Fluorinated solid electrolyte interphase enables highly reversible solid-state Li metal battery.

ABSTRACT: Solid-state electrolytes (SSEs) are receiving great interest because their high mechanical strength and transference number could potentially suppress Li dendrites and their high electrochemical stability allows the use of high-voltage cathodes, which enhances the energy density and safety of batteries. However, the much lower critical current density and easier Li dendrite propagation in SSEs than in nonaqueous liquid electrolytes hindered their possible applications. Herein, we successfully suppressed Li dendrite growth in SSEs by in situ forming an LiF-rich solid electrolyte interphase (SEI) between the SSEs and the Li metal. The LiF-rich SEI successfully suppresses the penetration of Li dendrites into SSEs, while the low electronic conductivity and the intrinsic electrochemical stability of LiF block side reactions between the SSEs and Li. The LiF-rich SEI enhances the room temperature critical current density of Li3PS4 to a record-high value of >2 mA cm-2. Moreover, the Li plating/stripping Coulombic efficiency was escalated from 88% of pristine Li3PS4 to more than 98% for LiF-coated Li3PS4. In situ formation of electronic insulating LiF-rich SEI provides an effective way to prevent Li dendrites in the SSEs, constituting a substantial leap toward the practical applications of next-generation high-energy solid-state Li metal batteries.

SUBMITTER: Fan X

PROVIDER: S-EPMC6303121 | biostudies-other | 2018 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Fluorinated electrolytes based on fluoroethylene carbonate (FEC) have been considered as promising alternative electrolytes for high-voltage and high-energy capacity lithium-ion batteries (LIBs). However, the compatibility of the fluorinated electrolytes with graphite negative electrodes is unclear. In this paper, we have systematically investigated, for the first time, the stability of fluorinated electrolytes with graphite negative electrodes, and the result shows that unlike the ethylene carbonate (EC)-based electrolyte, the FEC-based electrolyte (EC was totally replaced by FEC) is incapable of forming a protective and effective solid electrolyte interphase (SEI) that protects the electrolyte from runaway reduction on the graphite surface. The reason is that the lowest unoccupied molecular orbital energy levels are also lowered by the introduction of fluorine into the solvent, and the FEC solvent has poorer resistance against reduction, leading to instability on the graphite negative electrode. To tackle this problem, two lithium salts of lithium bis(oxalato)borate and lithium difluoro(oxalato)borate (LiDFOB) have been investigated as negative-electrode film-forming additives. Incorporation of only 0.5 wt % LiDFOB to a FEC-based electrolyte [1.0 M LiPF6 in 3:7 (FEC-ethyl methyl carbonate)] results in excellent cycling performance of the graphite negative electrode. This improved property originates from the generation of a thinner and better quality SEI film with little LiF by the sacrificial reduction of the LiDFOB additive on the graphite negative electrode surface. On the other hand, this additive can stabilize the electrolyte by scavenging HF. Meanwhile, the incorporated LiDFOB additive has positive influence on the interphase layer on the positive electrode surface and significantly decreases the amount of HF formation, finally leading to improved cycling stability and rate capability of LiNi0.5Mn1.5O4 electrodes at a high cutoff voltage of 5 V. The data demonstrate that the LiDFOB additive not only exhibits a superior compatibility with graphite but also improves the electrochemical properties of high-voltage spinel LiNi0.5Mn1.5O4 positive electrodes considerably, confirming its potential as a prospective, multifunctional additive for 5 V fluorinated electrolytes in high-energy capacity lithium-ion batteries (LIBs).

Dataset Information

Fluorinated solid electrolyte interphase enables highly reversible solid-state Li metal battery.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets