Assembling carbon quantum dots to a layered carbon for high-density supercapacitor electrodes.

ABSTRACT: It is found that carbon quantum dots (CQDs) self-assemble to a layer structure at ice crystals-water interface with freeze- drying. Such layers interconnect with each other, forming a free-standing CQD assembly, which has an interlayer distance of about 0.366?nm, due to the existence of curved carbon rings other than hexagons in the assembly. CQDs are fabricated by rupturing C60 by KOH activation with a production yield of ~15?wt.%. The CQDs obtained have an average height of 1.14?nm and an average lateral size of 7.48?nm, and are highly soluble in water. By packaging annealed CQD assembly to high density (1.23?g cm(-3)) electrodes in supercapacitors, a high volumetric capacitance of 157.4 F cm(-3) and a high areal capacitance of 0.66 F cm(-2) (normalized to the loading area of electrodes) are demonstrated in 6?M KOH aqueous electrolyte with a good rate capability.

SUBMITTER: Chen G

PROVIDER: S-EPMC4709517 | biostudies-literature | 2016 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Assembling carbon quantum dots to a layered carbon for high-density supercapacitor electrodes.

Chen Guanxiong G Wu Shuilin S Hui Liwei L Zhao Yuan Y Ye Jianglin J Tan Ziqi Z Zeng Wencong W Tao Zhuchen Z Yang Lihua L Zhu Yanwu Y

Scientific reports 20160112

It is found that carbon quantum dots (CQDs) self-assemble to a layer structure at ice crystals-water interface with freeze- drying. Such layers interconnect with each other, forming a free-standing CQD assembly, which has an interlayer distance of about 0.366 nm, due to the existence of curved carbon rings other than hexagons in the assembly. CQDs are fabricated by rupturing C60 by KOH activation with a production yield of ~15 wt.%. The CQDs obtained have an average height of 1.14 nm and an aver ...[more]

PMID: 26754463

Similar Datasets

Incorporation of Carbon Quantum Dots for Improvement of Supercapacitor Performance of Nickel Sulfide.

Project description:A facile hydrothermal method is adopted for the synthesis of hierarchical flowerlike nickel sulfide nanostructure materials and their composite with carbon quantum dot (NiS/C-dot) composite. The composite material exhibited good performance for electrochemical energy-storage devices as supercapacitor with a specific capacity of 880 F g-1 at a current density of 2 A g-1. The material remained stable up to the tested 2000 charge-discharge cycles. Carbon quantum dots of size 1.3 nm were synthesized from natural sources and the favorable electronic and surface property of C-dots were utilized for improvement of the supercapacitor performance of NiS. The results from Tafel analysis, double-layer capacitance, and the impedance measurement reveal that the incorporation of C-dots inside the NiS matrix has improved the charge-transfer process, which is mainly responsible for the enhancement of the supercapacitive property of the composite materials.

| S-EPMC6643915 | biostudies-literature

High-Capacitance Hybrid Supercapacitor Based on Multi-Colored Fluorescent Carbon-Dots.

Project description:Multi-colored, water soluble fluorescent carbon nanodots (C-Dots) with quantum yield changing from 4.6 to 18.3% were synthesized in multi-gram using dated cola beverage through a simple thermal synthesis method and implemented as conductive and ion donating supercapacitor component. Various properties of C-Dots, including size, crystal structure, morphology and surface properties along with their Raman and electron paramagnetic resonance spectra were analyzed and compared by means of their fluorescence and electronic properties. ?-Manganese Oxide-Polypyrrole (PPy) nanorods decorated with C-Dots were further conducted as anode materials in a supercapacitor. Reduced graphene oxide was used as cathode along with the dicationic bis-imidazolium based ionic liquid in order to enhance the charge transfer and wetting capacity of electrode surfaces. For this purpose, we used octyl-bis(3-methylimidazolium)diiodide (C8H16BImI) synthesized by N-alkylation reaction as liquid ionic membrane electrolyte. Paramagnetic resonance and impedance spectroscopy have been undertaken in order to understand the origin of the performance of hybrid capacitor in more depth. In particular, we obtained high capacitance value (C?=?17.3??F/cm2) which is exceptionally related not only the quality of synthesis but also the choice of electrode and electrolyte materials. Moreover, each component used in the construction of the hybrid supercapacitor is also played a key role to achieve high capacitance value.

| S-EPMC5593850 | biostudies-literature

Highly Porous Willow Wood-Derived Activated Carbon for High-Performance Supercapacitor Electrodes.

Project description:In this study, we present willow wood as a new low-cost, renewable, and sustainable biomass source for the production of a highly porous activated carbon for application in energy storage devices. The obtained activated carbon showed favorable features required for excellent electrochemical performance such as high surface area (?2 800 m2 g-1) and pore volume (1.45 cm3 g-1), with coexistence of micropores and mesopores. This carbon material was tested as an electrode for supercapacitor application and showed a high specific capacitance of 394 F g-1 at a current density of 1 A g-1 and good cycling stability, retaining ?94% capacitance after 5?000 cycles (at a current density of 5 A?g-1) in 6 M KOH electrolyte. The prepared carbon material also showed an excellent rate performance in a symmetrical two-electrode full cell configuration using 1 M Na2SO4 electrolyte, in a high working voltage of 1.8 V. The maximum energy density and power density of the fabricated symmetric cell reach 23 W h kg-1 and 10 000 W kg-1, respectively. These results demonstrate that willow wood can serve as a low-cost carbon feedstock for production of high-performance electrode material for supercapacitors.

| S-EPMC6843703 | biostudies-literature

Defect-induced B<sub>4</sub>C electrodes for high energy density supercapacitor devices.

Project description:Boron carbide powders were synthesized by mechanically activated annealing process using anhydrous boron oxide (B2O3) and varying carbon (C) sources such as graphite and activated carbon: The precursors were mechanically activated for different times in a high energy ball mill and reacted in an induction furnace. According to the Raman analyses of the carbon sources, the I(D)/I(G) ratio increased from ~ 0.25 to ~ 0.99, as the carbon material changed from graphite to active carbon, indicating the highly defected and disordered structure of active carbon. Complementary advanced EPR analysis of defect centers in B4C revealed that the intrinsic defects play a major role in the electrochemical performance of the supercapacitor device once they have an electrode component made of bare B4C. Depending on the starting material and synthesis conditions the conductivity, energy, and power density, as well as capacity, can be controlled hence high-performance supercapacitor devices can be produced.

| S-EPMC8172886 | biostudies-literature

High performance asymmetric supercapacitor based on Cobalt Nickle Iron-layered double hydroxide/carbon nanofibres and activated carbon.

Project description:A novel Cobalt Nickle Iron-layered double hydroxide/carbon nanofibres (CoNiFe-LDH/CNFs-0.5) composite was successfully fabricated through an easy in situ growth approach. The morphology and composition of the obtained materials were systematically investigated. When the two derived materials were used for supercapacitor electrodes, the CoNiFe-LDH/CNFs-0.5 composite displayed high specific surface area (114.2?m2?g-1), specific capacitance (1203?F?g-1 at 1?A?g-1) and rate capability (77.1% from 1?A?g-1 to 10?A?g-1), which were considerably higher than those of pure CoNiFe-LDH. Moreover, the specific capacitance of CoNiFe-LDH/CNFs-0.5 composite remained at 94.4% after 1000 cycles at 20?A?g-1, suggesting excellent long-time cycle life. The asymmetric supercapacitor based on CoNiFe-LDH/CNFs-0.5 as a positive electrode and activated carbon as a negative electrode was manufactured and it exhibited a specific capacitance of 84.9?F?g-1 at 1?A?g-1 and a high energy density of 30.2?W?h kg-1. More importantly, this device showed long-term cycling stability, with 82.7% capacity retention after 2000 cycles at 10?A?g-1. Thus, this composite with outstanding electrochemical performance could be a promising electrode material for supercapacitors.

| S-EPMC5498571 | biostudies-literature

Flexible Fe3O4@Carbon Nanofibers Hierarchically Assembled with MnO2 Particles for High-Performance Supercapacitor Electrodes.

Project description:Increasing use of wearable electronic devices have resulted in enhanced demand for highly flexible supercapacitor electrodes with superior electrochemical performance. In this study, flexible composite membranes with electrosprayed MnO2 particles uniformly anchored on Fe3O4 doped electrospun carbon nanofibers (Fe3O4@CNFMn) have been prepared as flexible electrodes for high-performance supercapacitors. The interconnected porous beaded structure ensures free movement of electrolyte within the composite membranes, therefore, the developed supercapacitor electrodes not only offer high specific capacitance of ~306?F/g, but also exhibit good capacitance retention of ~85% after 2000 cycles, which certify that the synthesized electrodes offer high and stable electrochemical performance. Additionally, the supercapacitors fabricated from our developed electrodes well maintain their performance under flexural stress and exhibit a very minute change in specific capacitance even up to 180° bending angle. The developed electrode fabrication strategy integrating electrospinning and electrospray techniques paves new insights into the development of potential functional nanofibrous materials for light weight and flexible wearable supercapacitors.

| S-EPMC5680204 | biostudies-literature

Co?O?@CoS Core-Shell Nanosheets on Carbon Cloth for High Performance Supercapacitor Electrodes.

Project description:In this work, a two-step electrodeposition strategy is developed for the synthesis of core-shell Co?O?@CoS nanosheet arrays on carbon cloth (CC) for supercapacitor applications. Porous Co?O? nanosheet arrays are first directly grown on CC by electrodeposition, followed by the coating of a thin layer of CoS on the surface of Co?O? nanosheets via the secondary electrodeposition. The morphology control of the ternary composites can be easily achieved by altering the number of cyclic voltammetry (CV) cycles of CoS deposition. Electrochemical performance of the composite electrodes was evaluated by cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy techniques. The results demonstrate that the Co?O?@CoS/CC with 4 CV cycles of CoS deposition possesses the largest specific capacitance 887.5 F·g-1 at a scan rate of 10 mV·s-1 (764.2 F·g-1 at a current density of 1.0 A·g-1), and excellent cycling stability (78.1% capacitance retention) at high current density of 5.0 A·g-1 after 5000 cycles. The porous nanostructures on CC not only provide large accessible surface area for fast ions diffusion, electron transport and efficient utilization of active CoS and Co?O?, but also reduce the internal resistance of electrodes, which leads to superior electrochemical performance of Co?O?@CoS/CC composite at 4 cycles of CoS deposition.

| S-EPMC5553425 | biostudies-literature

Hierarchical Porous Carbon with Interconnected Ordered Pores from Biowaste for High-Performance Supercapacitor Electrodes.

Project description:Using biowastes as precursors for the preparation of value-added nanomaterials is critical to the sustainable development of devices. Lignosulphonates are the by-products of pulp and paper-making industries and usually discarded as wastes. In the present study, lignosulphonate is used as the precursor to prepare hierarchical ordered porous carbon with interconnected pores for the electrochemical energy storage application. The unique molecular structure and properties of lignosulphonate ensure the acquisition of high-quality porous carbon with a controllable pore structure and improved physical properties. As a result, the as-prepared hierarchical order porous carbon show excellent energy storage performance when used to assemble the symmetric supercapacitor, which exhibits high-specific capacitance of 289 F g-1 at a current density of 0.5 A g-1, with the energy density of 40 Wh kg-1 at the power density of 900 W kg-1. The present study provides a promising strategy for the fabrication of high-performance energy storage devices at low cost.

| S-EPMC7174449 | biostudies-literature

Electrospun Enzymatic Hydrolysis Lignin-Based Carbon Nanofibers as Binder-Free Supercapacitor Electrodes with High Performance.

Project description:Carbon nanofibers consisting of Poly(acrylonitrile) (PAN) and enzymatic hydrolysis lignin (EHL) were prepared in the present study by electrospinning followed by stabilization in air and carbonization in N? environment. The morphology and structure of the electrospun carbon nanofibers were characterized by Scanning Electron Microscopy (SEM), Brunauer-Emmett-Teller (BET), Roman, and the electrochemical performances were then evaluated by cyclic voltammetry (CV), galvanostatic charge-discharge (GCD), and electrochemical impedance spectroscopy (EIS)methods. When the amount of EHL was 60 wt. %, the as-prepared nanofibers have the smallest average diameter of 172 nm and the largest BET specific surface area of 675 m²/g without activating treatment. The carbon nanofiber electrode showed excellent specific capacitance of 216.8 F/g at the current density of 1 A/g, maintaining 88.8% capacitance retention after 2000 cycles. Moreover, the carbon nanofiber electrode containing 60 wt. % exhibited a smaller time constant (0.5 s) in comparison to that of carbon nanofibers in literatures. These findings suggest the potential use of EHL could be a practical as a sustainable alternative for PAN in carbon electrode manufacturing.

| S-EPMC6401840 | biostudies-literature

Linear-Polyethyleneimine-Templated Synthesis of N-Doped Carbon Nanonet Flakes for High-performance Supercapacitor Electrodes.

Project description:Novel N-doped carbon nanonet flakes (NCNFs), consisting of three-dimensional interconnected carbon nanotube and penetrable mesopore channels were synthesized in the assistance of a hybrid catalytic template of silica-coated-linear polyethyleneimine (PEI). Resorcinol-formaldehyde resin and melamine were used as precursors for carbon and nitrogen, respectively, which were spontaneously formed on the silica-coated-PEI template and then annealed at 700 °C in a N2 atmosphere to be transformed into the hierarchical 3D N-doped carbon nanonetworks. The obtained NCNFs possess high surface area (946 m2 g-1), uniform pore size (2-5 nm), and excellent electron and ion conductivity, which were quite beneficial for electrochemical double-layered supercapacitors (EDLSs). The supercapacitor synthesized from NCNFs electrodes exhibited both extremely high capacitance (up to 613 F g-1 at 1 A g-1) and excellent long-term capacitance retention performance (96% capacitive retention after 20,000 cycles), which established the current processing among the most competitive strategies for the synthesis of high performance supercapacitors.

| S-EPMC6780425 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data