Effect of Applied Stress on the Mechanical Properties of a Zr-Cu-Ag-Al Bulk Metallic Glass with Two Different Structure States.

ABSTRACT: In order to investigate the effect of applied stress on mechanical properties in metallic glasses, nanoindentation tests were conducted on elastically bent Zr-Cu-Ag-Al metallic glasses with two different structure states. From spherical P-h curves, elastic modulus was found to be independent on applied stress. Hardness decreased by ~8% and ~14% with the application of 1.5% tensile strain for as-cast and 650 K annealed specimens, while it was slightly increased at the compressive side. Yield stress could be obtained from the contact pressure at first pop-in position with a conversion coefficient. The experimental result showed a symmetrical effect of applied stress on strengthening and a reduction of the contact pressure at compressive and tensile sides. It was observed that the applied stress plays a negligible effect on creep deformation in as-cast specimen. While for the annealed specimen, creep deformation was facilitated by applied tensile stress and suppressed by applied compressive stress. Strain rate sensitivities (SRS) were calculated from steady-state creep, which were constant for as-cast specimen and strongly correlated with applied stress for the annealed one. The more pronounced effect of applied stress in the 650 K annealed metallic glass could be qualitatively explained through the variation of the shear transformation zone (STZ) size.

SUBMITTER: Chen H

PROVIDER: S-EPMC5551754 | biostudies-other | 2017 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Zirconium–Copper-based metallic glass thin films represent promising coatings in the biomedical sector for their combination of antibacterial property and wear resistance. However, finding a Zr–Cu metallic glass composition with desirable cytocompatibility and antibacterial property is extremely challenging. In this work, we have created a cytocompatible and (super-)hydrophobic Zr–Cu–Ag metallic glass coating with ≈95% antifouling properties. First, a range of different chemical compositions were prepared via Physical Vapor Deposition magnetron by co-sputtering Zr, Cu, and Ag onto a Polybutylene terephthalate (PBT) substrate among which Zr93·5Cu6·2Ag0.2, Zr76·7Cu22·7Ag0.5, and Zr69·3Cu30·1Ag0.6 were selected to be further investigate for their surface properties, antibacterial activity, and cytocompatibility. Scanning electron microscopy (SEM) images revealed a micro-roughness fibrous structure holding superhydrophobic properties demonstrated by specimens' static and dynamic contact angle measurements ranging from 130° to 150°. The dynamic contact angle measurements have shown hysteresis below 10° for all coated samples which indicated the superhydrophobicity of the samples. To distinguish between antifouling and bactericidal effect of the coating, ions release from coatings into Luria Bertani Broth (LB), and Dulbecco's Modified Eagle Medium (DMEM) solutions were evaluated by inductively coupled plasma mass spectrometry (ICP-MS) measurements after 24 h and 5 days. Antifouling properties were evaluated by infecting the specimens' surface with the Gram-positive Staphylococcus aureus and the Gram-negative Escherichia coli strain reporting a ≈95% reduction of bacteria adhesion as visually confirmed by FESEM and fluorescent live/dead staining. Human mesenchymal stem cells (hMSC) were used for direct cytocompatibility evaluation of coated samples and their metabolic activity was evaluated via relative fluorescence unit after 24 h and 5 days confirming that it was comparable to the controls (>97% viable cells). The results were further visualized by FESEM, fluorescent staining by Live/Dead Viability/Cytotoxicity Kit and confirmed the cytocompatibility of all coated samples. Finally, hMSC′ cytoplasm was stained by May Grunwald and Giemsa after 5days to detect and visualize the released ions which have diffused through the cells' membrane. Graphical abstract Image 1

Dataset Information

Effect of Applied Stress on the Mechanical Properties of a Zr-Cu-Ag-Al Bulk Metallic Glass with Two Different Structure States.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets