Zeolite Composite Materials from Fly Ash: An Assessment of Physicochemical and Adsorption Properties.

ABSTRACT: Waste fly ash, with both low (with the addition of vermiculite) and high contents of unburned coal, were subjected to hydrothermal syntheses aiming to obtain zeolite composite materials-zeolite + vermiculite (NaX-Ver) and zeolite + unburned carbon (NaX-C). The composites were compared with parent zeolite obtained from waste fly ash with a low content of unburned carbon (NaX-FA). In this study, the physicochemical characteristics of the obtained materials were evaluated. The potential application of the investigated zeolites for the adsorption of ammonium ions from aqueous solutions was determined. Composite NaX-Ver and parent zeolite NaX-FA were characterized by comparable adsorption capacities toward ammonium ions of 38.46 and 40.00 mg (NH₄⁺) g^-1, respectively. The nearly 2-fold lower adsorption capacity of composite NaX-C (21.05 mg (NH₄⁺) g^-1) was probably a result of the lower availability of ion exchange sites within the material. Adsorbents were also regenerated using 1 M NaCl solution at a pH of 10 and subjected to 3 cycles of adsorption-desorption experiments, which proved only a small reduction in adsorption properties. This study follows the current trend of waste utilization (fly ash) and the removal of pollutants from aqueous solutions with respect to their reuse, which remains in line with the goals of the circular economy.

SUBMITTER: Mokrzycki J

PROVIDER: S-EPMC10051483 | biostudies-literature | 2023 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Zeolite Composite Materials from Fly Ash: An Assessment of Physicochemical and Adsorption Properties.

Mokrzycki Jakub J Franus Wojciech W Panek Rafał R Sobczyk Maciej M Rusiniak Piotr P Szerement Justyna J Jarosz Renata R Marcińska-Mazur Lidia L Bajda Tomasz T Mierzwa-Hersztek Monika M

Materials (Basel, Switzerland) 20230307 6

Waste fly ash, with both low (with the addition of vermiculite) and high contents of unburned coal, were subjected to hydrothermal syntheses aiming to obtain zeolite composite materials-zeolite + vermiculite (NaX-Ver) and zeolite + unburned carbon (NaX-C). The composites were compared with parent zeolite obtained from waste fly ash with a low content of unburned carbon (NaX-FA). In this study, the physicochemical characteristics of the obtained materials were evaluated. The potential application ...[more]

PMID: 36984022

Similar Datasets

Project description:Zeolites with different structures (P1, sodalite, and X) were synthesized from coal fly ash by applying ultrasonically assisted hydrothermal and fusion-hydrothermal synthesis. Bimetallic catalysts, containing 5 wt.% Ni and 2.5 wt.% Cu, supported on the zeolites, were prepared by a post-synthesis incipient wetness impregnation method. The catalysts were characterized by X-ray powder diffraction (XRPD), N2 physisorption, transmission electron microscopy (TEM), Mössbauer and X-ray photoelectron spectroscopies (XPS), and H2-temperature-programmed reduction (H2-TPR) analyses. The XRPD results showed that crystalline Cu0 and NixCuy intermetallic nanoparticles were formed in the reduced catalysts. The presence of the intermetallic phase affected the reducibility of the nickel by shifting it to a lower temperature, as confirmed by the H2-TPR curves. Based on the Mössbauer spectroscopic results, it was established that the iron contamination of the coal fly ash zeolites (CFAZs) was distributed in ionic positions of the zeolite lattice and as a finely dispersed iron oxide phase on the external surface of the supports. The formation of the NiFe alloy, not detectable by XRPD, was also evidenced on the impregnated samples. The catalysts were studied in the upgrading of levulinic acid (LA), derived from lignocellulosic biomass, to γ-valerolactone (GVL), in a batch reactor under 30 bar H2 pressure at 150 and 200 °C, applying water as a solvent. The NiCu/SOD and NiCu/X catalysts showed total LA conversion and a high GVL yield (>75%) at a reaction temperature of 200 °C. It was found that the textural parameters of the catalysts have less influence on the catalytic activity, but rather the stable dispersion of metals during the reaction. The characterization of the spent catalyst found the rearrangement of the support structure. The high LA conversion and GVL yield can be attributed to the weak acidic character of the support and the moderate hydrogenation activity of the Ni-Cu sites with high dispersion.

Dataset Information

Zeolite Composite Materials from Fly Ash: An Assessment of Physicochemical and Adsorption Properties.

Publications

Zeolite Composite Materials from Fly Ash: An Assessment of Physicochemical and Adsorption Properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets