Improvement of polycrystalline silicon wafer solar cell efficiency by forming nanoscale pyramids on wafer surface using a self-mask etching technique.

ABSTRACT: The creation of nanostructures on polycrystalline silicon wafer surface to reduce the solar reflection can enhance the solar absorption and thus increase the solar-electricity conversion efficiency of solar cells. The self-masking reactive ion etching (RIE) was studied to directly fabricate nanostructures on silicon surface without using a masking process for antireflection purpose. Reactive gases comprising chlorine (Cl2), sulfur hexafluoride (SF6), and oxygen (O2) were activated by radio-frequency plasma in an RIE system at a typical pressure of 120-130 mTorr to fabricate the nanoscale pyramids. Poly-Si wafers were etched directly without masking for 6-10 min to create surface nanostructures by varying the compositions of SF6, Cl2, and O2 gas mixtures in the etching process. The wafers were then treated with acid (KOH:H2O = 1:1) for 1 min to remove the damage layer (100 nm) induced by dry etching. The damage layer significantly reduced the solar cell efficiencies by affecting the electrical properties of the surface layer. The light reflectivity from the surface after acid treatment could be significantly reduced to <10% for the wavelengths between 500 and 900 nm. The effects of RIE and surface treatment conditions on the surface nanostructures and the optical performance as well as the efficiencies of solar cells will be presented and discussed. The authors have successfully fabricated large-area (156 × 156 mm(2)) subwavelength antireflection structure on poly-Si substrates, which could improve the solar cell efficiency reproducibly up to 16.27%, higher than 15.56% using wet etching.

SUBMITTER: Lin HH

PROVIDER: S-EPMC3634306 | biostudies-other | 2013 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Towards ultra-thin plasmonic silicon wafer solar cells with minimized efficiency loss.

Project description:The cost-effectiveness of market-dominating silicon wafer solar cells plays a key role in determining the competiveness of solar energy with other exhaustible energy sources. Reducing the silicon wafer thickness at a minimized efficiency loss represents a mainstream trend in increasing the cost-effectiveness of wafer-based solar cells. In this paper we demonstrate that, using the advanced light trapping strategy with a properly designed nanoparticle architecture, the wafer thickness can be dramatically reduced to only around 1/10 of the current thickness (180??m) without any solar cell efficiency loss at 18.2%. Nanoparticle integrated ultra-thin solar cells with only 3% of the current wafer thickness can potentially achieve 15.3% efficiency combining the absorption enhancement with the benefit of thinner wafer induced open circuit voltage increase. This represents a 97% material saving with only 15% relative efficiency loss. These results demonstrate the feasibility and prospect of achieving high-efficiency ultra-thin silicon wafer cells with plasmonic light trapping.

| S-EPMC4018607 | biostudies-literature

Efficiency Improvement of Industrial Silicon Solar Cells by the POCl3 Diffusion Process

Project description:To improve the efficiency of polycrystalline silicon solar cells, process optimization is a key technology in the photovoltaic industry. Despite the efficiency of this technique to be reproducible, economic, and simple, it presents a major inconvenience to have a heavily doped region near the surface which induces a high minority carrier recombination. To limit this effect, an optimization of diffused phosphorous profiles is required. A “low-high-low” temperature step of the POCl3 diffusion process was developed to improve the efficiency of industrial-type polycrystalline silicon solar cells. The low surface concentration of phosphorus doping of 4.54 × 1020 atoms/cm3 and junction depth of 0.31 μm at a dopant concentration of N = 1017 atoms/cm3 were obtained. The open-circuit voltage and fill factor of solar cells increased up to 1 mV and 0.30%, compared with the online low-temperature diffusion process, respectively. The efficiency of solar cells and the power of PV cells were increased by 0.1% and 1 W, respectively. This POCl3 diffusion process effectively improved the overall efficiency of industrial-type polycrystalline silicon solar cells in this solar field.

| S-EPMC10003932 | biostudies-literature

Nanoscale Characterization of Photocurrent and Photovoltage in Polycrystalline Solar Cells.

Project description:We investigate the role of grain structures in nanoscale carrier dynamics of polycrystalline solar cells. By using Kelvin probe force microscopy (KPFM) and near-field scanning photocurrent microscopy (NSPM) techniques, we characterize nanoscopic photovoltage and photocurrent patterns of inorganic CdTe and organic-inorganic hybrid perovskite solar cells. For CdTe solar cells, we analyze the nanoscale electric power patterns that are created by correlating nanoscale photovoltage and photocurrent maps on the same location. Distinct relations between the sample preparation conditions and the nanoscale photovoltaic properties of microscopic CdTe grain structures are observed. The same techniques are applied for characterization of a perovskite solar cell. It is found that a moderate amount of PbI2 near grain boundaries leads to the enhanced photogenerated carrier collections at grain boundaries. Finally, the capabilities and the limitations of the nanoscale techniques are discussed.

| S-EPMC10291557 | biostudies-literature

Efficiency Improvement Using Molybdenum Disulphide Interlayers in Single-Wall Carbon Nanotube/Silicon Solar Cells.

Project description:Molybdenum disulphide (MoS?) is one of the most studied and widely applied nanomaterials from the layered transition-metal dichalcogenides (TMDs) semiconductor family. MoS? has a large carrier diffusion length and a high carrier mobility. Combining a layered structure of single-wall carbon nanotube (SWCNT) and MoS? with n-type silicon (n-Si) provided novel SWCNT/n-Si photovoltaic devices. The solar cell has a layered structure with Si covered first by a thin layer of MoS? flakes and then a SWCNT film. The films were examined using scanning electron microscopy, atomic force microscopy and Raman spectroscopy. The MoS? flake thickness ranged from 5 to 90 nm while the nanosheet’s lateral dimensions size ranged up to 1 μm². This insertion of MoS? improved the photoconversion efficiency (PCE) of the SWCNT/n-Si solar cells by approximately a factor of 2.

| S-EPMC5951523 | biostudies-literature

Effect of Isopropyl Alcohol Concentration and Etching Time on Wet Chemical Anisotropic Etching of Low-Resistivity Crystalline Silicon Wafer.

Project description:A micropyramid structure was formed on the surface of a monocrystalline silicon wafer (100) using a wet chemical anisotropic etching technique. The main objective was to evaluate the performance of the etchant based on the silicon surface reflectance. Different isopropyl alcohol (IPA) volume concentrations (2, 4, 6, 8, and 10%) and different etching times (10, 20, 30, 40, and 50 min) were selected to study the total reflectance of silicon wafers. The other parameters such as NaOH concentration (12% wt.), the temperature of the solution (81.5°C), and range of stirrer speeds (400 rpm) were kept constant for all processes. The surface morphology of the wafer was analyzed by optical microscopy and atomic force microscopy (AFM). The AFM images confirmed a well-uniform pyramidal structure with various average pyramid sizes ranging from 1 to 1.6 μm. A UV-Vis spectrophotometer with integrating sphere was used to obtain the total reflectivity. The textured silicon wafers show high absorbance in the visible region. The optimum texture-etching parameters were found to be 4-6% vol. IPA and 40 min at which the average total reflectance of the silicon wafer was reduced to 11.22%.

| S-EPMC5554996 | biostudies-other

Wafer-Scale Fabrication of Silicon Nanocones via Controlling Catalyst Evolution in All-Wet Metal-Assisted Chemical Etching.

Project description:All-wet metal-assisted chemical etching (MACE) is a simple and low-cost method to fabricate one-dimensional Si nanostructures. However, it remains a challenge to fabricate Si nanocones (SiNCs) with this method. Here, we achieved wafer-scale fabrication of SiNC arrays through an all-wet MACE process. The key to fabricate SiNCs is to control the catalyst evolution from deposition to etching stages. Different from conventional MACE processes, large-size Ag particles by solution deposition are obtained through increasing AgNO3 concentration or extending the reaction time in the seed solution. Then, the large-size Ag particles are simultaneously etched during the Si etching process in an etching solution with a high H2O2 concentration due to the accelerated cathode process and inhibited anode process in Ag/Si microscopic galvanic cells. The successive decrease of Ag particle sizes causes the proportionate increase of diameters of the etched Si nanostructures, forming SiNC arrays. The SiNC arrays exhibit a stronger light-trapping ability and better photoelectrochemical performance compared with Si nanowire arrays. SiNCs were fabricated by using n-type 1-10 Ω cm Si(100) wafers in this work. Though the specific experimental conditions for preparing SiNCs may differ when using different Si wafers, the summarized diagram will still provide valuable guidance for morphology control of Si nanostructures in MACE processes.

| S-EPMC8772306 | biostudies-literature

Kerf-Less Exfoliated Thin Silicon Wafer Prepared by Nickel Electrodeposition for Solar Cells.

Project description:Ultra-thin and large-area silicon wafers with a thickness in the range of 20-70 μm, were produced by spalling using a nickel stressor layer. A new equation for predicting the thickness of the spalled silicon was derived from the Suo-Hutchinson mechanical model and the kinking mechanism. To confirm the reliability of the new equation, the proportional factor of stress induced by the nickel on the silicon wafer, was calculated. The calculated proportional factor of λ = 0.99 indicates that the thickness of the spalled silicon wafer is proportional to that of the nickel layer. A similar relationship was observed in the experimental data obtained in this study. In addition, the thickness of the stressor layer was converted to a value of stress as a guide when using other deposition conditions and materials. A silicon wafer with a predicted thickness of 50 μm was exfoliated for further analysis. In order to spall a large-area (150 × 150 mm2 or 6 × 6 in2) silicon wafer without kerf loss, initial cracks were formed by a laser pretreatment at a proper depth (50 μm) inside the exfoliated silicon wafer, which reduced the area of edge slope (kerf loss) from 33 to 3 mm2. The variations in thickness of the spalled wafer remained under 4%. Moreover, we checked the probability of degradation of the spalled wafers by using them to fabricate solar cells; the efficiency and ideality factor of the spalled silicon wafers were found to be 14.23%and 1.35, respectively.

| S-EPMC6339913 | biostudies-literature

Methodology to analyse small silicon samples by glow discharge mass spectrometry using a thin wafer mask.

Project description:Glow discharge mass spectrometry (GDMS) is widely used for trace element analysis of bulk solid samples. The geometry of the GD source limits the minimum size of the sample, which for the instrument used in this work (ThermoElementGD) is 20 mm in diameter. From time to time, there is the need to analyse smaller samples with this technique, and we present here a methodology to analyse samples of 9-20 mm diameter through the use of thin masks. Thin masks have been previously used mostly as secondary cathode for the analysis of non-conducting materials, with hole size smaller than the area of the glow discharge. The use of masks in this work includes the following customization:•The choice of highly-pure Si as mask material, to decrease the chance of interferences with the Si samples.•The use of a hole in the mask of the same size as the discharge area. This implies that the mask material is not sputtered, thus decreasing chances for contamination from the mask itself.

| S-EPMC4644257 | biostudies-literature

High efficiency hybrid silicon nanopillar-polymer solar cells.

Project description:Recently, inorganic/organic hybrid solar cells have been considered as a viable alternative for low-cost photovoltaic devices because the Schottky junction between inorganic and organic materials can be formed employing low temperature processing methods. We present an efficient hybrid solar cell based on highly ordered silicon nanopillars (SiNPs) and poly(3,4-ethylene-dioxythiophene):polystyrenesulfonate (PEDOT:PSS). The proposed device is formed by spin coating the organic polymer PEDOT:PSS on a SiNP array fabricated using metal assisted electroless chemical etching process. The characteristics of the hybrid solar cells are investigated as a function of SiNP height. A maximum power conversion efficiency (PCE) of 9.65% has been achieved for an optimized SiNP array hybrid solar cell with nanopillar height of 400 nm, despite the absence of a back surface field enhancement. The effect of an ultrathin atomic layer deposition (ALD), grown aluminum oxide (Al2O3), as a passivation layer (recombination barrier) has also been studied for the enhanced electrical performance of the device. With the inclusion of the ultrathin ALD deposited Al2O3 between the SiNP array textured surface and the PEDOT:PSS layer, the PCE of the fabricated device was observed to increase to 10.56%, which is ∼10% greater than the corresponding device without the Al2O3 layer. The device described herein is considered to be promising toward the realization of a low-cost, high-efficiency inorganic/organic hybrid solar cell.

| S-EPMC4142496 | biostudies-literature

Realistic Efficiency Limits for Singlet-Fission Silicon Solar Cells.

Project description:Singlet fission is a carrier multiplication mechanism that could make silicon solar cells much more efficient. The singlet-fission process splits one high-energy spin-singlet exciton into two lower-energy spin-triplet excitons. We calculated the efficiency potential of three technologically relevant singlet-fission silicon solar cell implementations. We assume realistic but optimistic parameters for the singlet-fission material and investigate the effect of singlet energy and entropic gain. If the transfer of triplet excitons occurs via charge transfer, the maximum efficiency is 34.6% at a surprisingly small singlet energy of 1.85 eV. For the Dexter-type triplet energy transfer, the maximum efficiency is 32.9% at a singlet energy of 2.15 eV. For Förster resonance energy transfer (FRET), the triplet excitons are first transferred into a quantum dot, from which they then undergo FRET into silicon. For this transfer mechanism, the maximum efficiency is 28.% at a singlet energy of 2.33 eV. We show that the efficiency gain from singlet fission is larger the more efficient the silicon base cell is, which stands in contrast to tandem perovskite-silicon solar cells.

| S-EPMC8389984 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data