Polymer/Nanocrystal Hybrid Solar Cells: Influence of Molecular Precursor Design on Film Nanomorphology, Charge Generation and Device Performance.

ABSTRACT: In this work, molecular tuning of metal xanthate precursors is shown to have a marked effect on the heterojunction morphology of hybrid poly(3-hexylthiophene-2,5-diyl) (P3HT)/CdS blends and, as a result, the photochemical processes and overall performance of in situ fabricated hybrid solar cells. A series of cadmium xanthate complexes is synthesized for use as in situ precursors to cadmium sulfide nanoparticles in hybrid P3HT/CdS solar cells. The formation of CdS domains is studied by simultaneous GIWAXS (grazing incidence wide-angle X-ray scattering) and GISAXS (grazing incidence small-angle X-ray scattering), revealing knowledge about crystal growth and the formation of different morphologies observed using TEM (transmission electron microscopy). These measurements show that there is a strong relationship between precursor structure and heterojunction nanomorphology. A combination of TAS (transient absorption spectroscopy) and photovoltaic device performance measurements is used to show the intricate balance required between charge photogeneration and percolated domains in order to effectively extract charges to maximize device power conversion efficiencies. This study presents a strong case for xanthate complexes as a useful route to designing optimal heterojunction morphologies for use in the emerging field of hybrid organic/inorganic solar cells, due to the fact that the nanomorphology can be tuned via careful design of these precursor materials.

SUBMITTER: MacLachlan AJ

PROVIDER: S-EPMC4384757 | biostudies-literature | 2015 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Polymer/Nanocrystal Hybrid Solar Cells: Influence of Molecular Precursor Design on Film Nanomorphology, Charge Generation and Device Performance.

MacLachlan Andrew J AJ Rath Thomas T Cappel Ute B UB Dowland Simon A SA Amenitsch Heinz H Knall Astrid-Caroline AC Buchmaier Christine C Trimmel Gregor G Nelson Jenny J Haque Saif A SA

Advanced functional materials 20141125 3

In this work, molecular tuning of metal xanthate precursors is shown to have a marked effect on the heterojunction morphology of hybrid poly(3-hexylthiophene-2,5-diyl) (P3HT)/CdS blends and, as a result, the photochemical processes and overall performance of in situ fabricated hybrid solar cells. A series of cadmium xanthate complexes is synthesized for use as in situ precursors to cadmium sulfide nanoparticles in hybrid P3HT/CdS solar cells. The formation of CdS domains is studied by simultaneo ...[more]

PMID: 25866496

Similar Datasets

Project description:Large-scale commercial synthesis of bulk-heterojunction (BHJ) solar cell materials is very challenging and both time and energy consuming. Synthesis of π-conjugated polymers (CPs) with uniform batch-to-batch molecular weight and low dispersity is a key requirement for better reproducibility of high-efficiency polymer solar cells. Herein, a conjugated polymer (CP) PTB7-Th, well known for its high performance, has been synthesized with high molecular weight and low dispersity in a closed microwave reactor. The microwave reaction procedure is known to be more controlled and consumes less energy. The precursors were strategically reacted for different reaction time durations to obtain the optimum molecular weight. All different CPs were well characterized using 1H NMR, gel permeation chromatography (GPC), UV-vis, photoluminescence (PL), electron spin resonance (ESR), and Raman spectroscopy, whereas the film morphology was extensively studied via atomic force microscopy (AFM) and grazing incidence X-ray diffraction (GIXRD) techniques. The effect of molecular weight on a conventional BHJ solar cell with PC71BM acceptor was investigated to derive systematic structure-property relationships. The CP obtained after 35 min of reaction time and integrated into BHJ devices under ambient conditions provided the best performance with a power conversion efficiency (PCE) of 8.09%, which was quite similar to the results of CPs synthesized via a thermal route. An enhanced PCE of 8.47% was obtained for the optimized polymer (35 min microwave reaction product) when device fabrication was carried out inside a glovebox. The organic thin-film transistor (OTFT) device with the microwave-synthesized CP displayed better hole mobility (0.137 cm2 V-1 s-1) as compared to that with the thermally synthesized CP. This study also proved that the device stability and reproducibility of the microwave-synthesized CP were much better and more consistent than those of the thermally developed CP.

Dataset Information

Polymer/Nanocrystal Hybrid Solar Cells: Influence of Molecular Precursor Design on Film Nanomorphology, Charge Generation and Device Performance.

Publications

Polymer/Nanocrystal Hybrid Solar Cells: Influence of Molecular Precursor Design on Film Nanomorphology, Charge Generation and Device Performance.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets