Novel Pyrrolidinium-Functionalized Styrene-b-ethylene-b-butylene-b-styrene Copolymer Based Anion Exchange Membrane with Flexible Spacers for Water Electrolysis.

ABSTRACT: Anion exchange membranes (AEM) are core components for alkaline electrochemical energy technologies, such as water electrolysis and fuel cells. They are regarded as promising alternatives for proton exchange membranes (PEM) due to the possibility of using platinum group metal (PGM)-free electrocatalysts. However, their chemical stability and conductivity are still of great concern, which is appearing to be a major challenge for developing AEM-based energy systems. Herein, we highlight an AEM with styrene-b-ethylene-b-butylene-b-styrene copolymer (SEBS) as a backbone and pyrrolidinium or piperidinium functional groups tethered on flexible ethylene oxide spacer side-chains (SEBS-Py2O6). This membrane reached 27.8 mS cm^-1 hydroxide ion conductivity at room temperature, which is higher compared to previously obtained piperidinium-functionalized SEBS reaching up to 10.09 mS cm^-1. The SEBS-Py206 combined with PGM-free electrodes in an AWE water electrolysis (AEMWE) cell achieves 520 mA cm^-2 at 2 V in 0.1 M KOH and 171 mA cm^-2 in ultra-pure water (UPW). This high performance indicates that SEBS-Py2O6 membranes are suitable for application in water electrolysis.

SUBMITTER: Xu Z

PROVIDER: S-EPMC10057012 | biostudies-literature | 2023 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Novel Pyrrolidinium-Functionalized Styrene-b-ethylene-b-butylene-b-styrene Copolymer Based Anion Exchange Membrane with Flexible Spacers for Water Electrolysis.

Xu Ziqi Z Delgado Sofia S Atanasov Vladimir V Morawietz Tobias T Gago Aldo Saul AS Friedrich Kaspar Andreas KA

Membranes 20230313 3

Anion exchange membranes (AEM) are core components for alkaline electrochemical energy technologies, such as water electrolysis and fuel cells. They are regarded as promising alternatives for proton exchange membranes (PEM) due to the possibility of using platinum group metal (PGM)-free electrocatalysts. However, their chemical stability and conductivity are still of great concern, which is appearing to be a major challenge for developing AEM-based energy systems. Herein, we highlight an AEM wit ...[more]

PMID: 36984715

Similar Datasets

Project description:Scaffolds from poly(ethylene oxide) and poly(butylene terephthalate), PEOT/PBT, with a PEO molecular weight of 1,000 and a PEOT content of 70 weight% (1000PEOT70PBT30) were prepared by leaching salt particles (425-500 microm). Scaffolds of 73.5, 80.6 and 85.0% porosity were treated with a CO(2) gas plasma and seeded with rat bone marrow stromal cells (BMSCs). After in vitro culture for 7 days (d) in an osteogenic medium the scaffolds were subcutaneously implanted for 4 weeks in nude mice. Poly(D, L-lactide) (PDLLA) and biphasic calcium phosphate (BCP) scaffolds were included as references. After 4 weeks (wks) all scaffolds showed ectopic formation of bone and bone marrow. For the scaffolds of different porosities, no significant differences were observed in the relative amounts of bone (7-9%) and bone marrow (6-11%) formed, even though micro computed tomography (mu-CT) data showed considerable differences in accessible pore volume and surface area. 1000PEOT70PBT30 scaffolds with a porosity of 85% could not maintain their original shape in vivo. Surprisingly, 1000PEOT70PBT30 scaffolds with a porosity of 73.5% showed cartilage formation. This cartilage formation is most likely due to poorly accessible pores in the scaffolds, as was observed in histological sections. mu-CT data showed a considerably smaller accessible pore volume (as a fraction of the total volume) than in 1000PEOT70PBT30 scaffolds of 80.6 and 85.0% porosity. BMSC seeded PDLLA (83.5% porosity) and BCP scaffolds (29% porosity) always showed considerably more bone and bone marrow formation (bone marrow formation is approximately 40%) and less fibrous tissue ingrowth than the 1000PEOT70PBT30 scaffolds. The scaffold material itself can be of great influence. In more hydrophobic and rigid scaffolds like the PDLLA or BCP scaffolds, the accessibility of the pore structure is more likely to be preserved under the prevailing physiological conditions than in the case of hydrophilic 1000PEOT70PBT30 scaffolds. Scaffolds prepared from other PEOT/PBT polymer compositions, might prove to be more suited.

Dataset Information

Novel Pyrrolidinium-Functionalized Styrene-b-ethylene-b-butylene-b-styrene Copolymer Based Anion Exchange Membrane with Flexible Spacers for Water Electrolysis.

Publications

Novel Pyrrolidinium-Functionalized Styrene-b-ethylene-b-butylene-b-styrene Copolymer Based Anion Exchange Membrane with Flexible Spacers for Water Electrolysis.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets