Metal-organic framework template-guided electrochemical lithography on substrates for SERS sensing applications.

ABSTRACT: The templating method holds great promise for fabricating surface nanopatterns. To enhance the manufacturing capabilities of complex surface nanopatterns, it is important to explore new modes of the templates beyond their conventional masking and molding modes. Here, we employed the metal-organic framework (MOF) microparticles assembled monolayer films as templates for metal electrodeposition and revealed a previously unidentified guiding growth mode enabling the precise growth of metallic films exclusively underneath the MOF microparticles. The guiding growth mode was induced by the fast ion transportation within the nanochannels of the MOF templates. The MOF template could be repeatedly used, allowing for the creation of identical metallic surface nanopatterns for multiple times on different substrates. The MOF template-guided electrochemical growth mode provided a robust route towards cost-effective fabrication of complex metallic surface nanopatterns with promising applications in metamaterials, plasmonics, and surface-enhanced Raman spectroscopy (SERS) sensing fields.

SUBMITTER: Lu Y

PROVIDER: S-EPMC10511444 | biostudies-literature | 2023 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Metal-organic framework template-guided electrochemical lithography on substrates for SERS sensing applications.

Lu Youyou Y Zhang Xuan X Zhao Liyan L Liu Hong H Yan Mi M Zhang Xiaochen X Mochizuki Kenji K Yang Shikuan S

Nature communications 20230920 1

The templating method holds great promise for fabricating surface nanopatterns. To enhance the manufacturing capabilities of complex surface nanopatterns, it is important to explore new modes of the templates beyond their conventional masking and molding modes. Here, we employed the metal-organic framework (MOF) microparticles assembled monolayer films as templates for metal electrodeposition and revealed a previously unidentified guiding growth mode enabling the precise growth of metallic films ...[more]

PMID: 37730799

Similar Datasets

Project description:Less defective, nitrogen-doped 3-dimensional graphene (N3DG) and defect-rich, nitrogen-doped 3-dimensional graphene (N3DG-D) were made by the thermal CVD (Chemical Vapor Deposition) process via varying the carbon precursors and synthesis temperature. These modified 3D graphene materials were compared with pristine 3-dimensional graphene (P3DG), which has fewer defects and no nitrogen in its structure. The different types of graphene obtained were characterized for morphological, structural, and compositional assessment through Scanning Electron Microscopy (SEM), Raman Spectroscopy, and X-ray Photoelectron Spectroscopy (XPS) techniques. Electrodes were fabricated, and electrochemical characterizations were conducted to evaluate the suitability of the three types of graphene for heavy metal sensing (lead) and Electric Double-Layer Capacitor (EDLC) applications. Initially, the various electrodes were treated with a mixture of 2.5 mM Ruhex (Ru (NH3)6Cl3 and 25 mM KCl to confirm that all the electrodes underwent a reversible and diffusion-controlled electrochemical process. Defect-rich graphene (N3DG-D) revealed the highest current density, followed by pristine (P3DG) and less-defect graphene (N3DG). Further, the three types of graphene were subjected to a sensing test by square wave anodic stripping voltammetry (SWASV) for lead detection. The obtained preliminary results showed that the N3DG material provided a great lead-sensing capability, detecting as little as 1 µM of lead in a water solution. The suitability of the electrodes to be employed in an Electric Double-Layer Capacitor (EDLC) was also comparatively assessed. Electrochemical characterization using 1 M sodium sulfate electrolyte was conducted through cyclic voltammetry and galvanostatic charge-discharge studies. The voltammogram and the galvanostatic charge-discharge (GCD) curves of the three types of graphene confirmed their suitability to be used as EDLC. The N3DG electrode proved superior with a gravimetric capacitance of 6.1 mF/g, followed by P3DG and N3DG, exhibiting 1.74 mF/g and 0.32 mF/g, respectively, at a current density of 2 A/g.

Dataset Information

Metal-organic framework template-guided electrochemical lithography on substrates for SERS sensing applications.

Publications

Metal-organic framework template-guided electrochemical lithography on substrates for SERS sensing applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets