Electron transport of WS2 transistors in a hexagonal boron nitride dielectric environment

ABSTRACT: We present the first study of the intrinsic electrical properties of WS2 transistors fabricated with two different dielectric environments WS2 on SiO2 and WS2 on h-BN/SiO2, respectively. A comparative analysis of the electrical characteristics of multiple transistors fabricated from natural and synthetic WS2 with various thicknesses from single- up to four-layers and over a wide temperature range from 300?K down to 4.2?K shows that disorder intrinsic to WS2 is currently the limiting factor of the electrical properties of this material. These results shed light on the role played by extrinsic factors such as charge traps in the oxide dielectric thought to be the cause for the commonly observed small values of charge carrier mobility in transition metal dichalcogenides.

SUBMITTER: Withers F

PROVIDER: S-EPMC4021321 | biostudies-literature | 2014 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Revealing low-loss dielectric near-field modes of hexagonal boron nitride by photoemission electron microscopy.

Project description:Low-loss dielectric modes are important features and functional bases of fundamental optical components in on-chip optical devices. However, dielectric near-field modes are challenging to reveal with high spatiotemporal resolution and fast direct imaging. Herein, we present a method to address this issue by applying time-resolved photoemission electron microscopy to a low-dimensional wide-bandgap semiconductor, hexagonal boron nitride (hBN). Taking a low-loss dielectric planar waveguide as a fundamental structure, static vector near-field vortices with different topological charges and the spatiotemporal evolution of waveguide modes are directly revealed. With the lowest-order vortex structure, strong nanofocusing in real space is realized, while near-vertical photoemission in momentum space and narrow spread in energy space are simultaneously observed due to the atomically flat surface of hBN and the small photoemission horizon set by the limited photon energies. Our approach provides a strategy for the realization of flat photoemission emitters.

| S-EPMC10415285 | biostudies-literature

Synthesis and Characterization of Hexagonal Boron Nitride as a Gate Dielectric.

Project description:Two different growth modes of large-area hexagonal boron nitride (h-BN) film, a conventional chemical vapor deposition (CVD) growth mode and a high-pressure CVD growth mode, were compared as a function of the precursor partial pressure. Conventional self-limited CVD growth was obtained below a critical partial pressure of the borazine precursor, whereas a thick h-BN layer (thicker than a critical thickness of 10 nm) was grown beyond a critical partial pressure. An interesting coincidence of a critical thickness of 10 nm was identified in both the CVD growth behavior and in the breakdown electric field strength and leakage current mechanism, indicating that the electrical properties of the CVD h-BN film depended significantly on the film growth mode and the resultant film quality.

| S-EPMC4960585 | biostudies-literature

Vertical transport in graphene-hexagonal boron nitride heterostructure devices.

Project description:Research in graphene-based electronics is recently focusing on devices based on vertical heterostructures of two-dimensional materials. Here we use density functional theory and multiscale simulations to investigate the tunneling properties of single- and double-barrier structures with graphene and few-layer hexagonal boron nitride (h-BN) or hexagonal boron carbon nitride (h-BC2N). We find that tunneling through a single barrier exhibit a weak dependence on energy. We also show that in double barriers separated by a graphene layer we do not observe resonant tunneling, but a significant increase of the tunneling probability with respect to a single barrier of thickness equal to the sum of the two barriers. This is due to the fact that the graphene layer acts as an effective phase randomizer, suppressing resonant tunneling and effectively letting a double-barrier structure behave as two single-barriers in series. Finally, we use multiscale simulations to reproduce a current-voltage characteristics resembling that of a resonant tunneling diode, that has been experimentally observed in single barrier structure. The peak current is obtained when there is perfect matching between the densities of states of the cathode and anode graphene regions.

| S-EPMC4586719 | biostudies-other

Tunable Anion-Selective Transport through Monolayer Graphene and Hexagonal Boron Nitride.

Project description:Membranes that selectively filter for both anions and cations are central to technological applications from clean energy generation to desalination devices. 2D materials have immense potential as these ion-selective membranes due to their thinness, mechanical strength, and tunable surface chemistry; however, currently, only cation-selective membranes have been reported. Here we demonstrate the controllable cation and anion selectivity of both monolayer graphene and hexagonal boron nitride. In particular, we measure the ionic current through membranes grown by chemical vapor deposition containing well-known defects inherent to scalably produced and wet-transferred 2D materials. We observe a striking change from cation selectivity with monovalent ions to anion selectivity by controlling the concentration of multivalent ions and inducing charge inversion on the 2D membrane. Furthermore, we find good agreement between our experimental data and theoretical predictions from the Goldman-Hodgkin-Katz equation and use this model to extract selectivity ratios. These tunable selective membranes conduct up to 500 anions for each cation and thus show potential for osmotic power generation.

| S-EPMC7098055 | biostudies-literature

Thermal transport and anharmonic phonons in strained monolayer hexagonal boron nitride.

Project description:Thermal transport and phonon-phonon coupling in monolayer hexagonal boron nitride (h-BN) under equibiaxial strains are investigated from first principles. Phonon spectra at elevated temperatures have been calculated from perturbation theory using the third-order anharmonic force constants. The stiffening of the out-of-plane transverse acoustic mode (ZA) near the Brillouin zone center and the increase of acoustic phonon lifetimes are found to contribute to the dramatic increase of thermal transport in strained h-BN. The transverse optical mode (TO) at the K point, which was predicted to lead to mechanical failure of h-BN, is found to shift to lower frequencies at elevated temperatures under equibiaxial strains. The longitudinal and transverse acoustic modes exhibit broad phonon spectra under large strains in sharp contrast to the ZA mode, indicating strong in-plane phonon-phonon coupling.

| S-EPMC5338266 | biostudies-literature

Percolative proton transport in hexagonal boron nitride membranes with edge-functionalization.

Project description:Two-dimensional layered materials have been used as matrices to study the structure and dynamics of trapped water and ions. Here, we demonstrate unique features of proton transport in layered hexagonal boron nitride membranes with edge-functionalization subject to hydration. The hydration-independent interlayer spacing indicates the absence of water intercalation between the h-BN sheets. An 18-fold increase in water sorption is observed upon amine functionalization of h-BN sheet edges. A 7-orders of magnitude increase in proton conductivity is observed with less than 5% water loading attributable to edge-conduction channels. The extremely low percolation threshold and non-universal critical exponents (2.90 ≤ α ≤ 4.43), are clear signatures of transport along the functionalized edges. Anomalous thickness dependence of conductivity is observed and its plausible origin is discussed.

| S-EPMC10496919 | biostudies-literature

Vapor-liquid-solid growth of large-area multilayer hexagonal boron nitride on dielectric substrates.

Project description:Multilayer hexagonal boron nitride (h-BN) is highly desirable as a dielectric substrate for the fabrication of two-dimensional (2D) electronic and optoelectronic devices. However, the controllable synthesis of multilayer h-BN in large areas is still limited in terms of crystallinity, thickness and stacking order. Here, we report a vapor-liquid-solid growth (VLSG) method to achieve uniform multilayer h-BN by using a molten Fe82B18 alloy and N2 as reactants. Liquid Fe82B18 not only supplies boron but also continuously dissociates nitrogen atoms from the N2 vapor to support direct h-BN growth on a sapphire substrate; therefore, the VLSG method delivers high-quality h-BN multilayers with a controllable thickness. Further investigation of the phase evolution of the Fe-B-N system reveals that isothermal segregation dominates the growth of the h-BN. The approach herein demonstrates the feasibility for large-area fabrication of van der Waals 2D materials and heterostructures.

| S-EPMC7015929 | biostudies-literature

Conformal hexagonal-boron nitride dielectric interface for tungsten diselenide devices with improved mobility and thermal dissipation.

Project description:Relatively low mobility and thermal conductance create challenges for application of tungsten diselenide (WSe2) in high performance devices. Dielectric interface is of extremely importance for improving carrier transport and heat spreading in a semiconductor device. Here, by near-equilibrium plasma-enhanced chemical vapour deposition, we realize catalyst-free growth of poly-crystalline two-dimensional hexagonal-boron nitride (2D-BN) with domains around 20~ 200 nm directly on SiO2/Si, quartz, sapphire, silicon or SiO2/Si with three-dimensional patterns at 300 °C. Owing to the atomically-clean van-der-Walls conformal interface and the fact that 2D-BN can better bridge the vibrational spectrum across the interface and protect interfacial heat conduction against substrate roughness, both improved performance and thermal dissipation of WSe2 field-effect transistor are realized with mobility around 56~ 121 cm2 V-1 s-1 and saturated power intensity up to 4.23 × 103 W cm-2. Owing to its simplicity, conformal growth on three-dimensional surface, compatibility with microelectronic process, it has potential for application in future two-dimensional electronics.

| S-EPMC6416324 | biostudies-literature

One-dimensional hexagonal boron nitride conducting channel.

Project description:Hexagonal boron nitride (hBN) is an insulating two-dimensional (2D) material with a large bandgap. Although known for its interfacing with other 2D materials and structural similarities to graphene, the potential use of hBN in 2D electronics is limited by its insulating nature. Here, we report atomically sharp twin boundaries at AA'/AB stacking boundaries in chemical vapor deposition-synthesized few-layer hBN. We find that the twin boundary is composed of a 6'6' configuration, showing conducting feature with a zero bandgap. Furthermore, the formation mechanism of the atomically sharp twin boundaries is suggested by an analogy with stacking combinations of AA'/AB based on the observations of extended Klein edges at the layer boundaries of AB-stacked hBN. The atomically sharp AA'/AB stacking boundary is promising as an ultimate 1D electron channel embedded in insulating pristine hBN. This study will provide insights into the fabrication of single-hBN electronic devices.

| S-EPMC7060069 | biostudies-literature

Photonic crystal cavities from hexagonal boron nitride.

Project description:Development of scalable quantum photonic technologies requires on-chip integration of photonic components. Recently, hexagonal boron nitride (hBN) has emerged as a promising platform, following reports of hyperbolic phonon-polaritons and optically stable, ultra-bright quantum emitters. However, exploitation of hBN in scalable, on-chip nanophotonic circuits and cavity quantum electrodynamics (QED) experiments requires robust techniques for the fabrication of high-quality optical resonators. In this letter, we design and engineer suspended photonic crystal cavities from hBN and demonstrate quality (Q) factors in excess of 2000. Subsequently, we show deterministic, iterative tuning of individual cavities by direct-write EBIE without significant degradation of the Q-factor. The demonstration of tunable cavities made from hBN is an unprecedented advance in nanophotonics based on van der Waals materials. Our results and hBN processing methods open up promising avenues for solid-state systems with applications in integrated quantum photonics, polaritonics and cavity QED experiments.

| S-EPMC6033931 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data