Degradation and biocompatibility of multistage nanovectors in physiological systems.

ABSTRACT: The careful scrutiny of drug delivery systems is essential to evaluate and justify their potential for the clinic. Among the various studies necessary for preclinical testing, the impact of degradation is commonly overlooked. In this article, we investigate the effect of fabrication (porosity and nucleation layer) and environment (buffer and pH) factors on the degradation kinetics of multistage nanovectors (MSV) composed of porous silicon. The degradation by-products of MSV were exposed to endothelial cells and analyzed for detrimental effects on cellular internalization, architecture, proliferation, and cell cycle. Increases in porosity resulted in accelerated degradation exhibiting smaller-sized particles at comparable times. Removal of the nucleation layer (thin layer of small pores formed during the initial steps of etching) triggered a premature collapse of the entire central porous region of MSV. Variations in buffers prompted a faster degradation rate yielding smaller MSV within faster time frames, whereas increases in pH stimulated erosion of MSV and thus faster degradation. In addition, exposure to these degradation by-products provoked negligible impact on the proliferation and cell cycle phases on primary endothelial cells. In this study, we propose methods that lay the foundation for future investigations toward understanding the impact of the degradation of drug delivery platforms.

SUBMITTER: Martinez JO

PROVIDER: S-EPMC4182937 | biostudies-literature | 2014 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Degradation and biocompatibility of multistage nanovectors in physiological systems.

Martinez Jonathan O JO Evangelopoulos Michael M Chiappini Ciro C Liu Xuewu X Ferrari Mauro M Tasciotti Ennio E

Journal of biomedical materials research. Part A 20131116 10

The careful scrutiny of drug delivery systems is essential to evaluate and justify their potential for the clinic. Among the various studies necessary for preclinical testing, the impact of degradation is commonly overlooked. In this article, we investigate the effect of fabrication (porosity and nucleation layer) and environment (buffer and pH) factors on the degradation kinetics of multistage nanovectors (MSV) composed of porous silicon. The degradation by-products of MSV were exposed to endot ...[more]

PMID: 25269799

Similar Datasets

Project description:Over the last few decades a great variety of nanotechnology based platforms have been synthesized and fabricated to improve the delivery of active compounds to a disease site. Nanoparticles currently used in the clinic, and the majority of nanotherapeutics/nanodiagnostics under investigation, accommodate single- or multiple- functionalities on the same entity. Because many heterogeneous biological barriers can prevent therapeutic and imaging agents from reaching their intended targets in sufficient concentrations, there is an emerging requirement to develop a multimodular nanoassembly, in which different components with individual specific functions act in a synergistic manner. The multistage nanovectors (MSVs) were introduced in 2008 as the first system of this type. It comprises several nanocomponents or "stages", each of which is designed to negotiate one or more biological barriers. Stage 1 mesoporous silicon particles (S1MPs) were rationally designed and fabricated in a nonspherical geometry to enable superior blood margination and to increase cell surface adhesion. The main task of S1MPs is to efficiently transport nanoparticles that are loaded into their porous structure and to protect them during transport from the administration site to the disease lesion. Semiconductor fabrication techniques including photolithography and electrochemical etching allow for the exquisite control and precise reproducibility of S1MP physical characteristics such as geometry and porosity. Furthermore, S1MPs can be chemically modified with negatively/positively charged groups, PEG and other polymers, fluorescent probes, contrast agents, and biologically active targeting moieties including antibodies, peptides, aptamers, and phage. The payload nanoparticles, termed stage 2 nanoparticles (S2NPs), can be any currently available nanoparticles such as liposomes, micelles, inorganic/metallic nanoparticles, dendrimers, and carbon structures, within the approximate size range of 5-100 nm in diameter. Depending upon the physicochemical features of the S1MP (geometry, porosity, and surface modifications), a variety of S2NPs or nanoparticle "cocktails" can be loaded and efficiently delivered to the disease site. As demonstrated in the studies reviewed here, once the S2NPs are loaded into the S1MPs, a variety of novel properties emerge, which enable the design of new and improved imaging contrast agents and therapeutics. For example, the loading of the MRI Gd-based contrast agents onto hemispherical and discoidal S1MPs significantly increased the longitudal relaxivity (r1) to values of up to 50 times larger than those of clinically available gadolinium-based agents (~4 mM(-1) s(-1)/Gd(3+) ion). Furthermore, administration of a single dose of MSVs loaded with neutral nanoliposomes containing small interfering RNA (siRNA) targeted against the EphA2 oncoprotein enabled sustained EphA2 gene silencing for at least 21 days. As a result, the tumor burden was reduced in an orthotopic mouse model of ovarian cancer. We envision that the versatility of the MSV platform and its emerging properties will enable the creation of personalized solutions with broad clinical implications within and beyond the realm of cancer theranostics.

Project description:The biocompatibility and degradation behavior of pure molybdenum (Mo) as a bioresorbable metallic material (BMM) for implant applications were investigated. In vitro degradation of a commercially available Mo wire (ø250 µm) was examined after immersion in modified Kokubo's SBF for 28 days at 37 °C and pH 7.4. For assessment of in vivo degradation, the Mo wire was implanted into the abdominal aorta of female Wistar rats for 3, 6 and 12 months. Microstructure and corrosion behavior were analyzed by means of SEM/EDX analysis. After explantation, Mo levels in serum, urine, aortic vessel wall and organs were investigated via ICP-OES analysis. Furthermore, histological analyses of the liver, kidneys, spleen, brain and lungs were performed, as well as blood count and differentiation by FACS analysis. Levels of the C-reactive protein were measured in blood plasma of all the animals. In vitro and in vivo degradation behavior was very similar, with formation of uniform, non-passivating and dissolving product layers without occurrence of a localized corrosion attack. The in vitro degradation rate was 101.6 µg/(cm2·d) which corresponds to 33.6 µm/y after 28 days. The in vivo degradation rates of 12, 33 and 36 µg/(cm2·d) were observed after 3, 6 and 12 months for the samples properly implanted in the aortic vessel wall. This corresponds with a degradation rate of 13.5 µm/y for the 12-month cohort. However, the magnitude of degradation strongly depended on the implant site, with the wires incorporated into the vessel wall showing the most severe degradation. Degradation of the implanted Mo wire neither induced an increase in serum or urine Mo levels nor were elevated Mo levels found in the liver and kidneys compared with the respective controls. Only in the direct vicinity of the implant in the aortic vessel wall, a significant amount of Mo was found, which, however, was far below the amounts to be expected from degrading wires. No abnormalities were detected for all timepoints in histological and blood analyses compared to the control group. The C-reactive protein levels were similar between all the groups, indicating no inflammation processes. These findings suggest that dissolved Mo from a degrading implant is physiologically transported and excreted. Furthermore, radiographic and µCT analyses revealed excellent radiopacity of Mo in tissues. These findings and the unique combination with its extraordinary mechanical properties make Mo an interesting alternative for established BMMs.

Dataset Information

Degradation and biocompatibility of multistage nanovectors in physiological systems.

Publications

Degradation and biocompatibility of multistage nanovectors in physiological systems.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets