Synthesis of nanocrystals by discharges in liquid nitrogen from Si-Sn sintered electrode.

ABSTRACT: The synthesis feasibility of silicon-tin nanocrystals by discharges in liquid nitrogen is studied using a Si-10 at % Sn sintered electrode. Time-resolved optical emission spectroscopy shows that silicon and tin melt almost simultaneously. The presence of both vapours does not lead to the synthesis of alloyed nanocrystals but to the synthesis of separate nanocrystals of silicon and tin with average sizes of 10 nm. These nanocrystals are transformed into amorphous silicon oxide (am-SiO2) and β-SnO2 by air oxidation, after evaporation of the liquid nitrogen. The synthesis of an am-Si0.95Sn0.05 phase around large silicon crystals (~500 nm) decorated by β-Sn spheroids is achieved if the current flowing through electrodes is high enough. When the sintered electrode is hit by powerful discharges, some grains are heated and tin diffuses in the large silicon crystals. Next, these grains are shelled and fall into the dielectric liquid.

SUBMITTER: Kabbara H

PROVIDER: S-EPMC4664926 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Colloidal Cu-Zn-Sn-Te Nanocrystals: Aqueous Synthesis and Raman Spectroscopy Study.

Project description:Cu-Zn-Sn-Te (CZTTe) is an inexpensive quaternary semiconductor that has not been investigated so far, unlike its intensively studied CZTS and CZTSe counterparts, although it may potentially have desirable properties for solar energy conversion, thermoelectric, and other applications. Here, we report on the synthesis of CZTTe nanocrystals (NCs) via an original low-cost, low-temperature colloidal synthesis in water, using a small-molecule stabilizer, thioglycolic acid. The absorption edge at about 0.8-0.9 eV agrees well with the value expected for Cu2ZnSnTe4, thus suggesting CZTTe to be an affordable alternative for IR photodetectors and solar cells. As the main method of structural characterization multi-wavelength resonant Raman spectroscopy was used complemented by TEM, XRD, XPS as well as UV-vis and IR absorption spectroscopy. The experimental study is supported by first principles density functional calculations of the electronic structure and phonon spectra. Even though the composition of NCs exhibits a noticeable deviation from the Cu2ZnSnTe4 stoichiometry, a common feature of multinary NCs synthesized in water, the Raman spectra reveal very small widths of the main phonon peak and also multi-phonon scattering processes up to the fourth order. These factors imply a very good crystallinity of the NCs, which is further confirmed by high-resolution TEM.

| S-EPMC8624267 | biostudies-literature

Liquid-Phase Monolayer Doping of InGaAs with Si-, S-, and Sn-Containing Organic Molecular Layers.

Project description:The functionalization and subsequent monolayer doping of InGaAs substrates using a tin-containing molecule and a compound containing both silicon and sulfur was investigated. Epitaxial InGaAs layers were grown on semi-insulating InP wafers and functionalized with both sulfur and silicon using mercaptopropyltriethoxysilane and with tin using allyltributylstannane. The functionalized surfaces were characterized using X-ray photoelectron spectroscopy (XPS). The surfaces were capped and subjected to rapid thermal annealing to cause in-diffusion of dopant atoms. Dopant diffusion was monitored using secondary ion mass spectrometry. Raman scattering was utilized to nondestructively determine the presence of dopant atoms, prior to destructive analysis, by comparison to a blank undoped sample. Additionally, due to the As-dominant surface chemistry, the resistance of the functionalized surfaces to oxidation in ambient conditions over periods of 24 h and 1 week was elucidated using XPS by monitoring the As 3d core level for the presence of oxide components.

| S-EPMC6640969 | biostudies-literature

Neutron Diffraction Study of a Sintered Iron Electrode In Operando.

Project description:Iron is a promising, earth-abundant material for future energy applications. In this study, we use a neutron diffractometer to investigate the properties of an iron electrode in an alkaline environment. As neutrons penetrate deeply into materials, neutron scattering gives us a unique insight into what is happening inside the electrode. We made our measurements while the electrode was charging or discharging. Our key questions are: Which phases occur for the first and second discharge plateaus? And why are iron electrodes less responsive at higher discharge rates? We conclude that metallic iron and iron hydroxide form the redox pair for the first discharge plateau. For the second discharge plateau, we found a phase similar to feroxyhyte but with symmetrical and equally spaced arrangement of hydrogen atoms. The data suggest that no other iron oxide or iron (oxy)hydroxide formed. Remarkable findings include the following: (1) substantial amounts of iron hydroxide are always present inside the electrode. (2) Passivation is mostly caused by iron hydroxide that is unable to recharge. (3) Iron fractions change as expected, while iron hydroxide fractions are delayed, resulting in substantial amounts of amorphous, undetectable iron phases. About 40% of the participating iron of the first plateau and about 55% of the participating iron for the second plateau are undetectable. (4) Massive and unexpected precipitation of iron hydroxide occurs in the transition from discharging to charging. (2), (3), and (4) together cause accumulation of iron hydroxide inside the electrode.

| S-EPMC8350908 | biostudies-literature

Mechanochemical synthesis of Si/Cu<sub>3</sub>Si-based composite as negative electrode materials for lithium ion battery.

Project description:Mechanochemical synthesis of Si/Cu3Si-based composite as negative electrode materials for lithium ion battery is investigated. Results indicate that CuO is decomposed and alloyed with Si forming amorphous Cu-Si solid solution due to high energy impacting during high energy mechanical milling (HEMM). Upon carbonization at 800 °C, heating energy induces Cu3Si to crystallize in nanocrystalline/amorphous Si-rich matrix enhancing composite rigidity and conductivity. In addition, residual carbon formed on outside surface of composite powder as a buff space further alleviates volume change upon lithiation/delithiation. Thus, coin cell made of C-coated Si/Cu3Si-based composite as negative electrode (active materials loading, 2.3 mg cm-2) conducted at 100 mA g-1 performs the initial charge capacity of 1812 mAh g-1 (4.08 mAh cm-2) columbic efficiency of 83.7% and retained charge capacity of 1470 mAh g-1 (3.31 mAh cm-2) at the end of the 100th cycle, opening a promised window as negative electrode materials for lithium ion batteries.

| S-EPMC6107536 | biostudies-literature

Emission efficiency limit of Si nanocrystals.

Project description:One of the important obstacles on the way to application of Si nanocrystals for development of practical devices is their typically low emissivity. In this study we explore the limits of external quantum yield of photoluminescence of solid-state dispersions of Si nanocrystals in SiO2. By making use of a low-temperature hydrogen passivation treatment we demonstrate a maximum emission quantum efficiency of approximately 35%. This is the highest value ever reported for this type of material. By cross-correlating PL lifetime with EQE values, we obtain a comprehensive understanding of the efficiency limiting processes induced by Pb-defects. We establish that the observed record efficiency corresponds to an interface density of Pb-centers of 1.3 × 10(12) cm(12), which is 2 orders of magnitude higher than for the best Si/SiO2 interface. This result implies that Si nanocrystals with up to 100% emission efficiency are feasible.

| S-EPMC4726123 | biostudies-literature

Thermally stimulated exciton emission in Si nanocrystals.

Project description:Increasing temperature is known to quench the excitonic emission of bulk silicon, which is due to thermally induced dissociation of excitons. Here, we demonstrate that the effect of temperature on the excitonic emission is reversed for quantum-confined silicon nanocrystals. Using laser-induced heating of silicon nanocrystals embedded in SiO2, we achieved a more than threefold (>300%) increase in the radiative (photon) emission rate. We theoretically modeled the observed enhancement in terms of the thermally stimulated effect, taking into account the massive phonon production under intense illumination. These results elucidate one more important advantage of silicon nanostructures, illustrating that their optical properties can be influenced by temperature. They also provide an important insight into the mechanisms of energy conversion and dissipation in ensembles of silicon nanocrystals in solid matrices. In practice, the radiative rate enhancement under strong continuous wave optical pumping is relevant for the possible application of silicon nanocrystals for spectral conversion layers in concentrator photovoltaics.

| S-EPMC6107050 | biostudies-literature

Size confinement of Si nanocrystals in multinanolayer structures.

Project description:Si nanocrystals (NCs) are often prepared by thermal annealing of multiple stacks of alternating sub-stoichiometric SiOx and SiO2 nanolayers. It is frequently claimed that in these structures, the NC diameter can be predefined by the thickness of the SiOx layer, while the NC concentration is independently controlled by the stoichiometry parameter x. However, several detailed structural investigations report that the NC size confinement to within the thickness of the SiOx layer is not strictly obeyed. In this study we address these contradicting findings: based on cross-correlation between structural and optical characterization of NCs grown in a series of purposefully prepared samples of different stoichiometry and layer thickness, we develop a comprehensive understanding of NC formation by Si precipitation in multinanolayer structures. We argue that the narrow NC size distribution generally observed in these materials appears due to reduction of the Si diffusion range, imposed by the SiO2 spacer layer. Therefore, both the SiOx layer thickness and composition as well as the actual thickness of the SiO2 spacer play an essential role in the NC formation.

| S-EPMC4658553 | biostudies-literature

Facile Synthesis of Sn/Nitrogen-Doped Reduced Graphene Oxide Nanocomposites with Superb Lithium Storage Properties.

Project description:Sn/Nitrogen-doped reduced graphene oxide (Sn@N-G) composites have been successfully synthesized via a facile method for lithium-ion batteries. Compared with the Sn or Sn/graphene anodes, the Sn@N-G anode exhibits a superb rate capability of 535 mAh g-1 at 2C and cycling stability up to 300 cycles at 0.5C. The improved lithium-storage performance of Sn@N-G anode could be ascribed to the effective graphene wrapping, which accommodates the large volume change of Sn during the charge-discharge process, while the nitrogen doping increases the electronic conductivity of graphene, as well as provides a large number of active sites as reservoirs for Li+ storage.

| S-EPMC6723252 | biostudies-literature

Submerged liquid plasma for the synthesis of unconventional nitrogen polymers.

Project description:Glow discharge polymerization is not well understood due to the rapid/complex reaction at the plasma/gas precursor interface. Plasma reaction in a submerged condition allows post-plasma-polymerization, leading to further polymer growth and thus a stable structure. Electron collision with acetonitrile at the interface initiates the formation of radical monomers, which undergoes further rearrangement to form low-molecular (LM) nitrogen polymers (NPs). The radical-rich LM NPs go through further polymerization, forming stable high-molecular (HM) NPs (as determined using liquid chromatography/mass spectrometry). LM NPs absorb light at a wavelength of 270 nm (? max) whereas HM NPs show absorption at 420 nm (? max), as determined from ultraviolet-visible absorption spectra. The fluorescence spectra of HM NPs show characteristic emission at 430 nm, which indicates the presence of nitrogen functional groups with external conjugation. The proposed structure of HM NPs is verified with different analytical instruments.

| S-EPMC3740282 | biostudies-literature

Recover the activity of sintered supported catalysts by nitrogen-doped carbon atomization.

Project description:The sintering of supported metal nanoparticles is a major route to the deactivation of industrial heterogeneous catalysts, which largely increase the cost and decrease the productivity. Here, we discover that supported palladium/gold/platinum nanoparticles distributed at the interface of oxide supports and nitrogen-doped carbon shells would undergo an unexpected nitrogen-doped carbon atomization process against the sintering at high temperatures, during which the nanoparticles can be transformed into more active atomic species. The in situ transmission electron microscopy images reveal the abundant nitrogen defects in carbon shells provide atomic diffusion sites for the mobile atomistic palladium species detached from the palladium nanoparticles. More important, the catalytic activity of sintered and deactivated palladium catalyst can be recovered by this unique N-doped carbon atomization process. Our findings open up a window to preparation of sintering-resistant single atoms catalysts and regeneration of deactivated industrial catalysts.

| S-EPMC6969067 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data