Simultaneous Post and Cone Fractures of a Polyethylene Insert in a Mobile-Bearing Posterior-Stabilized Total Knee Arthroplasty.

ABSTRACT: We report a novel case of the simultaneous post and cone fractures of a polyethylene (PE) insert in a mobile-bearing posterior-stabilized total knee arthroplasty. Twelve years after the primary total knee arthroplasty, the 72-year-old male patient presented with a recurring right knee instability and was diagnosed with the wear of the PE insert based on physical and radiological examinations. Revision surgery was performed. The post and cone of the PE insert had fractured simultaneously. Moreover, the femoral and tibial components were in direct contact with each other. One year post-revision, knee function had improved. To diagnose a PE breakage, such as a post or cone fracture, surgeons should consider the possibility of PE breakage even in the absence of pain since patients might complain of subjective instability only.

SUBMITTER: Ueyama H

PROVIDER: S-EPMC10881304 | biostudies-literature | 2024 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Simultaneous Post and Cone Fractures of a Polyethylene Insert in a Mobile-Bearing Posterior-Stabilized Total Knee Arthroplasty.

Ueyama Hideki H Fukunaga Kenji K Takemura Susumu S Koyanagi Junichiro J Yamamura Mitsuyoshi M Nakagawa Shigeru S

Arthroplasty today 20240216

We report a novel case of the simultaneous post and cone fractures of a polyethylene (PE) insert in a mobile-bearing posterior-stabilized total knee arthroplasty. Twelve years after the primary total knee arthroplasty, the 72-year-old male patient presented with a recurring right knee instability and was diagnosed with the wear of the PE insert based on physical and radiological examinations. Revision surgery was performed. The post and cone of the PE insert had fractured simultaneously. Moreove ...[more]

PMID: 38389865

Similar Datasets

Project description:Background and purpose - Backside wear of the polyethylene insert in total knee arthroplasty (TKA) can produce clinically significant levels of polyethylene debris, which can lead to loosening of the tibial component. Loosening due to polyethylene debris could theoretically be reduced in tibial components of monoblock polyethylene design, as there is no backside wear. We investigated the effect of 2 different tibial component designs, monoblock and modular polyethylene, on migration of the tibial component in uncemented TKA. Patients and methods - In this randomized study, 53 patients (mean age 61 years), 32 in the monoblock group and 33 in the modular group, were followed for 2 years. Radiostereometric analysis (RSA) was done postoperatively after weight bearing and after 3, 6, 12, and 24 months. The primary endpoint of the study was comparison of the tibial component migration (expressed as maximum total point motion (MTPM)) of the 2 different implant designs. Results - We did not find any statistically significant difference in MTPM between the groups at 3 months (p = 0.2) or at 6 months (p = 0.1), but at 12 and 24 months of follow-up there was a significant difference in MTPM of 0.36 mm (p = 0.02) and 0.42 mm (p = 0.02) between groups, with the highest amount of migration (1.0 mm) in the modular group. The difference in continuous migration (MTPM from 12 and 24 months) between the groups was 0.096 mm (p = 0.5), and when comparing MTPM from 3-24 months, the difference between the groups was 0.23 mm (p = 0.07). Interpretation - In both study groups, we found the early migration pattern expected, with a relatively high initial amount of migration from operation to 3 months of follow-up, followed by stabilization of the implant with little migration thereafter. However, the modular implants had a statistically significantly higher degree of migration compared to the monoblock. We believe that the greater stiffness of the modular implants was the main reason for the difference in migration, but an initial creep in the polyethylene metal-back locking mechanism of the modular group could also be a possible explanation for the observed difference in migration between the 2 study groups.

Dataset Information

Simultaneous Post and Cone Fractures of a Polyethylene Insert in a Mobile-Bearing Posterior-Stabilized Total Knee Arthroplasty.

Publications

Simultaneous Post and Cone Fractures of a Polyethylene Insert in a Mobile-Bearing Posterior-Stabilized Total Knee Arthroplasty.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets