In situ cross-linking of stimuli-responsive hemicellulose microgels during spray drying.

ABSTRACT: Chemical cross-linking during spray drying offers the potential for green fabrication of microgels with a rapid stimuli response and good blood compatibility and provides a platform for stimuli-responsive hemicellulose microgels (SRHMGs). The cross-linking reaction occurs rapidly in situ at elevated temperature during spray drying, enabling the production of microgels in a large scale within a few minutes. The SRHMGs with an average size range of ? 1-4 ?m contain O-acetyl-galactoglucomannan as a matrix and poly(acrylic acid), aniline pentamer (AP), and iron as functional additives, which are responsive to external changes in pH, electrochemical stimuli, magnetic field, or dual-stimuli. The surface morphologies, chemical compositions, charge, pH, and mechanical properties of these smart microgels were evaluated using scanning electron microscopy, IR, zeta potential measurements, pH evaluation, and quantitative nanomechanical mapping, respectively. Different oxidation states were observed when AP was introduced, as confirmed by UV spectroscopy and cyclic voltammetry. Systematic blood compatibility evaluations revealed that the SRHMGs have good blood compatibility. This bottom-up strategy to synthesize SRHMGs enables a new route to the production of smart microgels for biomedical applications.

SUBMITTER: Zhao W

PROVIDER: S-EPMC4535707 | biostudies-literature | 2015 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

In situ cross-linking of stimuli-responsive hemicellulose microgels during spray drying.

Zhao Weifeng W Nugroho Robertus Wahyu N RW Odelius Karin K Edlund Ulrica U Zhao Changsheng C Albertsson Ann-Christine AC

ACS applied materials & interfaces 20150209 7

Chemical cross-linking during spray drying offers the potential for green fabrication of microgels with a rapid stimuli response and good blood compatibility and provides a platform for stimuli-responsive hemicellulose microgels (SRHMGs). The cross-linking reaction occurs rapidly in situ at elevated temperature during spray drying, enabling the production of microgels in a large scale within a few minutes. The SRHMGs with an average size range of ∼ 1-4 μm contain O-acetyl-galactoglucomannan as a ...[more]

PMID: 25630464

Similar Datasets

Project description:The aim of the present study was to investigate how different polymers affect the dissociation of cocrystals prepared by co-spray-drying active pharmaceutical ingredient (API), coformer, and polymer. Diclofenac acid-l-proline cocrystal (DPCC) was selected in this study as a model cocrystal due to its previously reported poor physical stability in a high-humidity environment. Polymers investigated include polyvinylpyrrolidone (PVP), poly(1-vinylpyrrolidone-co-vinyl acetate) (PVPVA), hydroxypropyl methyl cellulose, hydroxypropylmethylcellulose acetate succinate, ethyl cellulose, and Eudragit L-100. Terahertz Raman spectroscopy (THz Raman) and powder X-ray diffraction (PXRD) were used to monitor the cocrystal dissociation rate in a high-humidity environment. A Raman probe was used in situ to monitor the extent of the dissociation of DPCC and DPCC in crystalline solid dispersions (CSDs) with polymer when exposed to pH 6.8 phosphate buffer and water. The solubility of DPCC and solid dispersions of DPCC in pH 6.8 phosphate buffer and water was also measured. The dissociation of DPCC was water-mediated, and more than 60% of DPCC dissociated in 18 h at 40 °C and 95% RH. Interestingly, the physical stability of the cocrystal was effectively improved by producing CSDs with polymers. The inclusion of just 1 wt % polymer in a CSD with DPCC protected the cocrystal from dissociation over 18 h under the same conditions. Furthermore, the CSD with PVPVA was still partially stable, and the CSD with PVP was stable (undissociated) after 7 days. The superior stability of DPCC in CSDs with PVP and PVPVA was also demonstrated when systems were exposed to water or pH 6.8 phosphate buffer and resulted in higher dynamic solubility of the CSDs compared to DPCC alone. The improvement in physical stability of the cocrystal in CSDs was thought to be due to an efficient mixing between polymer and cocrystal at the molecular level provided by spray drying and in situ gelling of polymer. It is hypothesized that polymer chains could undergo gelling in situ and form a physical barrier, preventing cocrystal interaction with water, which contributes to slowing down the water-mediated dissociation.

Dataset Information

In situ cross-linking of stimuli-responsive hemicellulose microgels during spray drying.

Publications

In situ cross-linking of stimuli-responsive hemicellulose microgels during spray drying.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets