In-situ ToF-SIMS analyses of deuterium re-distribution in austenitic steel AISI 304L under mechanical load.

ABSTRACT: Hydrocarbons fuel our economy. Furthermore, intermediate goods and consumer products are often hydrocarbon-based. Beside all the progress they made possible, hydrogen-containing substances can have severe detrimental effects on materials exposed to them. Hydrogen-assisted failure of iron alloys has been recognised more than a century ago. The present study aims to providing further insight into the degradation of the austenitic stainless steel AISI 304L (EN 1.4307) exposed to hydrogen. To this end, samples were electrochemically charged with the hydrogen isotope deuterium (2H, D) and analysed by scanning electron microscopy (SEM), electron back-scatter diffraction (EBSD) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). It was found that deuterium caused a phase transformation from the original ? austenite into ?- and ?'-martensite. Despite their low solubility for hydrogen, viz. deuterium, the newly formed phases showed high deuterium concentration which was attributed to the increased density of traps. Information about the behaviour of deuterium in the material subjected to external mechanical load was gathered. A four-point-bending device was developed for this purpose. This allowed to analyse in-situ pre-charged samples in the ToF-SIMS during the application of external mechanical load. The results indicate a movement of deuterium towards the regions of highest stress.

SUBMITTER: Rohsler A

PROVIDER: S-EPMC7046711 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

In-situ ToF-SIMS analyses of deuterium re-distribution in austenitic steel AISI 304L under mechanical load.

Röhsler Andreas A Sobol Oded O Hänninen Hannu H Böllinghaus Thomas T

Scientific reports 20200227 1

Hydrocarbons fuel our economy. Furthermore, intermediate goods and consumer products are often hydrocarbon-based. Beside all the progress they made possible, hydrogen-containing substances can have severe detrimental effects on materials exposed to them. Hydrogen-assisted failure of iron alloys has been recognised more than a century ago. The present study aims to providing further insight into the degradation of the austenitic stainless steel AISI 304L (EN 1.4307) exposed to hydrogen. To this e ...[more]

PMID: 32107420

Similar Datasets

Project description:Optimal treatment of bone fractures with minimal complications requires implant alloys that combine high strength with high ductility. Today, TiAl6V4 titanium and 316L steel are the most applied alloys in bone surgery, whereas both share advantages and disadvantages. The nickel-free, high-nitrogen austenitic steel X13CrMnMoN18-14-3 (1.4452, brand name: P2000) exhibits high strength in combination with superior ductility. In order to compare suitable alloys for bone implants, we investigated titanium, 316L steel, CoCrMo and P2000 for their biocompatibility and hemocompatibility (according to DIN ISO 10993-5 and 10993-4), cell metabolism, mineralization of osteoblasts, electrochemical and mechanical properties. P2000 exhibited good biocompatibility of fibroblasts and osteoblasts without impairment in vitality or changing of cell morphology. Furthermore, investigation of the osteoblasts function by ALP activity and protein levels of the key transcription factor RUNX2 revealed 2x increased ALP activity and more than 4x increased RUNX2 protein levels for P2000 compared to titanium or 316 steel, respectively. Additionally, analyses of osteoblast biomineralization by Alizarin Red S staining exhibited more than 6x increased significant mineralization of osteoblasts grown on P2000 as compared to titanium. Further, P2000 showed no hemolytic effect and no significant influence on hemocompatibility. Nanoindentation hardness tests of Titanium and 316L specimens exposed an indentation hardness (HIT) of about 4 GPa, whereas CoCrMo and P2000 revealed HIT of 7.5 and 5.6 GPa, respectively. Moreover, an improved corrosion resistance of P2000 compared to 316L steel was observed. In summary, we could demonstrate that the nickel-free high-nitrogen steel P2000 appears to be a promising alternative candidate for applications in bone surgery. As to nearly all aspects like biocompatibility and hemocompatibility, cell metabolism, mineralization of osteoblasts and mechanical properties, P2000 was similar to or revealed advantages against titanium, 316L or CoCrMo.

Dataset Information

In-situ ToF-SIMS analyses of deuterium re-distribution in austenitic steel AISI 304L under mechanical load.

Publications

In-situ ToF-SIMS analyses of deuterium re-distribution in austenitic steel AISI 304L under mechanical load.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets