Tantalum Nitride-Decorated Titanium with Enhanced Resistance to Microbiologically Induced Corrosion and Mechanical Property for Dental Application.

ABSTRACT: Microbiologically induced corrosion (MIC) of metallic devices/implants in the oral region is one major cause of implant failure and metal allergy in patients. Therefore, it is crucial to develop practical approaches which can effectively prevent MIC for broad clinical applications of these materials. In the present work, tantalum nitride (TaN)-decorated titanium with promoted bio-corrosion and mechanical property was firstly developed via depositing TaN layer onto pure Ti using magnetron sputtering. The microstructure and chemical constituent of TaN coatings were characterized, and were found to consist of a hard fcc-TaN outer layer. Besides, the addition of TaN coatings greatly increased the hardness and modulus of pristine Ti from 2.54 ± 0.20 to 29.88 ± 2.59 GPa, and from 107.19 ± 6.98 to 295.46 ± 19.36 GPa, respectively. Potentiodynamic polarization and electrochemical impedance spectroscopy studies indicated that TaN coating exhibited higher MIC resistance in comparison to bare Ti and TiN-coated coating in two bacteria-containing artificial saliva solutions. Moreover, the biofilm experiment showed that the TaN-decorated Ti sample possessed good antibacterial performance. The SEM and XPS results after biofilm removal demonstrated that TaN film remained its integrity and stability, while TiN layer detached from Ti surface in the bio-corrosion tests, demonstrating the anti-MIC behavior and the strong binding property of TaN coating to Ti substrate. Considering all these results, TaN-decorated Ti material exhibits the optimal comprehensive performance and holds great potential as implant material for dental applications.

SUBMITTER: Zhang Y

PROVIDER: S-EPMC4479376 | biostudies-literature | 2015

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Tantalum Nitride-Decorated Titanium with Enhanced Resistance to Microbiologically Induced Corrosion and Mechanical Property for Dental Application.

Zhang Yifei Y Zheng Yunfei Y Li Yongliang Y Wang Lixin L Bai Yanjie Y Zhao Qiang Q Xiong Xiaoling X Cheng Yan Y Tang Zhihui Z Deng Yi Y Wei Shicheng S

PloS one 20150624 6

Microbiologically induced corrosion (MIC) of metallic devices/implants in the oral region is one major cause of implant failure and metal allergy in patients. Therefore, it is crucial to develop practical approaches which can effectively prevent MIC for broad clinical applications of these materials. In the present work, tantalum nitride (TaN)-decorated titanium with promoted bio-corrosion and mechanical property was firstly developed via depositing TaN layer onto pure Ti using magnetron sputter ...[more]

PMID: 26107177

Similar Datasets

Project description:Currently, sulfate-reducing bacteria (SRB) is regarded as the main culprit of microbiologically influenced corrosion (MIC), mainly due to the low reported corrosion rates of other microorganisms. For example, the highest reported corrosion rate for methanogens is 0.065 mm/yr. However, by investigating methanogen-induced microbiologically influenced corrosion (Mi-MIC) using an in-house developed versatile multiport flow test column, extremely high corrosion rates were observed. We analyzed a large set of carbon steel beads, which were sectionally embedded into the test columns as substrates for iron-utilizing methanogen Methanobacterium IM1. After 14 days of operation using glass beads as fillers for section separation, the highest average corrosion rate of Methanobacterium IM1 was 0.2 mm/yr, which doubled that of Desulfovibrio ferrophilus IS5 and Desulfovibrio alaskensis 16109 investigated at the same conditions. At the most corroded region, nearly 80% of the beads lost 1% of their initial weight (fast-corrosion), resulting in an average corrosion rate of 0.2 mm/yr for Methanobacterium IM1-treated columns. When sand was used as filler material to mimic sediment conditions, average corrosion rates for Methanobacterium IM1 increased to 0.3 mm/yr (maximum 0.52 mm/yr) with over 83% of the beads having corrosion rates above 0.3 mm/yr. Scanning electron images of metal coupons extracted from the column showed methanogenic cells were clustered close to the metal surface. Methanobacterium IM1 is a hydrogenotrophic methanogen with higher affinity to metal than H2. Unlike SRB, Methanobacterium IM1 is not restricted to the availability of sulfate concentration in the environment. Thus, the use of the multiport flow column provided a new insight on the corrosion potential of methanogens, particularly in dynamic conditions, that offers new opportunities for monitoring and development of mitigation strategies. Overall, this study shows (1) under certain conditions methanogenic archaea can cause higher corrosion than SRB, (2) specific quantifications, i.e., maximum, average, and minimum corrosion rates can be determined, and (3) that spatial statistical evaluations of MIC can be carried out.

Project description:Microbiologically Influenced Corrosion (MIC) poses a significant challenge to various industries, leading to substantial economic losses and potential safety hazards. Despite extensive research on the MIC resistance of various materials, there is a lack of studies focusing on High Chromium White Iron (HCWI) alloys, which are widely used in wear-resistant applications. This study addresses this knowledge gap by providing a comprehensive investigation of the MIC resistance of three HCWI alloys with varying chromium contents (22 wt%, 30.7 wt%, and 21 wt%) in the presence of Pseudomonas aeruginosa (P. Aeruginosa), a common bacterial species associated with MIC. The alloys were exposed to an artificial seawater medium inoculated with P.Aeruginosa for 14 days, and their corrosion behaviour was evaluated using electrochemical techniques, surface analysis, and microscopy. Electrochemical Impedance Spectroscopy (EIS) results revealed that the alloy with the highest chromium content (A2, 30.7 wt% Cr) exhibited superior MIC resistance compared to the other alloys (A1, 22 wt% Cr and M1, 21 wt% Cr). The enhanced performance of alloy A2 was attributed to the formation of a more stable and protective passive film, as well as the development of a more compact and less permeable biofilm. The EIS data, interpreted using equivalent circuit models, showed that alloy A2 had the highest charge transfer resistance and the lowest biofilm capacitance, indicating a more effective barrier against corrosive species. Bode plots further confirmed the superior corrosion resistance of alloy A2, with higher impedance values and phase angles at low frequencies compared to alloys A1 and M1. Scanning Electron Microscopy (SEM) and optical microscopy analyses corroborated these findings, showing that alloy A2 had the lowest pit density and size after 14 days of exposure. The insights gained from this study highlight the critical role of chromium content in the MIC resistance of HCWI alloys and have significant implications for the design and selection of materials for applications prone to microbial corrosion.

Dataset Information

Tantalum Nitride-Decorated Titanium with Enhanced Resistance to Microbiologically Induced Corrosion and Mechanical Property for Dental Application.

Publications

Tantalum Nitride-Decorated Titanium with Enhanced Resistance to Microbiologically Induced Corrosion and Mechanical Property for Dental Application.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets