Characterization of conjugated polymer actuation under cerebral physiological conditions.

ABSTRACT: Conjugated polymer actuators have potential use in implantable neural interface devices for modulating the position of electrode sites within brain tissue or guiding insertion of neural probes along curved trajectories. The actuation of polypyrrole (PPy) doped with dodecylbenzenesulfonate (DBS) is characterized to ascertain whether it can be employed in the cerebral environment. Microfabricated bilayer beams are electrochemically cycled at either 22 or 37 °C in aqueous NaDBS or in artificial cerebrospinal fluid (aCSF). Nearly all the ions in aCSF are exchanged into the PPy-the cations Na(+) , K(+) , Mg(2+) , Ca(2+) , as well as the anion PO4 (3-) ; Cl(-) is not present. Nevertheless, deflections in aCSF are comparable to those in NaDBS and they are monotonic with oxidation level: strain increases upon reduction, with no reversal of motion despite the mixture of ionic charges and valences being exchanged. Actuation depends on temperature. Upon warming, the cyclic voltammograms show additional peaks and an increase of 70% in the consumed charge. Bending is, however, much less affected: strain increases somewhat (6%-13%) but remains monotonic, and deflections shift (up to 20%). These results show how the actuation environment must be taken into account, and demonstrate proof of concept for actuated implantable neural interfaces.

SUBMITTER: Daneshvar ED

PROVIDER: S-EPMC4106983 | biostudies-literature | 2014 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Characterization of conjugated polymer actuation under cerebral physiological conditions.

Daneshvar Eugene Dariush ED Smela Elisabeth E

Advanced healthcare materials 20140224 7

Conjugated polymer actuators have potential use in implantable neural interface devices for modulating the position of electrode sites within brain tissue or guiding insertion of neural probes along curved trajectories. The actuation of polypyrrole (PPy) doped with dodecylbenzenesulfonate (DBS) is characterized to ascertain whether it can be employed in the cerebral environment. Microfabricated bilayer beams are electrochemically cycled at either 22 or 37 °C in aqueous NaDBS or in artificial cer ...[more]

PMID: 24574101

Similar Datasets

Project description:Conjugated polymers such as poly(3,4-ethylenedioxythiphene) (PEDOT) are of interest for a variety of applications including interfaces between electronic biomedical devices and living tissue. The mechanical properties, strength, and adhesion of these materials to solid substrates are all vital for long-term applications. We have been developing methods to quantify the mechanical properties of conjugated polymer thin films. In this paper, the stiffness, strength and the interfacial shear strength (adhesion) of electrochemically deposited PEDOT and PEDOT-co-1,3,5-tri[2-(3,4-ethylene dioxythienyl)]-benzene (EPh) were studied. The estimated Young's modulus of the PEDOT films was 2.6±1.4GPa, and the strain to failure was around 2%. The tensile strength was measured to be 56±27MPa. The effective interfacial shear strength was estimated with a shear-lag model by measuring the crack spacing as a function of film thickness. For PEDOT on gold/palladium-coated hydrocarbon film substrates an interfacial shear strength of 0.7±0.3MPa was determined. The addition of 5mole% of a tri-functional EDOT crosslinker (EPh) increased the tensile strength of the films to 283±67MPa, while the strain to failure remained about the same (2%). The effective interfacial shear strength was increased to 2.4±0.6MPa.Statement of significanceThis paper describes methods for estimating the ultimate mechanical properties of electrochemically deposited conjugated polymer (here PEDOT and PEDOT copolymers) films. Of particular interest and novelty is our implementation of a cracking test to quantify the shear strength of the PEDOT thin films on these solid substrates. There is considerable interest in these materials as interfaces between biomedical devices and living tissue, however potential mechanisms and modes of failure are areas of continuing concern, and establishing methods to quantify the strengths of these interfaces are therefore of particular current interest. We are confident that these results will be useful to the broader biological materials community and are worthy of broader dissemination.

Dataset Information

Characterization of conjugated polymer actuation under cerebral physiological conditions.

Publications

Characterization of conjugated polymer actuation under cerebral physiological conditions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets