Double enhancement of hydrogen storage capacity of Pd nanoparticles by 20 at% replacement with Ir; systematic control of hydrogen storage in Pd-M nanoparticles (M = Ir, Pt, Au).

ABSTRACT: We report on binary solid-solution nanoparticles (NPs) composed of Pd and Ir, which are not miscible at the equilibrium state of the bulk, for the first time, by means of a process of hydrogen absorption/desorption from core (Pd)/shell (Ir) NPs. Only 20 at% replacement with Ir atoms doubled the hydrogen-storage capability compared to Pd NPs, which are a representative hydrogen-storage material. Furthermore, the systematic control of hydrogen concentrations and the corresponding pressure in Pd and Pd-M NPs (M = Ir, Pt, Au) have been achieved based on the band filling control of Pd NPs.

SUBMITTER: Kobayashi H

PROVIDER: S-EPMC6124882 | biostudies-other | 2018 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Publications

Double enhancement of hydrogen storage capacity of Pd nanoparticles by 20 at% replacement with Ir; systematic control of hydrogen storage in Pd-M nanoparticles (M = Ir, Pt, Au).

Kobayashi Hirokazu H Yamauchi Miho M Ikeda Ryuichi R Yamamoto Tomokazu T Matsumura Syo S Kitagawa Hiroshi H

Chemical science 20180524 25

We report on binary solid-solution nanoparticles (NPs) composed of Pd and Ir, which are not miscible at the equilibrium state of the bulk, for the first time, by means of a process of hydrogen absorption/desorption from core (Pd)/shell (Ir) NPs. Only 20 at% replacement with Ir atoms doubled the hydrogen-storage capability compared to Pd NPs, which are a representative hydrogen-storage material. Furthermore, the systematic control of hydrogen concentrations and the corresponding pressure in Pd an ...[more]

PMID: 30210762

Similar Datasets

Hydrogen storage and stability properties of Pd-Pt solid-solution nanoparticles revealed via atomic and electronic structure.

Project description:Bimetallic Pd1-x Pt x solid-solution nanoparticles (NPs) display charging/discharging of hydrogen gas, which has relevance for fuel cell technologies; however, the constituent elements are immiscible in the bulk phase. We examined these material systems using high-energy synchrotron X-ray diffraction, X-ray absorption fine structure and hard X-ray photoelectron spectroscopy techniques. Recent studies have demonstrated the hydrogen storage properties and catalytic activities of Pd-Pt alloys; however, comprehensive details of their structural and electronic functionality at the atomic scale have yet to be reported. Three-dimensional atomic-scale structure results obtained from the pair distribution function (PDF) and reverse Monte Carlo (RMC) methods suggest the formation of a highly disordered structure with a high cavity-volume-fraction for low-Pt content NPs. The NP conduction band features, as extracted from X-ray absorption near-edge spectra at the Pd and Pt L III -edge, suggest that the Pd conduction band is filled by Pt valence electrons. This behaviour is consistent with observations of the hydrogen storage capacity of these NPs. The broadening of the valence band width and the down-shift of the d-band centre away from the Fermi level upon Pt substitution also provided evidence for enhanced stability of the hydride (ΔH) features of the Pd1-x Pt x solid-solution NPs with a Pt content of 8-21 atomic percent.

| S-EPMC5668347 | biostudies-literature

Hydrogen Adsorption on Au-Supported Pt and Pd Nanoislands: A Computational Study of Hydrogen Coverage Effects.

Project description:We have studied the dissociative adsorption of hydrogen under high coverage conditions of adsorbed hydrogen on Pd and Pt nanoislands supported on Au(111) using Density Functional Theory calculations. The results reveal that for Pd/Au(111), the free energy of hydrogen adsorption ΔG is close to 0 kJ/mol when the coverage of adsorbed hydrogen is near 1 ML, where the available catalytic sites are located at the edges of the Pd nanoislands. In the case of Pt/Au(111), ΔG ≈ 0 kJ/mol under a broad range of hydrogen coverage conditions, from 1 ML to 3 ML, depending on the size of the Pt nanoislands. This is the case because the available catalytic sites are located at both the steps and terraces of Pt nanoislands. These findings indicate that Au surfaces with Pd or Pt nanoislands offer catalytic sites with ΔG ≈ 0 for hydrogen reactions, one key factor for an ideal electrocatalyst for hydrogen reactions.

| S-EPMC8225257 | biostudies-literature

Au-Nanorods Supporting Pd and Pt Nanocatalysts for the Hydrogen Evolution Reaction: Pd Is Revealed to Be a Better Catalyst than Pt.

Project description:Ordered thin films of Au nanorods (NRs) on Ti/Au/Si heterostructure substrates are electrodeposited in thin film aluminum oxide templates and, after template removal, serve as supports for Pd and Pt nanocatalysts. Based on previous work which showed a better electrocatalytic performance for layered Au/Pd nanostructures than monolithic Pd, electrodeposited 20 nm Pd discs on Au-NRs are first investigated in terms of their catalytic activity for the hydrogen evolution reaction (HER) and compared to monolithic 20 nm Pd and Pt discs. To further boost performance, the interfacial interaction area between the Au-NRs supports and the active metals (Pt and Pd) was increased via magnetron sputtering an extremely thin layer of Pt and Pd (20 nm overall sputtered thickness) on the Au-NRs after template removal. In this way, the whole NR surface (top and lateral) was covered with Pt and Pd nanoparticles, ensuring a maximum interfacial contact between the support and the active metal. The HER performance obtained was substantially higher than that of the other nanostructures. A Salient result of the present work, however, is the superior activity obtained for sputtered Pd on Au in comparison to that of sputtered Pt on Au. The results also show that increasing the Au-NR length translates in a strong increase in performance. Density functional theory calculations show that the interfacial electronic interactions between Au and Pd lead to suitable values of hydrogen adsorption energy on all possible sites, thus promoting faster (barrier-free diffusion) hydrogen adsorption and its recombination to H2. A Volmer-Heyrovsky mechanism for HER is proposed, and a volcano plot is suggested based on the results of the Tafel plots and the calculated hydrogen adsorption energies.

| S-EPMC10343570 | biostudies-literature

One-pot synthesis of Au-M@SiO<sub>2</sub> (M = Rh, Pd, Ir, Pt) core-shell nanoparticles as highly efficient catalysts for the reduction of 4-nitrophenol.

Project description:The conversion of p-nitrophenol (4-NP) to p-aminophenol (4-AP) is of great significance for pharmaceutical and material manufacturing. In this work, Au-M@SiO2 (M = Rh, Pd, Ir, Pt) nanoparticles (NPs) with core-shell structures, which are expected to be excellent catalysts for the transformation of 4-NP to 4-AP, were synthesized by a facile one-pot one-step method. The structure and composition of the NPs were characterized through transmission electron microscopy, X-ray powder diffraction and X-ray photoelectron spectroscopy. Au-M@SiO2 (M = Rh, Pd, Ir, Pt) core-shell NPs showed excellent catalytic activity in the reduction of 4-NP, which is superior to most catalysts reported in the previous literature. The enhanced catalytic activity of Au-M@SiO2 core-shell NPs is presumably related to the bimetallic synergistic effect. This study provides a simple strategy to synthesize core-shell bimetallic NPs for catalytic applications.

| S-EPMC9091199 | biostudies-literature

Catalyst System for Hydrogenation Catalysis Based on Multiarm Hyperbranched Polymer Templated Metal (Au, Pt, Pd, Cu) Nanoparticles.

Project description:With a hyperbranched poly(amidoamine) core and many water-soluble poly(ethylene glycol) monomethyl ether arms connected by pH-sensitive acylhydrazone bonds, multiarm hyperbranched polymer was used as nanoreactor and reductant to prepare metal nanoparticles endowed with intelligence and biocompatibility. The multiarm hyperbranched polymer encapsulated nanoparticles (NPs) showed excellent catalytic activity for hydrogenation, thus an excellent catalyst system for hydrogenation was established. The rate constants could reach as high as 3.48 L·s-1·m-2, which can be attributed to the lack of surface passivation afforded by the multiarm hyperbranched polymer.

| S-EPMC6418630 | biostudies-literature

Interfacial nanodroplets guided construction of hierarchical Au, Au-Pt, and Au-Pd particles as excellent catalysts.

Project description:Interfacial nanodroplets were grafted to the surfaces of self-sacrificed template particles in a galvanic reaction system to assist the construction of 3D Au porous structures. The interfacial nanodroplets were formed via direct adsorption of surfactant-free emulsions onto the particle surfaces. The interfacial nanodroplets discretely distributed at the template particle surfaces and served as soft templates to guide the formation of porous Au structures. The self-variation of footprint sizes of interfacial nanodroplets during Au growth gave rise to a hierarchical pore size distribution of the obtained Au porous particles. This strategy could be easily extended to synthesize bimetal porous particles such as Au-Pt and Au-Pd. The obtained porous Au, Au-Pt, and Au-Pd particles showed excellent catalytic activity in catalytic reduction of 4-nitrophenol.

| S-EPMC4010925 | biostudies-literature

Light-Mediated Growth of Noble Metal Nanostructures (Au, Ag, Cu, Pt, Pd, Ru, Ir, Rh) From Micro- and Nanoscale ZnO Tetrapodal Backbones.

Project description:Micro- and nanoscale ZnO tetrapods provide an attractive support for metallic nanostructures since they can be inexpensively produced using the flame transport method and nanoparticle synthesis schemes can take advantage of a coupled response facilitated by the formation of a semiconductor-metal interface. Here, we present a light-mediated solution-based growth mode capable of decorating the surface of ZnO tetrapods with nanostructures of gold, silver, copper, platinum, palladium, ruthenium, iridium, and rhodium. It involves two coupled reactions that are driven by the optical excitation of electron-hole pairs in the ZnO semiconductor by ultraviolet photons where the excited electrons are used to reduce aqueous metal ions onto the ZnO tetrapod as excited holes are scavenged from the surface. For the most part, the growth mode gives rise to nanoparticles with a roundish morphology that are uniformly distributed on the tetrapod surface. Larger structures with irregular shapes are, however, obtained for syntheses utilizing aqueous metal nitrates as opposed to chlorides, a result that suggests that the anion plays a role in shape determination. It is also demonstrated that changes to the molarity of the metal ion can influence the nanostructure nucleation rate. The catalytic activity of tetrapods decorated with each of the eight metals is assessed using the reduction of 4-nitrophenol by borohydride as a model reaction where it is shown that those decorated with Pd, Ag, and Rh are the most active.

| S-EPMC6139342 | biostudies-literature

Rationally designed bimetallic Au@Pt nanoparticles for glucose oxidation.

Project description:Bimetallic nanoparticles (NPs) have aroused interest in various fields because of their synergetic and unique properties. Among those nanoparticles, we strategically approached and synthesized Au@Pt NPs via the sonochemical method with different molar ratios (e.g. 3:7, 5:5, and 7:3) of Au to Pt precursors. The particle structure was confirmed to be core-shell, and the size was estimated to be 60, 52, and 47?nm, respectively, for 3:7, 5:5, and 7:3 ratios of Au to Pt. The detailed structure and crystallinity of as-prepared Au@Pt NPs were further studied by scanning electron microscopy, transmission electron microscopy with element mapping, and X-ray diffraction. It should be noted that thickness of the dendritic Pt shell in the core-shell structure can be easily tuned by controlling the molar ratio of Au to Pt. To explore the possibility of this material as glucose sensor, we confirmed the detection of glucose using amperometry. Two dynamic ranges in a calibration plot were displayed at 0.5-50.0?µM and 0.05-10.0?mM, and their detection limit as glucose sensor was determined to be 319.8 (±5.4) nM.

| S-EPMC6351680 | biostudies-other

Bifunctional Au@Pt/Au nanoparticles as electrochemiluminescence signaling probes for SARS-CoV-2 detection.

Project description:A novel immunosensor based on electrochemiluminescence resonance energy transfer (ECL-RET) for the sensitive determination of N protein of the SARS-CoV-2 coronavirus is described. For this purpose, bifunctional core@shell nanoparticles composed of a Pt-coated Au core and finally decorated with small Au inlays (Au@Pt/Au NPs) have been synthesized to act as ECL acceptor, using [Ru (bpy)3]2+ as ECL donor. These nanoparticles are efficient signaling probes in the immunosensor developed. The proposed ECL-RET immunosensor has a wide linear response to the concentration of N protein of the SARS-CoV-2 coronavirus with a detection limit of 1.27 pg/mL. Moreover, it has a high stability and shows no response to other proteins related to different virus. The immunosensor has achieved the quantification of N protein of the SARS-CoV-2 coronavirus in saliva samples. Results are consistent with those provided by a commercial colorimetric ELISA kit. Therefore, the developed immunosensor provides a feasible and reliable tool for early and effective detection of the virus to protect the population.

| S-EPMC10166582 | biostudies-literature

The relationship between crystalline disorder and electronic structure of Pd nanoparticles and their hydrogen storage properties.

Project description:We investigated the relationship between crystalline disorder and electronic structure deviations of Pd nanoparticles (NPs) and their hydrogen storage properties as a function of their particle diameter (2.0, 4.6 and 7.6 nm) using various synchrotron techniques. The lattice constant of the 2.0 nm-diameter Pd NPs was observed to be larger than that of the 4.6 or 7.6 nm-diameter Pd NPs. With increasing particle diameter the structural ordering was improved, the lattice constant and atomic displacement were reduced and the coordination numbers increased, as determined using high-energy X-ray diffraction, reverse Monte Carlo modelling and X-ray absorption fine structure spectroscopy. The structural order of the core part of the larger NPs was also better than that of the smaller NPs. In addition, the bond strength of the Pd-H formation increased with increasing particle diameter. Finally, the surface order of the Pd NPs was related to enhancement of the hydrogen storage capacity and Pd-H bond strength.

| S-EPMC9065999 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data