Effects of air-abrasion pressure on the resin bond strength to zirconia: a combined cyclic loading and thermocycling aging study.

ABSTRACT: To determine the combined effect of fatigue cyclic loading and thermocycling (CLTC) on the shear bond strength (SBS) of a resin cement to zirconia surfaces that were previously air-abraded with aluminum oxide (Al2O3) particles at different pressures.Seventy-two cuboid zirconia specimens were prepared and randomly assigned to 3 groups according to the air-abrasion pressures (1, 2, and 2.8 bar), and each group was further divided into 2 groups depending on aging parameters (n = 12). Panavia F 2.0 was placed on pre-conditioned zirconia surfaces, and SBS testing was performed either after 24 hours or 10,000 fatigue cycles (cyclic loading) and 5,000 thermocycles. Non-contact profilometry was used to measure surface roughness. Failure modes were evaluated under optical and scanning electron microscopy. The data were analyzed using 2-way analysis of variance and χ2 tests (α = 0.05).The 2.8 bar group showed significantly higher surface roughness compared to the 1 bar group (p < 0.05). The interaction between pressure and time/cycling was not significant on SBS, and pressure did not have a significant effect either. SBS was significantly higher (p = 0.006) for 24 hours storage compared to CLTC. The 2 bar-CLTC group presented significantly higher percentage of pre-test failure during fatigue compared to the other groups. Mixed-failure mode was more frequent than adhesive failure.CLTC significantly decreased the SBS values regardless of the air-abrasion pressure used.

SUBMITTER: Al-Shehri EZ

PROVIDER: S-EPMC5553020 | biostudies-other | 2017 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Comparative Evaluation of the Repair Bond Strength of Dental Resin Composite after Sodium Bicarbonate or Aluminum Oxide Air-Abrasion.

Project description:The dental prophylactic cleaning of a damaged resin-based composite (RBC) restoration with sodium bicarbonate can change the surface characteristics and influence the repair bond strength. The purpose of this study was to compare the effect of sodium bicarbonate (SB) and aluminum oxide (AO) surface treatments on the microtensile bond strength (µTBS) of repaired, aged RBC. Bar specimens were prepared from microhybrid RBC and aged in deionized water for 8 weeks. Different surface treatments (AO air-abrasion; SB air-polishing), as well as cleaning (phosphoric acid, PA; ethylene-diamine-tetraacetic-acid, EDTA) and adhesive applications (single bottle etch-and-rinse, ER; universal adhesive, UA), were used prior to the application of the repair RBC. Not aged and aged but not surface treated RBCs were used as positive and negative controls, respectively. The repaired blocks were cut into sticks using a precision grinding machine. The specimens were tested for tensile fracture and the µTBS values were calculated. Surface characteristics were assessed using scanning electron microscopy. AO-PA-UA (62.6 MPa) showed a 20% increase in µTBS compared to the NC (50.2 MPa), which proved to be the most significant. This was followed by SB-EDTA-UA (58.9 MPa) with an increase of 15%. In addition to AO-PA-UA, SB-EDTA-UA could also be a viable alternative in the RBC repair protocol.

| S-EPMC10380324 | biostudies-literature

The effect of subpressure on the bond strength of resin to zirconia ceramic.

Project description:ObjectiveThis study was conducted to investigate the effect of subpressure on the bond strength of resin to zirconia ceramic. The subpressure would create a pressure gradient which could clean out the bubbles in the adhesives or bonding interface.MethodsTwenty-eight pre-sintered zirconia discs were fabricated. Half of them were polished (group P, n = 14), and the rest were sandblasted (group S, n = 14). After sintered,the surface roughness of the zirconia discs was measured. Then, they were randomly divided into two subgroups (n = 7). The groups were named as follows: PC: P + no additional treatments; PP: P + 0.04 MPa after application of adhesives; SC: S + no additional treatments; and SP: S + 0.04 MPa after application of adhesives. Resin columns were bonded to the zirconia specimens to determine shear bond strength (SBS). The bonding interfaces were observed and the fracture modes were evaluated. Statistical analysis was performed on all data.ResultsThe surface roughness of group S was significantly higher than that of group P (P<0.05). The SBS values were PC = 13.48 ± 0.7 MPa, PP = 15.22 ± 0.8 MPa, SC = 17.23 ± 0.7 MPa and SP = 21.68 ± 1.4 MPa. There were significant differences among the groups (P<0.05). Scanning electron microscopy (SEM) results showed that the adhesives of group SP and PP were closer and denser to the zirconia ceramic than that of group PC and SC. The proportion of the mixed fracture mode significantly increased after adding subpressure (P< 0.05).ConclusionSubpressure can improve the shear bond strength of resin to zirconia ceramics and increase micro-infiltration between the adhesives and the zirconia ceramics, especially on the rough surfaces.

| S-EPMC5480956 | biostudies-literature

Influence of Hot-Etching Surface Treatment on Zirconia/Resin Shear Bond Strength.

Project description:This study was designed to evaluate the effect of hot-etching surface treatment on the shear bond strength between zirconia ceramics and two commercial resin cements. Ceramic cylinders (120 units; length: 2.5 mm; diameter: 4.7 mm) were randomly divided into 12 groups (n = 10) according to different surface treatments (blank control; airborne-particle-abrasion; hot-etching) and different resin cements (Panavia F2.0; Superbond C and B) and whether or not a thermal cycling fatigue test (5°-55° for 5000 cycles) was performed. Flat enamel surfaces, mounted in acrylic resin, were bonded to the zirconia discs (diameter: 4.7 mm). All specimens were subjected to shear bond strength testing using a universal testing machine with a crosshead speed of 1 mm/min. All data were statistically analyzed using one-way analysis of variance and multiple-comparison least significant difference tests (α = 0.05). Hot-etching treatment produced higher bond strengths than the other treatment with both resin cements. The shear bond strength of all groups significantly decreased after the thermal cycling test; except for the hot-etching group that was cemented with Panavia F2.0 (p < 0.05). Surface treatment of zirconia with hot-etching solution enhanced the surface roughness and bond strength between the zirconia and the resin cement.

| S-EPMC5458836 | biostudies-other

Influence of Pre-Sintered Zirconia Surface Conditioning on Shear Bond Strength to Resin Cement.

Project description:This study analyzed the shear bond strength (SBS) of resin composite on zirconia surface to which a specific conditioner was applied before sintering. After sintering of either conditioner-coated or uncoated specimens, both groups were divided into three subgroups by their respective surface modifications (n = 10 per group): no further treatment; etched with hydrofluoric acid; and sandblasted with 50 µm Al₂O₃ particles. Surfaces were characterized by measuring different surface roughness parameters (e.g., Ra and Rmax) and water contact angles. Half of the specimens underwent thermocycling (10,000 cycles, 5-55 °C) after self-adhesive resin cement build-up. The SBSs were measured using a universal testing machine, and the failure modes were analyzed by microscopy. Data were analyzed by nonparametric and parametric tests followed by post-hoc comparisons (α = 0.05). Conditioner-coated specimens increased both surface roughness and hydrophilicity (p < 0.01). In the non-thermocycled condition, sandblasted surfaces showed higher SBSs than other modifications, irrespective of conditioner application (p < 0.05). Adhesive fractures were commonly observed in the specimens. Thermocycling favored debonding and decreased SBSs. However, conditioner-coated specimens upon sandblasting showed the highest SBS (p < 0.05) and mixed fractures were partially observed. The combination of conditioner application before sintering and sandblasting after sintering showed the highest shear bond strength and indicated improvements concerning the failure mode.

| S-EPMC5456913 | biostudies-other

Effects of cyclic loading on the shear bond strength of metal orthodontic brackets bonded to resin composite veneer surface using different conditioning protocols.

Project description:The aim of this research is to evaluate cyclic (CSBS) and static shear bond strengths (SSBS) of metal orthodontic brackets bonded to composite laminates using different conditioning protocols.A total of 80 direct nanofilled composite laminate veneers were prepared on permanent incisors and divided into four equal groups according to different surface treatments. In group 1, diamond bur was used. In group 2, microetcher (50-?m alumina particles) was utilized. In group 3, 38% phosphoric acid treatment for 60 s was done. In group 4 (control group), metal brackets were bonded to the untreated veneer surfaces using no-mix adhesive resin. SSBS testing was carried out for ten specimens, while CSBS testing was done for another ten specimens from each group. The data were subjected to analysis of variance and Scheffe post hoc test. The chi-square test was used to determine significant differences in the adhesive remnant index scores among different groups.Statistically significant difference was only found between SSBS of brackets bonded when surface treatment was done using the diamond bur, microetcher, and the phosphoric acid at P<0.05. With regard to CSBS, the use of bur treatment and microetching achieved the highest values; however, there was no significant difference between these two groups. With phosphoric acid, surface treatment achieved the lowest CSBS value; there was no significant difference between this group and the control group. The SSBS was significantly higher than CSBS in all groups.Roughening composite laminate veneers with either diamond bur or microetcher could be used successfully as an alternative to provide higher bond strength than phosphoric acid surface treatment. Cyclic loading significantly decreased bond strength.

| S-EPMC4406983 | biostudies-literature

Influence of Different Surface Pretreatments on Shear Bond Strength of an Adhesive Resin Cement to Various Zirconia Ceramics.

Project description:The aim of this in vitro study was to assess the influence of surface pretreatment on shear bond strength (SBS) of an adhesive resin cement (G-CEM Link Force TM, GC Corporation, Tokyo, Japan) to three different yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics: (1) Copran Zirconia Monolith HT, COP; (2) Katana ML Zirconia, KAT; and (3) Metoxit Z-CAD HTL Zirconia, MET. In total, 45 cylinders (5 mm in diameter, 1 mm height) for each type of zirconia ceramic were prepared used a computer-aided design and computer-aided manufacturing (CAD/CAM) machine (software CEREC 4.2). Each type of zirconia was subdivided into three groups and each group received a different surface pretreatment; 15 samples were not conditioned as control (groups COP 1, KAT 1, MET 1), 15 samples were air-borne particle abraded with aluminum dioxide particles of 50-?m size at 0.3 MPa for 20 s (groups COP 2, KAT 2, MET 2), and 15 samples were hot-etched with a solution of hydrochloric acid and ferric chloride (groups COP 3, KAT 3, MET 3). After specimen fabrication, the adhesive cement-ceramic interface was analyzed using an SBS test. Subsequently, the adhesive remnant index (ARI) was measured. Data were submitted to statistical analysis. Air-borne particle abraded specimens showed the highest SBS values for COP and KAT groups. For MET, no significant difference was reported between air-borne particle abraded specimens and untreated controls. The lowest values were detected for acid-etched groups. A higher frequency of ARI = "1" and ARI = "2" was reported in control and air-borne particle abraded groups, whereas ARI = "3" was detected in hot-etched groups. No correlation was found between ARI score and shear bond strength. Air-borne particle abrasion is considered the best treatment for Zirconia Copran and Zirconia Katana ML, if it is followed by using dual-curing resin cement.

| S-EPMC7040603 | biostudies-literature

Zirconia bond strength durability following artificial aging: A systematic review and meta-analysis of in vitro studies.

Project description:The present study systematically reviewed the literature regarding the bond strength durability of zirconia ceramics to resin-based luting cements after application of different bonding protocols and aging conditions. Electronic searches in PubMed, Scopus, and Web of Science databases were performed for relevant literature published between January 1st 2015 and November 15th 2022. Ninety-three (93) English language in-vitro studies were included. The percentage of the mean bond strength change was recorded prior to and after artificial aging, and the weighted mean values and 95% confidence intervals were calculated. Bonding protocols were classified based on the combination of MDP/non-MDP containing cement/primer and surface pretreatment, as well as the level of artificial aging performed. Alumina sandblasting (SA) was identified as the most frequently used surface pre-treatment while an insufficient number of studies was identified for each category of alternative surface treatments. The combination of MDP cement with tribochemical silica coating (TSC) or SA yielded more durable results after aging, while the application of SA and TSC improved bond durability when a non-MDP cement and a non-MDP primer were used. TSC may lead to increased bond durability compared to SA, whereas MDP cements may act similarly when combined with SA or TSC.

| S-EPMC10238491 | biostudies-literature

Shear Bond Strength of Self-Adhesive Flowable Resin Composite.

Project description:This study aimed to evaluate the shear bond strength of self-adhesive flowable resin composite on both enamel and dentin and investigate whether surface pretreatment with a phosphoric acid etch affects the bond strength. In this in vitro study, 80 sound human premolars were flattened to create (40) uniform enamel (E) and (40) dentin (D) surfaces. Groups were divided according to surface pretreatment: E1 : Scotchbond™ Universal Etchant + Single Bond Universal Adhesive + Filtek™ Z350 XT flowable composite; E2: Single Bond Universal self-etch adhesive + Filtek Z350 XT flowable composite; E3 : Scotchbond Universal Etchant + Fusio Liquid Dentin self-adhesive flowable composite; E4: Fusio Liquid Dentin self-adhesive flowable composite; D1 : Scotchbond Universal Etchant + Single Bond Universal Adhesive + Filtek Z350 XT flowable composite; D2: Single Bond Universal self-etch adhesive + Filtek Z350 XT flowable composite; D3: Scotchbond Universal Etchant + Fusio Liquid Dentin self-adhesive flowable composite; D4: Fusio Liquid Dentin self-adhesive flowable composite. After 2500 thermal cycles, the SBS was measured with a universal testing machine. One-way analysis of variance and Tukey's test for multiple comparisons were used to compare results. Two-way ANOVA was done to observe the significance of interaction between the type of surface and treatment. The maximum (49.38 ± 1.23 MPa) and minimum (21.41 ± 5.27 MPa) SBS values were noted in groups D1 and E2, respectively. Shear bond test results showed that self-adhesive flowable composite exhibited similar shear bond strengths on enamel and dentin and the bond strength improved with selective acid etching.

| S-EPMC9106484 | biostudies-literature

Laser-Milled Microslits Improve the Bonding Strength of Acrylic Resin to Zirconia Ceramics.

Project description:Heightened aesthetic considerations in modern dentistry have generated increased interest in metal-free "zirconia-supported dentures." The lifespan of the denture is largely determined by the strength of adhesion between zirconia and the acrylic resin. Thus, the effect on shear bond strength (SBS) was investigated by using an acrylic resin on two types of zirconia ceramics with differently sized microslits. Micromechanical reticular retention was created on the zirconia surface as the novel treatment (microslits (MS)), and air-abrasion was used as the control (CON). All samples were primed prior to acrylic resin polymerization. After the resin was cured, the SBS was tested. The obtained data were analyzed by using multivariate analysis of variance(? = 0.05). After the SBS test, the interface failure modes were observed by scanning electron microscopy. The MS exhibited significantly higher bond strength after thermal cycles (p < 0.05) than the CON. Nevertheless, statistically comparisons resulted in no significant effect of the differently sized microslits on SBS (p > 0.05). Additionally, MS (before thermal cycles: 34.8 ± 3.6 to 35.7 ± 4.0 MPa; after thermal cycles: 26.9 ± 3.1 to 32.6 ± 3.3 MPa) demonstrated greater SBS and bonding durability than that of CON (before thermal cycles: 17.3 ± 4.7 to 17.9 ± 5.8 MPa; after thermal cycles: 1.0 ± 0.3 to 1.7 ± 1.1 MPa), confirming that the micromechanical retention with laser-milled microslits was effective at enhancing the bonding strength and durability of the acrylic resin and zirconia. Polycrystalline zirconia-based ceramics are a newly accessible material for improving removable prosthodontic treatment, as the bond strength with acrylic resin can be greatly enhanced by laser milling.

| S-EPMC7240430 | biostudies-literature

Influence of air abrasion and sonic technique on microtensile bond strength of one-step self-etch adhesive on human dentin.

Project description:The purpose of this in vitro study was to evaluate the microtensile bond strength of one-step self-etch adhesive to human dentin surface modified with air abrasion and sonic technique and to assess the morphological characteristics of the pretreated dentin surface. The occlusal enamel was removed to obtain a flat dentin surface for thirty-six human molar teeth. The teeth were randomly divided into three experimental groups (n = 12 per group), according to the pretreatment of the dentin: (1) control group, (2) air abrasion group, and (3) sonic preparation group. Microtensile bond strength test was performed on a universal testing machine. Two specimens from each experimental group were subjected to SEM examination. There was no statistically significant difference in bond strength between the three experimental groups (P > 0.05). Mean microtensile bond strength (MPa) values were 35.3 ± 12.8 for control group, 35.8 ± 13.5 for air abrasion group, and 37.7 ± 12.0 for sonic preparation group. The use of air abrasion and sonic preparation with one-step self-etch adhesive does not appear to enhance or impair microtensile bond strength in dentin.

| S-EPMC4386705 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data