Synthesis and Properties of Carbon Nanotube-Grafted Silica Nanoarchitecture-Reinforced Poly(Lactic Acid).

ABSTRACT: A novel nanoarchitecture-reinforced poly(lactic acid) (PLA) nanocomposite was prepared using multi-walled carbon nanotube (MWCNT)-grafted silica nanohybrids as reinforcements. MWCNT-grafted silica nanohybrids were synthesized by the generation of silica nanoparticles on the MWCNT surface through the sol-gel technique. This synthetic method involves organo-modified MWCNTs that are dispersed in tetrahydrofuran, which incorporates tetraethoxysilane that undergoes an ultrasonic sol-gel process. Gelation yielded highly dispersed silica on the organo-modified MWCNTs. The structure and properties of the nanohybrids were established using 29Si nuclear magnetic resonance, Raman spectroscopy, wide-angle X-ray diffraction, thermogravimetric analysis, and transmission electron microscopy. The resulting MWCNT nanoarchitectures were covalently assembled into silica nanoparticles, which exhibited specific and controllable morphologies and were used to reinforce biodegradable PLA. The tensile strength and the heat deflection temperature (HDT) of the PLA/MWCNT-grafted silica nanocomposites increased when the MWCNT-grafted silica was applied to the PLA matrix; by contrast, the surface resistivity of the PLA/MWCNT-grafted silica nanocomposites appeared to decline as the amount of MWCNT-grafted silica in the PLA matrix increased. Overall, the reinforcement of PLA using MWCNT-grafted silica nanoarchitectures was efficient and improved its mechanical properties, heat resistance, and electrical resistivity.

SUBMITTER: Hsu YW

PROVIDER: S-EPMC5551872 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Biodegradable Poly (lactic acid)/ Poly (ethylene glycol) Reinforced Multi-Walled Carbon Nanotube Nanocomposite Fabrication, Characterization, Properties, and Applications.

Project description:This paper presents the electromagnetic interference properties of multi-walled carbon nanotubes (MWCNTs) as a novel nano-reinforcement filler in poly (lactic acid) (PLA)/poly (ethylene glycol) (PEG) polymer matrix that was prepared via melt blending mode. Plasticization of PLA was first carried out by PEG, which overcomes its brittleness problem, in order to enhance its flexibility. A waveguide adapter technique was used to measure the dielectric properties ?r, and S-parameters reflection (S11) and transmission (S21) coefficients. The dielectric properties, microwave attenuation performances, and electromagnetic interference shielding effectiveness (EMISE) for all the material under test have been calculated over the full X-Band (8-12 GHz) due to its importance for military and commercial applications. The prepared samples were studied while using X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Fourier transforms infrared spectroscopy (FTIR), mechanical properties measurements, as well as thermogravimetric analysis (TGA). The results showed that the dielectric properties increased with increased multi-walled carbon nanotubes (MWCNTs) filler, as well as the shielding effectiveness of the MWCNT/PLA/PEG nanocomposites increased with the increasing of MWCNTs. The highest SE total value was found to be 42.07 dB at 12 GHz for 4 wt% filler content. It is also observed that the attenuation values of the nanocomposites increased with an increase in MWCNTs loading, as well as the power loss values for all of the samples increased with the increase in MWCNTs loading, except the amount of the transmitted wave through the nanocomposites.

| S-EPMC7077650 | biostudies-literature

Synthesis of Poly(methacrylic acid-co-butyl acrylate) Grafted onto Functionalized Carbon Nanotube Nanocomposites for Drug Delivery.

Project description:Design of a smart drug delivery system is a topic of current interest. Under this perspective, polymer nanocomposites (PNs) of butyl acrylate (BA), methacrylic acid (MAA), and functionalized carbon nanotubes (CNTsf) were synthesized by in situ emulsion polymerization (IEP). Carbon nanotubes were synthesized by chemical vapor deposition (CVD) and purified with steam. Purified CNTs were analyzed by FE-SEM and HR-TEM. CNTsf contain acyl chloride groups attached to their surface. Purified and functionalized CNTs were studied by FT-IR and Raman spectroscopies. The synthesized nanocomposites were studied by XPS, 13C-NMR, and DSC. Anhydride groups link CNTsf to MAA-BA polymeric chains. The potentiality of the prepared nanocomposites, and of their pure polymer matrices to deliver hydrocortisone, was evaluated in vitro by UV-VIS spectroscopy. The relationship between the chemical structure of the synthesized nanocomposites, or their pure polymeric matrices, and their ability to release hydrocortisone was studied by FT-IR spectroscopy. The hydrocortisone release profile of some of the studied nanocomposites is driven by a change in the inter-associated to self-associated hydrogen bonds balance. The CNTsf used to prepare the studied nanocomposites act as hydrocortisone reservoirs.

| S-EPMC7923197 | biostudies-literature

Uniformly Dispersed Poly(lactic acid)-Grafted Lignin Nanoparticles Enhance Antioxidant Activity and UV-Barrier Properties of Poly(lactic acid) Packaging Films.

Project description:Poly(lactic acid) (PLA) represents one of the most widely used biodegradable polymers for food packaging applications. While this material provides many advantages, it is characterized by limited antioxidant and UV-barrier properties. Blending PLA with lignin is an attractive strategy to address these limitations. Lignin possesses antioxidant properties and absorbs UV-light and is a widely available low value byproduct of the paper and pulp industry. This study has explored the use of lignin nanoparticles to augment the properties of PLA-based films. A central challenge in the preparation of PLA-lignin nanoparticle blend films is to avoid nanoparticle aggregation, which could compromise optical properties as well as antioxidant activity, among others. To avoid nanoparticle aggregation in the PLA matrix, PLA-grafted lignin nanoparticles were prepared via organocatalyzed lactide ring-opening polymerization. In contrast to lignin and unmodified lignin nanoparticles, these PLA-grafted lignin nanoparticles could be uniformly dispersed in PLA for lignin contents up to 10 wt %. The addition of as little as the equivalent of 1 wt % of lignin of these nanoparticles effectively blocked transmission of 280 nm UV-light. At the same time, these blend films retained reasonable visible light transmittance. The optical properties of the PLA lignin blend films also benefited from the well-dispersed nature of the PLA-grafted nanoparticles, as evidenced by significantly higher visible light transmittance of blends of PLA and PLA-grafted nanoparticles, as compared to blends prepared from PLA with lignin or unmodified lignin nanoparticles. Finally, blending PLA with PLA-grafted lignin nanoparticles greatly augments the antioxidant activity of these films.

| S-EPMC9274615 | biostudies-literature

Enhanced durability of carbon nanotube grafted hierarchical ceramic microfiber-reinforced epoxy composites.

Project description:As carbon nanotube (CNT) infused hybrid composites are increasingly identified as next-generation aerospace materials, it is vital to evaluate their long-term structural performance under aging environments. In this work, the durability of hierarchical, aligned CNT grafted aluminoborosilicate microfiber-epoxy composites (CNT composites) are compared against baseline aluminoborosilicate composites (baseline composites), before and after immersion in water at 25 °C (hydro) and 60 °C (hydrothermal), for extended durations (90 d and 180 d). The addition of CNTs is found to reduce water diffusivities by approximately 1.5 times. The mechanical properties (bending strength and modulus) and the damage sensing capabilities (DC conductivity) of CNT composites remain intact regardless of exposure conditions. The baseline composites show significant loss of strength (44 %) after only 15 d of hydrothermal aging. This loss of mechanical strength is attributed to fiber-polymer interfacial debonding caused by accumulation of water at high temperatures. In situ acoustic and DC electrical measurements of hydrothermally aged CNT composites identify extensive stress-relieving micro-cracking and crack deflections that are absent in the aged baseline composites. These observations are supported by SEM images of the failed composite cross-sections that highlight secondary matrix toughening mechanisms in the form of CNT pullouts and fractures which enhance the service life of composites and maintain their properties under accelerated aging environments.

| S-EPMC5695714 | biostudies-literature

Multiscale Polymer Dynamics in Hierarchical Carbon Nanotube Grafted Glass Fiber Reinforced Composites.

Project description:Carbon nanotube (CNT) grafted glass fiber reinforced epoxy nanocomposites (GFRP) present a range of stiffnesses (MPa to GPa) and length scales (μm to nm) at the fiber-matrix interface. The contribution of functionalized CNT networks to the local and bulk polymer dynamics is studied here by using a combination of torsion dynamical mechanical thermal analysis (DMTA), positron annihilation lifetime spectroscopy (PALS), and neutron scattering (NS) measurements. DMTA measurements highlight a reduction in the storage modulus (G') in the rubbery region and an asymmetric broadening of the loss modulus (G″) peak in the α-transition region. NS measurements show a suppressed hydrogen mean-square displacement (MSD) in the presence of glass fibers but a higher hydrogen MSD after grafting functionalized CNTs onto fiber surfaces. PALS measurements show greater free volume characteristics in the presence of the functionalized CNT modified composites, supporting the view that these interface layers increase polymer mobility. While NS and DMTA are sensitive to different modes of chain dynamics, the localization of functionalized nanotubes at the fiber interface is found to affect the distribution of polymer relaxation modes without significantly altering the thermally activated relaxation processes.

| S-EPMC7067277 | biostudies-literature

Poly(lactic acid) Matrix Reinforced with Diatomaceous Earth.

Project description:The poly(lactic acid) (PLA) biodegradable polymer, as well as natural, siliceous reinforcement in the form of diatomaceous earth, fit perfectly into the circular economy trend. In this study, various kinds of commercial PLA have been reinforced with diatomaceous earth (DE) to prepare biodegradable composites via the extrusion process. The structure of the manufactured composites as well as adhesion between the matrix and the filler were investigated using scanning electron microscopy (SEM). Differential scanning calorimetry (DSC) analyses were carried out to determine crystallinity of PLA matrix as function of DE additions. Additionally, the effect of the ceramic-based reinforcement on the mechanical properties (Young's modulus, elongation to failure, ultimate tensile strength) of PLA has been investigated. The results are discussed in terms of possible applications of PLA + DE composites.

| S-EPMC9501419 | biostudies-literature

Pd nanoparticles deposited on poly(lactic acid) grafted carbon nanotubes: synthesis, characterization and application in Heck C-C coupling reaction.

Project description:Herein we described the synthesis of a novel f-CNTs-Pd nanocatalyst by covalent grafting of poly(lactic acid) (PLA) onto carbon nanotubes (CNTs) and subsequent deposition of Pd nanoparticles. Prior to grafting of PLA, CNTs were oxidized with a mixture of HNO(3)/H(2)SO(4) and successively activated with thionyl chloride. The PLA grafted CNTs (f-CNTs) were then used as platform for in-situ deposition of Pd nanoparticles. The formation of f-CNTs-Pd nanocatalyst was analyzed by UV-vis, FTIR and Raman spectroscopy, powder XRD, energy dispersive spectroscopy and thermogravimetric analysis. The morphologies of the nanocatalyst were characterized using scanning and transmission electron microscopes. The f-CNTs stabilized Pd nanoparticles are found to be more effective in the promotion of Heck cross-coupling reaction between aryl halides and n-butyl acrylate. The f-CNTs-Pd nanocatalyst was regenerated for three cycles of reaction without any significant loss in its activity.

| S-EPMC3125581 | biostudies-literature

Antibacterial Property and Cytotoxicity of a Poly(lactic acid)/Nanosilver-Doped Multiwall Carbon Nanotube Nanocomposite.

Project description:A novel method was used to synthesize a nanosilver-doped multiwall carbon nanotube (MWCNT-Ag), and subsequently, the novel poly(lactic acid) (PLA)- and MWCNT-Ag-based biocompatible and antimicrobial nanocomposites were prepared by melt blending. Based on energy dispersive X-ray spectrometry images, an MWCNT-Ag was successfully synthesized. The effect of the MWCNT-Ag on the PLA bionanocomposites was investigated by evaluating their thermal and mechanical properties, antifungal activity, and cytotoxicity. The nanocomposites exhibited a high degree of biocompatibility with the MWCNT-Ag content, which was less than 0.3 phr. Furthermore, tensile strength testing, thermogravimetric analysis, differential scanning calorimetry, and antibacterial evaluation revealed that the tensile strength, thermostability, glass transition temperature, and antibacterial properties were enhanced by increasing the MWCNT-Ag content. Finally, hydrolysis analysis indicated that the low MWCNT-Ag content could increase the packing density of PLA.

| S-EPMC6431862 | biostudies-other

Enhanced thermal properties of poly(lactic acid)/MoS<sub>2</sub>/carbon nanotubes composites.

Project description:In this work, few-layered molybdenum disulfide (MoS2) was functionalized with metal oxide (MxOy) nanoparticles which served as a catalyst for carbon nanotubes (CNT) growth in the chemical vapour deposition (CVD) process. The resulting MoS2/MxOy/CNT functionalized nanomaterials were used for flame retarding application in poly(lactic acid) (PLA). The composites were extruded with a twin-screw extruder with different wt% loading of the nanomaterial. Full morphology characterization was performed, as well as detailed analysis of fire performance of the obtained composites in relation to pristine PLA and PLA containing an addition of the composites. The samples containing the addition of MoS2/MxOy/CNT displayed up to over 90% decrease in carbon oxide (CO) emission during pyrolysis in respect to pristine PLA. Microscale combustion calorimetry testing revealed reduction of key parameters in comparison to pristine PLA. Laser flash analysis revealed an increase in thermal conductivity of composite samples reaching up to 65% over pristine PLA. These results prove that few-layered 2D nanomaterials such as MoS2 functionalized with CNT can be effectively used as flame retardance of PLA.

| S-EPMC6971244 | biostudies-literature

Carbon Nanotube Reinforced Structural Composite Supercapacitor.

Project description:Carbon nanotubes exhibit mechanical properties ideally suited for reinforced structural composites and surface area and conductivity attractive for electrochemical capacitors. Here we demonstrate the multifunctional synergy between these properties in a composite material exhibiting simultaneous mechanical and energy storage properties. This involves a reinforcing electrode developed using dense, aligned carbon nanotubes grown on stainless steel mesh that is layered in an ion conducting epoxy electrolyte matrix with Kevlar or fiberglass mats. The resulting energy storage composites exhibit elastic modulus over 5?GPa, mechanical strength greater than 85?MPa, and energy density up to 3?mWh/kg for the total combined system including electrodes, current collector, Kevlar or fiberglass, and electrolyte matrix. Furthermore, findings from in-situ mechano-electro-chemical tests indicate simultaneous mechanical and electrochemical functionality with invariant and stable supercapacitor performance maintained throughout the elastic regime.

| S-EPMC6281659 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data