Synthesis, Characterization and Hexavalent Chromium Adsorption Characteristics of Aluminum- and Sucrose-Incorporated Tobermorite.

ABSTRACT: Tobermorites were synthesized from the lime-quartz slurries with incorporations of aluminum and sucrose under hydrothermal conditions, and then used for adsorption of Cr(VI). The chemical components, and structural and morphological properties of tobermorite were characterized by X-ray diffraction (XRD), thermogravimetric-differential scanning calorimetry (TG-DSC), Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance (NMR), scanning electron microscopy (SEM), X-ray photoelectron spectroscopic (XPS) and N₂ adsorption-desorption measurements. The formation and crystallinity of tobermorite could be largely enhanced by adding 2.3 wt.% aluminum hydroxide or 13.3 wt.% sucrose. Sucrose also played a significantly positive role in increasing the surface area. The adsorption performances for Cr(VI) were tested using a batch method taking into account the effects of pH, the adsorption kinetics, and the adsorption isotherms. The adsorption capacities of the aluminum- and sucrose-incorporated tobermorites reached up to 31.65 mg/g and 28.92 mg/g, respectively. Thus, the synthesized tobermorites showed good adsorption properties for removal of Cr(VI), making this material a promising candidate for efficient bulk wastewater treatment.

SUBMITTER: Zhao Z

PROVIDER: S-EPMC5553414 | biostudies-other | 2017 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Preparation and characterization of Allium cepa extract coated biochar and adsorption performance for hexavalent chromium.

Project description:The elimination of hazardous metal ions from contaminated water has been an important procedure to improve the quality of the water source. Hence, this study presents the fabrication of Allium cepa extract-coated biochar for the elimination of Cr (VI) from wastewater. The synthesized biochar (SBCH) and modified biochar (BMOJ) were characterized by making use of FTIR, BET, XRD, TGA and SEM. Optimum Cr (VI) removal was achieved at solution pH 2, 0.05 g adsorbent dosage and 180 min agitation period. The adsorptive removal of Cr (VI) onto SBCH and BMOJ followed the pseudo-second-order kinetic model with a satisfactory sum of square residuals (SSR) of 3.874 and 5.245 for SBCH and BMOJ, respectively. Meanwhile, Freundlich isotherm was found to best describe the uptake of Cr (VI) SBCH and BMOJ. Experimental data showed an adsorption capacity of 37.38 and 25.77 mg g-1 and a maximum efficiency of 85.42% and 51.63% for BMOJ and SBCH, respectively. BMOJ also showed good antioxidant characteristics. Thermodynamic data revealed that the uptake of Cr (VI) onto the SBCH and BMOJ was an exothermic and endothermic (ΔH: SBCH = - 16.22 kJ mol-1 and BMOJ = 13.74 kJ mol-1), entropy-driven (ΔS: SBCH = 40.96 J K-1 mol-1 and BMOJ = 93.26 J K-1 mol-1) and spontaneous process. Furthermore, BMOJ demonstrated excellent reusability and promising characteristics for industrial applications.

| S-EPMC10682498 | biostudies-literature

Adsorption of Hexavalent Chromium by Sodium Alginate Fiber Biochar Loaded with Lanthanum.

Project description:Lanthanun oxide (La2O3) is a lanthanum chemical compound incorporates a sensible anionic complexing ability; however, it lacks stability at a low pH scale. Biochar fibers will give the benefit of their massive space and plethoric uses on the surface to support a metal chemical compound. Herein, wet spinning technology was used to load La3+ onto sodium alginate fiber, and to convert La3+ into La2O3 through carbonization. The La2O3-modified biochar (La-BC) fiber was characterized by SEM, XRD and XPS, etc. An adsorption experiment proved that La-BC showed an excellent adsorption capacity for chromates, and its saturation adsorption capacity was about 104.9 mg/g. The information suggested that the adsorption was in step with both the Langmuir and Freundlich models, following pseudo-second-order surface assimilation mechanics, which showed that the Cr (VI) adsorption was characterized by single-phase and polyphase adsorption, mainly chemical adsorption. The thermodynamic parameters proved that the adsorption process was spontaneous and endothermic. The mechanistic investigation revealed that the mechanism of the adsorption of Cr (VI) by La-BC may include electrostatic interaction, ligand exchange, or complexation. Moreover, the co-existing anions and regeneration experiments proved that the La-BC is recyclable and has good prospects in the field of chrome-containing wastewater removal.

| S-EPMC8123644 | biostudies-literature

A Comparative Study on Hexavalent Chromium Adsorption onto Chitosan and Chitosan-Based Composites.

Project description:Chitosan (Cs)-based composites were developed by incorporating silica (Cs-Si), and both silica and hydroxyapatite (Cs-Si-Hap), comparatively tested to sequester hexavalent (Cr(VI)) ions from water. XRD and FT-IR data affirmed the formation of Cs-Si and Cs-Si-Hap composite. Morphological images exhibits homogeneous Cs-Si surface, decorated with SiO2 nanoparticles, while the Cs-Si-Hap surface was non-homogeneous with microstructures, having SiO2 and Hap nanoparticles. Thermal analysis data revealed excellent thermal stability of the developed composites. Significant influence of pH, adsorbent dose, contact time, temperature, and coexisting anions on Cr(VI) adsorption onto composites was observed. Maximum Cr(VI) uptakes on Cs and developed composites were observed at pH 3. The equilibration time for Cr(VI) adsorption on Cs-Si-Hap was 10 min, comparatively better than Cs and Cs-Si. The adsorption data was fitted to pseudo-second-order kinetic and Langmuir isotherm models with respective maximum monolayer adsorption capacities (qm) of 55.5, 64.4, and 212.8 mg/g for Cs, Cs-Si, and Cs-Si-Hap. Regeneration studies showed that composites could be used for three consecutive cycles without losing their adsorption potential.

| S-EPMC8512014 | biostudies-literature

Biogenic Synthesis of Iron Oxide Nanoparticles Using Enterococcus faecalis: Adsorption of Hexavalent Chromium from Aqueous Solution and In Vitro Cytotoxicity Analysis.

Project description:The biological synthesis of nanoparticles is emerging as a potential method for nanoparticle synthesis due to its non-toxicity and simplicity. In the present study, a bacterium resistant to heavy metals was isolated from a metal-contaminated site and we aimed to report the synthesis of Fe3O4 nanoparticles via co-precipitation using bacterial exopolysaccharides (EPS) derived from Enterococcus faecalis_RMSN6 strains. A three-variable Box-Behnken design was used for determining the optimal conditions of the Fe3O4 NPs synthesis process. The synthesized Fe3O4 NPs were thoroughly characterized through multiple analytical techniques such as XRD, UV-Visible spectroscopy, FTIR spectroscopy and finally SEM analysis to understand the surface morphology. Fe3O4 NPs were then probed for the Cr(VI) ion adsorption studies. The important parameters such as optimization of initial concentration of Cr(VI) ions, effects of contact time, pH of the solution and contact time on quantity of Cr(VI) adsorbed were studied in detail. The maximum adsorption capacity of the nanoparticles was found to be 98.03 mg/g. The nanoparticles could retain up to 73% of their efficiency of chromium removal for up to 5 cycles. Additionally, prepared Fe3O4 NPs in the concentration were subjected to cytotoxicity studies using an MTT assay. The investigations using Fe3O4 NPs displayed a substantial dose-dependent effect on the A594 cells. The research elucidates that the Fe3O4 NPs synthesized from EPS of E. faecalis_RMSN6 can be used for the removal of heavy metal contaminants from wastewater.

| S-EPMC8705913 | biostudies-literature

Selective adsorption and determination of hexavalent chromium ions using graphene oxide modified with amino silanes.

Project description:Novel adsorbents are described for the preconcentration of chromium(VI). Graphene oxide (GO) was modified with various amino silanes containing one, two, or three nitrogen atoms in the molecule. These include 3-aminopropyltriethoxysilane (APTES), N-(3-trimethoxysilylpropyl)ethylenediamine (TMSPEDA), and N1-(3-trimethoxysilylpropyl)diethylenetriamine (TMSPDETA). The resulting GO derivatives were characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, and energy-dispersive X-ray fluorescence spectrometry (EDXRF). Adsorption studies show that these GO based sorbents are highly selective for Cr(VI) in the presence of Cr(III) at pH 3.5. Although the amino silanes applied in modification of GO contain different numbers of nitrogen atoms, the maximum adsorption capacities of GO derivatives are very similar (13.3-15.1 mg·g-1). Such results are in accordance with spectroscopy studies which show that the amount of amino silanes attached to GO decreases in the order of APTES > TMSPEDA > TMSPDETA. The APTES-modified GO was applied to selective and sensitive extraction of Cr(VI) ions prior to quantitation by low-power EDXRF using the Cr Kα line. The Cr(VI) ions need not be eluted from the solid adsorbent. The method has a 0.17 ng·mL-1 detection limit, and the recovery is 99.7 ± 2.2% at a spiking level of 10 ng·mL-1. The method was successfully applied to the determination of Cr(VI) in water samples. Graphical abstractGraphene oxide adsorbents modified with various amino silanes are described for the preconcentration and speciation of trace and ultratrace levels of chromium ions.

| S-EPMC5770511 | biostudies-literature

Adsorption of Hexavalent Chromium and Divalent Lead Ions on the Nitrogen-Enriched Chitosan-Based Activated Carbon.

Project description:Optimizing the physicochemical properties of the chitosan-based activated carbon (Ch-ACs) can greatly enhance its performance toward heavy metal removal from contaminated water. Herein, Ch was converted into a high surface area (1556 m2/g) and porous (0.69 cm3/g) ACs with large content of nitrogen (~16 wt%) using K2CO3 activator and urea as nitrogen-enrichment agents. The prepared Ch-ACs were tested for the removal of Cr(VI) and Pb(II) at different pH, initial metal ions concentration, time, activated carbon dosage, and temperature. For Cr(VI), the best removal was at pH = 2, while for Pb(II) the best pH for its removal was in the range of 4-6. At 25 °C, the Temkin model gives the best fit for the adsorption of Cr(VI), while the Langmuir model was found to be better for Pb(II) ions. The kinetics of adsorption of both heavy metal ions were found to be well-fitted by a pseudo-second-order model. The findings show that the efficiency and the green properties (availability, recyclability, and cost effectiveness) of the developed adsorbent made it a good candidate for wastewaters treatment. As preliminary work, the prepared sorbent was also tested regarding the removal of heavy metals and other contaminations from real wastewater and the obtained results were found to be promising.

| S-EPMC8400071 | biostudies-literature

Bioremediation of Hexavalent Chromium by Chromium Resistant Bacteria Reduces Phytotoxicity.

Project description:Chromium (Cr) (VI) has long been known as an environmental hazard that can be reduced from aqueous solutions through bioremediation by living cells. In this study, we investigated the efficiency of reduction and biosorption of Cr(VI) by chromate resistant bacteria isolated from tannery effluent. From 28 screened Cr(VI) resistant isolates, selected bacterial strain SH-1 was identified as Klebsiella sp. via 16S rRNA sequencing. In Luria-Bertani broth, the relative reduction level of Cr(VI) was 95%, but in tannery effluent, it was 63.08% after 72 h of incubation. The cell-free extract of SH-1 showed a 72.2% reduction of Cr(VI), which indicated a higher activity of Cr(VI) reducing enzyme than the control. Live and dead biomass of SH-1 adsorbed 51.25 mg and 29.03 mg Cr(VI) per gram of dry weight, respectively. Two adsorption isotherm models-Langmuir and Freundlich-were used for the illustration of Cr(VI) biosorption using SH-1 live biomass. Scanning electron microscopy (SEM) analysis showed an increased cell size of the treated biomass when compared to the controlled biomass, which supports the adsorption of reduced Cr on the biomass cell surface. Fourier-transform infrared analysis indicated that Cr(VI) had an effect on bacterial biomass, including quantitative and structural modifications. Moreover, the chickpea seed germination study showed beneficial environmental effects that suggest possible application of the isolate for the bioremediation of toxic Cr(VI).

| S-EPMC7504174 | biostudies-literature

Improved atmospheric sampling of hexavalent chromium.

Project description:Hexavalent chromium (Cr(VI)) and trivalent chromium (Cr(III)) are the primary chromium oxidation states found in ambient atmospheric particulate matter. While Cr(III) is relatively nontoxic, Cr(VI) is toxic and exposure to Cr(VI) may lead to cancer, nasal damage, asthma, bronchitis, and pneumonitis. Accurate measurement of the ambient Cr(VI) concentrations is an environmental challenge since Cr(VI) can be reduced to Cr(III) and vice versa during sampling. In the present study, a new Cr(VI) sampler (Clarkson sampler) was designed, constructed, and field tested to improve the sampling of Cr(VI) in ambient air. The new Clarkson Cr(VI) sampler was based on the concept that deliquescence during sampling leads to aqueous phase reactions. Thus, the relative humidity of the sampled air was reduced below the deliquescence relative humidity (DRH) of the ambient particles. The new sampler was operated to collect total suspended particles (TSP), and compared side-by-side with the current National Air Toxics Trends Stations (NATTS) Cr(VI) sampler that is utilized in the US. Environmental Protection Agency (EPA) air toxics monitoring program. Side-by-side field testing of the samplers occurred in Elizabeth, NJ during the winter and summer of 2012. The average recovery values of Cr(VI) spikes after 24-hr sampling intervals during summer and winter sampling were 57 and 72%, respectively, for the Clarkson sampler while the corresponding average values for NATTS samplers were 46% for both summer and winter sampling, respectively. Preventing the ambient aerosol collected on the filters from deliquescing is a key to improving the sampling of Cr(VI).

| S-EPMC4406252 | biostudies-literature

Two-Dimensional Titanium Carbides (Ti3C2Tx) Functionalized by Poly(m-phenylenediamine) for Efficient Adsorption and Reduction of Hexavalent Chromium.

Project description:Titanium carbides (MXenes) are promising multifunctional materials. However, the negative surface charge and layer-by-layer restacking of MXenes severely restrict their application in the field of anionic pollutants, including in hexavalent chromium (Cr(VI)). Herein, Ti3C2Tx MXenes was functionalized through in situ polymerization and intercalation of poly(m-phenylenediamine) (PmPD), then Ti3C2Tx/PmPD composites were obtained. Delightedly, Ti3C2Tx/PmPD composites exhibited positive surface charge, expanded interlayer spacing, and enhanced hydrophobicity. Furthermore, the specific surface area of Ti3C2Tx/PmPD composite was five and 23 times that of Ti3C2Tx and PmPD, respectively. These advantages endowed Ti3C2Tx/PmPD composite with an excellent adsorption capacity of Cr(VI) (540.47 mg g-1), which was superior to PmPD (384.73 mg g-1), Ti3C2Tx MXene (137.45 mg g-1), and the reported MXene-based adsorbents. The Cr(VI) removal mechanism mainly involved electrostatic adsorption, reduction, and chelation interaction. This study developed a simple functionalization strategy, which would greatly explore the potential of MXenes in the field of anionic pollutants.

| S-EPMC6982338 | biostudies-literature

Phytofabrication of Iron Nanoparticles for Hexavalent Chromium Remediation.

Project description:Hexavalent chromium is a genotoxic and carcinogenic byproduct of a number of industrial processes, which is discharged into the environment in excessive and toxic concentrations worldwide. In this paper, the synthesis of green iron oxide nanoparticles using extracts of four novel plant species [Pittosporum undulatum, Melia azedarach, Schinus molle, and Syzygium paniculatum (var. australe)] using a "bottom-up approach" has been implemented for hexavalent chromium remediation. Nanoparticle characterizations show that different plant extracts lead to the formation of nanoparticles with different sizes, agglomeration tendencies, and shapes but similar amorphous nature and elemental makeup. Hexavalent chromium removal is linked with the particle size and monodispersity. Nanoparticles with sizes between 5 and 15 nm from M. azedarach and P. undulatum showed enhanced chromium removal capacities (84.1-96.2%, respectively) when compared to the agglomerated particles of S. molle and S. paniculatum with sizes between 30 and 100 nm (43.7-58.7%, respectively) in over 9 h. This study has shown that the reduction of iron salts with plant extracts is unlikely to generate vast quantities of stable zero valent iron nanoparticles but rather favor the formation of iron oxide nanoparticles. In addition, plant extracts with higher antioxidant concentrations may not produce nanoparticles with morphologies optimal for pollutant remediation.

| S-EPMC6199743 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data