Tuning Ionic Conductivity in Fluorite Gd-Doped CeO2-Bixbyite RE2O3 (RE = Y and Sm) Multilayer Thin Films by Controlling Interfacial Strain
Ontology highlight
ABSTRACT:
SUBMITTER: Yang G
PROVIDER: S-EPMC10449009 | biostudies-literature | 2023 Aug
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Sm2-xCaxZr2O7-x/2 (x = 0, 0.05, 0.1) and Gd2-xCaxZr2O7-x/2 (x = 0.05, 0.1) mixed oxides in a pyrochlore-fluorite morphotropic phase region were prepared via the mechanical activation of oxide mixtures, followed by annealing at 1600 °C. The structure of the solid solutions was studied by X-ray diffraction and refined by the Rietveld method, water content was determined by thermogravimetry (TG), their bulk and grain-boundary conductivity was determined by impedance spectroscopy in dry and wet air (100-900 °C), and their total conductivity was measured as a function of oxygen partial pressure in the temperature range: 700-950 °C. The Sm2-xCaxZr2O7-x/2 (x = 0.05, 0.1) pyrochlore solid solutions, lying near the morphotropic phase boundary, have proton conductivity contribution both in the grain bulk and on grain boundaries below 600 °C, and pure oxygen-ion conductivity above 700 °C. The 500 °C proton conductivity contribution of Sm2-xCaxZr2O7-x/2 (x = 0.05, 0.1) is ~ 1 × 10-4 S/cm. The fluorite-like Gd2-xCaxZr2O7-x/2 (x = 0.1) solid solution has oxygen-ion bulk conductivity in entire temperature range studied, whereas proton transport contributes to its grain-boundary conductivity below 700 °C. As a result, of the morphotropic phase transition from pyrochlore Sm2-xCaxZr2O7-x/2 (x = 0.05, 0.1) to fluorite-like Gd2-xCaxZr2O7-x/2 (x = 0.05, 0.1), the bulk proton conductivity disappears and oxygen-ion conductivity decreases. The loss of bulk proton conductivity of Gd2-xCaxZr2O7-x/2 (x = 0.05, 0.1) can be associated with the fluorite structure formation. It is important to note that the degree of Ca substitution in such solid solutions (Ln2-xCax)Zr2O7-δ (Ln = Sm, Gd) is low, x < 0.1. In both series, grain-boundary conductivity usually exceeds bulk conductivity. The high grain-boundary proton conductivity of Ln2-xCaxZr2O7-x/2 (Ln = Sm, Gd; x = 0.1) is attributable to the formation of an intergranular CaZrO3-based cubic perovskite phase doped with Sm or Gd in Zr sublattice.
| S-EPMC6696096 | biostudies-literature
Project description:Oxygen vacancies in complex oxides are indispensable for information and energy technologies. There are several means to create oxygen vacancies in bulk materials. However, the use of ionic interfaces to create oxygen vacancies has not been fully explored. Herein, we report an oxide nanobrush architecture designed to create high-density interfacial oxygen vacancies. An atomically well-defined (111) heterointerface between the fluorite CeO2 and the bixbyite Y2O3 is found to induce a charge modulation between Y3+ and Ce4+ ions enabled by the chemical valence mismatch between the two elements. Local structure and chemical analyses, along with theoretical calculations, suggest that more than 10% of oxygen atoms are spontaneously removed without deteriorating the lattice structure. Our fluorite-bixbyite nanobrush provides an excellent platform for the rational design of interfacial oxide architectures to precisely create, control, and transport oxygen vacancies critical for developing ionotronic and memristive devices for advanced energy and neuromorphic computing technologies.
| S-EPMC7069997 | biostudies-literature
Project description:New sodium-based battery concepts require solid electrolytes as ion conducting separators. Besides NaSICON and β-Al2O3 in the Na2O-R2O3-SiO2 system (R = rare earth), a rarely noticed glass-ceramic solid electrolyte with the composition Na5RSi4O12 (N5-type) exists. The present study addresses the investigation of the ionic conductivity of Na5RSi4O12 solid electrolytes sintered from pre-crystallized glass-ceramic powders. The sintering behavior (optical dilatometry), the microstructure (SEM/EDX), and phase composition (XRD), as well as electrochemical properties (impedance spectroscopy), were investigated. To evaluate the effect of the ionic radii, Y, Sm and Gd rare elements were chosen. All compositions were successfully synthesized to fully densified compacts having the corresponding conducting N5-type phase as the main component. The densification behavior was in agreement with the melting point, which decreased with increasing ionic radii and specific cell volume. Alternatively, the ionic conductivities of N5-phases decreased from Y to Gd and Sm containing samples. The highest ionic conductivity of 1.82 × 10-3 S cm-1 at 20 °C was obtained for Na5YSi4O12 composition. The impact of grain boundaries and bulk conductivity on measured values is discussed. A powder-based synthesis method of this glass-ceramic solid electrolyte using different rare earth elements opens possibilities for optimizing ionic conductivity and scalable technological processing by tape casting.
| S-EPMC8838226 | biostudies-literature
Project description:The transition to solid-state Li-ion batteries will enable progress toward energy densities of 1000 W·hour/liter and beyond. Composites of a mesoporous oxide matrix filled with nonvolatile ionic liquid electrolyte fillers have been explored as a solid electrolyte option. However, the simple confinement of electrolyte solutions inside nanometer-sized pores leads to lower ion conductivity as viscosity increases. Here, we demonstrate that the Li-ion conductivity of nanocomposites consisting of a mesoporous silica monolith with an ionic liquid electrolyte filler can be several times higher than that of the pure ionic liquid electrolyte through the introduction of an interfacial ice layer. Strong adsorption and ordering of the ionic liquid molecules render them immobile and solid-like as for the interfacial ice layer itself. The dipole over the adsorbate mesophase layer results in solvation of the Li+ ions for enhanced conduction. The demonstrated principle of ion conduction enhancement can be applied to different ion systems.
| S-EPMC6954068 | biostudies-literature
Project description:The structure and ion-conducting properties of the defect-fluorite ring structure formed around amorphous ion-tracks by swift heavy ion irradiation of Gd2Ti2O7 pyrochlore are investigated. High angle annular dark field imaging complemented with ion-track molecular dynamics simulations show that the atoms in the ring structure are disordered, and have relatively larger cation-cation interspacing than in the bulk pyrochlore, illustrating the presence of tensile strain in the ring region. Density functional theory calculations show that the non-equilibrium defect-fluorite structure can be stabilized by tensile strain. The pyrochlore to defect-fluorite structure transformation in the ring region is predicted to be induced by recrystallization during a melt-quench process and stabilized by tensile strain. Static pair-potential calculations show that planar tensile strain lowers oxygen vacancy migration barriers in pyrochlores, in agreement with recent studies on fluorite and perovskite materials. In view of these results, it is suggested that strain engineering could be simultaneously used to stabilize the defect-fluorite structure and gain control over its high ion-conducting properties.
| S-EPMC4639808 | biostudies-literature
Project description:Sm-doped CeO2-? (Ce0.9Sm0.1O2-?; SDC) thin films were prepared on Al2O3 (0001) substrates by radio frequency magnetron sputtering. The prepared thin films were preferentially grown along the [111] direction, with the spacing of the (111) plane (d111) expanded by 2.6% to compensate for a lattice mismatch against the substrate. The wet-annealed SDC thin film, with the reduced d111 value, exhibited surface protonic conduction in the low-temperature region below 100?°C. The O1s photoemission spectrum exhibits H2O and OH- peaks on the SDC surface. These results indicate the presence of physisorbed water layers and the generation of protons on the SDC (111) surface with oxygen vacancies. The protons generated on the SDC surface were conducted through a physisorbed water layer by the Grotthuss mechanism.
| S-EPMC7026374 | biostudies-literature
Project description:Mixed ionic-electronic conductors are widely used in devices for energy conversion and storage. Grain boundaries in these materials have nanoscale spatial dimensions, which can generate substantial resistance to ionic transport due to dopant segregation. Here, we report the concept of targeted phase formation in a Ce0.8Gd0.2O2-?-CoFe2O4 composite that serves to enhance the grain boundary ionic conductivity. Using transmission electron microscopy and spectroscopy approaches, we probe the grain boundary charge distribution and chemical environments altered by the phase reaction between the two constituents. The formation of an emergent phase successfully avoids segregation of the Gd dopant and depletion of oxygen vacancies at the Ce0.8Gd0.2O2-?-Ce0.8Gd0.2O2-? grain boundary. This results in superior grain boundary ionic conductivity as demonstrated by the enhanced oxygen permeation flux. This work illustrates the control of mesoscale level transport properties in mixed ionic-electronic conductor composites through processing induced modifications of the grain boundary defect distribution.
| S-EPMC4403342 | biostudies-literature
Project description:Straintronics is a new concept to enhance electronic device performances by strain for next-generation information sensors and energy-saving technologies. The lattice deformation in graphene can modulate the thermal conductivity because phonons are the main heat carriers. However, the device fabrication process affects graphene's heat transport properties due to its high stretchability. This study experimentally investigates the change in the thermal conductivity when biaxial tensile strain is applied to graphene. To eliminate non-strain factors, two mechanisms are considered: pressure-induced and electrostatic attraction-induced strain. Raman spectroscopy and atomic force microscopy precisely estimate the strain. The thermal conductivity of graphene decreases by approximately 70% with a strain of only 0.1%. Such thermal conductivity controllability paves the way for applying graphene as high-efficiency thermal switches and diodes in future thermal management devices.
| S-EPMC8486806 | biostudies-literature
Project description:With the evolution of semiconducting industries, thermomechanical failure induced in a multilayered structure with a high aspect ratio during manufacturing and operation has become one of the critical reliability issues. In this work, the effect of thermomechanical stress on the failure of multilayered thin films on Si substrates was studied using analytical calculations and various thermomechanical tests. The residual stress induced during material processing was calculated based on plate bending theory. The calculations enabled the prediction of the weakest region of failure in the thin films. To verify our prediction, additional thermomechanical stress was applied to induce cracking and interfacial delamination by various tests. We assumed that, when accumulated thermomechanical-residual and externally applied mechanical stress becomes larger than a critical value the thin-film cracking or interfacial delamination will occur. The test results agreed well with the prediction based on the analytical calculation in that the film with maximum tensile residual stress is the most vulnerable to failure. These results will provide useful analytical and experimental prediction tools for the failure of multilayered thin films in the device design stage.
| S-EPMC9330259 | biostudies-literature
Project description:The ionic conductivity in lamellar block copolymer electrolytes is often anisotropic, where the in-plane conductivity exceeds the through-plane conductivity by up to an order of magnitude. In a prior work, we showed significant anisotropy in the ionic conductivity of a lamellar block copolymer based on polystyrene (PS) and a polymer ionic liquid (PIL), and we proposed that the through-film ionic conductivity was depressed by layering of lamellar domains near the electrode surface. In the present work, we first tested that conclusion by measuring the through-plane ionic conductivity of two model PIL-based systems having controlled interfacial profiles using impedance spectroscopy. The measurements were not sensitive to changes in interfacial composition or structure, so anisotropy in the ionic conductivity of PS-block-PIL materials must arise from an in-plane enhancement rather than a through-plane depression. We then examined the origin of this in-plane enhancement with a series of PS-block-PIL materials, a P(S-r-IL) copolymer, and a PIL homopolymer, where impedance spectra were acquired with a top-contact electrode configuration. These studies show that enhanced in-plane ionic conductivities are correlated with the formation of an IL-rich wetting layer at the free surface, which presumably provides a low-resistance path for ion transport between the electrodes. Importantly, the enhanced in-plane ionic conductivities in these PS-block-PIL materials are consistent with simple geometric arguments based on properties of the PIL, while the through-plane values are an order of magnitude lower. Consequently, it is critical to understand how surface and bulk effects contribute to impedance spectroscopy measurements when developing structure-conductivity relations in this class of materials.
| S-EPMC10416321 | biostudies-literature