Creep Behavior of High-Strength Concrete Subjected to Elevated Temperatures.

ABSTRACT: Strain is generated in concrete subjected to elevated temperatures owing to the influence of factors such as thermal expansion and design load. Such strains resulting from elevated temperatures and load can significantly influence the stability of a structure during and after a fire. In addition, the lower the water-to-binder (W-B) ratio and the smaller the quantity of aggregates in high-strength concrete, the more likely it is for unstable strain to occur. Hence, in this study, the compressive strength, elastic modulus, and creep behavior were evaluated at target temperatures of 100, 200, 300, 500, and 800 °C for high-strength concretes with W-B ratios of 30%, 26%, and 23%. The loading conditions were set as non-loading and 0.33fcu. It was found that as the compressive strength of the concrete increased, the mechanical characteristics deteriorated and transient creep increased. Furthermore, when the point at which creep strain occurred at elevated temperatures after the occurrence of transient creep was considered, greater shrinkage strain occurred as the compressive strength of the concrete increased. At a heating temperature of 800 °C, the 80 and 100 MPa test specimens showed creep failure within a shrinkage strain range similar to the strain at the maximum load.

SUBMITTER: Yoon M

PROVIDER: S-EPMC5551824 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Creep behavior of reinforced concrete-filled steel tubular columns under axial compression.

Project description:The reinforced concrete-filled steel tube (RCFST) column solves several of the problems of the concrete-filled steel tube (CFST) column in practical engineering applications. Moreover, RCFST has a simple joint structure, high bearing capacity, good ductility, and superior fire resistance. From a structural safety perspective, designers prioritize the creep performance of CFST members in structural design. Therefore, the creep behavior of RCFST columns should be thoroughly investigated in practical engineering design. To study the influence of the creep behavior of RCFST columns under axial compression, this work analyzed the mechanical behavior of composite columns based on their mechanical characteristics under axial compression and established a creep formula suitable for RCFST columns under axial compression. A creep analysis program was also developed to obtain the creep strain-time curve, and its correctness was verified by existing tests. On this basis, the effects of the main design parameters, such as the stress level, steel ratio, and reinforcement ratio, on the creep behavior were determined and analyzed. The creep of the tested composite columns increased rapidly in the early stages (28 days) of load action; the growth rate was relatively low after 28 days and tended to stabilize after approximately six months. The stress level had the greatest influence on the creep of RCFST columns under axial compression, followed by the steel ratio. The influence of the reinforcement ratio on the creep behavior was less. The results of this study can provide a reference for engineering practice.

| S-EPMC8452051 | biostudies-literature

Effect of Aggregate Size on Strength Characteristics of High Strength Lightweight Concrete.

Project description:Effects of aggregate size on the mechanical properties of lightweight concrete (LC) were investigated. Four gradings of lightweight aggregate (LWA) were designed and used to prepare the specimens for compressive strength, splitting tensile strength, and flexural strength tests. An estimating method for compressive strength of LC was then established. The compressive strength of tested LC was up to 95 MPa at 90-day curing time. The test results suggested that the absence of medium-size particles decreased the compaction of LC, therefore the density and compressive strength were negatively affected. Specimens having single size of aggregate showed lower splitting tensile and flexural strengths than that having three sizes of LWA. The parameters of the estimating model were determined according to the test results, and the compressive strength predictions of estimation model were compared with the results from other literature.

| S-EPMC7143055 | biostudies-literature

Thermodynamics and Chemical Behavior of Uranyl Superoxide at Elevated Temperatures

Project description:Understanding the

| S-EPMC9928197 | biostudies-literature

Spalling Resistance of Fiber-Reinforced Ultra-High-Strength Concrete Subjected to the ISO-834 Standard Fire Curve: Effects of Thermal Strain and Water Vapor Pressure.

Project description:The prevention and mitigation of spalling in high-strength concrete (HSC) rely on mixing polypropylene (PP) as an additive reinforcement. The dense internal structures of ultra-high-strength concrete (UHSC) result in risks associated with a high thermal stress and high water vapor pressure. Herein, the effects of pore formation and thermal strain on spalling are examined by subjecting fiber-laden UHSC to conditions similar to those under which the ISO-834 standard fire curve was obtained. Evaluation of the initial melting properties of the fibers based on thermogravimetric analysis (TGA) and differential thermal analysis (DTA) demon strated that although nylon fibers exhibit a higher melting point than polypropylene and polyethylene fibers, weight loss occurs below 200 °C. Nylon fibers were effective at reducing spalling in UHSC compared to polypropylene and polyethylene fibers as they rapidly melt, leading to pore formation. We anticipate that these results will serve as references for future studies on the prevention of spalling in fiber-reinforced UHSC.

| S-EPMC7503885 | biostudies-literature

Effect of Elevated Temperature on Compressive Strength and Physical Properties of Neem Seed Husk Ash Concrete.

Project description:High temperature rise mostly caused by a fire outbreak is currently becoming a threat that endangers concrete's structural performance for buildings and the safety of occupants. The behavior of concrete after fire subjection has been of much interest for the structural materials design purposes. This study investigated the physical properties and the compressive strength of M25 concrete incorporating Neem Seed Husk Ash (NSHA), exposed to and through targeted different levels of temperature (200 °C to 800 °C) for a period of three hours in an electric furnace. The NSHA was produced by calcining neem seed husks at 800 °C for six hours and then sieved through the 125 ?m sieve. Different amounts of NSHA were investigated while considering the plain concrete as the control sample. 150 concrete cubes of 150 mm sizes were cast and properly cured for 7 and 28 days. The experimental results show that the compressive strength of the 5% NSHA concrete exposed to temperatures up to 400 °C is 21.3% and 23.8% better than the normal concrete at 7 and 28 curing days, respectively. Surface cracks and spalling are noticeable at 600 °C and 800 °C for all samples considered in this study.

| S-EPMC7085068 | biostudies-literature

Composite Behavior of Insulated Concrete Sandwich Wall Panels Subjected to Wind Pressure and Suction.

Project description:A full-scale experimental test was conducted to analyze the composite behavior of insulated concrete sandwich wall panels (ICSWPs) subjected to wind pressure and suction. The experimental program was composed of three groups of ICSWP specimens, each with a different type of insulation and number of glass-fiber-reinforced polymer (GFRP) shear grids. The degree of composite action of each specimen was analyzed according to the load direction, type of the insulation, and number of GFRP shear grids by comparing the theoretical and experimental values. The failure modes of the ICSWPs were compared to investigate the effect of bonds according to the load direction and type of insulation. Bonds based on insulation absorptiveness were effective to result in the composite behavior of ICSWP under positive loading tests only, while bonds based on insulation surface roughness were effective under both positive and negative loading tests. Therefore, the composite behavior based on surface roughness can be applied to the calculation of the design strength of ICSWPs with continuous GFRP shear connectors.

| S-EPMC5455426 | biostudies-other

Toward High Selectivity Aniline Synthesis Catalysis at Elevated Temperatures

Project description:In

| S-EPMC8802303 | biostudies-literature

Predicting Ultra-High-Performance Concrete Compressive Strength Using Tabular Generative Adversarial Networks.

Project description:There have been abundant experimental studies exploring ultra-high-performance concrete (UHPC) in recent years. However, the relationships between the engineering properties of UHPC and its mixture composition are highly nonlinear and difficult to delineate using traditional statistical methods. There is a need for robust and advanced methods that can streamline the diverse pertinent experimental data available to create predictive tools with superior accuracy and provide insight into its nonlinear materials science aspects. Machine learning is a powerful tool that can unravel underlying patterns in complex data. Accordingly, this study endeavors to employ state-of-the-art machine learning techniques to predict the compressive strength of UHPC using a comprehensive experimental database retrieved from the open literature consisting of 810 test observations and 15 input features. A novel approach based on tabular generative adversarial networks was used to generate 6513 plausible synthetic data for training robust machine learning models, including random forest, extra trees, and gradient boosting regression. While the models were trained using the synthetic data, their ability to generalize their predictions was tested on the 810 experimental data thus far unknown and never presented to the models. The results indicate that the developed models achieved outstanding predictive performance. Parametric studies using the models were able to provide insight into the strength development mechanisms of UHPC and the significance of the various influential parameters.

| S-EPMC7663629 | biostudies-literature

Thermal Creep Behavior and Creep Crystallization of Al-Mg-Si Aluminum Alloys.

Project description:The experimental temperature is 613.15~763.15 K, and the strain rate is 0.01~10 s-1. The hot compression creep test of the 6082-T6 aluminum alloy sample is carried out by Gleeble-3500 hot compression simulation compressor, and its creep behavior is studied by scanning electron microscope. The results show that the DRX crystal has an irregular shape and that content of the Mg phase, Si phase, and Mn phase in the crystal are the main factors to change the color of DRX crystal. Temperature and strain rate are important factors affecting dynamic recrystallization. Reducing temperature and increasing strain rate will weaken dynamic recrystallization, and DRX critical condition and peak stress (strain) will increase. The constitutive equation of hot creep of 6082 aluminum alloy was established by introducing the work hardening rate-rheological stress curve, and the relationship between DRX critical condition, peak stress (strain) and parameter Z during creep was explored. Based on the Av rami equation, the prediction equation of the DRX volume fraction is established. With the increase of strain, DRX volume fraction is characterized by slow increase, then rapid increase and then slowly increase. In the hot -forming extrusion process of 6082 aluminum alloy, according to the volume fraction prediction equation, the DRX can be reduced, and the internal structure of the material can be optimized by changing the extrusion conditions and particle size.

| S-EPMC9692693 | biostudies-literature

Effect of surrogate aggregates on the thermal conductivity of concrete at ambient and elevated temperatures.

Project description:The accurate assessment of the thermal conductivity of concretes is an important part of building design in terms of thermal efficiency and thermal performance of materials at various temperatures. We present an experimental assessment of the thermal conductivity of five thermally insulated concrete specimens made using lightweight aggregates and glass bubbles in place of normal aggregates. Four different measurement methods are used to assess the reliability of the thermal data and to evaluate the effects of the various sensor types. The concrete specimens are also assessed at every 100 °C during heating to ~800 °C. Normal concrete is shown to have a thermal conductivity of ~2.25 W m(-1) K(-1). The surrogate aggregates effectively reduce the conductivity to ~1.25 W m(-1) K(-1) at room temperature. The aggregate size is shown not to affect thermal conduction: fine and coarse aggregates each lead to similar results. Surface contact methods of assessment tend to underestimate thermal conductivity, presumably owing to high thermal resistance between the transducers and the specimens. Thermogravimetric analysis shows that the stages of mass loss of the cement paste correspond to the evolution of thermal conductivity upon heating.

| S-EPMC3947845 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data