Modifications of Hydroxyapatite by Gallium and Silver Ions-Physicochemical Characterization, Cytotoxicity and Antibacterial Evaluation.

ABSTRACT: Hydroxyapatite (HA) powders enriched with silver or gallium ions or both were synthesized by two different routes: standard precipitation and the solid-state method. The powders were characterized by using several methods: inductively coupled plasma optical emission spectrometry (ICP-OES), powder X-ray diffractometry (PXRD), transmission electron microscopy (TEM), infrared spectroscopy (FT-IR) and solid-state nuclear magnetic resonance spectroscopy (ssNMR). The effects of enrichment of the HAs in Ag+ or Ga3+ or both on in vitro cytotoxicity and microbiological activity were discussed. PXRD experiments showed that the samples obtained by the wet method consisted of single-phase nanocrystalline HA, while the samples prepared via the solid-state method are microcrystalline with a small amount of calcium oxide. The introduction of higher amounts of silver ions was found to be more effective than enriching HA with small amounts of Ag+. Gallium and silver ions were found not to affect the lattice parameters. Ga3+ affected the crystallinity of the samples as well as the content of structural hydroxyl groups. Among samples synthesized by the wet method, only one (5Ag-HAw) was cytotoxic, whereas all Ga-containing samples obtained by the dry method showed cytotoxicity. In the preliminary antimicrobial test all the materials containing "foreign" ions showed high antibacterial activity.

SUBMITTER: Pajor K

PROVIDER: S-EPMC7404191 | biostudies-literature | 2020 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Modifications of Hydroxyapatite by Gallium and Silver Ions-Physicochemical Characterization, Cytotoxicity and Antibacterial Evaluation.

Pajor Kamil K Pajchel Łukasz Ł Zgadzaj Anna A Piotrowska Urszula U Kolmas Joanna J

International journal of molecular sciences 20200715 14

Hydroxyapatite (HA) powders enriched with silver or gallium ions or both were synthesized by two different routes: standard precipitation and the solid-state method. The powders were characterized by using several methods: inductively coupled plasma optical emission spectrometry (ICP-OES), powder X-ray diffractometry (PXRD), transmission electron microscopy (TEM), infrared spectroscopy (FT-IR) and solid-state nuclear magnetic resonance spectroscopy (ssNMR). The effects of enrichment of the HAs i ...[more]

PMID: 32679901

Similar Datasets

Project description:Calcium phosphates (CaPs) have been used in bone regeneration for decades. Among the described CaPs, synthetic hydroxyapatite (HAp) has a chemical composition similar to that of natural bone. Gallium-containing compounds have been studied since the 1970s for the treatment of autoimmune diseases and have shown beneficial properties, such as antibacterial activity and inhibition of osteoclast activity. In this study, we synthesized hydroxyapatite (HAp) powder with Ga doping ratios up to 6.9 ± 0.5 wt% using the wet chemical precipitation method. The obtained products were characterized using XRD, BET, FTIR, and ICP-MS. Ga3+ ion release was determined in the cell culture media for up to 30 days. Antibacterial activity was assessed against five bacterial species: Pseudomonas aeruginosa, Escherichia coli, Staphylococcus aureus, Staphylococcus epidermidis, and Streptococcus pyogenes. The biocompatibility of the GaHAp samples was determined in human fibroblasts (hTERT-BJ1) through direct and indirect tests. The structure of the synthesized products was characteristic of HAp, as revealed with XRD and FTIR, although the addition of Ga caused a decrease in the crystallite size. Ga3+ was released from GaHAp paste in a steady manner, with approximately 40% being released within 21 days. GaHAp with the highest gallium contents, 5.5 ± 0.1 wt% and 6.9 ± 0.5 wt%, inhibited the growth of all five bacterial species, with the greatest activity being against Pseudomonas aeruginosa. Biocompatibility assays showed maintained cell viability (~80%) after seven days of indirect exposure to GaHAp. However, when GaHAp with Ga content above 3.3 ± 0.4 wt% was directly applied on the cells, a decrease in metabolic activity was observed on the seventh day. Overall, these results show that GaHAp with Ga content below 3.3 ± 0.4 wt% has attractive antimicrobial properties, without affecting the cell metabolic activity, creating a material that could be used for bone regeneration and prevention of infection.

Dataset Information

Modifications of Hydroxyapatite by Gallium and Silver Ions-Physicochemical Characterization, Cytotoxicity and Antibacterial Evaluation.

Publications

Modifications of Hydroxyapatite by Gallium and Silver Ions-Physicochemical Characterization, Cytotoxicity and Antibacterial Evaluation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets