In Situ Imaging during Compression of Plastic Bonded Explosives for Damage Modeling.

ABSTRACT: The microstructure of plastic bonded explosives (PBXs) is known to influence behavior during mechanical deformation, but characterizing the microstructure can be challenging. For example, the explosive crystals and binder in formulations such as PBX 9501 do not have sufficient X-ray contrast to obtain three-dimensional data by in situ, absorption contrast imaging. To address this difficulty, we have formulated a series of PBXs using octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine (HMX) crystals and low-density binder systems. The binders were hydroxyl-terminated polybutadiene (HTPB) or glycidyl azide polymer (GAP) cured with a commercial blend of acrylic monomers/oligomers. The binder density is approximately half of the HMX, allowing for excellent contrast using in situ X-ray computed tomography (CT) imaging. The samples were imaged during unaxial compression using micro-scale CT in an interrupted in situ modality. The rigidity of the binder was observed to significantly influence fracture, crystal-binder delamination, and flow. Additionally, 2D slices from the segmented 3D images were meshed for finite element simulation of the mesoscale response. At low stiffness, the binder and crystal do not delaminate and the crystals move with the material flow; at high stiffness, marked delamination is noted between the crystals and the binder, leading to very different mechanical properties. Initial model results exhibit qualitatively similar delamination.

SUBMITTER: Manner VW

PROVIDER: S-EPMC5554019 | biostudies-other | 2017 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Experimental Investigation of the Acoustic Nonlinear Behavior in Granular Polymer Bonded Explosives with Progressive Fatigue Damage.

Project description:The measurement of acoustic nonlinear response is known as a promising technique to characterize material micro-damages. In this paper, nonlinear ultrasonic approach is used to characterize the evolution of fatigue induced micro-cracks in polymer bonded explosives. The variations of acoustic nonlinearity with respect to fatigue cycles in the specimens are obtained in this investigation. The present results show a significant increase of acoustic nonlinearity with respect to fatigue cycles. The experimental observation of the correlation between the acoustic nonlinearity and fatigue cycles in carbon/epoxy laminates, verifies that an acoustic nonlinear response can be used to evaluate the progressive fatigue damage in the granular polymer bonded explosives. The sensitivity comparison of nonlinear and linear parameters of ultrasonic waves in the specimens shows that nonlinear acoustic parameters are more promising indicators to fatigue induced micro-damage than linear ones. The feasibility study of the micro-damage assessment of polymer bonded explosives by nonlinear ultrasonic technique in this work can be applied to damage identification, material degradation monitoring, and lifetime prediction of the explosive parts.

| S-EPMC5554041 | biostudies-other

Damage Characterization during Compression in a Perlite-Aluminum Syntactic Foam.

Project description:Aluminum matrix (Al99.5) syntactic foam containing expanded perlite particles was produced using the pressure infiltration technique. The dominant deformation mechanisms during compression of this foam were determined by sequential k-means analysis of the acoustic emission data. Since the different deformation mechanisms were concurrently active even at small strains, successive unloading and reloading measurement was proposed for cluster identification. The repetitive unloading and reloading allowed us to identify two mechanical parameters, namely the unloading modulus and the loss for unloading-reloading cycles. Based on the correlations among the strain localization within the specimen, the acoustic emission results, the changes in these mechanical parameters, and the transition from quasi-elastic deformation to plasticity were revealed in this material.

| S-EPMC6829569 | biostudies-literature

A Reactive Inelasticity Theoretical Framework for Modeling Viscoelasticity, Plastic Deformation, and Damage in Soft Tissue.

Project description:Fibrous tissues are biopolymeric materials that are made of extracellular proteins including several collagens and proteoglycans, and have a high water content. These tissues have non-linear, anisotropic, and inelastic mechanical behaviors that are often categorized into viscoelastic behavior, plastic deformation, and damage. While tissue's elastic and viscoelastic mechanical properties have been measured for decades, there is no comprehensive theoretical framework for modeling inelastic behaviors of these tissues that is based on their structure. To model the three major inelastic mechanical behaviors of tissue's fibrous matrix we formulated a structurally inspired continuum mechanics framework based on the energy of molecular bonds that break and reform in response to external loading (reactive bonds). In this framework, we employed the theory of internal state variables and kinetics of molecular bonds. The number fraction of bonds, their reference deformation gradient, and damage parameter were used as state variables that allowed for consistent modeling of all three of the inelastic behaviors of tissue by using the same sets of constitutive relations. Several numerical examples are provided that address practical problems in tissue mechanics, including the difference between plastic deformation and damage. This model can be used to identify relationships between tissue's mechanical response to external loading and its biopolymeric structure.

| S-EPMC6298536 | biostudies-literature

Evolution of Preset Void and Damage Characteristics in Aluminum during Shock Compression and Release.

Project description:It is well known that initial defects play an essential role in the dynamic failure of materials. In practice, dynamic tension is often realized by release of compression waves. In this work, we consider void-included single-crystal aluminum and investigate the damage characteristics under different shock compression and release based on direct atomistic simulations. Elastic deformation, limited growth and closure of voids, and the typical spall and new nucleation of voids were all observed. In the case of elastic deformation, we observed the oscillatory change of void volume under multiple compression and tension. With the increase of impact velocity, the void volume reduced oscillations to the point of disappearance with apparent strain localization and local plastic deformation. The incomplete or complete collapsed void became the priority of damage growth under tension. An increase in sample length promoted the continuous growth of preset void and the occurrence of fracture. Of course, on the release of strong shock, homogeneous nucleation of voids covered the initial void, leading to a wider range of damaged zones. Finally, the effect of the preset void on the spall strength was presented for different shock pressures and strain rates.

| S-EPMC9182468 | biostudies-literature

Deformation Behavior of Cross-Linked Supercrystalline Nanocomposites: An in Situ SAXS/WAXS Study during Uniaxial Compression.

Project description:With the ever-expanding functional applications of supercrystalline nanocomposites (a relatively new category of materials consisting of organically functionalized nanoparticles arranged into periodic structures), it becomes necessary to ensure their structural stability and understand their deformation and failure mechanisms. Inducing the cross-linking of the functionalizing organic ligands, for instance, leads to a remarkable enhancement of the nanocomposites' mechanical properties. It is however still unknown how the cross-linked organic phase redistributes applied loads, how the supercrystalline lattice accommodates the imposed deformations, and thus in general what phenomena govern the overall material's mechanical response. This work elucidates these aspects for cross-linked supercrystalline nanocomposites through an in situ small- and wide-angle X-ray scattering study combined with uniaxial pressing. Because of this loading condition, it emerges that the cross-linked ligands effectively carry and distribute loads homogeneously throughout the nanocomposites, while the superlattice deforms via rotation, slip, and local defects generation.

| S-EPMC8155193 | biostudies-literature

Aligned genomic data compression via improved modeling.

Project description:With the release of the latest Next-Generation Sequencing (NGS) machine, the HiSeq X by Illumina, the cost of sequencing the whole genome of a human is expected to drop to a mere $1000. This milestone in sequencing history marks the era of affordable sequencing of individuals and opens the doors to personalized medicine. In accord, unprecedented volumes of genomic data will require storage for processing. There will be dire need not only of compressing aligned data, but also of generating compressed files that can be fed directly to downstream applications to facilitate the analysis of and inference on the data. Several approaches to this challenge have been proposed in the literature; however, focus thus far has been on the low coverage regime and most of the suggested compressors are not based on effective modeling of the data. We demonstrate the benefit of data modeling for compressing aligned reads. Specifically, we show that, by working with data models designed for the aligned data, we can improve considerably over the best compression ratio achieved by previously proposed algorithms. Our results indicate that the pareto-optimal barrier for compression rate and speed claimed by Bonfield and Mahoney (2013) [Bonfield JK and Mahoneys MV, Compression of FASTQ and SAM format sequencing data, PLOS ONE, 8(3):e59190, 2013.] does not apply for high coverage aligned data. Furthermore, our improved compression ratio is achieved by splitting the data in a manner conducive to operations in the compressed domain by downstream applications.

| S-EPMC5666573 | biostudies-literature

On compression and damage evolution in two thermoplastics.

Project description:The well-known Taylor cylinder impact test, which follows the impact of a flat-ended cylindrical rod onto a rigid stationary anvil, is conducted over a range of impact speeds for two polymers, polytetrafluoroethylene (PTFE) and polyetheretherketone (PEEK). In previous work, experiments and a model were developed to capture the deformation behaviour of the cylinder after impact. These works showed a region in which spatial and temporal variation of both longitudinal and radial deformation provided evidence of changes in phase within the material. In this further series of experiments, this region is imaged in a range of impacted targets at the Diamond synchrotron. Further techniques were fielded to resolve compressed regions within the recovered polymer cylinders that showed a fracture zone in the impact region. The combination of macroscopic high-speed photography and three-dimensional X-ray imaging has identified the development of failure with these polymers and shown that there is no abrupt transition in behaviours but rather a continuous range of responses to competing operating mechanisms. The behaviours noted in PEEK in these polymers show critical gaps in understanding of polymer high strain-rate response.

| S-EPMC5312121 | biostudies-literature

In situ laboratory for plastic degradation in the Red Sea.

Project description:Degradation and fragmentation of plastics in the environment are still poorly understood. This is partly caused by the lack of long-term studies and methods that determine weathering duration. We here present a novel study object that preserves information on plastic age: microplastic (MP) resin pellets from the wreck of the SS Hamada, a ship that foundered twenty-nine years ago at the coast of Wadi el Gemal national park, Egypt. Its sinking date enabled us to precisely determine how long MP rested in the wreck and a nearby beach, on which part of the load was washed off. Pellets from both sampling sites were analyzed by microscopy, X-ray tomography, spectroscopy, calorimetry, gel permeation chromatography, and rheology. Most pellets were made of low-density polyethylene, but a minor proportion also consisted of high-density polyethylene. MP from inside the wreck showed no signs of degradation compared to pristine reference samples. Contrary, beached plastics exhibited changes on all structural levels, which sometimes caused fragmentation. These findings provide further evidence that plastic degradation under saltwater conditions is comparatively slow, whereas UV radiation and high temperatures on beaches are major drivers of that process. Future long-term studies should focus on underlying mechanisms and timescales of plastic degradation.

| S-EPMC9279475 | biostudies-literature

Cyanea capillata bell kinematics analysis through corrected in situ imaging and modeling using strategic discretization techniques.

Project description:Obtaining accurate kinematic data of animals is essential for many biological studies and bio-inspired engineering. Many animals, however, are either too large or too delicate to transport to controlled environments where accurate kinematic data can be easily obtained. Often, in situ recordings are the only means available but are often subject to multi-axis motion and relative magnification changes with time leading to large discrepancies in the animal kinematics. Techniques to compensate for these artifacts were applied to a large jellyfish, Cyanea capillata, freely swimming in ocean waters. The bell kinematics were captured by digitizing exumbrella profiles for two full swimming cycles. Magnification was accounted for by tracking a reference point on the ocean floor and by observing the C. capillata exumbrella arclength in order to have a constant scale through the swimming cycles. A linear fit of the top bell section was used to find the body angle with respect to the camera coordinate system. Bell margin trajectories over two swimming cycles confirmed the accuracy of the correction techniques. The corrected profiles were filtered and interpolated to provide a set of time-dependent points along the bell. Discrete models of the exumbrella were used to analyze the bell kinematics. Exumbrella discretization was conducted using three different methods. Fourier series were fitted to the discretized models and subsequently used to analyze the bell kinematics of the C. capillata. The analysis showed that the bell did not deform uniformly over time with different segments lagging behind each other. Looping of the bell trajectory between contraction and relaxation was also present through most of the exumbrella. The bell margin had the largest looping with an outer path during contraction and inner path during relaxation. The subumbrella volume was approximated based on the exumbrella kinematics and was found to increase during contraction.

| S-EPMC4277286 | biostudies-literature

SDPMOD: an automated comparative modeling server for small disulfide-bonded proteins.

Project description:Small disulfide-bonded proteins (SDPs) are rich sources for therapeutic drugs. Designing drugs from these proteins requires three-dimensional structural information, which is only available for a subset of these proteins. SDPMOD addresses this deficit in structural information by providing a freely available automated comparative modeling service to the research community. For expert users, SDPMOD offers a manual mode that permits the selection of a desired template as well as a semi-automated mode that allows users to select the template from a suggested list. Besides the selection of templates, expert users can edit the target-template alignment, thus allowing further customization of the modeling process. Furthermore, the web service provides model stereochemical quality evaluation using PROCHECK. SDPMOD is freely accessible to academic users via the web interface at http://proline.bic.nus.edu.sg/sdpmod.

| S-EPMC441532 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data