Temperature-dependent gas transport performance of vertically aligned carbon nanotube/parylene composite membranes.

ABSTRACT: A novel composite membrane consisting of vertically aligned carbon nanotubes (CNTs) and parylene was successfully fabricated. Seamless filling of the spaces in CNT forests with parylene was achieved by a low-pressure chemical vapor deposition (CVD) technique and followed with the Ar/O2 plasma etching to expose CNT tips. Transport properties of various gases through the CNT/parylene membranes were explored. And gas permeances were independent on feed pressure in accordance with the Knudsen model, but the permeance values were over 60 times higher than that predicted by the Knudsen diffusion kinetics, which was attributed to specular momentum reflection inside smooth CNT pores. Gas permeances and enhancement factors over the Knudsen model firstly increased and then decreased with rising temperature, which confirmed the existence of non-Knudsen transport. And surface adsorption diffusion could affect the gas permeance at relatively low temperature. The gas permeance of the CNT/parylene composite membrane could be improved by optimizing operating temperature.

SUBMITTER: Zhang L

PROVIDER: S-EPMC4158770 | biostudies-literature | 2014

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Temperature-dependent gas transport performance of vertically aligned carbon nanotube/parylene composite membranes.

Zhang Lei L Yang Junhe J Wang Xianying X Zhao Bin B Zheng Guangping G

Nanoscale research letters 20140828 1

A novel composite membrane consisting of vertically aligned carbon nanotubes (CNTs) and parylene was successfully fabricated. Seamless filling of the spaces in CNT forests with parylene was achieved by a low-pressure chemical vapor deposition (CVD) technique and followed with the Ar/O2 plasma etching to expose CNT tips. Transport properties of various gases through the CNT/parylene membranes were explored. And gas permeances were independent on feed pressure in accordance with the Knudsen model, ...[more]

PMID: 25246864

Similar Datasets

Project description:The catalytic chemical vapour deposition (c-CVD) technique was applied in the synthesis of vertically aligned arrays of nitrogen-doped carbon nanotubes (N-CNTs). A mixture of toluene (main carbon source), pyrazine (1,4-diazine, nitrogen source) and ferrocene (catalyst precursor) was used as the injection feedstock. To optimize conditions for growing the most dense and aligned N-CNT arrays, we investigated the influence of key parameters, i.e., growth temperature (660, 760 and 860 °C), composition of the feedstock and time of growth, on morphology and properties of N-CNTs. The presence of nitrogen species in the hot zone of the quartz reactor decreased the growth rate of N-CNTs down to about one twentieth compared to the growth rate of multi-wall CNTs (MWCNTs). As revealed by electron microscopy studies (SEM, TEM), the individual N-CNTs (half as thick as MWCNTs) grown under the optimal conditions were characterized by a superior straightness of the outer walls, which translated into a high alignment of dense nanotube arrays, i.e., 5 × 10(8) nanotubes per mm(2) (100 times more than for MWCNTs grown in the absence of nitrogen precursor). In turn, the internal crystallographic order of the N-CNTs was found to be of a 'bamboo'-like or 'membrane'-like (multi-compartmental structure) morphology. The nitrogen content in the nanotube products, which ranged from 0.0 to 3.0 wt %, was controlled through the concentration of pyrazine in the feedstock. Moreover, as revealed by Raman/FT-IR spectroscopy, the incorporation of nitrogen atoms into the nanotube walls was found to be proportional to the number of deviations from the sp(2)-hybridisation of graphene C-atoms. As studied by XRD, the temperature and the [pyrazine]/[ferrocene] ratio in the feedstock affected the composition of the catalyst particles, and hence changed the growth mechanism of individual N-CNTs into a 'mixed base-and-tip' (primarily of the base-type) type as compared to the purely 'base'-type for undoped MWCNTs.

Dataset Information

Temperature-dependent gas transport performance of vertically aligned carbon nanotube/parylene composite membranes.

Publications

Temperature-dependent gas transport performance of vertically aligned carbon nanotube/parylene composite membranes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure