Superior radiation-resistant nanoengineered austenitic 304L stainless steel for applications in extreme radiation environments.

ABSTRACT: Nuclear energy provides more than 10% of electrical power internationally, and the increasing engagement of nuclear energy is essential to meet the rapid worldwide increase in energy demand. A paramount challenge in the development of advanced nuclear reactors is the discovery of advanced structural materials that can endure extreme environments, such as severe neutron irradiation damage at high temperatures. It has been known for decades that high dose radiation can introduce significant void swelling accompanied by precipitation in austenitic stainless steel (SS). Here we report, however, that through nanoengineering, ultra-fine grained (UFG) 304 L SS with an average grain size of ~100 nm, can withstand Fe ion irradiation at 500 °C to 80 displacements-per-atom (dpa) with moderate grain coarsening. Compared to coarse grained (CG) counterparts, swelling resistance of UFG SS is improved by nearly an order of magnitude and swelling rate is reduced by a factor of 5. M(23)C(6) precipitates, abundant in irradiated CG SS, are largely absent in UFG SS. This study provides a nanoengineering approach to design and discover radiation tolerant metallic materials for applications in extreme radiation environments.

SUBMITTER: Sun C

PROVIDER: S-EPMC4295098 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:We describe here the relationship between grain structure, deformation mechanism and fracture characteristics in an austenitic stainless steel. This was accomplished using the novel concept of phase reversion that enabled a wide range of grain size from nanograined/ultrafine grained (NG/UFG) to coarse-grained (CG) regime to be obtained in a single material through change in temperature-time annealing sequence. In the NG/UFG structure, a marked increase in abundance of stacking faults (SFs) and twin density with strain was observed that led to a decrease in the average spacing between adjacent SFs, thus converting stacking faults into twins. Twinning in NG/UFG structure involved partial dislocations and their interaction with the grain boundaries, including SF overlapping and the coordinated nucleation of partial dislocations from the grain boundaries. The plastic zone in the NG/UFG structure resembled a network knitted by the intersecting twins and SFs. With SFE ~30 mJ/m2, the minimum stress for twin nucleation was ~250?MPa for the experiment steel and the corresponding optimal grain size (dop) wa ~120?nm. In contrast, in the CG structure, strain induced martensite formation was the deformation mechanism. The difference in the deformation mechanism led to a clear distinction in the fracture behavior from striated fracture in high strength-high ductility NG/UFG alloy to microvoid coalescence in the low strength-high ductility CG counterpart. The underlying reason for the change in fracture behavior was consistent with change in deformation mechanism from nanoscale twinning in NG/UFG alloy to strain-induced martensite in the CG alloy, which is related to change in the stability of austenite with grain size. An analysis of critical shear stress required to initiate twinning partial dislocations in comparison to that required to nucleate shear bands is presented. The appearance of striated fracture in the NG/UFG alloy suggests a quasi-static step wise crack growth process.

Dataset Information

Superior radiation-resistant nanoengineered austenitic 304L stainless steel for applications in extreme radiation environments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets