Transparent Electrodes Based on Silver Nanowire Networks: From Physical Considerations towards Device Integration.

ABSTRACT: The past few years have seen a considerable amount of research devoted to nanostructured transparent conducting materials (TCM), which play a pivotal role in many modern devices such as solar cells, flexible light-emitting devices, touch screens, electromagnetic devices, and flexible transparent thin film heaters. Currently, the most commonly used TCM for such applications (ITO: Indium Tin oxide) suffers from two major drawbacks: brittleness and indium scarcity. Among emerging transparent electrodes, silver nanowire (AgNW) networks appear to be a promising substitute to ITO since such electrically percolating networks exhibit excellent properties with sheet resistance lower than 10 Ω/sq and optical transparency of 90%, fulfilling the requirements of most applications. In addition, AgNW networks also exhibit very good mechanical flexibility. The fabrication of these electrodes involves low-temperature processing steps and scalable methods, thus making them appropriate for future use as low-cost transparent electrodes in flexible electronic devices. This contribution aims to briefly present the main properties of AgNW based transparent electrodes as well as some considerations relating to their efficient integration in devices. The influence of network density, nanowire sizes, and post treatments on the properties of AgNW networks will also be evaluated. In addition to a general overview of AgNW networks, we focus on two important aspects: (i) network instabilities as well as an efficient Atomic Layer Deposition (ALD) coating which clearly enhances AgNW network stability and (ii) modelling to better understand the physical properties of these networks.

SUBMITTER: Bellet D

PROVIDER: S-EPMC5552077 | biostudies-other | 2017 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Nanoscale Chemical and Electrical Stabilities of Graphene-covered Silver Nanowire Networks for Transparent Conducting Electrodes.

Project description:The hybrid structure of Ag nanowires (AgNWs) covered with graphene (Gr) shows synergetic effects on the performance of transparent conducting electrodes (TCEs). However, these effects have been mainly observed via large-scale characterization, and precise analysis at the nanoscale level remains inadequate. Here, we present the nanoscale verification and visualization of the improved chemical and electrical stabilities of Gr-covered AgNW networks using conductive atomic force microscopy (C-AFM), Auger electron spectroscopy (AES), and X-ray photoelectron spectroscopy (XPS) combined with the gas cluster ion beam (GCIB) sputtering technique. Specifically by transferring island Gr on top of the AgNW network, we were able to create samples in which both covered and uncovered AgNWs are simultaneously accessible to various surface-characterization techniques. Furthermore, our ab initio molecular dynamics (AIMD) simulation elucidated the specific mechanistic pathway and a strong propensity for AgNW sulfidation, even in the presence of ambient oxidant gases.

| S-EPMC5020617 | biostudies-literature

Improved Flexible Transparent Conductive Electrodes based on Silver Nanowire Networks by a Simple Sunlight Illumination Approach.

Project description:Silver nanowire (Ag NW) networks have attracted wide attention as transparent electrodes for emerging flexible optoelectronics. However, the sheet resistance is greatly limited by large wire-to-wire contact resistances. Here, we propose a simple sunlight illumination approach to remarkably improve their electrical conductivity without any significant degradation of the light transmittance. Because the power density is extremely low (0.1?W/cm2, 1-Sun), only slight welding between Ag NWs has been observed. Despite this, a sheet resistance of <20??/sq and transmittance of ~87% at wavelength of 550?nm as well as excellent mechanical flexibility have still been achieved for Ag NW networks after sunlight illumination for 1?hour or longer, which are significant upgrades over those of ITO. Slight plasmonic welding together with the associated self-limiting effect has been investigated by numerical simulations and further verified experimentally through varied solar concentrations. Due to the reduced resistance, high-performance transparent film heaters as well as efficient defrosters have been demonstrated, which are superior to the previously-reported Ag NW based film heaters. Since the sunlight is environmentally friendly and easily available, sophisticated or expensive facilities are not necessary. Our findings are particularly meaningful and show enormous potential for outdoor applications.

| S-EPMC5294563 | biostudies-literature

The effect of rod orientation on electrical anisotropy in silver nanowire networks for ultra-transparent electrodes.

Project description:Two-dimensional networks made of metal nanowires are excellent paradigms for the experimental observation of electrical percolation caused by continuous jackstraw-like physical pathways. Such systems became very interesting as alternative material in transparent electrodes, which are fundamental components in display devices. This work presents the experimental characterization of low-haze and ultra-transparent electrodes based on silver nanowires. The films are created by dip-coating, a feasible and scalable liquid film coating technique. We have found dominant alignment of the silver nanowires in withdrawal direction. The impact of this structural anisotropy on electrical anisotropy becomes more pronounced for low area coverage. The rod alignment does not influence the technical usability of the films as significant electrical anisotropy occurs only at optical transmission higher than 99 %. For films with lower transmission, electrical anisotropy becomes negligible. In addition to the experimental work, we have carried out computational studies in order to explain our findings further and compare them to our experiments and previous literature. This paper presents the first experimental observation of electrical anisotropy in two-dimensional silver nanowire networks close at the percolation threshold.

| S-EPMC5039631 | biostudies-literature

Aligned silver nanowire-based transparent electrodes for engineering polarisation-selective optoelectronics.

Project description:We herein report on a remarkably simple, fast, and economic way of fabricating homogeneous and well oriented silver nanowires (AgNWs) that exhibit strong in-plane electrical and optical anisotropies. Using a small quantity of AgNW suspension, the horizontal-dip (H-dip) coating method was applied, in which highly oriented AgNWs were deposited unidirectionally along the direction of coating over centimetre-scale lengths very rapidly. In applying the H-dip-coating method, we adjusted the shear strain rate of the capillary flow in the Landau-Levich meniscus of the AgNW suspension, which induced a high degree of uniaxial orientational ordering (0.37-0.43) of the AgNWs, comparable with the ordering seen in archetypal nematic liquid crystal (LC) materials. These AgNWs could be used to fabricate not only transparent electrodes, but also LC-alignment electrodes for LC devices and/or polarising electrodes for organic photovoltaic devices, having the potential to revolutionise the architectures of a number of polarisation-selective opto-electronic devices for use in printed/organic electronics.

| S-EPMC4725987 | biostudies-literature

Roller-Induced Bundling of Long Silver Nanowire Networks for Strong Interfacial Adhesion, Highly Flexible, Transparent Conductive Electrodes.

Project description:Silver nanowires (AgNWs) have been the most promising electrode materials for fabrication of flexible transparent touch panel, displays and many other electronics because of their excellent electrical properties, cost effectiveness, synthesis scalability, and suitability for mass production. Although a few literature reports have described the use of short Ag NWs in fabrication of randomly oriented Ag NW network-based electrode, their electrical conductivities are still far lower than that of Ag films. So far, no any literature report was able to provide any simple solution to fabrication of large-area and mass-manufactural ability to address the issues, such as, conductivity, transparency, electrical current withstand, bending stability, and interfacial adhesion. In the current work, we provide a simple solution to conquer the above-mentioned challenges, and report the development of long Ag NW bundle network electrodes on large area PET films that were coated, aligned, and bundled quickly and simply using a steel roller. Our developed AgNWs-bundle networks had superior performance in optoelectronic properties (sheet resistance 5.8 ? sq-1; optical transmittance 89% at 550?nm wavelength), electrical current withstand up to 500?mA, and bending stability over 5000 bending cycles, and strong interfacial adhesion.

| S-EPMC5709471 | biostudies-literature

High-Stability Silver Nanowire-Al2O3 Composite Flexible Transparent Electrodes Prepared by Electrodeposition.

Project description:Silver nanowire (AgNW) conductive film fabricated by solution processing was investigated as an alternative to indium tin oxide (ITO) in flexible transparent electrodes. In this paper, we studied a facile and effective method by electrodepositing Al2O3 on the surface of AgNWs. As a result, flexible transparent electrodes with improved stability could be obtained by electrodepositing Al2O3. It was found that, as the annealing temperature rises, the Al2O3 coating layer can be transformed from Al2O3·H2O into a denser amorphous state at 150 °C. By studying the increase of electrodeposition temperature, it was observed that the transmittance of the AgNW-Al2O3 composite films first rose to the maximum at 70 °C and then decreased. With the increase of the electrodeposition time, the figure of merit (FoM) of the composite films increased and reached the maximum when the time was 40 s. Through optimizing the experimental parameters, a high-stability AgNW flexible transparent electrode using polyimide (PI) as a substrate was prepared without sacrificing optical and electrical performance by electrodepositing at -1.1 V and 70 °C for 40 s with 0.1 mol/L Al(NO3)3 as the electrolyte, which can withstand a high temperature of 250 °C or 250,000 bending cycles with a bending radius of 4 mm.

| S-EPMC8621956 | biostudies-literature

High energy electron beam stimulated nanowelding of silver nanowire networks encapsulated with graphene for flexible and transparent electrodes.

Project description:Low-dimensional nanostructures and their complementary hybridization techniques are in the vanguard of technological advances for applications in transparent and flexible nanoelectronics due to the intriguing electrical properties related to their atomic structure. In this study, we demonstrated that welding of Ag nanowires (NWs) encapsulated in graphene was stimulated by flux-optimized, high-energy electron beam irradiation (HEBI) under ambient conditions. This methodology can inhibit the oxidation of Ag NWs which is induced by the inevitably generated reactive ozone as well as improve of their electrical conductivity. We have systematically explored the effects of HEBI on Ag NWs and graphene. The optimized flux for HEBI welding of the Ag NWs with graphene was 150 kGy, which decreased the sheet resistance of the graphene/Ag NWs to 12 Ohm/sq. Following encapsulation with graphene, the initial chemical states of the Ag NWs were well-preserved after flux-tuned HEBI, whereas graphene underwent local HEBI-induced defect generation near the junction area. We further employed resonant Raman spectroscopy to follow the structural evolution of the sacrificial graphene in the hybrid film after HEBI. Notably, the sheet resistance of the welded Ag NWs encapsulated with graphene after HEBI was well-maintained even after 85 days.

| S-EPMC6598987 | biostudies-literature

Silver Nanowire Transparent Conductive Electrodes for High-Efficiency III-Nitride Light-Emitting Diodes.

Project description:Silver nanowires (AgNWs) have been successfully demonstrated to function as next-generation transparent conductive electrodes (TCEs) in organic semiconductor devices owing to their figures of merit, including high optical transmittance, low sheet resistance, flexibility, and low-cost processing. In this article, high-quality, solution-processed AgNWs with an excellent optical transmittance of 96.5% at 450 nm and a low sheet resistance of 11.7 Ω/sq were demonstrated as TCEs in inorganic III-nitride LEDs. The transmission line model applied to the AgNW contact to p-GaN showed that near ohmic contact with a specific contact resistance of ~10(-3) Ωcm(2) was obtained. The contact resistance had a strong bias-voltage (or current-density) dependence: namely, field-enhanced ohmic contact. LEDs fabricated with AgNW electrodes exhibited a 56% reduction in series resistance, 56.5% brighter output power, a 67.5% reduction in efficiency droop, and a approximately 30% longer current spreading length compared to LEDs fabricated with reference TCEs. In addition to the cost reduction, the observed improvements in device performance suggest that the AgNWs are promising for application as next-generation TCEs, to realise brighter, larger-area, cost-competitive inorganic III-nitride light emitters.

| S-EPMC4558582 | biostudies-literature

Hybrid Ag nanowire transparent conductive electrodes with randomly oriented and grid-patterned Ag nanowire networks.

Project description:To improve the electrical properties of silver nanowire (Ag NW) transparent conductive electrodes (TCEs), the density of Ag NW networks should be increased, to increase the number of percolation paths. However, because of the inverse relationship between optical transmittance and electrical resistivity, the optical properties of Ag NW TCEs deteriorate with increasing density of the Ag NW network. In this study, a hybrid Ag NW electrode composed of randomly oriented and grid-patterned Ag NW networks is demonstrated. The hybrid Ag NW electrodes exhibit significantly improved sheet resistances and slightly decreased transmittances compared to randomly oriented Ag NW networks. Hybrid Ag NW TCEs show excellent mechanical flexibilities and durabilities in bending tests with a 5?mm radius of curvature. Moreover, flexible transparent film heaters (TFHs) based on the hybrid Ag NW electrodes show elevated maximum temperatures relative to TFHs based on randomly oriented Ag NW electrodes, when operated at the same input voltages.

| S-EPMC5599587 | biostudies-literature

Flexible, transparent patterned electrodes based on graphene oxide/silver nanowire nanocomposites fabricated utilizing an accelerated ultraviolet/ozone process to control silver nanowire degradation.

Project description:We developed flexible, transparent patterned electrodes, which were fabricated utilizing accelerated ultraviolet/ozone (UV/O3)-treated graphene oxide (GO)/silver nanowire (Ag-NW) nanocomposites via a simple, low-cost pattern process to investigate the feasibility of promising applications in flexible/wearable electronic and optoelectronic devices. The UV/O3 process of the GO/Ag-NW electrode was accelerated by the pre-heat treatment, and the degradation interruption of Ag NWs was removed by the GO treatment. After the deposition of the GO-treated Ag NW electrodes, the sheet resistance of the thermally annealed GO-treated Ag-NW electrodes was significantly increased by using the UV/O3 treatment, resulting in a deterioration of the GO-treated Ag NWs in areas exposed to the UV/O3 treatment. The degradation of the Ag NWs caused by the UV/O3 treatment was confirmed by using the sheet resistances, scanning electron microscopy images, X-ray photoelectron microscopy spectra, and transmittance spectra. While the sheet resistance of the low-density Ag-NW electrode was considerably increased due to the pre-thermal treatment at 90 °C for 10 min, that of the high-density Ag-NW electrode did not vary significantly even after a UV/O3 treatment for a long time. The degradation interference phenomenon caused by the UV/O3 treatment in the high-density Ag NWs could be removed by using a GO treatment, which resulted in the formation of a Ag-NW electrode pattern suitable for promising applications in flexible organic light-emitting devices. The GO treatment decreased the sheet resistance of the Ag-NW electrode and enabled the pattern to be formed by using the UV/O3 treatment. The selective degradation of Ag NWs due to UV/O3 treatment decreased the transparency of the Ag-NW electrode by about 8% and significantly increased its sheet resistance more than 100 times.

| S-EPMC6445337 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data