Nanotomographic evaluation of precipitate structure evolution in a Mg-Zn-Zr alloy during plastic deformation.

ABSTRACT: Magnesium and its alloys attract increasingly wide attention in various fields, ranging from transport to medical solutions, due to their outstanding structural and degradation properties. These properties can be tailored through alloying and thermo-mechanical processing, which is often complex and multi-step, thus requiring in-depth analysis. In this work, we demonstrate the capability of synchrotron-based nanotomographic X-ray imaging methods, namely holotomography and transmission X-ray microscopy, for the quantitative 3D analysis of the evolution of intermetallic precipitate (particle) morphology and distribution in magnesium alloy Mg-5.78Zn-0.44Zr subjected to a complex multi-step processing. A rich history of variation of the intermetallic particle structure in the processed alloy provided a testbed for challenging the analytical capabilities of the imaging modalities studied. The main features of the evolving precipitate structure revealed earlier by traditional light and electron microscopy methods were confirmed by the 3D techniques of synchrotron-based X-ray imaging. We further demonstrated that synchrotron-based X-ray imaging enabled uncovering finer details of the variation of particle morphology and number density at various stages of processing-above and beyond the information provided by visible light and electron microscopy.

SUBMITTER: Zeller-Plumhoff B

PROVIDER: S-EPMC7527343 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Microstructure Evolution and Localized Corrosion Susceptibility of an Al-Zn-Mg-Cu-Zr 7xxx Alloy with Minor Cr Addition.

Project description:Microstructure optimization of Al-Zn-Mg-Cu-Zr aluminum alloys, particularly through recrystallization inhibition, for improved strength and corrosion resistance properties has been an important consideration in alloy development for aerospace applications. Addition of rare earth elements, sometimes combined with Cr, has been found to be beneficial in this regard. In this study, the role of a single addition of 0.1 wt.% Cr on microstructure evolution of an Al-Zn-Mg-Cu-Zr (7449) alloy during processing was systematically investigated by optical light microscopy, scanning electron microscopy, electron backscatter diffraction and scanning transmission electron microscopy. Susceptibility to localized corrosion after aging to T4, T6 and T76 conditions was evaluated by potentiodynamic polarization (PDP) measurements and an intergranular corrosion (IGC) test. A decrease in recrystallized fraction with 0.1 wt.% Cr addition was observed, which is attributed to the formation of Cu- and Zn-containing E (Al18Mg3Cr2) dispersoids and the larger as-cast grain size. Moreover, the depletion of alloying elements from solid solution due to the formation of the Cu- and Zn-containing E (Al18Mg3Cr2) dispersoids and η Mg(Zn,Cu,Al)2 phase at its interface affects grain-boundary precipitation. The observed decrease in localized corrosion susceptibility with minor Cr addition is correlated with the microstructure and equally discussed.

| S-EPMC9918105 | biostudies-literature

Change of Deformation Mechanisms Leading to High Strength and Large Ductility in Mg-Zn-Zr-Ca Alloy with Fully Recrystallized Ultrafine Grained Microstructures.

Project description:Recently, we have found that fully recrystallized ultrafine-grained (UFG) microstructures could be realized in a commercial precipitation-hardened Magnesium (Mg) alloy. The UFG specimens exhibited high strength and large ductility under tensile test, but underlying mechanisms for good mechanical properties remained unclear. In this study, we have carried out systematic observations of deformation microstructures for revealing the influence of grain size on the change of dominant deformation modes. We found that plastic deformation of conventionally coarse-grained specimen was predominated by {0001} <11-20> slip and {10-12} <10-11> twinning, and the quick decrease of work-hardening rate was mainly due to the early saturation of deformation twins. For the UFG specimens, {10-12} <10-11> twinning was dramatically suppressed, while non-basal slip systems containing <c> component of Burgers vector were activated, which contributed significantly to the enhanced work-hardening rate leading to high strength and large ductility. It was clarified by this study that limited ductility of hexagonal Mg alloys could be overcome by activating unusual slip systems (<c + a> dislocations) in fully recrystallized UFG microstructures.

| S-EPMC6691010 | biostudies-literature

Microstructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation.

Project description:The hot deformation behavior and microstructural evolution of an Al-Zn-Mg-Cu (7150) alloy was studied during hot compression at various temperatures (300 to 450 °C) and strain rates (0.001 to 10 s-1). A decline ratio map of flow stresses was proposed and divided into five deformation domains, in which the flow stress behavior was correlated with different microstructures and dynamic softening mechanisms. The results reveal that the dynamic recovery is the sole softening mechanism at temperatures of 300 to 400 °C with various strain rates and at temperatures of 400 to 450 °C with strain rates between 1 and 10 s-1. The level of dynamic recovery increases with increasing temperature and with decreasing strain rate. At the high deformation temperature of 450 °C with strain rates of 0.001 to 0.1 s-1, a partially recrystallized microstructure was observed, and the dynamic recrystallization (DRX) provided an alternative softening mechanism. Two kinds of DRX might operate at the high temperature, in which discontinuous dynamic recrystallization was involved at higher strain rates and continuous dynamic recrystallization was implied at lower strain rates.

| S-EPMC5453149 | biostudies-other

Fretting properties of biodegradable Mg-Nd-Zn-Zr alloy in air and in Hank's solution.

Project description:Fretting is a significant cause for the failure of orthopedic implants. Currently, since magnesium and its alloys have been developed as promising biodegradable implant materials, the fretting behavior of the Mg alloys is of great research significance. In this study, a Mg-Nd-Zn-Zr alloy (hereafter, denoted as JDBM alloy) was selected as experimental material, and its fretting behaviors were evaluated under 5 N, 10 N and 20 N normal loads with a displacement of 200 μm under the frequency of 10 Hz at 37 °C in air and in Hank's solution, respectively. The results indicated that while the friction coefficient decreased with the increment of the normal load, the wear volume of the alloy increased with the increment of the normal load both in air and in Hank's solution. Both the friction coefficients and the wear volume of the fretting in Hank's solution were much lower than those in air environment. The evolution trend of friction coefficients with time had different performance in air environment and the Hank's solution group. Although oxidation occurred during the fretting tests in Hank's solution, the damage of JDBM alloy was still reduced due to the lubrication effects of Hank's solution. Moreover, the addition of Fetal bovine serum (FBS) could act as lubrication and result in the reduction of the fretting damage.

| S-EPMC5095712 | biostudies-literature

Strengthening Effects of Zn Addition on an Ultrahigh Ductility Mg-Gd-Zr Magnesium Alloy.

Project description:A newly developed Mg-2Gd-0.5Zr-xZn (x = 0.5, 1.0, 2.0, 3.0 wt %) alloy system exhibits significant strengthening by doping with Zn. In order to understand the strengthening mechanism, the microstructure, texture evolution, and mechanical properties of ultrahigh ductility Mg-2Gd-0.5Zr alloys with a Zn addition were systematically investigated. The addition of Zn results in the formation of Mg-Gd-Zn intermetallic compounds along grain boundaries, which encourages grain refinement during hot extrusion via the particle stimulated nucleation (PSN) mechanism. Furthermore, during texture sharpening the pole changes from <20 2 ¯ 1> to <01 1 ¯ 0>, which also occurred in the extruded alloys with Zn addition, which is unfavorable for the basal slip and tensile twinning. Mg-2Gd-0.5Zr-3Zn shows well-balanced strength and ductility with a tensile yield strength (YS) and ultimate tensile strength (UTS) of 285 and 314 MPa, accompanied by a high tensile elongation of 24%. They are superior to those of commercial AZ31. The enhanced strength is attributed to grain refinement, precipitation strengthening, and texture sharpening induced by alloying with Zn. The research result is also of great value to the development of low rare-earth, high strength, and high room temperature ductility magnesium alloy.

| S-EPMC6213636 | biostudies-other

Deformation twinning induced decomposition of lamellar LPSO structure and its re-precipitation in an Mg-Zn-Y alloy.

Project description:The high hardness or yield strength of an alloy is known to benefit from the presence of small-scale precipitation, whose hardening effect is extensively applied in various engineering materials. Stability of the precipitates is of critical importance in maintaining the high performance of a material under mechanical loading. The long period stacking ordered (LPSO) structures play an important role in tuning the mechanical properties of an Mg-alloy. Here, we report deformation twinning induces decomposition of lamellar LPSO structures and their re-precipitation in an Mg-Zn-Y alloy. Using atomic resolution scanning transmission electron microscopy (STEM), we directly illustrate that the misfit dislocations at the interface between the lamellar LPSO structure and the deformation twin is corresponding to the decomposition and re-precipitation of LPSO structure, owing to dislocation effects on redistribution of Zn/Y atoms. This finding demonstrates that deformation twinning could destabilize complex precipitates. An occurrence of decomposition and re-precipitation, leading to a variant spatial distribution of the precipitates under plastic loading, may significantly affect the precipitation strengthening.

| S-EPMC4951811 | biostudies-other

Effect of Heat Treatments on the Corrosion Resistance of a High Strength Mg-Gd-Y-Zn-Zr Alloy.

Project description:Magnesium-rare earth (Mg-Re) alloys are very promising structural materials in lightweight industries, while the poor corrosion resistance limits their widespread application. In this work, to provide insights into the functions of precipitate characteristics on the corrosion behaviors of Mg-Re alloys, the influence of heat treatments on the corrosion behavior of Mg-11.46Gd-4.08Y-2.09Zn-0.56Zr alloy was investigated via an immersion test, electrochemical experiment and scanning electron microscope (SEM). The results showed that the corrosion rate of Mg-11.46Gd-4.08Y-2.09Zn-0.56Zr alloy specimens decreased by 17.58% and 20.44% after T5 and T6 heat treatment, respectively. In the heat-treated specimens, the corrosion did not extend further into the matrix but formed fine corrosion grooves along the extrusion direction. The improved homogeneity reduced the residual stress and the β' precipitate introduced as a corrosion barrier after T5 and T6 heat treatment reduced the corrosion rate of the studied Mg alloy. In addition, the volume fraction of the long-period stacking-ordered (LPSO) phase decreased after heat treatment, which effectively reduced galvanic corrosion and enhanced the protective effect on the Mg matrix.

| S-EPMC9025149 | biostudies-literature

The Influence of Severe Plastic Deformation and Subsequent Annealing on the Microstructure and Hardness of a Cu-Cr-Zr Alloy.

Project description:A Cu-1.1%Cr-0.04%Zr (wt.%) alloy was processed by severe plastic deformation (SPD) using the equal channel angular pressing (ECAP) technique at room temperature (RT). It was found that when the number of passes increased from one to four, the dislocation density significantly increased by 35% while the crystallite size decreased by 32%. Subsequent rolling at RT did not influence considerably the crystallite size and dislocation density. At the same time, cryorolling at liquid nitrogen temperature yielded a much higher dislocation density. All the samples contained Cr particles with an average size of 1 µm. Both the size and fraction of the Cr particles did not change during the increase in ECAP passes and the application of rolling after ECAP. The hardness of the severely deformed Cu alloy samples can be well correlated to the dislocation density using the Taylor equation. Heat treatment at 430 °C for 30 min in air caused a significant reduction in the dislocation density for all the deformed samples, while the hardness considerably increased. This apparent contradiction can be explained by the solute oxygen hardening, but the annihilation of mobile dislocations during annealing may also contribute to hardening.

| S-EPMC7288192 | biostudies-literature

Exploring the mechanism of "Rare Earth" texture evolution in a lean Mg-Zn-Ca alloy.

Project description:The entire recrystallisation sequence and associated crystallographic texture evolution of Mg-0.8Zn-0.2Ca (wt.%) alloy was tracked using a quasi-in-situ electron backscatter diffraction (EBSD) method. Characteristic "Rare Earth" (RE) texture was formed, originating mainly from double twins and twinning-related shear bands consisting of compression and double twins. The RE textures appeared during the nucleation stage and were preserved during the relative uniform grain growth period because of solute segregation and concurrent precipitation although the alloying element content was very low. Ca and Zn co-segregated along grain boundaries with no evidence that segregation was preferred along special types of grain boundaries. The interactions between deformation microstructures, concurrent precipitation, solute drag, grain growth and texture evolution are discussed in detail. All the results indicate that Ca performs a similar role to that of RE elements in forming RE texture.

| S-EPMC6509330 | biostudies-literature

Effect of solution treatment on the fatigue behavior of an as-forged Mg-Zn-Y-Zr alloy.

Project description:Through investigating and comparing the fatigue behavior of an as-forged Mg-6.7Zn-1.3Y-0.6Zr (wt.%) alloy before and after solid solution treatment (T4) in laboratory air, the effect of T4 treatment on fatigue crack initiation was disclosed. S-N curves illustrated that the fatigue strength of as-forged samples was 110 MPa, whereas the fatigue strength of T4 samples was only 80 MPa. Observations to fracture surfaces demonstrated that for as-forged samples, fatigue crack initiation sites were covered with a layer of oxide film. However, due to the coarse grain structure and the dissolution of MgZn2 precipitates, the activation and accumulation of {10-12} twins in T4 samples were much easier, resulting in the preferential fatigue crack initiation at cracked twin boundaries (TBs). Surface characterization demonstrated that TB cracking was mainly ascribed to the incompatible plastic deformation in the twinned area and nearby α-Mg matrix.

| S-EPMC4817045 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data