Characterization of a Laser Surface-Treated Martensitic Stainless Steel.

ABSTRACT: Laser surface treatment was carried out on AISI 416 machinable martensitic stainless steel containing 0.225 wt.% sulfur. Nd:YAG laser with a 2.2-KW continuous wave was used. The aim was to compare the physical and chemical properties achieved by this type of selective surface treatment with those achieved by the conventional treatment. Laser power of different values (700 and 1000 W) with four corresponding different laser scanning speeds (0.5, 1, 2, and 3 m•min-1) was adopted to reach the optimum conditions for impact toughness, wear, and corrosion resistance for laser heat treated (LHT) samples. The 0 °C impact energy of LHT samples indicated higher values compared to the conventionally heat treated (CHT) samples. This was accompanied by the formation of a hard surface layer and a soft interior base metal. Microhardness was studied to determine the variation of hardness values with respect to the depth under the treated surface. The wear resistance at the surface was enhanced considerably. Microstructure examination was characterized using optical and scanning electron microscopes. The corrosion behavior of the LHT samples was also studied and its correlation with the microstructures was determined. The corrosion data was obtained in 3.5% NaCl solution at room temperature by means of a potentiodynamic polarization technique.

SUBMITTER: Al-Sayed SR

PROVIDER: S-EPMC5553412 | biostudies-other | 2017 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Nanosecond laser coloration on stainless steel surface.

Project description:In this work, we present laser coloration on 304 stainless steel using nanosecond laser. Surface modifications are tuned by adjusting laser parameters of scanning speed, repetition rate, and pulse width. A comprehensive study of the physical mechanism leading to the appearance is presented. Microscopic patterns are measured and employed as input to simulate light-matter interferences, while chemical states and crystal structures of composites to figure out intrinsic colors. Quantitative analysis clarifies the final colors and RGB values are the combinations of structural colors and intrinsic colors from the oxidized pigments, with the latter dominating. Therefore, the engineering and scientific insights of nanosecond laser coloration highlight large-scale utilization of the present route for colorful and resistant steels.

| S-EPMC5541041 | biostudies-literature

Wear resistance of an additively manufactured high-carbon martensitic stainless steel.

Project description:The dry sliding wear behaviour of a high carbon martensitic stainless steel (HCMSS) consisting of ~ 22.5 vol% of chromium (Cr)- and vanadium (V)-rich carbides processed by electron beam melting (EBM) has been captured. The microstructure consisted of martensite and retained austenite phases with a homogeneous distribution of sub-micron-sized V-rich and micron-sized Cr-rich carbides, leading to relatively high hardness. The CoF decreased ~ 14.1% with increasing load in the steady-state, due to the material transferred from the wear track over the counterbody. The wear rate of the HCMSS compared to martensitic tool steel processed in the same manner, and it was nearly identical under low applied load. The dominant wear mechanism was removal of the steel matrix through abrasion, followed by the oxidation of the wear track, while three-body abrasive wear occurred with increasing load. A plastically deformed zone beneath the wear track was revealed through cross-sectional hardness mapping. Specific phenomena occurred with increasingly aggressive wear conditions were described with carbide cracking, pull-out of V-rich carbides and matrix cracking. This study revealed the wear performance of the additively manufactured HCMSS, which could pave the way for producing components for wear-related applications ranging from shafts to plastic injection moulds via EBM.

| S-EPMC9307504 | biostudies-literature

Effect of nanograin-boundary networks generation on corrosion of carburized martensitic stainless steel.

Project description:Martensitic stainless steel parts used in carbonaceous atmosphere at high temperature are subject to corrosion which results in a large amount of lost energy and high repair and maintenance costs. This work therefore proposes a model for surface development and corrosion mechanism as a solution to reduce corrosion costs. The morphology, phase, and corrosion behavior of steel are investigated using GIXRD, XANES, and EIS. The results show formation of nanograin-boundary networks in the protective layer of martensitic stainless steel. This Cr2O3-Cr7C3 nanograin mixture on the FeCr2O4 layer causes ion transport which is the main reason for the corrosion reaction during carburizing of the steel. The results reveal the rate determining steps in the corrosion mechanism during carburizing of steel. These steps are the diffusion of uncharged active gases in the stagnant-gas layer over the steel surface followed by the conversion of C into C4- and O into O2- at the gas-oxide interface simultaneously with the migration of Cr3+ from the metal-oxide interface to the gas-oxide interface. It is proposed that previous research on Al2O3 coatings may be the solution to producing effective coatings that overcome the corrosion challenges discussed in this work.

| S-EPMC5797200 | biostudies-literature

Formation of Nanospikes on AISI 420 Martensitic Stainless Steel under Gallium Ion Bombardment.

Project description:The focused ion beam (FIB) has proven to be an extremely powerful tool for the nanometer-scale machining and patterning of nanostructures. In this work, we experimentally study the behavior of AISI 420 martensitic stainless steel when bombarded by Ga+ ions in a FIB system. The results show the formation of nanometer sized spiky structures. Utilizing the nanospiking effect, we fabricated a single-tip needle with a measured 15.15 nanometer curvature radius and a microneedle with a nanometer sized spiky surface. The nanospikes can be made straight or angled, depending on the incident angle between the sample and the beam. We also show that the nanospiking effect is present in ferritic AISI 430 stainless steel. The weak occurrence of the nanospiking effect in between nano-rough regions (nano-cliffs) was also witnessed for austenitic AISI 316 and martensitic AISI 431 stainless steel samples.

| S-EPMC6836003 | biostudies-literature

Surface micro- and nano-texturing of stainless steel by femtosecond laser for the control of cell migration.

Project description:The precise control over the interaction between cells and the surface of materials plays a crucial role in optimizing the integration of implanted biomaterials. In this regard, material surface with controlled topographic features at the micro- and nano-scales has been proved to affect the overall cell behavior and therefore the final osseointegration of implants. Within this context, femtosecond (fs) laser micro/nano machining technology was used in this work to modify the surface structure of stainless steel aiming at controlling cell adhesion and migration. The experimental results show that cells tend to attach and preferentially align to the laser-induced nanopatterns oriented in a specific direction. Accordingly, the laser-based fabrication method here described constitutes a simple, clean, and scalable technique which allows a precise control of the surface nano-patterning process and, subsequently, enables the control of cell adhesion, migration, and polarization. Moreover, since our surface-patterning approach does not involve any chemical treatments and is performed in a single step process, it could in principle be applied to most metallic materials.

| S-EPMC5090360 | biostudies-literature

Effects of Austenitizing Temperature on Tensile and Impact Properties of a Martensitic Stainless Steel Containing Metastable Retained Austenite.

Project description:Austenitizing temperature is one decisive factor for the mechanical properties of medium carbon martensitic stainless steels (MCMSSs). In the present work, the effects of austenitizing temperature (1000, 1020, 1040 and 1060 °C) on the microstructure and mechanical properties of MCMSSs containing metastable retained austenite (RA) were investigated by means of electron microscopy, X-ray diffraction (XRD), as well as tensile and impact toughness tests. Results suggest that the microstructure including an area fraction of undissolved M23C6, carbon and chromium content in matrix, prior austenite grain size (PAGS), fraction and composition of RA in studied MCMSSs varies with employed austenitizing temperature. By optimizing austenitizing temperature (1060 °C for 40 min) and tempering (250 °C for 30 min) heat treatments, the MCMSS demonstrates excellent mechanical properties with the ultimate tensile strength of 1740 ± 8 MPa, a yield strength of 1237 ± 19 MPa, total elongation (ductility) of 10.3 ± 0.7% and impact toughness of 94.6 ± 8.0 Jcm-2 at room temperature. The increased ductility of alloys is mainly attributed to the RA with a suitable stability via a transformation-induced plasticity (TRIP) effect, and a matrix containing reduced carbon and chromium content. However, the impact toughness of MCMSSs largely depends on M23C6 carbides.

| S-EPMC7924182 | biostudies-literature

Mouse Lung Response to Stainless Steel and Mild Steel Welding Fume

Project description:A/J mice are genetically predisposed to spontaneous and/or chemically-induced lung tumors while C57BL/6J (B6) mice are resistant. This genetic disparity provides a unique scenario to identify molecular mechanisms associated with the lung response to welding fume at the transcriptome level.

2010-04-30 | GSE20174 | GEO

Wettability and friction control of a stainless steel surface by combining nanosecond laser texturing and adsorption of superhydrophobic nanosilica particles.

Project description:In this work, we present functionalization of AISI 316?L surfaces by nanosecond Nd:YAG laser texturing and adsorption of superhydrophobic fluoroalkylsilane functionalized 30-nm silica nanoparticles. Surface modification by varying the distance between laser-produced micro(?)-channels leads to different surface roughnesses. After nanosilica coating, the superhydrophilic laser-textured surfaces change into superhydrophobic surfaces with the same ?-roughness. A higher ?-channel density leads to more hydrophobic surfaces after coating. This enables a study of the combined effect of surface wettability and morphology on the friction coefficient and wear resistance. Experiments were performed in dry and water environments. In the case of dry friction, increased ?-roughness leads to a higher friction coefficient, and the water-repellency modification by nanosilica particles has no influence on the tribological behaviour. In contrast, in the water environment, the wettability presents an important contribution to the properties of contact surfaces: hydrophobic surfaces exhibit a lower friction coefficient, especially at higher densities of ?-channels. Energy-dispersive X-ray spectroscopy analysis of surfaces before and after the tribological experiments is performed, revealing the difference in weight % of Si in the worn surface compared to the unworn surface, which varies according to the nature of the surface morphology due to laser texturing in both dry and water environments.

| S-EPMC5945667 | biostudies-literature

Functional Antimicrobial Surface Coatings Deposited onto Nanostructured 316L Food-Grade Stainless Steel.

Project description:In our study, we demonstrated the performance of antimicrobial coatings on properly functionalized and nanostructured 316L food-grade stainless steel pipelines. For the fabrication of these functional coatings, we employed facile and low-cost electrochemical techniques and surface modification processes. The development of a nanoporous structure on the 316L stainless steel surface was performed by following an electropolishing process in an electrolytic bath, at a constant anodic voltage of 40 V for 10 min, while the temperature was maintained between 0 and 10 °C. Subsequently, we incorporated on this nanostructure additional coatings with antimicrobial and bactericide properties, such as Ag nanoparticles, Ag films, or TiO2 thin layers. These functional coatings were grown on the nanostructured substrate by following electroless process, electrochemical deposition, and atomic layer deposition (ALD) techniques. Then, we analyzed the antimicrobial efficiency of these functionalized materials against different biofilms types (Candida parapsilosis, Escherichia coli, Pseudomonas aeruginosa, Staphylococcus aureus, and Staphylococcus epidermidis). The results of the present study demonstrate that the nanostructuring and surface functionalization processes constitute a promising route to fabricate novel functional materials exhibiting highly efficient antimicrobial features. In fact, we have shown that our use of an appropriated association of TiO2 layer and Ag nanoparticle coatings over the nanostructured 316L stainless steel exhibited an excellent antimicrobial behavior for all biofilms examined.

| S-EPMC8074267 | biostudies-literature

Fatigue data for laser beam powder bed fused 17-4 PH stainless steel specimens in different heat treatment and surface roughness conditions.

Project description:This article presents the data demonstrating the synergistic effect of surface roughness and heat treatment on the fatigue behavior of 17-4 PH stainless steel (SS) fabricated via laser beam powder bed fusion (LB-PBF) [1]. Two sets of specimens, in as-built and machined surface conditions, were heat treated using five different recommended procedures for 17-4 PH SS by ASTM A693. Axial fully-reversed fatigue tests (R = -1) were conducted on heat treated as-built and machined specimens. The stable hysteresis stress-strain data, as well as the maximum and minimum stress and strain values for the cycle in a log10 increment are included for all conducted fatigue experiments. In addition, fractography images are provided for selected set of specimens.

| S-EPMC6646923 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data