ceramic, manifesting the unprecedented strengthening effect of MWCNT assisted by LPS.

| S-EPMC7610309 | biostudies-literature

Microstructural, Tribology and Corrosion Properties of Optimized Fe3O4-SiC Reinforced Aluminum Matrix Hybrid Nano Filler Composite Fabricated through Powder Metallurgy Method.

Project description:Hybrid reinforcement's novel composite (Al-Fe3O4-SiC) via powder metallurgy method was successfully fabricated. In this study, the aim was to define the influence of SiC-Fe3O4 nanoparticles on microstructure, mechanical, tribology, and corrosion properties of the composite. Various researchers confirmed that aluminum matrix composite (AMC) is an excellent multifunctional lightweight material with remarkable properties. However, to improve the wear resistance in high-performance tribological application, hardening and developing corrosion resistance was needed; thus, an optimized hybrid reinforcement of particulates (SiC-Fe3O4) into an aluminum matrix was explored. Based on obtained results, the density and hardness were 2.69 g/cm3, 91 HV for Al-30Fe3O4-20SiC, after the sintering process. Coefficient of friction (COF) was decreased after adding Fe3O4 and SiC hybrid composite in tribology behaviors, and the lowest COF was 0.412 for Al-30Fe3O4-20SiC. The corrosion protection efficiency increased from 88.07%, 90.91%, and 99.83% for Al-30Fe3O4, Al-15Fe3O4-30SiC, and Al-30Fe3O4-20SiC samples, respectively. Hence, the addition of this reinforcement (Al-Fe3O4-SiC) to the composite shows a positive outcome toward corrosion resistance (lower corrosion rate), in order to increase the durability and life span of material during operation. The accomplished results indicated that, by increasing the weight percentage of SiC-Fe3O4, it had improved the mechanical properties, tribology, and corrosion resistance in aluminum matrix. After comparing all samples, we then selected Al-30Fe3O4-20SiC as an optimized composite.

| S-EPMC7560354 | biostudies-literature

Interphase Engineering of a Cellulose-Based Carbon Fiber Reinforced Composite by Applying Click Chemistry.

Project description:Given our possible future dependence on carbon fiber reinforced composites, the introduction of a renewable matrix might be advantageous for the vision of a sustainable world. Cellulose is a superior green candidate and provides exceptional freedom in composite design as the free OH groups can be conveniently functionalized to give tailor-made materials. To obtain a high-performing carbon fiber reinforced cellulose propionate composite, we accurately tailored the interfacial adhesion by invoking click chemistry. The synthetic strategy involved grafting of a phenylacetylene structure onto the carbon fiber surface, onto which O-acylated 6-azido-6-deoxycellulose and a number of aromatic azides could be covalently attached. Single-fiber fragmentation tests indicated that the lipophilicity and size of the substituent on the deposited structure played a crucial role in determining molecular entanglement and mechanical interlocking effects, as penetration into the cellulose propionate matrix was of utmost importance. Enhanced interfacial shear strength was obtained for the carbon fiber covalently functionalized with the cellulose derivative. Nevertheless, the greatest increase was observed for the derivative substituted with a compact and highly lipophilic CF3 substituent. In a broader sense, our study provides a synthetic platform to bind cellulose derivatives to graphitic surfaces and paves the ways towards the preparation of innovative cellulose-based carbonaceous materials.

| S-EPMC6151626 | biostudies-literature

Carbon Nanotube Reinforced Structural Composite Supercapacitor.

Project description:Carbon nanotubes exhibit mechanical properties ideally suited for reinforced structural composites and surface area and conductivity attractive for electrochemical capacitors. Here we demonstrate the multifunctional synergy between these properties in a composite material exhibiting simultaneous mechanical and energy storage properties. This involves a reinforcing electrode developed using dense, aligned carbon nanotubes grown on stainless steel mesh that is layered in an ion conducting epoxy electrolyte matrix with Kevlar or fiberglass mats. The resulting energy storage composites exhibit elastic modulus over 5?GPa, mechanical strength greater than 85?MPa, and energy density up to 3?mWh/kg for the total combined system including electrodes, current collector, Kevlar or fiberglass, and electrolyte matrix. Furthermore, findings from in-situ mechano-electro-chemical tests indicate simultaneous mechanical and electrochemical functionality with invariant and stable supercapacitor performance maintained throughout the elastic regime.

| S-EPMC6281659 | biostudies-literature

Pullout Behavior of Bundled Aramid Fiber in Fiber-Reinforced Cementitious Composite.

Project description:The tensile performance of fiber-reinforced cementitious composite (FRCC) after first matrix cracking is characterized by a tensile stress-crack width relationship called the bridging law. The bridging law can be obtained by an integral calculus of forces carried by individual bridging fibers considering the effect of the fiber inclination angle. The main objective of this study is to investigate experimentally and evaluate the pullout behavior of a single aramid fiber, which is made with a bundling of original yarns of aramid fiber. The bundled aramid fiber has a nonsmooth surface, and it is expected to have good bond performance with the matrix. The test variables in the pullout test are the thickness of the matrix and the inclined angle of the fiber. From the test results, the pullout load-slip curves showed that the load increases lineally until maximum load, after which it decreases gradually. The maximum pullout load and slip at the maximum load increase as the embedded length of the fiber becomes larger. The pullout load-crack width relationship is modeled by a bilinear model, and the bridging law is calculated. The calculated result shows good agreement with the experimental curves obtained by the uniaxial tension test of aramid-FRCC.

| S-EPMC7179034 | biostudies-literature

Characterization and Effects of Fiber Pull-Outs in Hole Quality of Carbon Fiber Reinforced Plastics Composite.

Project description:Hole quality plays a crucial role in the production of close-tolerance holes utilized in aircraft assembly. Through drilling experiments of carbon fiber-reinforced plastic composites (CFRP), this study investigates the impact of varying drilling feed and speed conditions on fiber pull-out geometries and resulting hole quality parameters. For this study, hole quality parameters include hole size variance, hole roundness, and surface roughness. Fiber pull-out geometries are quantified by using scanning electron microscope (SEM) images of the mechanically-sectioned CFRP-machined holes, to measure pull-out length and depth. Fiber pull-out geometries and the hole quality parameter results are dependent on the drilling feed and spindle speed condition, which determines the forces and undeformed chip thickness during the process. Fiber pull-out geometries influence surface roughness parameters from a surface profilometer, while their effect on other hole quality parameters obtained from a coordinate measuring machine is minimal.

| S-EPMC5456610 | biostudies-other

Hybrid Effect Evaluation of Steel Fiber and Carbon Fiber on the Performance of the Fiber Reinforced Concrete.

Project description:Fiber reinforcement is an important method to enhance the performance of concrete. In this study, the compressive test and impact test were conducted, and then the hybrid effect between steel fiber (SF) and carbon fiber (CF) was evaluated by employing the hybrid effect index. Compressive toughness and impact toughness of steel fiber reinforced concrete (SFRC), carbon fiber reinforced concrete (CFRC) and hybrid fiber reinforced concrete (HFRC) were explored at steel fiber volume fraction 0.5%, 1%, 1.5% and carbon fiber 0.1%, 0.2%, 0.3%. Results showed that the addition of steel fiber and carbon fiber can increase the compressive strength. SF, CF and the hybridization between them could increase the compressive toughness significantly. The impact test results showed that as the volume of fiber increased, the impact number of the first visible crack and the ultimate failure also increased. The improvement of toughness mainly lay in improving the crack resistance after the first crack. Based on the test results, the positive hybrid effect of steel fiber and carbon fiber existed in hybrid fiber reinforced concrete. The relationship between the compressive toughness and impact toughness was also explored.

| S-EPMC5512526 | biostudies-other

Mitigation of Galvanic Corrosion in Bolted Joint of AZ31B and Carbon Fiber-Reinforced Composite Using Polymer Insulation.

Project description:The use of polymer insulation to mitigate galvanic corrosion was examined for bolted joints of AZ31B Mg alloy and carbon fiber-reinforced composite. To assess the corrosion behaviors of bolted joints with and without polymer insulation, solution immersion and salt spray exposure (ASTM B117) tests were conducted, and the corrosion depths and volumes were determined for the joint specimens after the tests. The polymer-insulated bolted joints exhibited much lower corrosion depths and volumes, highlighting the effective mitigation of galvanic corrosion. The reductions of joint strength in the post-corrosion joint specimens were relatively small (up to ~10%) in the polymer-insulated group but greater (up to 90%) in the group with no insulation. Cross-sectional characterization of post-corrosion joints with polymer insulation revealed local pits developed on AZ31B under galvanic influence, indicating that limited galvanic attack (that did not decrease the joining integrity significantly) could still occur during a long salt spray exposure (~1264 h) owing to the permeation of an aqueous corrosive medium.

| S-EPMC8036256 | biostudies-literature

On the Structural Performance of Recycled Aggregate Concrete Columns with Glass Fiber-Reinforced Composite Bars and Hoops.

Project description:Structural members comprising geopolymer recycled aggregate concrete (RAC) reinforced with glass fiber-reinforced polymer (GFRP) bars have not been investigated appropriately for axial compressive loading cases. The present study addresses this knowledge gap by evaluating the structural efficiency of GFRP-reinforced geopolymer recycled aggregate concrete (GGRAC)-based members subjected to axial compressive loading. A total of nine compressive members (250 mm in cross-section and 1150 mm in height) were constructed to examine the effect of the number of longitudinal GFRP bars and the vertical spacing of transverse GFRP hoops/ties. The experimental results portrayed that the ductility of GGRAC compressive members improved with the reduction in the pitch of GFRP hoops. The axial load-carrying capacity (LCC) of GGRAC compressive members increased by increasing the number of GFRP bars up to eight (corresponding to a reinforcement ratio of 2.11%) while it decreased by using ten longitudinal GFRP bars (corresponding to a reinforcement ratio of 2.65%). Additionally, an empirical model was suggested to predict the axial LCC of GGRAC compressive members based on a large amount of experimental data of similar members. The experimental results and related theoretical predictions substantially prove the applicability and accuracy of the proposed model. The proposed column represents a feasible structural member in terms of material availability and environmental sustainability.

| S-EPMC8125636 | biostudies-literature

Laser Ablation Mechanism and Performance of Carbon Fiber-Reinforced Poly Aryl Ether Ketone (PAEK) Composites.

Project description:The ablation mechanism and performance of carbon fiber (CF)-reinforced poly aryl ether ketone (PAEK) thermoplastic composites were studied in this paper. The results show that the ablation damaged area is controlled by the irradiation energy, while the mass loss rate is controlled by the irradiation power density. In the ablation center, the PAEK resin and CFs underwent decomposition and sublimation in an anaerobic environment. In the transition zone, the resin experienced decomposition and remelting in an aerobic environment, and massive char leaves were present in the cross section. In the heat-affected zone, only remelting of the resin was observed. The fusion and decomposition of the resin caused delamination and pores in the composites. Moreover, oxygen appeared crucial to the ablation morphology of CFs. In an aerobic environment, a regular cross section formed, while in an anaerobic environment, a cortex-core structure formed. The cortex-core structure of CF inside the ablation pit was caused by the inhomogeneity of fibers along the radial direction and the residual carbon layer generated by resin decomposition in an anoxic environment. The description of the ablation mechanism presented in this study broadens our understanding of damage evolution in thermoplastic composites subjected to high-energy CW laser irradiation.

| S-EPMC9269289 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data