Diameter-driven crossover in resistive behaviour of heavily doped self-seeded germanium nanowires.

ABSTRACT: The dependence of the resistivity with changing diameter of heavily-doped self-seeded germanium nanowires was studied for the diameter range 40 to 11 nm. The experimental data reveal an initial strong reduction of the resistivity with diameter decrease. At about 20 nm a region of slowly varying resistivity emerges with a peak feature around 14 nm. For diameters above 20 nm, nanowires were found to be describable by classical means. For smaller diameters a quantum-based approach was required where we employed the 1D Kubo-Greenwood framework and also revealed the dominant charge carriers to be heavy holes. For both regimes the theoretical results and experimental data agree qualitatively well assuming a spatial spreading of the free holes towards the nanowire centre upon diameter reduction.

SUBMITTER: Connaughton S

PROVIDER: S-EPMC5082314 | biostudies-literature | 2016

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Diameter-driven crossover in resistive behaviour of heavily doped self-seeded germanium nanowires.

Connaughton Stephen S Koleśnik-Gray Maria M Hobbs Richard R Lotty Olan O Holmes Justin D JD Krstić Vojislav V

Beilstein journal of nanotechnology 20160913

The dependence of the resistivity with changing diameter of heavily-doped self-seeded germanium nanowires was studied for the diameter range 40 to 11 nm. The experimental data reveal an initial strong reduction of the resistivity with diameter decrease. At about 20 nm a region of slowly varying resistivity emerges with a peak feature around 14 nm. For diameters above 20 nm, nanowires were found to be describable by classical means. For smaller diameters a quantum-based approach was required wher ...[more]

PMID: 27826502

Similar Datasets

Diameter-dependent dopant location in silicon and germanium nanowires.

Project description:We report studies defining the diameter-dependent location of electrically active dopants in silicon (Si) and germanium (Ge) nanowires (NWs) prepared by nanocluster catalyzed vapor-liquid-solid (VLS) growth without measurable competing homogeneous decomposition and surface overcoating. The location of active dopants was assessed from electrical transport measurements before and after removal of controlled thicknesses of material from NW surfaces by low-temperature chemical oxidation and etching. These measurements show a well-defined transition from bulk-like to surface doping as the diameter is decreased <22-25 nm for n- and p-type Si NWs, although the surface dopant concentration is also enriched in the larger diameter Si NWs. Similar diameter-dependent results were also observed for n-type Ge NWs, suggesting that surface dopant segregation may be general for small diameter NWs synthesized by the VLS approach. Natural surface doping of small diameter semiconductor NWs is distinct from many top-down fabricated NWs, explains enhanced transport properties of these NWs and could yield robust properties in ultrasmall devices often dominated by random dopant fluctuations.

| S-EPMC2730964 | biostudies-literature

Direct Synthesis of Hyperdoped Germanium Nanowires.

Project description:A low-temperature chemical vapor growth of Ge nanowires using Ga as seed material is demonstrated. The structural and chemical analysis reveals the homogeneous incorporation of ?3.5 at. % Ga in the Ge nanowires. The Ga-containing Ge nanowires behave like metallic conductors with a resistivity of about ?300 ??cm due to Ga hyperdoping with electronic contributions of one-third of the incorporated Ga atoms. This is the highest conduction value observed by in situ doping of group IV nanowires reported to date. This work demonstrates that Ga is both an efficient seed material at low temperatures for Ge nanowire growth and an effective dopant changing the semiconductor into a metal-like conductor.

| S-EPMC5830687 | biostudies-literature

Fingerprints of a size-dependent crossover in the dimensionality of electronic conduction in Au-seeded Ge nanowires.

Project description:We studied the electrical transport properties of Au-seeded germanium nanowires with radii ranging from 11 to 80 nm at ambient conditions. We found a non-trivial dependence of the electrical conductivity, mobility and carrier density on the radius size. In particular, two regimes were identified for large (lightly doped) and small (stronger doped) nanowires in which the charge-carrier drift is dominated by electron-phonon and ionized-impurity scattering, respectively. This goes in hand with the finding that the electrostatic properties for radii below ca. 37 nm have quasi one-dimensional character as reflected by the extracted screening lengths.

| S-EPMC5238664 | biostudies-literature

Promoting cell proliferation using water dispersible germanium nanowires.

Project description:Group IV Nanowires have strong potential for several biomedical applications. However, to date their use remains limited because many are synthesised using heavy metal seeds and functionalised using organic ligands to make the materials water dispersible. This can result in unpredicted toxic side effects for mammalian cells cultured on the wires. Here, we describe an approach to make seedless and ligand free Germanium nanowires water dispersible using glutamic acid, a natural occurring amino acid that alleviates the environmental and health hazards associated with traditional functionalisation materials. We analysed the treated material extensively using Transmission electron microscopy (TEM), High resolution-TEM, and scanning electron microscope (SEM). Using a series of state of the art biochemical and morphological assays, together with a series of complimentary and synergistic cellular and molecular approaches, we show that the water dispersible germanium nanowires are non-toxic and are biocompatible. We monitored the behaviour of the cells growing on the treated germanium nanowires using a real time impedance based platform (xCELLigence) which revealed that the treated germanium nanowires promote cell adhesion and cell proliferation which we believe is as a result of the presence of an etched surface giving rise to a collagen like structure and an oxide layer. Furthermore this study is the first to evaluate the associated effect of Germanium nanowires on mammalian cells. Our studies highlight the potential use of water dispersible Germanium Nanowires in biological platforms that encourage anchorage-dependent cell growth.

| S-EPMC4169628 | biostudies-literature

Selection and Functionalization of Germanium Nanowires for Bio-Sensing.

Project description:In this paper, we investigate the use of dielectrophoresis to align germanium nanowire arrays to realize nanowire-based diodes and their subsequent use for bio-sensing. After establishing that dielectrophoresis is a controllable and repeatable fabrication method to create devices from germanium nanowires, we use the optimum process conditions to form a series of diodes. These are subsequently functionalized with an aptamer, which is able to bind specifically to the spike protein of SARS-Cov2 and investigated as a potential sensor. We observe a linear increase in the source to drain current as the concentration of spike protein is increased from 100 fM/L to 1 nM/L.

| S-EPMC9535719 | biostudies-literature

Non-thermal resistive switching in Mott insulator nanowires.

Project description:Resistive switching can be achieved in a Mott insulator by applying current/voltage, which triggers an insulator-metal transition (IMT). This phenomenon is key for understanding IMT physics and developing novel memory elements and brain-inspired technology. Despite this, the roles of electric field and Joule heating in the switching process remain controversial. Using nanowires of two archetypal Mott insulators-VO2 and V2O3 we unequivocally show that a purely non-thermal electrical IMT can occur in both materials. The mechanism behind this effect is identified as field-assisted carrier generation leading to a doping driven IMT. This effect can be controlled by similar means in both VO2 and V2O3, suggesting that the proposed mechanism is generally applicable to Mott insulators. The energy consumption associated with the non-thermal IMT is extremely low, rivaling that of state-of-the-art electronics and biological neurons. These findings pave the way towards highly energy-efficient applications of Mott insulators.

| S-EPMC7293290 | biostudies-literature

Solution synthesis of germanium nanowires using a Ge2+ alkoxide precursor.

Project description:A simple solution synthesis of germanium (Ge0) nanowires under mild conditions (<400 degrees C and 1 atm) was demonstrated using germanium 2,6-dibutylphenoxide, Ge(DBP)2 (1), as the precursor where DBP = 2,6-OC6H3(C(CH3)3)2. Compound 1, synthesized from Ge(NR2)2 where R = SiMe3 and 2 equiv of DBP-H, was characterized as a mononuclear species by single-crystal X-ray diffraction. Dissolution of 1 in oleylamine, followed by rapid injection into a 1-octadecene solution heated to 300 degrees C under an atmosphere of Ar, led to the formation of Ge0 nanowires. The Ge0 nanowires were characterized by transmission electron microscopy (TEM), X-ray diffraction analysis, and Fourier transform infrared spectroscopy. These characterizations revealed that the nanowires are single crystalline in the cubic phase and coated with oleylamine surfactant. We also observed that the nanowire length (0.1-10 microm) increases with increasing temperature (285-315 degrees C) and time (5-60 min). Two growth mechanisms are proposed based on the TEM images intermittently taken during the growth process as a function of time: (1) self-seeding mechanism where one of two overlapping nanowires serves as a seed, while the other continues to grow as a wire; and (2) self-assembly mechanism where an aggregate of small rods (<50 nm in diameter) recrystallizes on the tip of a longer wire, extending its length.

| S-EPMC2538547 | biostudies-literature

Low-threshold optically pumped lasing in highly strained germanium nanowires.

Project description:The integration of efficient, miniaturized group IV lasers into CMOS architecture holds the key to the realization of fully functional photonic-integrated circuits. Despite several years of progress, however, all group IV lasers reported to date exhibit impractically high thresholds owing to their unfavourable bandstructures. Highly strained germanium with its fundamentally altered bandstructure has emerged as a potential low-threshold gain medium, but there has yet to be a successful demonstration of lasing from this seemingly promising material system. Here we demonstrate a low-threshold, compact group IV laser that employs a germanium nanowire under a 1.6% uniaxial tensile strain as the gain medium. The amplified material gain in strained germanium can sufficiently overcome optical losses at 83?K, thus allowing the observation of multimode lasing with an optical pumping threshold density of ~3.0?kW?cm-2. Our demonstration opens new possibilities for group IV lasers for photonic-integrated circuits.

| S-EPMC5705600 | biostudies-literature

Diameter Dependence of Planar Defects in InP Nanowires.

Project description:In this work, extensive characterization and complementary theoretical analysis have been carried out on Au-catalyzed InP nanowires in order to understand the planar defect formation as a function of nanowire diameter. From the detailed transmission electron microscopic measurements, the density of stacking faults and twin defects are found to monotonically decrease as the nanowire diameter is decreased to 10?nm, and the chemical analysis clearly indicates the drastic impact of In catalytic supersaturation in Au nanoparticles on the minimized planar defect formation in miniaturized nanowires. Specifically, during the chemical vapor deposition of InP nanowires, a significant amount of planar defects is created when the catalyst seed sizes are increased with the lower degree of In supersaturation as dictated by the Gibbs-Thomson effect, and an insufficient In diffusion (or Au-rich enhancement) would lead to a reduced and non-uniform In precipitation at the NW growing interface. The results presented here provide an insight into the fabrication of "bottom-up" InP NWs with minimized defect concentration which are suitable for various device applications.

| S-EPMC5018732 | biostudies-literature

Tuning the electro-optical properties of germanium nanowires by tensile strain.

Project description:In this Letter we present the electrical and electro-optical characterization of single crystalline germanium nanowires (NWs) under tensile strain conditions. The measurements were performed on vapor-liquid-solid (VLS) grown germanium (Ge) NWs, monolithically integrated into a micromechanical 3-point strain module. Uniaxial stress is applied along the ⟨111⟩ growth direction of individual, 100 nm thick Ge NWs while at the same time performing electrical and optical characterization at room temperature. Compared to bulk germanium, an anomalously high and negative-signed piezoresistive coefficient has been found. Spectrally resolved photocurrent characterization on strained NWs gives experimental evidence on the strain-induced modifications of the band structure. Particularly we are revealing a rapid decrease in resistivity and a red-shift in photocurrent spectra under high strain conditions. For a tensile strain of 1.8%, resistivity decreased by a factor of 30, and the photocurrent spectra shifted by 88 meV. Individual stressed NWs are recognized as an ideal platform for the exploration of strain-related electronic and optical effects and may contribute significantly to the realization of novel optoelectronic devices, strain-enhanced field-effect transistors (FETs), or highly sensitive strain gauges.

| S-EPMC3558012 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data