Dataset Information

Thermally sensitive block copolymer particles prepared via aerosol flow reactor method: Morphological characterization and behavior in water.

ABSTRACT: This work describes properties of thermo-sensitive submicron sized particles having the same chemical composition but different morphologies. These particles have been prepared with an aerosol technique using dimethylformamide solutions of linear polystyrene-block-poly(N-isopropylacrylamide-block-polystyrene, PS-b-PNIPAM-b-PS. The particles were characterized by cryo-electron microscopy, microcalorimetry, and light scattering. Block-copolymers self-assembled within the particles forming onion-like, gyroid-like, and spherical morphologies having poly(N-isopropylacrylamide) matrix and physically cross-linking polystyrene domains. The particles were dispersed in aqueous media and their behavior in water was studied both below and above the lower critical solution temperature of poly(N-isopropylacrylamide). We found out that the particles with spherical and gyroid-like morphologies swell considerably in water at 20 °C, whereas at 40 °C the particles resemble more of those studied without water treatment. Light scattering experiments showed that the particles gradually aggregate and precipitate with time at 40 °C. Microcalorimetric studies revealed for all three studied morphologies that PNIPAM undergoes a two-step transition due to the different hydration levels of PNIPAM inside and outside the particles. Thicknesses of the PS and PNIPAM layers within the onion-like particles were analyzed using the TEM micrographs by fitting a model of electron density to the integrated electron intensity data. The surface layer of the particles was found out to be PNIPAM, which was supported by light scattering and microcalorimetry. It was also found out from the TEM micrograph analysis that the width of the outmost PS layer is considerably thinner than the one in the dry state prior to immersion in water, and a degradation scheme is proposed to explain these results.

SUBMITTER: Nykanen A

PROVIDER: S-EPMC3494880 | biostudies-literature | 2012 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Thermally sensitive block copolymer particles prepared via aerosol flow reactor method: Morphological characterization and behavior in water.

Nykänen Antti A Rahikkala Antti A Hirvonen Sami-Pekka SP Aseyev Vladimir V Tenhu Heikki H Mezzenga Raffaele R Raula Janne J Kauppinen Esko E Ruokolainen Janne J

Macromolecules 20121010 20

This work describes properties of thermo-sensitive submicron sized particles having the same chemical composition but different morphologies. These particles have been prepared with an aerosol technique using dimethylformamide solutions of linear polystyrene-block-poly(N-isopropylacrylamide-block-polystyrene, PS-b-PNIPAM-b-PS. The particles were characterized by cryo-electron microscopy, microcalorimetry, and light scattering. Block-copolymers self-assembled within the particles forming onion-li ...[more]

PMID: 23150721

Similar Datasets

Project description:Cationic non-viral vectors show great potential to introduce genetic material into cells, due to their ability to transport large amounts of genetic material and their high synthetic versatility. However, designing materials that are effective without showing toxic effects or undergoing non-specific interactions when applied systemically remains a challenge. The introduction of shielding polymers such as polyethylene glycol (PEG) can enhance biocompatibility and circulation time, however, often impairs transfection efficiency. Herein, a multicomponent polymer system is introduced, based on cationic and hydrophobic particles (P(nBMA46-co-MMA47-co-DMAEMA90), (PBMD)) with high delivery performance and a pH-responsive block copolymer (poly((N-acryloylmorpholine)-b-(2-(carboxy)ethyl acrylamide)) (P(NAM72-b-CEAm74), PNC)) as shielding system, with PNAM as alternative to PEG. The pH-sensitive polymer design promotes biocompatibility and excellent stability at extracellular conditions (pH 7.4) and also allows endosomal escape and thus high transfection efficiency under acidic conditions. PNC shielded particles are below 200 nm in diameter and showed stable pDNA complexation. Further, interaction with human erythrocytes at extracellular conditions (pH 7.4) was prevented, while acidic conditions (pH 6) enabled membrane leakage. The particles demonstrate transfection in adherent (HEK293T) as well as difficult-to-transfect suspension cells (K-562), with comparable or superior efficiency compared to commercial linear poly(ethylenimine) (LPEI). Besides, the toxicity of PNC-shielded particles was significantly minimized, in particular in K-562 cells and erythrocytes. In addition, a pilot in vivo experiment on bone marrow blood cells of mice that were injected with PNC-shielded particles, revealed slightly enhanced cell transfection in comparison to naked pDNA. This study demonstrates the applicability of cationic hydrophobic polymers for transfection of adherent and suspension cells in culture as well as in vivo by co-formulation with pH-responsive shielding polymers, without substantially compromising transfection performance.

Project description:Well-defined sterically stabilized diblock copolymer nanoparticles of 29 nm diameter are prepared by RAFT aqueous emulsion polymerization of methyl methacrylate using a dithiobenzoate-capped poly(glycerol monomethacrylate) precursor. These nanoparticles are evaluated as a dispersant for the preparation of organic crystalline microparticles via ball milling. This is exemplified for azoxystrobin, which is a broad-spectrum fungicide that is widely used to protect various food crops. Laser diffraction and optical microscopy studies indicate the formation of azoxystrobin microparticles of approximately 2 μm diameter after ball milling for 10 min at 400 rpm. Nanoparticle adsorption at the surface of these azoxystrobin microparticles is confirmed by electron microscopy studies. The extent of nanoparticle adsorption on the azoxystrobin microparticles can be quantified using a supernatant assay based on solution densitometry. This technique indicates an adsorbed amount of approximately 5.5 mg m-2, which is sufficient to significantly reduce the negative zeta potential exhibited by azoxystrobin. Moreover, this adsorbed amount appears to be essentially independent of the nature of the core-forming block, with similar data being obtained for both poly(methyl methacrylate)- and poly(2,2,2-trifluoroethyl methacrylate)-based nanoparticles. Finally, X-ray photoelectron spectroscopy studies confirm attenuation of the underlying N1s signal arising from the azoxystrobin microparticles by the former adsorbed nanoparticles, suggesting a fractional surface coverage of approximately 0.24. This value is consistent with a theoretical surface coverage of 0.25 calculated from the adsorption isotherm data. Overall, this study suggests that sterically stabilized diblock copolymer nanoparticles may offer a useful alternative approach to traditional soluble copolymer dispersants for the preparation of suspension concentrates affecting the context of agrochemical applications.

Dataset Information

Thermally sensitive block copolymer particles prepared via aerosol flow reactor method: Morphological characterization and behavior in water.

Publications

Thermally sensitive block copolymer particles prepared via aerosol flow reactor method: Morphological characterization and behavior in water.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets