Effect of selected biocides on microbiologically influenced corrosion caused by Desulfovibrio ferrophilus IS5.

ABSTRACT: The marine bacterial strain Desulfovibrio ferrophilus IS5, known for its lithotrophic growth ability to use metallic iron as a sole electron donor and for causing corrosion of steel, was used in the current study. Four commonly used biocides in the oil and gas industry, namely tetrakis(hydroxymethyl) phosphonium sulfate (THPS), glutaraldehyde (GLUT), benzalkonium chloride (BAC), and GLUT/BAC were selected to study their efficacy in controlling carbon steel corrosion in the presence of this strain. Incubations containing strain IS5 and low carbon steel coupons were prepared in the presence and absence of the four biocides, and these were monitored using both electrochemical methods (electrochemical impedance spectroscopy, linear polarization resistance and potentiodynamic polarization) and surface analyses (scanning electron microscopy, confocal measurements, optical microscopy, and profilometry) to assess the biofilm/metal interactions. When THPS, BAC, and GLUT/BAC treatments were applied, minimal corrosion was measured by all methods. In contrast, severe pitting was observed in the presence of 50 ppm GLUT, similar to what was observed when D. ferrophilus IS5 was incubated in the absence of biocide, suggesting that GLUT alone may not be effective in controlling MIC in marine environments. This study also showed that the use of non-destructive electrochemical methods is effective for screening for real time biocide selection and monitoring of the impact of chemicals post-dosage in oil and gas operations.

SUBMITTER: Sharma M

PROVIDER: S-EPMC6226443 | biostudies-literature | 2018 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of selected biocides on microbiologically influenced corrosion caused by Desulfovibrio ferrophilus IS5.

Sharma Mohita M Liu Hongwei H Chen Shiqiang S Cheng Frank F Voordouw Gerrit G Gieg Lisa L

Scientific reports 20181109 1

The marine bacterial strain Desulfovibrio ferrophilus IS5, known for its lithotrophic growth ability to use metallic iron as a sole electron donor and for causing corrosion of steel, was used in the current study. Four commonly used biocides in the oil and gas industry, namely tetrakis(hydroxymethyl) phosphonium sulfate (THPS), glutaraldehyde (GLUT), benzalkonium chloride (BAC), and GLUT/BAC were selected to study their efficacy in controlling carbon steel corrosion in the presence of this strai ...[more]

PMID: 30413730

Similar Datasets

Project description:Microbiologically Influenced Corrosion (MIC) poses a significant challenge to various industries, leading to substantial economic losses and potential safety hazards. Despite extensive research on the MIC resistance of various materials, there is a lack of studies focusing on High Chromium White Iron (HCWI) alloys, which are widely used in wear-resistant applications. This study addresses this knowledge gap by providing a comprehensive investigation of the MIC resistance of three HCWI alloys with varying chromium contents (22 wt%, 30.7 wt%, and 21 wt%) in the presence of Pseudomonas aeruginosa (P. Aeruginosa), a common bacterial species associated with MIC. The alloys were exposed to an artificial seawater medium inoculated with P.Aeruginosa for 14 days, and their corrosion behaviour was evaluated using electrochemical techniques, surface analysis, and microscopy. Electrochemical Impedance Spectroscopy (EIS) results revealed that the alloy with the highest chromium content (A2, 30.7 wt% Cr) exhibited superior MIC resistance compared to the other alloys (A1, 22 wt% Cr and M1, 21 wt% Cr). The enhanced performance of alloy A2 was attributed to the formation of a more stable and protective passive film, as well as the development of a more compact and less permeable biofilm. The EIS data, interpreted using equivalent circuit models, showed that alloy A2 had the highest charge transfer resistance and the lowest biofilm capacitance, indicating a more effective barrier against corrosive species. Bode plots further confirmed the superior corrosion resistance of alloy A2, with higher impedance values and phase angles at low frequencies compared to alloys A1 and M1. Scanning Electron Microscopy (SEM) and optical microscopy analyses corroborated these findings, showing that alloy A2 had the lowest pit density and size after 14 days of exposure. The insights gained from this study highlight the critical role of chromium content in the MIC resistance of HCWI alloys and have significant implications for the design and selection of materials for applications prone to microbial corrosion.

Project description:Currently, sulfate-reducing bacteria (SRB) is regarded as the main culprit of microbiologically influenced corrosion (MIC), mainly due to the low reported corrosion rates of other microorganisms. For example, the highest reported corrosion rate for methanogens is 0.065 mm/yr. However, by investigating methanogen-induced microbiologically influenced corrosion (Mi-MIC) using an in-house developed versatile multiport flow test column, extremely high corrosion rates were observed. We analyzed a large set of carbon steel beads, which were sectionally embedded into the test columns as substrates for iron-utilizing methanogen Methanobacterium IM1. After 14 days of operation using glass beads as fillers for section separation, the highest average corrosion rate of Methanobacterium IM1 was 0.2 mm/yr, which doubled that of Desulfovibrio ferrophilus IS5 and Desulfovibrio alaskensis 16109 investigated at the same conditions. At the most corroded region, nearly 80% of the beads lost 1% of their initial weight (fast-corrosion), resulting in an average corrosion rate of 0.2 mm/yr for Methanobacterium IM1-treated columns. When sand was used as filler material to mimic sediment conditions, average corrosion rates for Methanobacterium IM1 increased to 0.3 mm/yr (maximum 0.52 mm/yr) with over 83% of the beads having corrosion rates above 0.3 mm/yr. Scanning electron images of metal coupons extracted from the column showed methanogenic cells were clustered close to the metal surface. Methanobacterium IM1 is a hydrogenotrophic methanogen with higher affinity to metal than H2. Unlike SRB, Methanobacterium IM1 is not restricted to the availability of sulfate concentration in the environment. Thus, the use of the multiport flow column provided a new insight on the corrosion potential of methanogens, particularly in dynamic conditions, that offers new opportunities for monitoring and development of mitigation strategies. Overall, this study shows (1) under certain conditions methanogenic archaea can cause higher corrosion than SRB, (2) specific quantifications, i.e., maximum, average, and minimum corrosion rates can be determined, and (3) that spatial statistical evaluations of MIC can be carried out.

Dataset Information

Effect of selected biocides on microbiologically influenced corrosion caused by Desulfovibrio ferrophilus IS5.

Publications

Effect of selected biocides on microbiologically influenced corrosion caused by Desulfovibrio ferrophilus IS5.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets