Tribological Behavior of the 316L Stainless Steel with Heterogeneous Lamella Structure.

ABSTRACT: In this paper, the tribological behavior of 316L stainless steel with heterogeneous lamella structure (HLS), prepared through 85% cold rolling technology and subsequent annealing treatment (750 °C, 10 min), were conducted on a ball-on-disc tribometer under different normal loads in dry ambient air conditions. The morphologies, structures, and compositions of the raw and worn surfaces were analyzed by 3D surface profilometer, XRD, SEM, EDS and TEM. Based on this, the results showed that the HLS 316L stainless steel samples exhibited lower and more steady friction coefficients than coarse-grained samples, especially under higher loads, which can be attributed to the existence of numerous oxidative particles across sliding interfaces. However, the wear resistance of HLS 316L stainless steel sample was a little weakened compared to that of the coarse-grained sample under a normal load of 5 N. When the load increases up to 15 N, an obviously decreased wear resistance was found for the HLS of the 316L stainless steel sample, which was 50% lower than that of coarse-grained sample. This can be ascribed to the more severe oxidative and abrasive wear performance of HLS 316L stainless steel sample under dry sliding conditions.

SUBMITTER: Qin W

PROVIDER: S-EPMC6213424 | biostudies-other | 2018 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

Tribological Behavior of the 316L Stainless Steel with Heterogeneous Lamella Structure.

Qin Wenbo W Kang Jiajie J Li Jiansheng J Yue Wen W Liu Yaoyao Y She Dingshun D Mao Qingzhong Q Li Yusheng Y

Materials (Basel, Switzerland) 20180927 10

In this paper, the tribological behavior of 316L stainless steel with heterogeneous lamella structure (HLS), prepared through 85% cold rolling technology and subsequent annealing treatment (750 °C, 10 min), were conducted on a ball-on-disc tribometer under different normal loads in dry ambient air conditions. The morphologies, structures, and compositions of the raw and worn surfaces were analyzed by 3D surface profilometer, XRD, SEM, EDS and TEM. Based on this, the results showed that the HLS 3 ...[more]

PMID: 30261699

Similar Datasets

Project description:Advances in additive manufacturing enable the production of tailored lattice structures and thus, in principle, coronary stents. This study investigates the effects of process-related irregularities, heat and surface treatment on the morphology, mechanical response, and expansion behavior of 316L stainless steel stents produced by laser powder bed fusion and provides a methodological approach for their numerical evaluation. A combined experimental and computational framework is used, based on both actual and computationally reconstructed laser powder bed fused stents. Process-related morphological deviations between the as-designed and actual laser powder bed fused stents were observed, resulting in a diameter increase by a factor of 2-2.6 for the stents without surface treatment and 1.3-2 for the electropolished stent compared to the as-designed stent. Thus, due to the increased geometrically induced stiffness, the laser powder bed fused stents in the as-built (7.11 ± 0.63 N) or the heat treated condition (5.87 ± 0.49 N) showed increased radial forces when compressed between two plates. After electropolishing, the heat treated stents exhibited radial forces (2.38 ± 0.23 N) comparable to conventional metallic stents. The laser powder bed fused stents were further affected by the size effect, resulting in a reduced yield strength by 41% in the as-built and by 59% in the heat treated condition compared to the bulk material obtained from tensile tests. The presented numerical approach was successful in predicting the macroscopic mechanical response of the stents under compression. During deformation, increased stiffness and local stress concentration were observed within the laser powder bed fused stents. Subsequent numerical expansion analysis of the derived stent models within a previously verified numerical model of stent expansion showed that electropolished and heat treated laser powder bed fused stents can exhibit comparable expansion behavior to conventional stents. The findings from this work motivate future experimental/numerical studies to quantify threshold values of critical geometric irregularities, which could be used to establish design guidelines for laser powder bed fused stents/lattice structures.

Dataset Information

Tribological Behavior of the 316L Stainless Steel with Heterogeneous Lamella Structure.

Publications

Tribological Behavior of the 316L Stainless Steel with Heterogeneous Lamella Structure.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets