Enhancing Specific Energy and Power in Asymmetric Supercapacitors - A Synergetic Strategy based on the Use of Redox Additive Electrolytes.

ABSTRACT: The strategy of using redox additive electrolyte in combination with multiwall carbon nanotubes/metal oxide composites leads to a substantial improvements in the specific energy and power of asymmetric supercapacitors (ASCs). When the pure electrolyte is optimally modified with a redox additive viz., KI, ~105% increase in the specific energy is obtained with good cyclic stability over 3,000 charge-discharge cycles and ~14.7% capacitance fade. This increase is a direct consequence of the iodine/iodide redox pairs that strongly modifies the faradaic and non-faradaic type reactions occurring on the surface of the electrodes. Contrary to what is shown in few earlier reports, it is established that indiscriminate increase in the concentration of redox additives will leads to performance loss. Suitable explanations are given based on theoretical laws. The specific energy or power values being reported in the fabricated ASCs are comparable or higher than those reported in ASCs based on toxic acetonitrile or expensive ionic liquids. The paper shows that the use of redox additive is economically favorable strategy for obtaining cost effective and environmentally friendly ASCs.

SUBMITTER: Singh A

PROVIDER: S-EPMC4868987 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

New Supercapacitors Based on the Synergetic Redox Effect between Electrode and Electrolyte.

Project description:Redox electrolytes can provide significant enhancement of capacitance for supercapacitors. However, more important promotion comes from the synergetic effect and matching between the electrode and electrolyte. Herein, we report a novel electrochemical system consisted of a polyanilline/carbon nanotube composite redox electrode and a hydroquinone (HQ) redox electrolyte, which exhibits a specific capacitance of 7926 F/g in a three-electrode system when the concentration of HQ in H₂SO₄ aqueous electrolyte is 2 mol/L, and the maximum energy density of 114 Wh/kg in two-electrode symmetric configuration. Moreover, the specific capacitance retention of 96% after 1000 galvanostatic charge/discharge cycles proves an excellent cyclic stability. These ultrahigh performances of the supercapacitor are attributed to the synergistic effect both in redox polyanilline-based electrolyte and the redox hydroquinone electrode.

| S-EPMC5457064 | biostudies-other

Ultrahigh Energy and Power Densities of d-MXene-Based Symmetric Supercapacitors.

Project description:Here, rational design electrodes are fabricated by mixing MXene with an aqueous solution of chloroauric acid (HAuCl4). In order to prevent MXene from self-restacking, the groups of -OH on the surface of Ti3C2Tx nanosheets underwent a one-step simultaneous self-reduction from AuCl4-, generating spaces for rapid ion transit. Additionally, by using this procedure, MXene's surface oxidation can be decreased while preserving its physio-chemical properties. The interlayered MX/Au NPs that have been obtained are combined into a conducting network structure that offers more active electrochemical sites and improved mass transfer at the electrode-electrolyte interface, both of which promote quick electron transfer during electrochemical reactions and excellent structural durability. The Ti3C2Tx-AuNPs film thus demonstrated a rate performance that was preferable to that of pure Ti3C2Tx film. According to the results of the characterization, the AuNPs effectively adorn the MXene nanosheets. Due to the renowned pseudocapacitance charge storage mechanism, MXene-based electrode materials also work well as supercapacitors in sulfuric acid, which is why MXene AuNPs electrodes have been tested in 3 M and 1 M H2SO4. The symmetric supercapacitors made of MXene and AuNPs have shown exceptional specific capacitance of 696.67 Fg-1 at 5 mVs-1 in 3 M H2SO4 electrolyte, and they can sustain 90% of their original capacitance for 5000 cycles. The highest energy and power density of this device, which operates within a 1.2 V potential window, are 138.4 Wh kg-1 and 2076 W kg-1, respectively. These findings offer a productive method for creating high-performance metal oxide-based symmetric capacitors and a straightforward, workable approach for improving MXene-based electrode designs, which can be applied to other electro-chemical systems that are ion transport-restricted, such as metal ion batteries and catalysis.

| S-EPMC9565486 | biostudies-literature

Flexible Asymmetric Supercapacitors with Ultrahigh Energy Density through Synergistic Design of Electrodes.

Project description:Despite being among the most researched energy storage devices, supercapacitors have often suffered from their relatively low operating voltage and energy density, which greatly limit their practical applications. In this work, asymmetric supercapacitors (ASCs) are developed by synergistically designing carbon nanotube composite electrodes with 3D porous structures. The resultant ASC devices exhibit an extended operating voltage of 1.8 V, much higher than that of symmetric supercapacitors (?1.0 V). Significantly, the obtained ASC devices deliver ultrahigh volumetric energy density as high as 19.8 mWh cm-3 (corresponding to an areal energy density of 198 µWh cm-2), which is the highest value among reported ASC devices. In addition, the ASC devices not only possess outstanding cycling stability and long self-discharging time, but also exhibit excellent mechanical flexibility under any bending states, even over 5000 bending cycles. The demonstrated flexible ASC devices with high performance are promising to be used as power sources for next-generation portable and wearable electronics.

| S-EPMC6247045 | biostudies-literature

Lanthanum Oxide Nickel Hydroxide Composite Triangle Nanosheets for Energy Density Asymmetric Supercapacitors.

Project description:Transition metal hydroxides are a kind of promising electrode material in electrochemical energy storage, but the poor conductivity limits their application. Lanthanides are good proton conductors and can usually improve the intrinsic conductivity of other materials. By integrating the merits of lanthanide elements and transition metal hydroxide, we designed lanthanum oxide nickel hydroxide composites (LONH) with unique ultrathin triangle nanosheet morphology via a controllable synthetic strategy for high-performance supercapacitors. When the LONH is used as positive electrode material in aqueous asymmetric supercapacitor, it reveals an energy density (107.8 W h kg-1 at 800 W kg-1), rate performance (86.9% retention at 4 kW kg-1) and outstanding cycle stability (more than 90% retention after 3,000 cycles). This work confirms that compositing La2O3 and Ni(OH)2 can significantly improve the supercapacitor performance of both pristine La2O3 and transition metal hydroxide composites. We hope this work would offer a good prospect for developing other lanthanide-transition metal hydroxide composites as an attractive class of electrode materials in electrochemical energy storage.

| S-EPMC8632525 | biostudies-literature

Graphene-based in-plane micro-supercapacitors with high power and energy densities.

Project description:Micro-supercapacitors are important on-chip micro-power sources for miniaturized electronic devices. Although the performance of micro-supercapacitors has been significantly advanced by fabricating nanostructured materials, developing thin-film manufacture technologies and device architectures, their power or energy densities remain far from those of electrolytic capacitors or lithium thin-film batteries. Here we demonstrate graphene-based in-plane interdigital micro-supercapacitors on arbitrary substrates. The resulting micro-supercapacitors deliver an area capacitance of 80.7??F?cm?² and a stack capacitance of 17.9?F?cm?³. Further, they show a power density of 495?W?cm?³ that is higher than electrolytic capacitors, and an energy density of 2.5?mWh?cm?³ that is comparable to lithium thin-film batteries, in association with superior cycling stability. Such microdevices allow for operations at ultrahigh rate up to 1,000?V?s?¹, three orders of magnitude higher than that of conventional supercapacitors. Micro-supercapacitors with an in-plane geometry have great promise for numerous miniaturized or flexible electronic applications.

| S-EPMC3778542 | biostudies-literature

High energy flexible supercapacitors formed via bottom-up infilling of gel electrolytes into thick porous electrodes.

Project description:Formation of thick, high energy density, flexible solid supercapacitors is challenging because of difficulties infilling gel electrolytes into porous electrodes. Incomplete infilling results in a low capacitance and poor mechanical properties. Here we report a bottom-up infilling method to overcome these challenges. Electrodes up to 500??m thick, formed from multi-walled carbon nanotubes and a composite of poly(3,4-ethylenedioxythiophene), polystyrene sulfonate and multi-walled carbon nanotubes are successfully infilled with a polyvinyl alcohol/phosphoric acid gel electrolyte. The exceptional mechanical properties of the multi-walled carbon nanotube-based electrode enable it to be rolled into a radius of curvature as small as 0.5?mm without cracking and retain 95% of its initial capacitance after 5000 bending cycles. The areal capacitance of our 500??m thick poly(3,4-ethylenedioxythiophene), polystyrene sulfonate, multi-walled carbon nanotube-based flexible solid supercapacitor is 2662?mF?cm-2 at 2?mV?s-1, at least five times greater than current flexible supercapacitors.

| S-EPMC6030180 | biostudies-literature

Aligned Ionogel Electrolytes for High-Temperature Supercapacitors.

Project description:Ionogels are a new class of promising materials for use in all-solid-state energy storage devices in which they can function as an integrated separator and electrolyte. However, their performance is limited by the presence of a crosslinking polymer, which is needed to improve the mechanical properties, but compromises their ionic conductivity. Here, directional freezing is used followed by a solvent replacement method to prepare aligned nanocomposite ionogels which exhibit enhanced ionic conductivity, good mechanical strength, and thermal stability simultaneously. The aligned ionogel based supercapacitor achieves a 29% higher specific capacitance (176 F g-1 at 25 °C and 1 A g-1) than an equivalent nonaligned form. Notably, this thermally stable aligned ionogel has a high ionic conductivity of 22.1 mS cm-1 and achieves a high specific capacitance of 167 F g-1 at 10 A g-1 and 200 °C. Furthermore, the diffusion simulations conducted on 3D reconstructed tomography images are employed to explain the improved conductivity in the relevant direction of the aligned structure compared to the nonaligned. This work demonstrates the synthesis, analysis, and use of aligned ionogels as supercapacitor separators and electrolytes, representing a promising direction for the development of wearable electronics coupled with image based process and simulations.

| S-EPMC6402534 | biostudies-literature

3D Carbon Frameworks for Ultrafast Charge/Discharge Rate Supercapacitors with High Energy-Power Density.

Project description:Carbon-based electric double layer capacitors (EDLCs) hold tremendous potentials due to their high-power performance and excellent cycle stability. However, the practical use of EDLCs is limited by the low energy density in aqueous electrolyte and sluggish diffusion kinetics in organic or/and ionic liquids electrolyte. Herein, 3D carbon frameworks (3DCFs) constructed by interconnected nanocages (10-20 nm) with an ultrathin wall of ca. 2 nm have been fabricated, which possess high specific surface area, hierarchical porosity and good conductive network. After deoxidization, the deoxidized 3DCF (3DCF-DO) exhibits a record low IR drop of 0.064 V at 100 A g-1 and ultrafast charge/discharge rate up to 10 V s-1. The related device can be charged up to 77.4% of its maximum capacitance in 0.65 s at 100 A g-1 in 6 M KOH. It has been found that the 3DCF-DO has a great affinity to EMIMBF4, resulting in a high specific capacitance of 174 F g-1 at 1 A g-1, and a high energy density of 34 Wh kg-1 at an ultrahigh power density of 150 kW kg-1 at 4 V after a fast charge in 1.11 s. This work provides a facile fabrication of novel 3D carbon frameworks for supercapacitors with ultrafast charge/discharge rate and high energy-power density.

| S-EPMC8187691 | biostudies-literature

Boosting Specific Energy and Power of Carbon-Ionic Liquid Supercapacitors by Engineering Carbon Pore Structures.

Project description:Carbon-ionic liquid (C-IL) supercapacitors (SCs) promise to provide high capacitance and high operating voltage, and thus high specific energy. It is still highly demanding to enhance the capacitance in order to achieve high power and energy density. We synthesized a high-pore-volume and specific-surface-area activated carbon material with a slit mesoporous structure by two-step processes of carbonization and the activation from polypyrrole. The novel slit-pore-structured carbon materials provide a specific capacity of 310 F g-1 at 0.5 A g-1 for C-IL SCs, which is among one of the highest recorded specific capacitances. The slit mesoporous activated carbons have a maximum ion volume utilization of 74%, which effectively enhances ion storage, and a better interaction with ions in ionic liquid electrolyte, thus providing superior capacitance. We believe that this work provides a new strategy of engineering pore structure to enhance specific capacitance and rate performance of C-IL SCs.

| S-EPMC7040027 | biostudies-literature

Activated Biomass-derived Graphene-based Carbons for Supercapacitors with High Energy and Power Density.

Project description:Here, we present a facile and low-cost method to produce hierarchically porous graphene-based carbons from a biomass source. Three-dimensional (3D) graphene-based carbons were produced through continuous sequential steps such as the formation and transformation of glucose-based polymers into 3D foam-like structures and their subsequent carbonization to form the corresponding macroporous carbons with thin graphene-based carbon walls of macropores and intersectional carbon skeletons. Physical and chemical activation was then performed on this carbon to create micro- and meso-pores, thereby producing hierarchically porous biomass-derived graphene-based carbons with a high Brunauer-Emmett-Teller specific surface area of 3,657?m2?g-1. Owing to its exceptionally high surface area, interconnected hierarchical pore networks, and a high degree of graphitization, this carbon exhibited a high specific capacitance of 175?F?g-1 in ionic liquid electrolyte. A supercapacitor constructed with this carbon yielded a maximum energy density of 74?Wh?kg-1 and a maximum power density of 408?kW?kg-1, based on the total mass of electrodes, which is comparable to those of the state-of-the-art graphene-based carbons. This approach holds promise for the low-cost and readily scalable production of high performance electrode materials for supercapacitors.

| S-EPMC5789836 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data