Chemical Treatment of Waste Abaca for Natural Fiber-Reinforced Geopolymer Composite.

ABSTRACT: The use of natural fibers in reinforced composites to produce eco-friendly materials is gaining more attention due to their attractive features such as low cost, low density and good mechanical properties, among others. This work thus investigates the potential of waste abaca (Manila hemp) fiber as reinforcing agent in an inorganic aluminosilicate material known as geopolymer. In this study, the waste fibers were subjected to different chemical treatments to modify the surface characteristics and to improve the adhesion with the fly ash-based geopolymer matrix. Definitive screening design of experiment was used to investigate the effect of successive chemical treatment of the fiber on its tensile strength considering the following factors: (1) NaOH pretreatment; (2) soaking time in aluminum salt solution; and (3) final pH of the slurry. The results show that the abaca fiber without alkali pretreatment, soaked for 12 h in Al₂(SO₄)₃ solution and adjusted to pH 6 exhibited the highest tensile strength among the treated fibers. Test results confirmed that the chemical treatment removes the lignin, pectin and hemicellulose, as well as makes the surface rougher with the deposition of aluminum compounds. This improves the interfacial bonding between geopolymer matrix and the abaca fiber, while the geopolymer protects the treated fiber from thermal degradation.

SUBMITTER: Malenab RAJ

PROVIDER: S-EPMC5552086 | biostudies-other | 2017 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Brief dataset on chemical and mechanical properties of Corypha utan leaf fiber-reinforced composite with alkaline and silane treatment.

Project description:This paper presents the chemical and mechanical properties of Corypha utan leaf fiber (CULF) subjected to different chemical treatments for reinforced composite materials. Natural fibers are currently considered as an alternative constituent for composite reinforcement due to their friendly environment character. The CULF were chemically treated during a pre-fabrication process using NaOH, and 3-(Trimethoxysilyl) propyl methacrylate was introduced at three different concentrations of 0%, 5%, and 10%, respectively. All the chemical treatments on CULF were observed using Fourier Transform Infrared (FTIR) Spectroscopy. Furthermore, vacuum bagging method with unsaturated polyester was used to manufacture CULF as composite reinforcement. Tensile and bending tests were carried out to collect mechanical properties data of the produced CULF reinforced composites. The data obtained could support further study in the area and development of natural fiber-reinforced composite.

| S-EPMC8685977 | biostudies-literature

Preparation, characterization, and evaluation of compressive strength of polypropylene fiber reinforced geopolymer mortars.

Project description:The study of the fiber-matrix interface represents a crucial topic to determine the mechanical performance of geopolymer-based materials reinforced with polypropylene fibers (PPF). This research proposes the use of natural zeolite in the preparation geopolymers mortars through alkaline activation with NaOH, Ca(OH)2 and Na2SiO3, and with river sand as a fine aggregate. PPF were incorporated into the geopolymer-based mortar matrix in different proportions like 0, 0.5, and 1 wt.%. The mortars were cured for 24 h at 60 °C and then aged for six days more at room temperature. All samples analyzed through compressive strength were also characterized by X-ray diffraction, thermal analysis, Infrared Spectroscopy, and scanning electron microscopy techniques. The results indicated that the best mix design among the ones used: NaOH (10 M), Na2SiO3/NaOH = 3, Ca(OH)2 = 1.5 wt.% and PPF = 0.5 wt.%. The optimum mix design showed a compressive strength of 4.63 MPa on average. Besides, the fibers enhanced the compressive strength of those samples which the PP fibers probably have better dispersion inside the matrix of the geopolymer mortar.

| S-EPMC7168747 | biostudies-literature

Pullout Behavior of Bundled Aramid Fiber in Fiber-Reinforced Cementitious Composite.

Project description:The tensile performance of fiber-reinforced cementitious composite (FRCC) after first matrix cracking is characterized by a tensile stress-crack width relationship called the bridging law. The bridging law can be obtained by an integral calculus of forces carried by individual bridging fibers considering the effect of the fiber inclination angle. The main objective of this study is to investigate experimentally and evaluate the pullout behavior of a single aramid fiber, which is made with a bundling of original yarns of aramid fiber. The bundled aramid fiber has a nonsmooth surface, and it is expected to have good bond performance with the matrix. The test variables in the pullout test are the thickness of the matrix and the inclined angle of the fiber. From the test results, the pullout load-slip curves showed that the load increases lineally until maximum load, after which it decreases gradually. The maximum pullout load and slip at the maximum load increase as the embedded length of the fiber becomes larger. The pullout load-crack width relationship is modeled by a bilinear model, and the bridging law is calculated. The calculated result shows good agreement with the experimental curves obtained by the uniaxial tension test of aramid-FRCC.

| S-EPMC7179034 | biostudies-literature

Numerical Modelling of Geopolymer Concrete In-Filled Fibre-Reinforced Polymer Composite Columns Subjected to Axial Compression Loading

Project description:In this research study, the performance of geopolymer concrete (GPC) in-filled fibre-reinforced polymer (FRP) composite (GPC-FRP) columns exposed to compressive loading is examined using the finite element (FE) analysis. The load–deflection behaviour is investigated by considering the impact of the strength of concrete, different fibre orientations and thicknesses of FRP tubes in terms of the diameter/thickness (D/t) ratio, surface friction in between the concrete and enclosing FRP tube, the lateral confinement and the axial stress distribution characteristics. The load-carrying capacity (LCC) of the GPC-FRP composite columns and cement concrete (CC) in-filled FRP composite (CC-FRP) columns is compared and the results imply that the LCC of the GPC-FRP composite columns is (0.9 to 2.04%) greater than the CC-FRP composite columns. The improvement in the LCC and lateral confining pressure of the GPC-FRP composite columns is observed as the thickness of the FRP tube increases. The LCC of the GPC-FRP composite columns with a D/t ratio of 30 was almost (12.70 to 14.23%) greater than the GPC-FRP composite columns with a D/t ratio of 50. The GPC-FRP composite columns with a fibre orientation in the axial and hoop directions (0°) exhibit (8.4 to 11.39%) better performance than the columns with any other orientations (30° and 53°). The LCC of the GPC-FRP composite columns with a coefficient of friction of 0.25 and 0.5 are quite comparable. The axial stress distribution in the GPC-FRP composite columns with different tube thicknesses is explored in this research. This FE model is validated with the experimental results obtained by Kim et al., (2015) and the load and deflection are predicted with the validation error of 6.5 and 6.1%, respectively.

| S-EPMC9102813 | biostudies-literature

Improvement of Performances of the Gypsum-Cement Fiber Reinforced Composite (GCFRC).

Project description:The novelty of this paper lies in the identification of the scientific patterns of the influence of thermal power plant waste (TPPW) on the hydration mechanism and the structure of the gypsum-cement binder (GCB). The classification of raw materials for the production of GCB has been developed taking into account the genesis, which contributes to the prediction of the properties of composites. The features of the hydration phase formation and hardening of GCB have been studied taking into account the chemical, structural and morphological features of fly ash and slag. In addition, the microstructural, morphological, and thermal properties of the cured binders at a 28 day cure were determined. For the first time, scientific data on the properties of gypsum-cement fiber-reinforced composite using TPPW and microfiber have been obtained. The results show that the synergistic effect of gypsum-cement binder, TPPW, and polyamide or basalt microfiber improves the physicomechanical properties of a 28 day cured binder: compressive strength of 20 MPa, flexural strength of 8.9 MPa, and softening coefficient 0.87.

| S-EPMC7503270 | biostudies-literature

Short fiber reinforced 3d printed ceramic composite with shear induced alignment.

Project description:This paper accounts for utilization of shear induced alignment method during ceramic stereolithography. Lateral oscillation mechanism, combined with 3d printed wall pattern, was employed to generate necessary shear to align fiber in desired direction. First, semicircular channel pattern was printed to assess the effect of difference between wall direction and oscillation direction on the fiber alignment. Then, flexural strength of ceramic matrix was tested with nickel coated carbon fiber and ceramic fiber reinforcements. The results demonstrated that the shear induced alignment further improves the flexural strength compare to randomly distributed samples. Flexural strength of aligned samples with 1.0 wt% carbon fiber loading was improved by ~90% compared to randomly orientated samples and by ~333% compared to unreinforced samples. Finally, fracture surface morphology of the flexural strength test specimens was evaluated. The main fracture mechanism was observed as fiber pull-out.

| S-EPMC6191193 | biostudies-literature

Cationic Copolymers of Norbornylized Seed Oils for Fiber-Reinforced Composite Applications

Project description:Norbornylized seed oils, i.e., norbornylized linseed

| S-EPMC9520558 | biostudies-literature

Woven Natural Fibre Reinforced Composite Materials for Medical Imaging.

Project description:Repeatable patient positioning is key to minimising the burden on planning radiotherapy treatment. There are very few materials commercially available which are suitable for use in all common imaging and treatment modalities such as magnetic resonance imaging (MRI), X-Ray computed tomography (CT) and radiotherapy. In this article, we present several such materials based on woven natural fibres embedded in a range of different resin materials which are suitable for such applications. By investigating a range of resins and natural fibre materials in combination and evaluating their performance in terms of MRI and X-Ray imaging, we show that a woven cotton material impregnated with a two-part epoxy resin provides a 15% improvement in passage of X-Rays and has no impact on the MRI signal (unlike the 40% MRI signal attenuation from carbon fibre), whilst also retaining a flexural modulus up to 71% of that of carbon fibre. These results demonstrate that natural fibre composites produced using such materials provide desirable properties for use in patient support and positioning devices for multi-modal imaging, without the need to significantly compromise on the strength of the material.

| S-EPMC7178646 | biostudies-literature

Synergic effect of polyester fiber and nano silica on chemical resistance of geopolymer mortar.

Project description:The aim of this study is to evaluate the synergistic effect of polyester fiber-reinforced and nanoslica on the technical performance and durability of geopolymer mortar in terms of the chemical resistance. The study examined how the addition of polyester fiber and nanosilica affects the short-term severe durability of geopolymer mortar specimens made with fly ash (type F). The specimens were cured under ambient conditions. Different percentages (0.6%, 1.2%, and 1.8%) of polyester fiber were used, both with and without nanosilica. Additionally, a reference mixture containing only nanosilica was prepared.All mixtures had a liquid to binder ratio of 0.50, and the ratio of NaOH to Na2SiO3 solution was kept at 2.5:1 by weight. The produced mixes, after 28 days of ambient curing, were immersed for another 28 days in solutions containing 3.5%, 5%, and 5% of sodium chloride, magnesium sulphate and sulfuric acid, respectively. For comparison, control specimens which were not exposed to chemical attacks were tested at the same age of 56 days. Moreover, water absorption and sorptivity tests were conducted to explain the durability performance in a more detailed way. The test results express that the combination of both materials showed a synergistic effect and resulted in greater improvements in compressive and flexural strengths. Both materials can reduce the reduction in compressive strength caused by sulfuric acid exposure, but polyester fiber can increase mass loss. The presence of magnesium sulfate and sodium chloride can lead to a reduction in strength, but the addition of both polyester fiber and nanosilica can mitigate these effects. The addition of fibers creates a network of pores that can limit water absorption, and nanosilica can further enhance the microstructure and reduce water absorption. However, using polyester fiber beyond 1.2 percent can adversely affect the rate of water absorption.

| S-EPMC10522001 | biostudies-literature

Expanding Puck and Schurmann Inter Fiber Fracture Criterion for Fiber Reinforced Thermoplastic 3D-Printed Composite Materials.

Project description:The present work expands the application of Puck and Schürmann Inter-Fiber Fracture criterion to fiber reinforced thermoplastic 3D-printed composite materials. The effect of the ratio between the transverse compressive strength and the in-plane shear strength is discussed and a new transition point between the fracture conditions under compressive loading is proposed. The recommended values of the inclination parameters, as well as their effects on the proposed method, are also discussed. Failure envelopes are presented for different 3D-printed materials and also for traditional composite materials. The failure envelopes obtained here are compared to those provided by the original Puck and Schürmann criterion and to those provided by Gu and Chen. The differences between them are analyzed with the support of geometrical techniques and also statistical tools. It is demonstrated that the Expanded Puck and Schürmann is capable of providing more suitable failure envelopes for fiber reinforced thermoplastic 3D-printed composite materials in addition to traditional semi-brittle, brittle and intrinsically brittle composite materials.

| S-EPMC7178404 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data