Mechanical Behavior of Stainless Steel Fiber-Reinforced Composites Exposed to Accelerated Corrosion.

ABSTRACT: Recent advancements in metal fibers have introduced a promising new type of stainless steel fiber with high stiffness, high failure strain, and a thickness < 100 μm (<0.00394 in.) that can be utilized in a steel fiber-reinforced polymer. However, stainless steel is known to be susceptible to pitting corrosion. The main goal of this study is to compare the impact of corrosion on the mechanical properties of steel fiber-reinforced composites with those of conventional types of stainless steel. By providing experimental evidences, this study may promote the application of steel fiber-reinforced composite as a viable alternative to conventional metals. Samples of steel fiber-reinforced polymer and four different types of stainless steel were subjected to 144 and 288 h of corrosion in ferric chloride solution to simulate accelerated corrosion conditions. The weight losses due to corrosion were recorded. The corroded and control samples were tested under monotonic tensile loading to measure the ultimate stresses and strains. The effect of corrosion on the mechanical properties of the different materials was evaluated. The digital image correlation (DIC) technique was used to investigate the failure mechanism of the corrosion-damaged specimens. Overall, steel fiber-reinforced composites had the greatest corrosion resistance.

SUBMITTER: O'Brien C

PROVIDER: S-EPMC5551815 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Mechanical Characterization of High-Performance Steel-Fiber Reinforced Cement Composites with Self-Healing Effect.

Project description:The crack self-healing behavior of high-performance steel-fiber reinforced cement composites (HPSFRCs) was investigated. High-strength deformed steel fibers were employed in a high strength mortar with very fine silica sand to decreasing the crack width by generating higher interfacial bond strength. The width of micro-cracks, strongly affected by the type of fiber and sand, clearly produced the effects on the self-healing behavior. The use of fine silica sand in HPSFRCs with high strength deformed steel fibers successfully led to rapid healing owing to very fine cracks with width less than 20 µm. The use of very fine silica sand instead of normal sand produced 17%-19% higher tensile strength and 51%-58% smaller width of micro-cracks.

| S-EPMC5453159 | biostudies-literature

Corrosion Behavior of AISI 304 Stainless Steel Reinforcements in SCBA-SF Ternary Ecological Concrete Exposed to MgSO4.

Project description:In this study, ternary ecological concrete (TEC) mixtures were produced with partial substitution of the ordinary Portland cement (OPC) by 10%, 20%, and 30% of sugar cane bagasse ash (SCBA) and silica fume (SF); a control mixture (100% OPC) was prepared according to ACI 211.1 standard. The studied TEC specimens were reinforced with AISI 304 stainless steel and AISI 1018 carbon steel rebars. TEC reinforced specimens were immersed in two different electrolytes, a control (DI-water) and 3.5 wt.% MgSO4 solution, for 180 days. The electrochemical corrosion was monitored by corrosion potential (Ecorr) according to ASTM C-876-15 standard, and the linear polarization resistance (LPR) technique using ASTM G59 standard. The Ecorr and current density icorr results show that AISI 304 stainless steel rebars have a high corrosion resistance, with icorr values below 0.1 µA/cm2, which is interpreted as a level of negligible corrosion. The best corrosion performance was found for the TEC mixture made with a 20% addition of blend of sugar cane bagasse ash-silica fume (SCBA-SF) to the OPC.

| S-EPMC7288276 | biostudies-literature

Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites.

Project description:Metallic glass-reinforced metal matrix composites are an emerging class of composite materials. The metallic nature and the high mechanical strength of the reinforcing phase offers unique possibilities for improving the engineering performance of composites. Understanding the structure at the amorphous/crystalline interfaces and the deformation behavior of these composites is of vital importance for their further development and potential application. In the present work, Zr-based metallic glass fibers have been introduced in Al7075 alloy (Al-Zn-Mg-Cu) matrices using spark plasma sintering (SPS) producing composites with low porosity. The addition of metallic glass reinforcements in the Al-based matrix significantly improves the mechanical behavior of the composites in compression. High-resolution TEM observations at the interface reveal the formation of a thin interdiffusion layer able to provide good bonding between the reinforcing phase and the Al-based matrix. The deformation behavior of the composites was studied, indicating that local plastic deformation occurred in the matrix near the glassy reinforcements followed by the initiation and propagation of cracks mainly through the matrix. The reinforcing phase is seen to inhibit the plastic deformation and retard the crack propagation. The findings offer new insights into the mechanical behavior of metal matrix composites reinforced with metallic glasses.

| S-EPMC4828712 | biostudies-literature

Mechanical and Tribological Behavior of Functionally Graded Unidirectional Glass Fiber-Reinforced Epoxy Composites.

Project description:This paper aims to assess experimentally the mechanical and tribological behavior of conventional and functionally graded (FG) polymeric matrix composites reinforced with continuous glass fibers. The small punch test (SPT) and a pin-on-disc device were used in the present work to examine the mechanical and wear behavior, respectively. The hand lay-up technique was used in the present investigation to manufacture the conventional and FG composites. Various wooden looms with different nailed spacing were employed to manufacture the FG composites. According to test type, the FG composite is composed of four and ten layers, with a different glass fiber volume of fraction (Vf%) for each layer. In addition, the finite element simulation based on Hashin's failure criterion and cohesive zone modeling was used to show the progressive failure and give more explanation regarding the flexural behavior of such composites. The present results indicate that the wear rate of an FG composite could be affected by many factors, including the disk speed, applied load, the composite layers number, and average glass fiber volume fraction. On the other hand, the arrangement of layers in the composite materials by variation of Vf% for each layer can improve the wear rate and value of the ultimate load before the fracture of the composite material when subjected to SPT. The experimental and numerical results for all SPT specimens showed that the fracture of the SPT specimens began beneath the punch tip and grew along the fiber direction. The ultimate flexural capacity of FG composites increased by 30% compared with the conventional composites.

| S-EPMC9147567 | biostudies-literature

Mechanical Behavior of Steel Fiber-Reinforced Concrete Beams Bonded with External Carbon Fiber Sheets.

Project description:This study investigates the mechanical behavior of steel fiber-reinforced concrete (SFRC) beams internally reinforced with steel bars and externally bonded with carbon fiber-reinforced polymer (CFRP) sheets fixed by adhesive and hybrid jointing techniques. In particular, attention is paid to the load resistance and failure modes of composite beams. The steel fibers were used to avoiding the rip-off failure of the concrete cover. The CFRP sheets were fixed to the concrete surface by epoxy adhesive as well as combined with various configurations of small-diameter steel pins for mechanical fastening to form a hybrid connection. Such hybrid jointing techniques were found to be particularly advantageous in avoiding brittle debonding failure, by promoting progressive failure within the hybrid joints. The use of CFRP sheets was also effective in suppressing the localization of the discrete cracks. The development of the crack pattern was monitored using the digital image correlation method. As revealed from the image analyses, with an appropriate layout of the steel pins, brittle failure of the concrete-carbon fiber interface could be effectively prevented. Inverse analysis of the moment-curvature diagrams was conducted, and it was found that a simplified tension-stiffening model with a constant residual stress level at 90% of the strength of the SFRC is adequate for numerically simulating the deformation behavior of beams up to the debonding of the CFRP sheets.

| S-EPMC5554047 | biostudies-other

Corrosion Behavior and In Vitro Cytotoxicity of Ni-Ti and Stainless Steel Arch Wires Exposed to Lysozyme, Ovalbumin, and Bovine Serum Albumin.

Project description:In this study, the tendency and mechanisms by which protein and mechanical loads contribute to corrosion were determined by exposing Ni-Ti and stainless steel arch wires under varying mechanical loads to artificial saliva containing different types of protein (lysozyme, ovalbumin, and bovine serum albumin). The corrosion behavior and in vitro cytotoxicity results show that exposure to both protein and mechanical stress significantly decreased the corrosion resistance of stainless steel and increased the release of toxic corrosion products. Adding protein inhibited the corrosion of Ni-Ti, but the mechanical loads counteracted this effect. Even proteins containing the same types of amino acids had different effects on the corrosion resistance of the same alloy. The effect of protein or stress, or their combination, should be considered in the application of metal medical materials.

| S-EPMC7408227 | biostudies-literature

Heteroatom Modification Enhances Corrosion Durability in High-Mechanical-Performance Graphene-Reinforced Aluminum Matrix Composites.

Project description:The antagonism between strength and corrosion resistance in graphene-reinforced aluminum matrix composites is an inherent challenge to designing reliable structural components. Heteroatom microstructural modification is highly appreciated to conquer the obstacle. Here, a bottom-up strategy to exploit the heterogeneous phase interface to enable high corrosion durability is proposed. Deformation-driven metallurgy derived from severe plastic deformation is developed to produce Mg-alloyed fluorinated graphene structures with homogeneous dispersion. These structures allow for absorbing corrosion products, forming a dense protective layer against corrosion, and local micro-tuning of the suppression of charge transfer. This results in superior corrosion resistance with an outstanding strength-ductility balance of the composites via ultrafine-grained and precipitation strengthening. The anti-corrosion polarization resistance remains 89% of the initial state after 2-month immersion in chloride-containing environment, while the ultra-tensile strength and elongation of 532 ± 39 MPa and 17.3 ± 1.2% are obtained. The economical strategy of heteroatom modification broadens the horizon for anti-corrosion engineering in aluminum matrix composites, which is critical for the design of carbonaceous nanomaterial-reinforced composites to realize desired performances for practical applications.

| S-EPMC9376822 | biostudies-literature

Carbon Fiber Reinforced Recycled Polypropylene/Polyolefin Elastomer Composites with High Mechanical Properties.

Project description:The treatment of waste plastics has gradually become a hot topic in the current scientific community. In response to the needs for high-impact performance R-PP-based composites, carbon fiber (CF)-reinforced polyolefin elastomer (POE)/recycled polypropylene (R-PP) composite (CF/POE/R-PP) was prepared by the mechanical blending method, and its mechanical and thermal properties were systematically studied. It was found that the CF could effectively improve the bending and notch impact strength as well as enhance the thermal stability of POE/R-PP. Furthermore, a stable and dispersed composite interface formed by the combination of maleic anhydride-grafted polypropylene (PP-g-MAH) with the surface of CF and the fusion alkyl chains in R-PP and POE further enhanced the CF's reinforcing effect. As a result, the addition of 9 wt.% CF successfully improved the heat resistance of the composite material, and the residual carbon content increased by 97.84% after sintering. The composite toughening of POE and CF effectively improved the impact strength of the composite material, with a maximum increase of over 1000%. This study ultimately resulted in a high-impact-resistant composite material.

| S-EPMC11013364 | biostudies-literature

Aramid Pulp Reinforced Clay Aerogel Composites: Mechanical, Thermal and Combustion Behavior.

Project description:In this work, we reported that aramid pulps (AP) reinforced clay aerogel composites with improved mechanical strength, good thermal insulation and fire resistance based on the combination of AP, Poly(vinyl alcohol) (PVA) and sodium montmorillonite (MMT), which present a promising prospect in the thermal insulation application. The PVA-MMT-APx (x: denotes the mass content of AP) aerogel composites present an isotropic "lamella-honeycomb" porous structure, which endows them with excellent comprehensive performance. With the AP content increasing, the extremely low density is kept, ranging between 67-73 mg/cm3, and the low thermal conductivity is maintained within 40.9-47.9 mW·m-1·K-1. The mechanical strength is significantly improved with the maximum compressive modulus increasing from 2.95 to 5.96 MPa and the specific modulus rising from 44.03 to 81.64 MPa∙cm3/g. Their detailed heat transfer process has been analyzed, which provides a deep understanding to the low thermal conductivity of the PVA-MMT-APx aerogel composites. Based on the combination of thermogravimetric analysis and combustion behavior, the PVA-MMT-APx aerogel composites are demonstrated to possess improved thermal stability and fire resistance. This study puts forward a facile approach to utilizing AP to reinforce clay aerogel composites, which provides new insight into the development of thermal-insulating, fire-safe and high-strength thermal insulation materials.

| S-EPMC9601384 | biostudies-literature

Dataset on mechanical properties of natural fiber reinforced polyester composites for engineering applications.

Project description:This dataset comprises the mechanical properties of sisal, sorghum bicolor and coconut coir reinforced polyester composites. The mechanical dataset illustrates the tensile, flexural, impact and hardness strength of natural fiber composites by varying the weight percentages from 5 to 25 wt.% of sorghum bicolor and coconut coir. The composites samples were fabricated by hand layup process. The mechanical properties were determined from in-plane tensile, flexural, impact and hardness of the natural composites. The dataset here helps the readers to understand the important properties of the natural fibres reinforced polyester composites. However, it is revealed that the addition of sisal and coconut coir fiber can enhance the properties.

| S-EPMC6953528 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data