Heterostructured electrode with concentration gradient shell for highly efficient oxygen reduction at low temperature.

ABSTRACT: Heterostructures of oxides have been widely investigated in optical, catalytic and electrochemical applications, because the heterostructured interfaces exhibit pronouncedly different transport, charge, and reactivity characteristics compared to the bulk of the oxides. Here we fabricated a three-dimensional (3D) heterostructured electrode with a concentration gradient shell. The concentration gradient shell with the composition of Ba(0.5-x)Sr(0.5-y)Co(0.8)Fe(0.2)O(3-δ) (BSCF-D) was prepared by simply treating porous Ba(0.5)Sr(0.5)Co(0.8)Fe(0.2)O(3-δ) (BSCF) backbone with microwave-plasma. Electrochemical impedance spectroscopy reveals that the oxygen surface exchange rate of the BSCF-D is enhanced by ~250% that of the pristine BSCF due to the appearance of the shell. The heterostructured electrode shows an interfacial resistance as low as 0.148 Ω cm(2) at 550°C and an unchanged electrochemical performance after heating treatment for 200 h. This method offers potential to prepare heterostructured oxides not only for electrochemical devices but also for many other applications that use ceramic materials.

SUBMITTER: Zhou W

PROVIDER: S-EPMC3240982 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Hierarchical CO(2)-protective shell for highly efficient oxygen reduction reaction.

Project description:The widespread application of intermediate-temperature solid oxide fuel cells is mainly being hurdled by the cathode's low efficiency on oxygen reduction reaction and poor resistance to carbon dioxide impurity. Here we report the fabrication of a hierarchical shell-covered porous cathode through infiltration followed by microwave plasma treatment. The hierarchical shell consists of a dense thin-film substrate with cones on the top of the substrate, leading to a three-dimensional (3D) heterostructured electrode. The shell allows the cathode working stably in CO(2)-containing air, and significantly improving the cathode's oxygen reduction reactivity with an area specific resistance of ?0.13 ?cm(2) at 575°C. The method is also suitable for fabricating functional shell on the irregularly shaped substrate in various applications.

| S-EPMC3309399 | biostudies-literature

Small Reduced Graphene Oxides for Highly Efficient Oxygen Reduction Catalysts.

Project description:We demonstrated highly efficient oxygen reduction catalysts composed of uniform Pt nanoparticles on small, reduced graphene oxides (srGO). The reduced graphene oxide (rGO) size was controlled by applying ultrasonication, and the resultant srGO enabled the morphological control of the Pt nanoparticles. The prepared catalysts provided efficient surface reactions and exhibited large surface areas and high metal dispersions. The resulting Pt/srGO samples exhibited excellent oxygen reduction performance and high stability over 1000 cycles of accelerated durability tests, especially the sample treated with 2 h of sonication. Detailed investigations of the structural and electrochemical properties of the resulting catalysts suggested that both the chemical functionality and electrical conductivity of these samples greatly influence their enhanced oxygen reduction efficiency.

| S-EPMC8625579 | biostudies-literature

Highly efficient oxygen reduction electrocatalysts based on winged carbon nanotubes.

Project description:Developing electrocatalysts with both high selectivity and efficiency for the oxygen reduction reaction (ORR) is critical for several applications including fuel cells and metal-air batteries. In this work we developed high performance electrocatalysts based on unique winged carbon nanotubes. We found that the outer-walls of a special type of carbon nanotubes/nanofibers, when selectively oxidized, unzipped and exfoliated, form graphene wings strongly attached to the inner tubes. After doping with nitrogen, the winged nanotubes exhibited outstanding activity toward catalyzing the ORR through the four-electron pathway with excellent stability and methanol/carbon monoxide tolerance. While the doped graphene wings with high active site density bring remarkable catalytic activity, the inner tubes remain intact and conductive to facilitate electron transport during electrocatalysis.

| S-EPMC3824170 | biostudies-other

Flame Spray Pyrolysis Co3O4/CoO as Highly-Efficient Nanocatalyst for Oxygen Reduction Reaction.

Project description:The oxygen reduction reaction (ORR) is the rate-limiting reaction in the cathode side of fuel cells. In the quest for alternatives to Pt-electrodes as cathodes in ORR, appropriate transition metal oxide-based electrocatalysts are needed. In the present work, we have synthesized Co3O4 and CoO/Co3O4 nanostructures using flame spray pyrolysis (FSP), as electrocatalysts for ORR in acidic and alkaline media. A detailed study of the effect of (Co-oxide)/Pt ratio on ORR efficiency shows that the present FSP-made Co-oxides are able to perform ORR at very low-Pt loading, 0.4% of total metal content. In acid medium, an electrode with (5.2% Pt + 4.8% Co3O4), achieved the highest ORR performance (Jmax = 8.31 mA/cm2, E1/2 = 0.66 V). In alkaline medium, superior performance and stability have been achieved by an electrode with (0.4%Pt + 9.6% (CoO/Co3O4)) with ORR activity (Jmax = 3.5 mA/cm2, E1/2 = 0.08 V). Using XRD, XPS, Raman and TEM data, we discuss the structural and electronic aspects of the FSP-made Co-oxide catalysts in relation to the ORR performance. Cyclic voltammetry data indicate that the ORR process involves active sites associated with Co3+ cations at the cobalt oxide surface. Technology-wise, the present work demonstrates that the developed FSP-protocols, constitutes a novel scalable process for production of co-oxides appropriate for oxygen reduction reaction electrodes.

| S-EPMC8066371 | biostudies-literature

Highly Efficient Oxygen Reduction N-Doped Carbon Nanosheets Were Prepared by Hydrothermal Carbonization.

Project description:A metal-free carbon catalyst is a kind of oxygen reduction catalyst with great prospects. It is an important material with potential to replace the traditional Pt catalyst. In this paper, a kind of irregular and ultra-thin carbon nanosheet (K180M-300-900) with high catalytic activity was synthesized by hydrothermal calcination using okra as a biomass and NH4Cl as an N source. The prepared nitrogen-doped metal-free catalyst with high pyridine-N and graphitic-N provides an extremely large number of active sites and has certain lattice defects. Ultra-thin carbon nanosheets promote sufficient contact between the catalyst and electrolyte, promote the diffusion of oxygen, and result in a faster transfer rate of electrons. The initial potential and half-slope potential of K180M-300-900 are 0.99 V and 0.82 V, respectively, which are comparable to those of 20% Pt/C. In addition, the stability and methanol tolerance of this catalyst (K180M-300-900) are better than 20% Pt/C, so it has great development potential and application value. This result provides a new method to prepare metal-free carbon materials that will take the place of traditional Pt catalysts.

| S-EPMC10780226 | biostudies-literature

Nano conductive ceramic wedged graphene composites as highly efficient metal supports for oxygen reduction.

Project description:A novel conductive ceramic/graphene nanocomposite is prepared to prohibit the re-stacking of reduced graphene oxide (RGO) by wedging zirconium diboride (ZrB2) nanoparticles (NPs) into multiple layer nanosheets using a simple solvothermal method. Surprisingly, the RGO/ZrB2 nanocomposite supported Pt NPs shows very excellent catalytic activity. Its electrochemical surface area (ECSA) is up to 148 m(2)g(-1) (very approaches the geometry surface area of 155 m(2)g(-1)), much greater than that of the previous report (usually less than 100 m(2)g(-1)). The mass activity is as high as 16.8 A/g(-1), which is almost 2 times and 5 times that of Pt/RGO (8.6 A/g(-1)) and Pt/C (3.2 A/g(-1)), respectively, as benchmarks. Moreover, after 4000 cycles the catalyst shows only 61% of ECSA loss, meaning a predominantly electrochemical stability. The remarkably improved electrochemical properties with much high Pt utilization of the new catalyst show a promising application in low temperature fuel cells and broader fields.

| S-EPMC3913918 | biostudies-literature

Enhanced Oxygen Electrocatalysis in Heterostructured Ceria Electrolytes for Intermediate-Temperature Solid Oxide Fuel Cells.

Project description:Heterostructured composite ceria electrolytes have been shown to accelerate the oxygen reduction activity and provide a new approach to improve solid oxide fuel cell (SOFC) performance. In this study, barium carbonate was added to gadolinium-doped ceria, Gd0.2Ce0.8O2-δ (GDC) electrolyte to improve the electrochemical performance of intermediate-temperature SOFCs. The heterostructured electrolyte was formed by the addition of 5 wt % BaCO3 to a GDC electrolyte, resulting in a reaction during sintering that formed well-dispersed BaCe0.8Gd0.2O3-δ (BCG) throughout the electrolyte. The resulting material was tested as an electrolyte using La0.6Sr0.4Co0.2Fe0.8O3-δ as a cathode, resulting in a dramatic reduction to the polarization resistance of more than half the value (600 and 700 °C, the resistance was reduced from 2.49 and 0.23 Ω cm2 to 1.21 and 0.12 Ω cm2) obtained by using pure GDC as an electrolyte. Furthermore, full cell SOFC tests employing the heterostructured electrolyte conducted during overextended durations indicated that the BCG phase in the 5BCG-GDC electrolyte was stable in an air atmosphere with no observed reactions with residual CO2. This approach of tailoring surface reactivity by tailoring the composition and structure of the electrolyte as opposed to electrode materials provides an alternative method to improve fuel cell performance.

| S-EPMC6644590 | biostudies-literature

Al13@Pt42 core-shell cluster for oxygen reduction reaction.

Project description:To increase Pt utilization for oxygen reduction reaction (ORR) in fuel cells, reducing particle sizes of Pt is a valid way. However, poisoning or surface oxidation limits the smallest size of Pt particles at 2.6 nm with a low utility of 20%. Here, using density functional theory calculations, we develop a core-shell Al13@Pt42 cluster as a catalyst for ORR. Benefit from alloying with Al in this cluster, the covalent Pt-Al bonding effectively activates the Pt atoms at the edge sites, enabling its high utility up to 70%. Valuably, the adsorption energy of O is located at the optimal range with 0.0-0.4 eV weaker than Pt(111), while OH-poisoning does not observed. Moreover, ORR comes from O2 dissociation mechanism where the rate-limiting step is located at OH formation from O and H with a barrier of 0.59 eV, comparable with 0.50 eV of OH formation from O and H2O on Pt(111).

| S-EPMC5381497 | biostudies-literature

Highly Active and Stable Pt-Pd Alloy Catalysts Synthesized by Room-Temperature Electron Reduction for Oxygen Reduction Reaction.

Project description:Carbon-supported platinum (Pt) and palladium (Pd) alloy catalyst has become a promising alternative electrocatalyst for oxygen reduction reaction (ORR) in proton exchange membrane fuel cells. In this work, the synthesis of highly active and stable carbon-supported Pt-Pd alloy catalysts is reported with a room-temperature electron reduction method. The alloy nanoparticles thus prepared show a particle size around 2.6 nm and a core-shell structure with Pt as the shell. With this structure, the breaking of O-O bands and desorption of OH are both promoted in electrocatalysis of ORR. In comparison with the commercial Pt/C catalyst prepared by conventional method, the mass activity of the Pt-Pd/C catalyst for ORR is shown to increase by a factor of ?4. After 10 000-cycle durability test, the Pt-Pd/C catalyst is shown to retain 96.5% of the mass activity, which is much more stable than that of the commercial Pt/C catalyst.

| S-EPMC5396164 | biostudies-other

Stable, Efficient, Copper Coordination Polymer-Derived Heterostructured Catalyst for Oxygen Evolution under pH-Universal Conditions.

Project description:The constructure of a heterostructured interface is an effective way to design highly durable and efficient water oxidation electrocatalysts. Herein, Cu/CuCN with heterointerfaces is the first synthesized case through a simple epitaxial-like growth method, displaying superior activity and stability under pH-universal media. Associated with high electron transport and transfer of the epitaxial interfacial area, the Cu/CuCN pre-catalyst is applied to deliver the oxygen evolution reaction (OER) with lower overpotentials of 250 mV (forward scan) and 380 mV (backward scan) at 10 mA cm-2 and demonstrates better intrinsic activity (jECSA of 1.0 mA cm-2 at 420 mV) and impressive stability (136 h) in 1.0 M KOH, which exceeds most previous catalysts. Even using a nominal voltage of 1.5 V of a AA battery can drive the overall water-splitting setup. Experiments combined with theoretical simulations further uncover the existence of CuO species at the heterointerface during basic OER, which is evidence of better OER performance with abundant active sites that accelerate the conversion kinetics.

| S-EPMC8289192 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data