Methodology to analyse small silicon samples by glow discharge mass spectrometry using a thin wafer mask.

ABSTRACT: Glow discharge mass spectrometry (GDMS) is widely used for trace element analysis of bulk solid samples. The geometry of the GD source limits the minimum size of the sample, which for the instrument used in this work (ThermoElementGD) is 20 mm in diameter. From time to time, there is the need to analyse smaller samples with this technique, and we present here a methodology to analyse samples of 9-20 mm diameter through the use of thin masks. Thin masks have been previously used mostly as secondary cathode for the analysis of non-conducting materials, with hole size smaller than the area of the glow discharge. The use of masks in this work includes the following customization:•The choice of highly-pure Si as mask material, to decrease the chance of interferences with the Si samples.•The use of a hole in the mask of the same size as the discharge area. This implies that the mask material is not sputtered, thus decreasing chances for contamination from the mask itself.

SUBMITTER: Modanese C

PROVIDER: S-EPMC4644257 | biostudies-literature | 2015

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Methodology to analyse small silicon samples by glow discharge mass spectrometry using a thin wafer mask.

Modanese C C Arnberg L L Di Sabatino M M

MethodsX 20151019

Glow discharge mass spectrometry (GDMS) is widely used for trace element analysis of bulk solid samples. The geometry of the GD source limits the minimum size of the sample, which for the instrument used in this work (ThermoElementGD) is 20 mm in diameter. From time to time, there is the need to analyse smaller samples with this technique, and we present here a methodology to analyse samples of 9-20 mm diameter through the use of thin masks. Thin masks have been previously used mostly as seconda ...[more]

PMID: 26649274

Similar Datasets

Liquid Cathode Glow Discharge as an Excitation Source for the Analysis of Complex Water Samples with Atomic Emission Spectrometry.

Project description:A liquid cathode glow discharge (LCGD) was developed as a low-power and miniaturized excitation source of atomic emission spectrometry (AES) for the determination of K, Na, Ca, and Mg in water samples from rivers and lakes. The discharge stability and parameter influencing the analytical performance of LCGD-AES were systematically examined. Moreover, the measurement results of water samples using LCGD-AES were verified by ion chromatography (IC). The results showed that the optimized operating parameters are a 660 V discharge voltage, pH = 1.0 HNO3 as the supporting electrolyte, and a 4.0 mL min-1 solution flow rate. High concentrations of some metals may interfere with the detection of Ca and Mg. Low-molecular-weight organic substances do not have a remarkable enhancement on signal intensity. With the addition of 0.5% cetyltrimethylammonium chloride (CTAC), the emission intensity of elements can enhance significantly. However, it is not used to further evaluate the analytical performance due to instability of plasma after adding CTAC. The maximum power of LCGD is 52 W. The limits of detection and precision (RSD, in 1 mg L-1) of K, Na, Ca, and Mg are 0.20, 0.02, 0.01, and 0.01 mg L-1 and 0.9, 1.5, 0.6, and 1.2%, respectively. The measurement results of K, Na, Ca, and Mg in water samples by LCGD-AES are basically in agreement with the reference values measured by IC. The recovery of samples ranged from 84 to 113% except for Na, suggesting that the measurement results have high accuracy and reliability. All the results indicated that the LCGD-AES can provide an alternative analytical method for in situ, real-time, on-line determination of K, Na, Ca, and Mg in water samples from rivers and lakes.

| S-EPMC7424731 | biostudies-literature

Studies of Dopamine Oxidation Process by Atmospheric Pressure Glow Discharge Mass Spectrometry.

Project description:An atmospheric pressure glow discharge ionisation source was constructed and utilized to study the dopamine (DA) oxidation process coupling with mass spectrometry. During the DA oxidation process catalysed by polyphenol oxidase (PPO), six cationic intermediates were directly detected by the atmospheric pressure glow discharge mass spectrometry (APGD-MS). Combined with tandem mass spectrometry, the structures of the dopamine o-semiquinone radical (DASQ) and leukodopaminochrome radical (LDAC●) intermediates and structures of the isomers of dopaminochrome (DAC) and 5,6-dihydroxyindole (DHI) were further characterised with the introduction of 2,2,6,6-tetramethylpiperidine 1-oxyl (TEMPO) and deuterium oxide (D2O) to APGD-MS. Meanwhile, UV-Vis studies confirmed the important role of PPO in catalyzing the DA oxidation reaction. Based on APGD-MS studies, a possible mechanism could be proposed for DA oxidation catalysed by PPO. Furthermore, APGD-MS could provide possibilities for the effective detection and characterisation of short-lived intermediates, even in complicated systems.

| S-EPMC10179796 | biostudies-literature

Towards ultra-thin plasmonic silicon wafer solar cells with minimized efficiency loss.

Project description:The cost-effectiveness of market-dominating silicon wafer solar cells plays a key role in determining the competiveness of solar energy with other exhaustible energy sources. Reducing the silicon wafer thickness at a minimized efficiency loss represents a mainstream trend in increasing the cost-effectiveness of wafer-based solar cells. In this paper we demonstrate that, using the advanced light trapping strategy with a properly designed nanoparticle architecture, the wafer thickness can be dramatically reduced to only around 1/10 of the current thickness (180??m) without any solar cell efficiency loss at 18.2%. Nanoparticle integrated ultra-thin solar cells with only 3% of the current wafer thickness can potentially achieve 15.3% efficiency combining the absorption enhancement with the benefit of thinner wafer induced open circuit voltage increase. This represents a 97% material saving with only 15% relative efficiency loss. These results demonstrate the feasibility and prospect of achieving high-efficiency ultra-thin silicon wafer cells with plasmonic light trapping.

| S-EPMC4018607 | biostudies-literature

Kerf-Less Exfoliated Thin Silicon Wafer Prepared by Nickel Electrodeposition for Solar Cells.

Project description:Ultra-thin and large-area silicon wafers with a thickness in the range of 20-70 μm, were produced by spalling using a nickel stressor layer. A new equation for predicting the thickness of the spalled silicon was derived from the Suo-Hutchinson mechanical model and the kinking mechanism. To confirm the reliability of the new equation, the proportional factor of stress induced by the nickel on the silicon wafer, was calculated. The calculated proportional factor of λ = 0.99 indicates that the thickness of the spalled silicon wafer is proportional to that of the nickel layer. A similar relationship was observed in the experimental data obtained in this study. In addition, the thickness of the stressor layer was converted to a value of stress as a guide when using other deposition conditions and materials. A silicon wafer with a predicted thickness of 50 μm was exfoliated for further analysis. In order to spall a large-area (150 × 150 mm2 or 6 × 6 in2) silicon wafer without kerf loss, initial cracks were formed by a laser pretreatment at a proper depth (50 μm) inside the exfoliated silicon wafer, which reduced the area of edge slope (kerf loss) from 33 to 3 mm2. The variations in thickness of the spalled wafer remained under 4%. Moreover, we checked the probability of degradation of the spalled wafers by using them to fabricate solar cells; the efficiency and ideality factor of the spalled silicon wafers were found to be 14.23%and 1.35, respectively.

| S-EPMC6339913 | biostudies-literature

Improvement of polycrystalline silicon wafer solar cell efficiency by forming nanoscale pyramids on wafer surface using a self-mask etching technique.

Project description:The creation of nanostructures on polycrystalline silicon wafer surface to reduce the solar reflection can enhance the solar absorption and thus increase the solar-electricity conversion efficiency of solar cells. The self-masking reactive ion etching (RIE) was studied to directly fabricate nanostructures on silicon surface without using a masking process for antireflection purpose. Reactive gases comprising chlorine (Cl2), sulfur hexafluoride (SF6), and oxygen (O2) were activated by radio-frequency plasma in an RIE system at a typical pressure of 120-130 mTorr to fabricate the nanoscale pyramids. Poly-Si wafers were etched directly without masking for 6-10 min to create surface nanostructures by varying the compositions of SF6, Cl2, and O2 gas mixtures in the etching process. The wafers were then treated with acid (KOH:H2O = 1:1) for 1 min to remove the damage layer (100 nm) induced by dry etching. The damage layer significantly reduced the solar cell efficiencies by affecting the electrical properties of the surface layer. The light reflectivity from the surface after acid treatment could be significantly reduced to <10% for the wavelengths between 500 and 900 nm. The effects of RIE and surface treatment conditions on the surface nanostructures and the optical performance as well as the efficiencies of solar cells will be presented and discussed. The authors have successfully fabricated large-area (156 × 156 mm(2)) subwavelength antireflection structure on poly-Si substrates, which could improve the solar cell efficiency reproducibly up to 16.27%, higher than 15.56% using wet etching.

| S-EPMC3634306 | biostudies-other

Grid batch-dependent tuning of glow discharge parameters.

Project description:Sample preparation on cryo-EM grids can give various results, from very thin ice and homogeneous particle distribution (ideal case) to unwanted behavior such as particles around the "holes" or complexes that do not entirely correspond to the one in solution (real life). We recently run into such a case and finally found out that variations in the 3D reconstructions were systematically correlated with the grid batches that were used. We report the use of several techniques to investigate the grids' characteristics, namely TEM, SEM, Auger spectroscopy and Infrared Interferometry. This allowed us to diagnose the origin of grid preparation problems and to adjust glow discharge parameters. The methods used for each approach are described and the results obtained on a common specific case are reported.

| S-EPMC9436422 | biostudies-literature

Glow discharge plasma stabilization of azo dye on PMMA polymer.

Project description:The effects of argon gas glow discharge plasma on the surface of DR1 dye-loaded PMMA polymer films are examined in this work. Plasma immobilizes the dye on the surface of polymer without using stabilizers. Argon plasma activates the surface through breaking some bonds and generation of radical sites. It affects the acrylate groups of PMMA leading to covalent bonds between dye and surface of polymer. In addition, plasma treatment and contact with ambient air may result in the creation of new polar components, such as carbonyl and carboxyl compounds and links that enhance the dye attachment to the polymer matrix. Besides, the dye adsorption on the polymer film is impacted by changes in surface topography. Furthermore, plasma modifies the dye conformation, which affects the adherence of the dye to the polymer surface through bringing the dye to the higher energy state. The chemical and topographical modification of dye-loaded PMMA films by plasma are investigated by spectroscopic and AFM methods. Furthermore, aging process was used to confirm dye retention on the polymer film after plasma modification as opposed to dye-loaded polymer film that was left untreated as a reference sample. Finally, investigated method suggests a novel and very affordable technique for fabrication of poly(MMA-co-DR1) copolymer in the form of a homogeneous surface layer.

| S-EPMC9626643 | biostudies-literature

Hanging drop cathode-atmospheric pressure glow discharge as a new method of sample introduction for inductively coupled plasma-optical emission spectrometry.

Project description:This work reports the use of hanging drop cathode-atmospheric pressure glow discharge (HDC-APGD) as a new method of sample introduction for inductively coupled plasma-optical emission spectrometry (ICP-OES). The developed arrangement was characterized by a low sample uptake (0.56 mL min-1) and the fact that the entire sample solution volume was consumed by the discharge. This resulted in a very high transport efficiency of analytes from the sample solution into the ICP torch (usually > 80%). Under the optimal operating conditions of HDC-APGD, intensities of emission lines of studied elements were, on average, 2 times higher as compared to those obtained with conventional pneumatic nebulization (PN). Moreover, in the case of I and Y, the observed signal enhancements were even higher, i.e., 6.2 and 6.1 times, respectively. It was also shown that in the case of B and some elements that are known to form different volatile species (Ag, Bi, Cd, Hg, Os, Pb, and Se), the presence of low molecular weight organic compounds in the sample solution, i.e., CH3OH, C2H5OH, HCOOH, CH3COOH, or HCHO, resulted in the additional enhancement of their signals. It was especially evident in the case of Hg for which a 8.6-fold signal enhancement in the presence of HCOOH was noticed. The system presented herein was distinguished from other competitive APGD-type discharges because it could be successfully used for the determination of a vast group of elements, including alkali metals, alkaline earth metals, transition metals, and non-metals.

| S-EPMC7320056 | biostudies-literature

Wafer-scale heterostructured piezoelectric bio-organic thin films.

Project description:Piezoelectric biomaterials are intrinsically suitable for coupling mechanical and electrical energy in biological systems to achieve in vivo real-time sensing, actuation, and electricity generation. However, the inability to synthesize and align the piezoelectric phase at a large scale remains a roadblock toward practical applications. We present a wafer-scale approach to creating piezoelectric biomaterial thin films based on γ-glycine crystals. The thin film has a sandwich structure, where a crystalline glycine layer self-assembles and automatically aligns between two polyvinyl alcohol (PVA) thin films. The heterostructured glycine-PVA films exhibit piezoelectric coefficients of 5.3 picocoulombs per newton or 157.5 × 10-3 volt meters per newton and nearly an order of magnitude enhancement of the mechanical flexibility compared with pure glycine crystals. With its natural compatibility and degradability in physiological environments, glycine-PVA films may enable the development of transient implantable electromechanical devices.

| S-EPMC8516594 | biostudies-literature

Rapid Elemental Analysis of Aerosols Using Atmospheric Glow Discharge Optical Emission Spectroscopy.

Project description:A new, low-cost approach based on the application of atmospheric radio frequency glow discharge (rf-GD) optical emission spectroscopy (OES) has been developed for near real-time measurement of multielemental concentration in airborne particulate phase. This method involves deposition of aerosol particles on the tip of a cathode in a coaxial microelectrode system, followed by ablation, atomization, and excitation of the particulate matter using the rf-GD. The resulting atomic emissions are recorded using a spectrometer for elemental identification and quantification. The glow discharge plasma in our system was characterized by measuring spatially resolved gas temperatures (378-1438 K) and electron densities (2-5 × 1014 cm-3). Spatial analysis of the spectral features showed that the excitation of the analyte occurred in the region near the collection electrode. The temporal analysis of spectral features in the rf-GD showed that the collected particles were continuously ablated; the time for complete ablation of 193 ng of sucrose particles was found to be approximately 2 s. The system was calibrated using 100 nm particles containing C, Cd, Mn, and Na, respectively. The method provides limits of detection in the range of 0.055-1.0 ng, and a measurement reproducibility of 5-28%. This study demonstrates that the rf-GD can be an excellent excitation source for the development of low-cost hand-held sensors for elemental measurement of aerosols.

| S-EPMC5555147 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data