Fretting properties of biodegradable Mg-Nd-Zn-Zr alloy in air and in Hank's solution.

ABSTRACT: Fretting is a significant cause for the failure of orthopedic implants. Currently, since magnesium and its alloys have been developed as promising biodegradable implant materials, the fretting behavior of the Mg alloys is of great research significance. In this study, a Mg-Nd-Zn-Zr alloy (hereafter, denoted as JDBM alloy) was selected as experimental material, and its fretting behaviors were evaluated under 5 N, 10 N and 20 N normal loads with a displacement of 200??m under the frequency of 10?Hz at 37?°C in air and in Hank's solution, respectively. The results indicated that while the friction coefficient decreased with the increment of the normal load, the wear volume of the alloy increased with the increment of the normal load both in air and in Hank's solution. Both the friction coefficients and the wear volume of the fretting in Hank's solution were much lower than those in air environment. The evolution trend of friction coefficients with time had different performance in air environment and the Hank's solution group. Although oxidation occurred during the fretting tests in Hank's solution, the damage of JDBM alloy was still reduced due to the lubrication effects of Hank's solution. Moreover, the addition of Fetal bovine serum (FBS) could act as lubrication and result in the reduction of the fretting damage.

SUBMITTER: Li W

PROVIDER: S-EPMC5095712 | biostudies-literature | 2016 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Fretting properties of biodegradable Mg-Nd-Zn-Zr alloy in air and in Hank's solution.

Li Wenting W Li Nan N Zheng Yufeng Y Yuan Guangyin G

Scientific reports 20161104

Fretting is a significant cause for the failure of orthopedic implants. Currently, since magnesium and its alloys have been developed as promising biodegradable implant materials, the fretting behavior of the Mg alloys is of great research significance. In this study, a Mg-Nd-Zn-Zr alloy (hereafter, denoted as JDBM alloy) was selected as experimental material, and its fretting behaviors were evaluated under 5 N, 10 N and 20 N normal loads with a displacement of 200 μm under the frequency of 10 H ...[more]

PMID: 27812007

Similar Datasets

Project description:Due to their excellent biodegradability characteristics, Mg and Mg-based alloys have become an emerging material in biomedical implants, notably for repair of bone as well as coronary arterial stents. However, the main problem with Mg-based alloys is their rapid corrosion in aggressive environments such as human bodily fluids. Previously, many approaches such as control of alloying materials, composition and surface treatments, have been attempted to regulate the corrosion rate. This article presents a comprehensive review of recent research focusing on surface treatment techniques utilised to control the corrosion rate and surface integrity of Mg-based alloys in both in vitro and in vivo environments. Surface treatments generally involve the controlled deposition of thin film coatings using various coating processes, and mechanical surfacing such as machining, deep rolling or low plasticity burnishing. The aim is to either make a protective thin layer of a material or to change the micro-structure and mechanical properties at the surface and sub-surface levels, which will prevent rapid corrosion and thus delay the degradation of the alloys. We have organised the review of past works on coatings by categorising the coatings into two classes-conversion and deposition coatings-while works on mechanical treatments are reviewed based on the tool-based processes which affect the sub-surface microstructure and mechanical properties of the material. Various types of coatings and their processing techniques under two classes of coating and mechanical treatment approaches have been analysed and discussed to investigate their impact on the corrosion performance, biomechanical integrity, biocompatibility and cell viability. Potential challenges and future directions in designing and developing the improved biodegradable Mg/Mg-based alloy implants were addressed and discussed. The literature reveals that no solutions are yet complete and hence new and innovative approaches are required to leverage the benefit of Mg-based alloys. Hybrid treatments combining innovative biomimetic coating and mechanical processing would be regarded as a potentially promising way to tackle the corrosion problem. Synergetic cutting-burnishing integrated with cryogenic cooling may be another encouraging approach in this regard. More studies focusing on rigorous testing, evaluation and characterisation are needed to assess the efficacy of the methods.

Dataset Information

Fretting properties of biodegradable Mg-Nd-Zn-Zr alloy in air and in Hank's solution.

Publications

Fretting properties of biodegradable Mg-Nd-Zn-Zr alloy in air and in Hank's solution.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets