Effects of Grain Size on Ultrasonic Attenuation in Type 316L Stainless Steel.

ABSTRACT: A lead bismuth eutectic (LBE) spallation target will be installed in the Target Test Facility (TEF-T) in the Japan Proton Accelerator Research Complex (J-PARC). The spallation target vessel filled with LBE is made of type 316L stainless steel. However, various damages, such as erosion/corrosion damage and liquid metal embrittlement caused by contact with flowing LBE at high temperature, and irradiation hardening caused by protons and neutrons, may be inflicted on the target vessel, which will deteriorate the steel and might break the vessel. To monitor the target vessel for prevention of an accident, an ultrasonic technique has been proposed to establish off-line evaluation for estimating vessel material status during the target maintenance period. Basic R&D must be carried out to clarify the dependency of ultrasonic wave propagation behavior on material microstructures and obtain fundamental knowledge. As a first step, ultrasonic waves scattered by the grains of type 316L stainless steel are investigated using new experimental and numerical approaches in the present study. The results show that the grain size can be evaluated exactly and quantitatively by calculating the attenuation coefficient of the ultrasonic waves scattered by the grains. The results also show that the scattering regimes of ultrasonic waves depend heavily on the ratio of wavelength to average grain size, and are dominated by grains of extraordinarily large size along the wave propagation path.

SUBMITTER: Wan T

PROVIDER: S-EPMC5551796 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effect of nano-grain carbide formation on electrochemical behavior of 316L stainless steel.

Project description:The effect of low oxygen-partial pressured carburizing on relaxation process for 316L stainless steel is reported. Phase, morphology, and amount of compound formation during initial stage of carburizing are investigated using X-ray diffractometry (XRD) and X-ray photoelectron spectroscopy (XPS). The results show formation and development of surface multilayer with nano-grain-carbide (Cr7C3, Fe7C3, and/or Cr3C2) generation in the layer located below outermost protective layer. The relaxation process has been investigated using electrochemical impedance spectroscopy (EIS). Formation of nano-grain carbide(s) during carburizing causes deterioration effect on the electrochemical behavior of steel. However, the steel with large amount of carbide generation (carburized for 30 min) tends to have higher corrosion resistance (indicated by higher values of Rcl and Rct) than the smaller ones (10 and 20 min) due to the effect of phase, grain size, morphology, and amount of compound formation.

| S-EPMC8206347 | biostudies-literature

Stability research on polydopamine and immobilized albumin on 316L stainless steel.

Project description:In this study, the polydopamine (PDA) film was coated on polished 316Lss and then thermally treated at 150 °C (labeled as PDA-Th150), and the stability of coatings was also investigated. Straining test indicated that PDA-Th150 coating performed better in affording sufficient adherence to 316 L SS substrate. Moreover, both PDA and PDA-Th150 coating suffered slight swelling during immersion in deionized water (pH = 6.5). X-ray photoelectron spectroscopy results showed that during immersion, latent nucleophilic reaction via amines inside PDA coating occurred. This led to an enhanced cross-linking and thus gradually promoted the coating stability. Moreover, larger amount of bovine serum albumin (BSA) was immobilized onto PDA-Th150 coating and performed well in anti-platelet adhesion. A high retention of immobilized BSA was observed even after immersion for 30 days. These tests suggested that PDA was stable enough and performed well in surface functionalization, which might enrich the research and application of PDA.

| S-EPMC5043154 | biostudies-literature

Inhibition of Bacterial Adhesion on Nanotextured Stainless Steel 316L by Electrochemical Etching.

Project description:Bacterial adhesion to stainless steel 316L (SS316L), which is an alloy typically used in many medical devices and food processing equipment, can cause serious infections along with substantial healthcare costs. This work demonstrates that nanotextured SS316L surfaces produced by electrochemical etching effectively inhibit bacterial adhesion of both Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus, but exhibit cytocompatibility and no toxicity toward mammalian cells in vitro. Additionally, the electrochemical surface modification on SS316L results in formation of superior passive layer at the surface, improving corrosion resistance. The nanotextured SS316L offers significant potential for medical applications based on the surface structure-induced reduction of bacterial adhesion without use of antibiotic or chemical modifications while providing cytocompatibility and corrosion resistance in physiological conditions.

| S-EPMC5761049 | biostudies-literature

Functional Antimicrobial Surface Coatings Deposited onto Nanostructured 316L Food-Grade Stainless Steel.

Project description:In our study, we demonstrated the performance of antimicrobial coatings on properly functionalized and nanostructured 316L food-grade stainless steel pipelines. For the fabrication of these functional coatings, we employed facile and low-cost electrochemical techniques and surface modification processes. The development of a nanoporous structure on the 316L stainless steel surface was performed by following an electropolishing process in an electrolytic bath, at a constant anodic voltage of 40 V for 10 min, while the temperature was maintained between 0 and 10 °C. Subsequently, we incorporated on this nanostructure additional coatings with antimicrobial and bactericide properties, such as Ag nanoparticles, Ag films, or TiO2 thin layers. These functional coatings were grown on the nanostructured substrate by following electroless process, electrochemical deposition, and atomic layer deposition (ALD) techniques. Then, we analyzed the antimicrobial efficiency of these functionalized materials against different biofilms types (Candida parapsilosis, Escherichia coli, Pseudomonas aeruginosa, Staphylococcus aureus, and Staphylococcus epidermidis). The results of the present study demonstrate that the nanostructuring and surface functionalization processes constitute a promising route to fabricate novel functional materials exhibiting highly efficient antimicrobial features. In fact, we have shown that our use of an appropriated association of TiO2 layer and Ag nanoparticle coatings over the nanostructured 316L stainless steel exhibited an excellent antimicrobial behavior for all biofilms examined.

| S-EPMC8074267 | biostudies-literature

On the Strength of a 316L-Type Stainless Steel Subjected to Cold or Warm Rolling Followed by Annealing.

Project description:The ultrafine-grained microstructures and their effect on the yield strength of a 316L-type austenitic stainless steel processed by large strain cold/warm rolling and subsequent annealing were studied. A kind of continuous recrystallization developed during annealing, resulting in the evolution of uniform ultrafine-grained microstructures with relatively high residual dislocation densities. The development of such microstructure at 973 K led to excellent combination of tensile properties including high yield strength (?0.2 > 900 MPa) and satisfactory plasticity (? > 15%). A unique power law function between the annealed grain size and the dislocation density with a dislocation density exponent of -0.5 was obtained for these continuously recrystallized microstructures. A physically justified explanation of the observed structural/substructural strengthening is introduced.

| S-EPMC7254252 | biostudies-literature

Effect of Ultrasonic Nano-Crystal Surface Modification (UNSM) on the Passivation Behavior of Aged 316L Stainless Steel.

Project description:Stainless steels have good corrosion resistance in many environments but welding or aging can decrease their resistance. This work focused on the effect of aging time and ultrasonic nano-crystal surface modification on the passivation behavior of 316L stainless steel. In the case of slightly sensitized 316L stainless steel, increasing the aging time drastically decreased the pitting potential, increased the passive current density, and decreased the resistance of the passive film, even though aging did not form chromium carbide and a chromium depletion zone. This behavior is due to the micro-galvanic corrosion between the matrix and carbon segregated area, and this shows the importance of carbon segregation in grain boundaries to the pitting corrosion resistance of stainless steel, in addition to the formation of the chromium depletion zone. UNSM (Ultrasonic Nano Crystal Surface Modification)-treatment to the slightly sensitized 316L stainless steel increased the pitting potential, decreased the passive current density, and increased the resistance of the passive film. However, in the case of heavily sensitized 316L stainless steel, UNSM-treatment decreased the pitting potential, increased the passive current density, and decreased the resistance of the passive film. This behavior is due to the dual effects of the UNSM-treatment. That is, the UNSM-treatment reduced the carbon segregation, regardless of whether the stainless steel 316L was slightly or heavily sensitized. However, since this treatment made mechanical flaws in the outer surface in the case of the heavily sensitized stainless steel, UNSM-treatment may eliminate chromium carbide, and this flaw can be a pitting initiation site, and therefore decrease the pitting corrosion resistance.

| S-EPMC5551756 | biostudies-other

Reducing Staphylococcus aureus biofilm formation on stainless steel 316L using functionalized self-assembled monolayers.

Project description:Stainless steel 316L (SS316L) is a common material used in orthopedic implants. Bacterial colonization of the surface and subsequent biofilm development can lead to refractory infection of the implant. Since the greatest risk of infection occurs perioperatively, strategies that reduce bacterial adhesion during this time are important. As a strategy to limit bacterial adhesion and biofilm formation on SS316L, self-assembled monolayers (SAMs) were used to modify the SS316L surface. SAMs with long alkyl chains terminated with hydrophobic (-CH3) or hydrophilic (oligoethylene glycol) tail groups were used to form coatings and in an orthogonal approach, SAMs were used to immobilize gentamicin or vancomycin on SS316L for the first time to form an "active" antimicrobial coating to inhibit early biofilm development. Modified SS316L surfaces were characterized using surface infrared spectroscopy, contact angles, MALDI-TOF mass spectrometry and atomic force microscopy. The ability of SAM-modified SS316L to retard biofilm development by Staphylococcus aureus was functionally tested using confocal scanning laser microscopy with COMSTAT image analysis, scanning electron microscopy and colony forming unit analysis. Neither hydrophobic nor hydrophilic SAMs reduced biofilm development. However, gentamicin-linked and vancomycin-linked SAMs significantly reduced S. aureus biofilm formation for up to 24 and 48 h, respectively.

| S-EPMC3609649 | biostudies-literature

The Mechanisms of Inhibition Effects on Bubble Growth in He-Irradiated 316L Stainless Steel Fabricated by Selective Laser Melting.

Project description:The AISI 316L austenitic stainless steel fabricated by selective laser melting (SLM) is considered to have great prospects for applications in nuclear systems. This study investigated the He-irradiation response of SLM 316L, and several possible reasons for the improved He-irradiation resistance of SLM 316L were systematically revealed and evaluated by using TEM and related techniques. The results show that the effects of unique sub-grain boundaries have primary contributions to the decreased bubble diameter in SLM 316L compared to that in the conventional 316L counterpart, while the effects of oxide particles on bubble growth are not the dominant factor in this study. Moreover, the He densities inside the bubbles were carefully measured using electron energy loss spectroscopy (EELS). The mechanism of stress-dominated He densities in bubbles was validated, and the corresponding reasons for the decrease in bubble diameter were freshly proposed in SLM 316L. These insights help to shed light on the evolution of He bubbles and contribute to the ongoing development of the steels fabricated by SLM for advanced nuclear applications.

| S-EPMC10253493 | biostudies-literature

Dataset of the synthesis parameters to deposit YSZ on stainless steel AISI 316L by sputtering technique.

Project description:The data presented in this article are related to the research previously published "improvement of adhesion and barrier properties of biomedical stainless steel by deposition of YSZ coatings using RF magnetron sputtering". It contains the structural, morphological, compositional and electrochemical characterization of bare AISI 316L substrate which was used as a substrate to coat with yttria-stabilized zirconia (YSZ). The chemical composition and topography analyses from X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and micrographs from atomic force microscopy (AFM) as well as the roughness value of the YSZ-sputtered coating on AISI 316L substrates are presented as complementary data of the article.

| S-EPMC6811928 | biostudies-literature

Tribological Behavior of the 316L Stainless Steel with Heterogeneous Lamella Structure.

Project description:In this paper, the tribological behavior of 316L stainless steel with heterogeneous lamella structure (HLS), prepared through 85% cold rolling technology and subsequent annealing treatment (750 °C, 10 min), were conducted on a ball-on-disc tribometer under different normal loads in dry ambient air conditions. The morphologies, structures, and compositions of the raw and worn surfaces were analyzed by 3D surface profilometer, XRD, SEM, EDS and TEM. Based on this, the results showed that the HLS 316L stainless steel samples exhibited lower and more steady friction coefficients than coarse-grained samples, especially under higher loads, which can be attributed to the existence of numerous oxidative particles across sliding interfaces. However, the wear resistance of HLS 316L stainless steel sample was a little weakened compared to that of the coarse-grained sample under a normal load of 5 N. When the load increases up to 15 N, an obviously decreased wear resistance was found for the HLS of the 316L stainless steel sample, which was 50% lower than that of coarse-grained sample. This can be ascribed to the more severe oxidative and abrasive wear performance of HLS 316L stainless steel sample under dry sliding conditions.

| S-EPMC6213424 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data