Nontraumatic tibial polyethylene insert cone fracture in mobile-bearing posterior-stabilized total knee arthroplasty.

ABSTRACT: A 72-year-old male patient underwent mobile-bearing posterior-stabilized total knee arthroplasty for osteoarthritis. He experienced a nontraumatic polyethylene tibial insert cone fracture 27 months after surgery. Scanning electron microscopy of the fracture surface of the tibial insert cone suggested progress of ductile breaking from the posterior toward the anterior of the cone due to repeated longitudinal bending stress, leading to fatigue breaking at the anterior side of the cone, followed by the tibial insert cone fracture at the anterior side of the cone, resulting in fracture at the base of the cone. This analysis shows the risk of tibial insert cone fracture due to longitudinal stress in mobile-bearing posterior-stabilized total knee arthroplasty in which an insert is designed to highly conform to the femoral component.

SUBMITTER: Tanikake Y

PROVIDER: S-EPMC5247562 | biostudies-literature | 2016 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nontraumatic tibial polyethylene insert cone fracture in mobile-bearing posterior-stabilized total knee arthroplasty.

Tanikake Yohei Y Hayashi Koji K Ogawa Munehiro M Inagaki Yusuke Y Kawate Kenji K Tomita Tetsuya T Tanaka Yasuhito Y

Arthroplasty today 20160915 4

A 72-year-old male patient underwent mobile-bearing posterior-stabilized total knee arthroplasty for osteoarthritis. He experienced a nontraumatic polyethylene tibial insert cone fracture 27 months after surgery. Scanning electron microscopy of the fracture surface of the tibial insert cone suggested progress of ductile breaking from the posterior toward the anterior of the cone due to repeated longitudinal bending stress, leading to fatigue breaking at the anterior side of the cone, followed by ...[more]

PMID: 28326421

Similar Datasets

Project description:BackgroundThe controversy regarding the outcome of total knee arthroplasties after high tibial osteotomy may relate to malalignment secondary to overcorrection after high tibial osteotomy (HTO) [1, 2] and to the type of arthroplasty itself (posterior-stabilized arthroplasty or posterior cruciate ligament-retaining prosthesis).Questions/purposeWe asked two questions: (1) Would a posterior-stabilized arthroplasty provide sufficient constrain and improve pain and function in patients with severe malalignment due to a previous HTO? (2) Will malalignment of the previous HTO jeopardize the long-term results of a total knee reconstruction with a posterior-stabilized implant?Patients and methodsWe retrospectively reviewed 25 posterior-stabilized TKAs in 25 patients with severe valgus deformity after HTO (ranging from 10° to 20° of valgus) and compared the results with a series of matched 25 posterior-stabilized TKAs in 25 patients with normocorrection after HTO ranging from 5° of valgus to 5° of varus. Clinical, operative, and radiographic data were reviewed. Minimum follow-up was 10 years after the arthroplasty (average, 15 years; range, 10-20 years).ResultsAll the knees had standard posterior-stabilized total knee arthroplasty implants. Patients with an overcorrected HTO were more likely to require a soft tissue release to balance the knee. However, Average Knee Society and Function Score improved, respectively, from 48 to 85 and from 50 to 90 points in the severely overcorrected group, versus, respectively, 50 to 89 and 52 to 97 in the normocorrected group, but the range of mobility was superior for patients with normal alignment. Fifteen-year survivorship after the arthroplasty comparison showed no significant difference between the two groups (one revision in each group).ConclusionsPatients with an overcorrected HTO are more likely to require a soft tissue release to balance the knee. However, both groups show improvements in function and pain. With a posterior-stabilized arthroplasty, the degree of deformity has no impact on the longevity of the TKA.

Project description:Background and purpose - Backside wear of the polyethylene insert in total knee arthroplasty (TKA) can produce clinically significant levels of polyethylene debris, which can lead to loosening of the tibial component. Loosening due to polyethylene debris could theoretically be reduced in tibial components of monoblock polyethylene design, as there is no backside wear. We investigated the effect of 2 different tibial component designs, monoblock and modular polyethylene, on migration of the tibial component in uncemented TKA. Patients and methods - In this randomized study, 53 patients (mean age 61 years), 32 in the monoblock group and 33 in the modular group, were followed for 2 years. Radiostereometric analysis (RSA) was done postoperatively after weight bearing and after 3, 6, 12, and 24 months. The primary endpoint of the study was comparison of the tibial component migration (expressed as maximum total point motion (MTPM)) of the 2 different implant designs. Results - We did not find any statistically significant difference in MTPM between the groups at 3 months (p = 0.2) or at 6 months (p = 0.1), but at 12 and 24 months of follow-up there was a significant difference in MTPM of 0.36 mm (p = 0.02) and 0.42 mm (p = 0.02) between groups, with the highest amount of migration (1.0 mm) in the modular group. The difference in continuous migration (MTPM from 12 and 24 months) between the groups was 0.096 mm (p = 0.5), and when comparing MTPM from 3-24 months, the difference between the groups was 0.23 mm (p = 0.07). Interpretation - In both study groups, we found the early migration pattern expected, with a relatively high initial amount of migration from operation to 3 months of follow-up, followed by stabilization of the implant with little migration thereafter. However, the modular implants had a statistically significantly higher degree of migration compared to the monoblock. We believe that the greater stiffness of the modular implants was the main reason for the difference in migration, but an initial creep in the polyethylene metal-back locking mechanism of the modular group could also be a possible explanation for the observed difference in migration between the 2 study groups.

Dataset Information

Nontraumatic tibial polyethylene insert cone fracture in mobile-bearing posterior-stabilized total knee arthroplasty.

Publications

Nontraumatic tibial polyethylene insert cone fracture in mobile-bearing posterior-stabilized total knee arthroplasty.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets