Physicochemical and Antibacterial Characterization of a Novel Fluorapatite Coating.

ABSTRACT: Peri-implantitis remains the major impediment to the long-term use of dental implants. With increasing concern over the growth in antibiotic resistance, there is considerable interest in the preparation of antimicrobial dental implant coatings that also induce osseointegration. One such potential coating material is fluorapatite (FA). The aim of this study was to relate the antibacterial effectiveness of FA coatings against pathogens implicated in peri-implantitis to the physicochemical properties of the coating. Ordered and disordered FA coatings were produced on the under and upper surfaces of stainless steel (SS) discs, respectively, using a hydrothermal method. Surface charge, surface roughness, wettability, and fluoride release were measured for each coating. Surface chemistry was assessed using X-ray photoelectron spectroscopy and FA crystallinity using X-ray diffraction. Antibacterial activity against periodontopathogens was assessed in vitro using viable counts, confocal microscopy, and scanning electron microscopy (SEM). SEM showed that the hydrothermal method produced FA coatings that were predominately aligned perpendicular to the SS substrate or disordered FA coatings consisting of randomly aligned rodlike crystals. Both FA coatings significantly reduced the growth of all examined bacterial strains in comparison to the control. The FA coatings, especially the disordered ones, presented significantly lower charge, greater roughness, and higher area when compared to the control, enhancing bacteria-material interactions and therefore bacterial deactivation by fluoride ions. The ordered FA layer reduced not only bacterial viability but adhesion too. The ordered FA crystals produced as a potential novel implant coating showed significant antibacterial activity against bacteria implicated in peri-implantitis, which could be explained by a detailed understanding of their physicochemical properties.

SUBMITTER: Alhilou A

PROVIDER: S-EPMC5026462 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:This study aimed to develop, characterize, and evaluate antibacterial and cytotoxic properties of novel fullerene derivative composed of C60 fullerenol and standard aminoglycoside antibiotic-gentamicin (C60 fullerenol-gentamicin conjugate). The successful introduction of gentamicin to fullerenol was confirmed by X-ray photoelectron spectroscopy which together with thermogravimetric and spectroscopic analysis revealing the formula of the composition as C60(OH)12(GLYMO)11(Gentamicin)0.8. The dynamic light scattering (DLS) revealed that conjugate possessed ability to form agglomerates in water (size around 115 nm), while Zeta potential measurements demonstrated that such agglomerates possessed neutral character. In vitro biological assays indicated that obtained C60 fullerenol-gentamicin conjugate possessed the same antibacterial activity as standard gentamicin against Staphylococcus aureus, Staphylococcus epidermidis, Pseudomonas aeruginosa, and Escherichia coli, which proves that combination of fullerenol with gentamicin does not cause the loss of antibacterial activity of antibiotic. Moreover, cytotoxicity assessment demonstrated that obtained fullerenol-gentamicin derivative did not decrease viability of normal human fibroblasts (model eukaryotic cells) compared to control fibroblasts. Thus, taking into account all of the results, it can be stated that this research presents effective method to fabricate C60 fullerenol-gentamicin conjugate and proves that such derivative possesses desired antibacterial properties without unfavorable cytotoxic effects towards eukaryotic cells in vitro. These promising preliminary results indicate that obtained C60 fullerenol-gentamicin conjugate could have biomedical potential. It may be presumed that obtained fullerenol may be used as an effective carrier for antibiotic, and developed fullerenol-gentamicin conjugate may be apply locally (i.e., at the wound site). Moreover, in future we will evaluate possibility of its applications in inter alia tissue engineering, namely as a component of wound dressings and implantable biomaterials.

Project description:Carbon nanomaterials have shown great potential in several fields, including biosensing, bioimaging, drug delivery, energy, catalysis, diagnostics, and nanomedicine. Recently, a new class of carbon nanomaterials, carbon dots (CDs), have attracted much attention due to their easy and inexpensive synthesis from a wide range of precursors and fascinating physical, chemical, and biological properties. In this work we have developed CDs derived from olive solid wastes of two Mediterranean regions, Puglia (CDs_P) and Calabria (CDs_C) and evaluated them in terms of their physicochemical properties and antibacterial activity against Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa). Results show the nanosystems have a quasi-spherical shape of 12-18 nm in size for CDs_P and 15-20 nm in size for CDs_C. UV-Vis characterization indicates a broad absorption band with two main peaks at about 270 nm and 300 nm, respectively, attributed to the π-π* and n-π* transitions of the CDs, respectively. Both samples show photoluminescence (PL) spectra excitation-dependent with a maximum at λem = 420 nm (λexc = 300 nm) for CDs_P and a red-shifted at λem = 445 nm (λexc = 300 nm) for CDs_C. Band gaps values of ≈ 1.48 eV for CDs_P and ≈ 1.53 eV for CDs_C are in agreement with semiconductor behaviour. ζ potential measures show very negative values for CDs_C compared to CDs_P (three times higher, -38 mV vs. -18 mV at pH = 7). The evaluation of the antibacterial properties highlights that both CDs have higher antibacterial activity towards Gram-positive than to Gram-negative bacteria. In addition, CDs_C exhibit bactericidal behaviour at concentrations of 360, 240, and 120 µg/mL, while lesser activity was found for CDs_P (bacterial cell reduction of only 30% at the highest concentration of 360 µg/mL). This finding was correlated to the higher surface charge of CDs_C compared to CDs_P. Further investigations are in progress to confirm this hypothesis and to gain insight on the antibacterial mechanism of both cultivars.

Dataset Information

Physicochemical and Antibacterial Characterization of a Novel Fluorapatite Coating.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets