Phase Diagram and Transformations of Iron Pentacarbonyl to nm Layered Hematite and Carbon-Oxygen Polymer under Pressure.

ABSTRACT: We present the phase diagram of Fe(CO)5, consisting of three molecular polymorphs (phase I, II and III) and an extended polymeric phase that can be recovered at ambient condition. The phase diagram indicates a limited stability of Fe(CO)5 within a pressure-temperature dome formed below the liquid- phase II- polymer triple point at 4.2?GPa and 580?K. The limited stability, in turn, signifies the temperature-induced weakening of Fe-CO back bonds, which eventually leads to the dissociation of Fe-CO at the onset of the polymerization of CO. The recovered polymer is a composite of novel nm-lamellar layers of crystalline hematite Fe2O3 and amorphous carbon-oxygen polymers. These results, therefore, demonstrate the synthesis of carbon-oxygen polymer by compressing Fe(CO)5, which advocates a novel synthetic route to develop atomistic composite materials by compressing organometallic compounds.

SUBMITTER: Ryu YJ

PROVIDER: S-EPMC4601022 | biostudies-literature | 2015 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Phase Diagram and Transformations of Iron Pentacarbonyl to nm Layered Hematite and Carbon-Oxygen Polymer under Pressure.

Ryu Young Jay YJ Kim Minseob M Yoo Choong-Shik CS

Scientific reports 20151012

We present the phase diagram of Fe(CO)5, consisting of three molecular polymorphs (phase I, II and III) and an extended polymeric phase that can be recovered at ambient condition. The phase diagram indicates a limited stability of Fe(CO)5 within a pressure-temperature dome formed below the liquid- phase II- polymer triple point at 4.2 GPa and 580 K. The limited stability, in turn, signifies the temperature-induced weakening of Fe-CO back bonds, which eventually leads to the dissociation of Fe-CO ...[more]

PMID: 26456761

Similar Datasets

Sub-50 nm Iron-Nitrogen-Doped Hollow Carbon Sphere-Encapsulated Iron Carbide Nanoparticles as Efficient Oxygen Reduction Catalysts.

Project description:Sub-50 nm iron-nitrogen-doped hollow carbon sphere-encapsulated iron carbide nanoparticles (Fe3C-Fe,N/C) are synthesized by using a triblock copolymer of poly(styrene-b-2-vinylpyridine-b-ethylene oxide) as a soft template. Their typical features, including a large surface area (879.5 m2 g-1), small hollow size (≈16 nm), and nitrogen-doped mesoporous carbon shell, and encapsulated Fe3C nanoparticles generate a highly active oxygen reduction reaction (ORR) performance. Fe3C-Fe,N/C hollow spheres exhibit an ORR performance comparable to that of commercially available 20 wt% Pt/C in alkaline electrolyte, with a similar half-wave potential, an electron transfer number close to 4, and lower H2O2 yield of less than 5%. It also shows noticeable ORR catalytic activity under acidic conditions, with a high half-wave potential of 0.714 V, which is only 59 mV lower than that of 20 wt% Pt/C. Moreover, Fe3C-Fe,N/C has remarkable long-term durability and tolerance to methanol poisoning, exceeding Pt/C regardless of the electrolyte.

| S-EPMC6051398 | biostudies-literature

Polymer/Iron-Based Layered Double Hydroxides as Multifunctional Wound Dressings.

Project description:This work presents the development of multifunctional therapeutic membranes based on a high-performance block copolymer scaffold formed by polyether (PE) and polyamide (PA) units (known as PEBA) and layered double hydroxide (LDH) biomaterials, with the aim to study their uses as wound dressings. Two LDH layer compositions were employed containing Mg2+ or Zn2+, Fe3+ and Al3+ cations, intercalated with chloride anions, abbreviated as Mg-Cl or Zn-Cl, or intercalated with naproxenate (NAP) anions, abbreviated as Mg-NAP or Zn-NAP. Membranes were structurally and physically characterized, and the in vitro drug release kinetics and cytotoxicity assessed. PEBA-loading NaNAP salt particles were also prepared for comparison. Intercalated NAP anions improved LDH-polymer interaction, resulting in membranes with greater mechanical performance compared to the polymer only or to the membranes containing the Cl-LDHs. Drug release (in saline solution) was sustained for at least 8 h for all samples and release kinetics could be modulated: a slower, an intermediate and a faster NAP release were observed from membranes containing Zn-NAP, NaNAP and Mg-NAP particles, respectively. In general, cell viability was higher in the presence of Mg-LDH and the membranes presented improved performance in comparison with the powdered samples. PEBA containing Mg-NAP sample stood out among all membranes in all the evaluated aspects, thus being considered a great candidate for application as multifunctional therapeutic dressings.

| S-EPMC7700130 | biostudies-literature

Identification of new pillared-layered carbon nitride materials at high pressure.

Project description:The compression of the layered carbon nitride C6N9H3 · HCl was studied experimentally and with density functional theory (DFT) methods. This material has a polytriazine imide structure with Cl(-) ions contained within C12N12 voids in the layers. The data indicate the onset of layer buckling accompanied by movement of the Cl(-) ions out of the planes beginning above 10-20 GPa followed by an abrupt change in the diffraction pattern and c axis spacing associated with formation of a new interlayer bonded phase. The transition pressure is calculated to be 47 GPa for the ideal structures. The new material has mixed sp(2)-sp(3) hybridization among the C and N atoms and it provides the first example of a pillared-layered carbon nitride material that combines the functional properties of the graphitic-like form with improved mechanical strength. Similar behavior is predicted to occur for Cl-free structures at lower pressures.

| S-EPMC3698513 | biostudies-other

Rapid oxygen exchange between hematite and water vapor.

Project description:Oxygen exchange at oxide/liquid and oxide/gas interfaces is important in technology and environmental studies, as it is closely linked to both catalytic activity and material degradation. The atomic-scale details are mostly unknown, however, and are often ascribed to poorly defined defects in the crystal lattice. Here we show that even thermodynamically stable, well-ordered surfaces can be surprisingly reactive. Specifically, we show that all the 3-fold coordinated lattice oxygen atoms on a defect-free single-crystalline "r-cut" ([Formula: see text]) surface of hematite (α-Fe2O3) are exchanged with oxygen from surrounding water vapor within minutes at temperatures below 70 °C, while the atomic-scale surface structure is unperturbed by the process. A similar behavior is observed after liquid-water exposure, but the experimental data clearly show most of the exchange happens during desorption of the final monolayer, not during immersion. Density functional theory computations show that the exchange can happen during on-surface diffusion, where the cost of the lattice oxygen extraction is compensated by the stability of an HO-HOH-OH complex. Such insights into lattice oxygen stability are highly relevant for many research fields ranging from catalysis and hydrogen production to geochemistry and paleoclimatology.

| S-EPMC8580966 | biostudies-literature

High performance asymmetric supercapacitor based on Cobalt Nickle Iron-layered double hydroxide/carbon nanofibres and activated carbon.

Project description:A novel Cobalt Nickle Iron-layered double hydroxide/carbon nanofibres (CoNiFe-LDH/CNFs-0.5) composite was successfully fabricated through an easy in situ growth approach. The morphology and composition of the obtained materials were systematically investigated. When the two derived materials were used for supercapacitor electrodes, the CoNiFe-LDH/CNFs-0.5 composite displayed high specific surface area (114.2?m2?g-1), specific capacitance (1203?F?g-1 at 1?A?g-1) and rate capability (77.1% from 1?A?g-1 to 10?A?g-1), which were considerably higher than those of pure CoNiFe-LDH. Moreover, the specific capacitance of CoNiFe-LDH/CNFs-0.5 composite remained at 94.4% after 1000 cycles at 20?A?g-1, suggesting excellent long-time cycle life. The asymmetric supercapacitor based on CoNiFe-LDH/CNFs-0.5 as a positive electrode and activated carbon as a negative electrode was manufactured and it exhibited a specific capacitance of 84.9?F?g-1 at 1?A?g-1 and a high energy density of 30.2?W?h kg-1. More importantly, this device showed long-term cycling stability, with 82.7% capacity retention after 2000 cycles at 10?A?g-1. Thus, this composite with outstanding electrochemical performance could be a promising electrode material for supercapacitors.

| S-EPMC5498571 | biostudies-literature

Non-redox doping boosts oxygen evolution electrocatalysis on hematite.

Project description:The oxygen evolution reaction (OER) is the major bottleneck to develop viable and cost-effective water electrolysis, a key process in the production of renewable fuels. Hematite, all iron α-Fe2O3, would be an ideal OER catalyst in alkaline media due to its abundance and easy processing. Despite its promising theoretical potential, it has demonstrated very poor OER activity under multiple experimental conditions, significantly worse than that of Co or Ni-based oxides. In the search for improving hematite performance, we have analysed the effect of doping with redox vs. non-redox active species (Ni or Zn). Our results indicate that Zn doping clearly outperforms Ni, commonly accepted as a preferred dopant. Zn-doped hematite exhibits catalytic performances close to the state-of-the-art for alkaline water splitting: reaching 10 mA cm-2 at just 350 mV overpotential (η) at pH 13, thus twenty times that of hematite. Such a catalytic enhancement can be traced back to a dramatic change in the reaction pathway. Incorporation of Ni, as previously suggested, decreases the energetic barrier for the OER on the available centres. In contrast, Zn facilitates the appearance of a dominant and faster alternative via a two-site reaction, where the four electron oxidation reaction starts on Fe, but is completed on Zn after thermodynamically favoured proton coupled electron transfer between adjacent metal centres. This unique behaviour is prompted by the non-redox character of Zn centres, which maintain the same charge during OER. Our results open an alternative role for dopants on oxide surfaces and provide a powerful approach for catalytic optimisation of oxides, including but not limited to highly preferred all-iron oxides.

| S-EPMC8157419 | biostudies-literature

The phase diagram of high-pressure superionic ice.

Project description:Superionic ice is a special group of ice phases at high temperature and pressure, which may exist in ice-rich planets and exoplanets. In superionic ice liquid hydrogen coexists with a crystalline oxygen sublattice. At high pressures, the properties of superionic ice are largely unknown. Here we report evidence that from 280 GPa to 1.3 TPa, there are several competing phases within the close-packed oxygen sublattice. At even higher pressure, the close-packed structure of the oxygen sublattice becomes unstable to a new unusual superionic phase in which the oxygen sublattice takes the P2(1)/c symmetry. We also discover that higher pressure phases have lower transition temperatures. The diffusive hydrogen in the P2(1)/c superionic phase shows strong anisotropic behaviour and forms a quasi-two-dimensional liquid. The ionic conductivity changes abruptly in the solid to close-packed superionic phase transition, but continuously in the solid to P2(1)/c superionic phase transition.

| S-EPMC4560814 | biostudies-literature

Boosting oxygen evolution of single-atomic ruthenium through electronic coupling with cobalt-iron layered double hydroxides.

Project description:Single atom catalyst, which contains isolated metal atoms singly dispersed on supports, has great potential for achieving high activity and selectivity in hetero-catalysis and electrocatalysis. However, the activity and stability of single atoms and their interaction with support still remains a mystery. Here we show a stable single atomic ruthenium catalyst anchoring on the surface of cobalt iron layered double hydroxides, which possesses a strong electronic coupling between ruthenium and layered double hydroxides. With 0.45 wt.% ruthenium loading, the catalyst exhibits outstanding activity with overpotential 198 mV at the current density of 10 mA cm-2 and a small Tafel slope of 39 mV dec-1 for oxygen evolution reaction. By using operando X-ray absorption spectroscopy, it is disclosed that the isolated single atom ruthenium was kept under the oxidation states of 4+ even at high overpotential due to synergetic electron coupling, which endow exceptional electrocatalytic activity and stability simultaneously.

| S-EPMC6461613 | biostudies-literature

Iron-Palladium Decorated Carbon Nanotubes Achieve Radiosensitization via Reactive Oxygen Species Burst.

Project description:Radiotherapy is recommended as a modality for cancer treatment in clinic. However, cancerous cells were resistant to therapeutic irradiation due to its DNA repair. In this work, single-walled carbon nanotubes with unique physical properties of hollow structures and high specific surface area were introduced as carrier for iron-palladium (FePd) to obtain iron-palladium decorated carbon nanotubes (FePd@CNTs). On one hand, FePd nanoparticles possess significant ability in radiosensitization as previously reported. On the other hand, carbon nanotubes offer higher efficiency in crossing biological barriers, inducing the accumulation and retention of FePd nanoparticles within tumor tissue. In order to verify the radiosensitization effect of FePd@CNTs, both in vitro and in vivo experiments were conducted. These experiments showed that the FePd@CNTs exhibited remarkably better radiosensitization effect and more obvious accumulation than FePd NPs, suggesting a potential of FePd@CNTs in radiosensitization.

| S-EPMC8176102 | biostudies-literature

High-Pressure Carbon Monoxide and Oxygen Mixture is Effective for Lung Preservation.

Project description:(1) Background: Heme oxygenase-1 (HO-1) degrades heme and generates carbon monoxide (CO), producing various anti-inflammatory, anti-oxidative, and anti-apoptotic effects. This study aimed to confirm the effects of CO on the ischemia-reperfusion injury (IRI) of donor lungs using a high-pressure gas (HPG) preservation method. (2) Methods: Donor rat and canine lungs were preserved in a chamber filled with CO (1.5 atm) and oxygen (O2; 2 atm) and were ventilated with either CO and O2 mixture (CO/O2 group) or air (air group) immediately before storage. Rat lungs were subjected to heterotopic cervical transplantation and evaluated after reperfusion, whereas canine lungs were subjected to allogeneic transplantation and evaluated. (3) Results: Alveolar hemorrhage in the CO/O2 group was significantly milder than that in the air group. mRNA expression levels of HO-1 remained unchanged in both the groups; however, inflammatory mediator levels were significantly lower in the CO/O2 group than in the air group. The oxygenation of graft lungs was comparable between the two groups, but lactic acid level tended to be higher in the air group. (4) Conclusions: The HO-1/CO system in the HPG preservation method is effective in suppressing IRI and preserving donor lungs.

| S-EPMC6600409 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data