Photodegradation of organic pollutants RhB dye using UV simulated sunlight on ceria based TiO₂ nanomaterials for antibacterial applications.

ABSTRACT: To photo-catalytically degrade RhB dye using solar irradiation, CeO₂ doped TiO₂ nanocomposites were synthesized hydrothermally at 700 °C for 9 hrs. All emission spectra showed a prominent band centered at 442 nm that was attributed to oxygen related defects in the CeO₂-TiO₂ nanocrystals. Two sharp absorption bands at 1418 cm^-1 and 3323 cm^-1 were attributed to the deformation and stretching vibration, and bending vibration of the OH group of water physisorbed to TiO₂, respectively. The photocatalytic activities of Ce-TiO₂ nanocrystals were investigated through the degradation of RhB under UV and UV+ visible light over a period of 8 hrs. After 8 hrs, the most intense absorption peak at 579 nm disappeared under the highest photocatalytic activity and 99.89% of RhB degraded under solar irradiation. Visible light-activated TiO₂ could be prepared from metal-ion incorporation, reduction of TiO₂, non-metal doping or sensitizing of TiO₂ using dyes. Studying the antibacterial activity of Ce-TiO₂ nanocrystals against E. coli revealed significant activity when 10 μg was used, suggesting that it can be used as an antibacterial agent. Its effectiveness is likely related to its strong oxidation activity and superhydrophilicity. This study also discusses the mechanism of heterogeneous photocatalysis in the presence of TiO₂.

SUBMITTER: Kasinathan K

PROVIDER: S-EPMC5128916 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Mechanism of Photodegradation of Organic Pollutants in Seawater by TiO2-Based Photocatalysts and Improvement in Their Performance.

Project description:The mechanism of photodegradation of organic pollutants in seawater by TiO2-based catalysts irradiated by visible light was first explored by adding holes and free radical traps. The results showed that the photogenerated holes formed by the catalyst played a key role in the degradation of organic pollutants, regardless of whether the photodegradation occurred in seawater or pure water. Considering that the Yb-TiO2-rGO catalyst has a strong adsorption for organics, the salt ion almost did not interfere with the adsorption of pollutants by Yb-TiO2-rGO. Therefore, the degradation performance of Yb-TiO2-rGO did not remarkably change in the two water systems. For P25-ZN with a weak adsorption capacity for organics, several salt ions in the seawater hindered the contact of pollutants with the catalyst surface. Thus, the degradation rate of P25-ZN for phenol was significantly reduced. After the solvothermal reduction treatment for catalysts using ethylene glycol (EG) as the solvent, the increase in the Ti3+ content in the catalyst improved the visible-light response and activity of the catalyst. In addition, a small amount of EG grafted on the catalyst surface promoted the photocatalytic reaction process on the catalyst surface, thereby effectively resisting the interference of salt ions.

| S-EPMC8600626 | biostudies-literature

Aquatic photodegradation of clofibric acid under simulated sunlight irradiation: kinetics and mechanism analysis.

Project description:Clofibric acid is one of the most frequently detected pharmaceuticals in various aquatic environments. Photodegradation of clofibric acid in water under simulated sunlight was investigated. The effects of different initial concentrations, pH conditions and dissolved oxygen were examined. Photodegradation of clofibric acid followed a pseudo-first-order kinetics model, and the rate decreased gradually with the increasing initial concentration of clofibric acid. Dissolved oxygen inhibited the photodegradation of clofibric acid. As a result of varying reaction species of clofibric acid, the initial pH conditions greatly influenced its photodegradation. Quenching experiments showed that the self-sensitization process via ·OH and 1O2 occured during photodegradation of clofibric acid, and the bimolecular reaction rate constants of clofibric acid with ·OH and 1O2 were determined via the competition kinetics method to be 3.93(±0.20) × 108 and 2.38(±0.12) × 106 L mol-1 s-1, respectively. In addition, the transformation products of clofibric acid were identified by the UPLC-Q-TOF-MS microsystem, and eight products were detected. It is proposed that the photodegradation of clofibric acid occurred mainly via decarboxylation, dechlorination, ·OH addition and 1O2 attack reaction.

| S-EPMC9083450 | biostudies-literature

Visible-Light Driven Photodegradation of Industrial Pollutants Using Nitrogen-Tungsten Co-Doped Nanocrystalline TiO2: Spectroscopic Analysis of Degradation Reaction Path.

Project description:The purpose to conduct this research work is to study the effect of photocatalytic degradation by developing cost-effective and eco-friendly nitrogen and tungsten (metal/non-metal) co-doped titania (TiO2). The inherent characteristics of synthesized nanoparticles (NPs) were analyzed by Fourier transform infra-red spectroscopy (FT-IR), ultra-violet visible (UV-Vis) spectroscopy, Raman spectroscopy, Field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS), X-ray diffraction (XRD) spectrometry, and atomic force microscopy (AFM). Co-doping of metal and non-metal has intensified the photocatalysis trait of TiO2 nanoparticles in an aqueous medium. This co-doping of transition metal ions and modification of nitrogen extended the absorption into the visible region subsequently restraining the recombination of electrons/holes pair. The stronger light absorption in the visible region was required for the higher activity of photodegradation of dye under visible light illumination to confine bandgap energy which results in accelerating the rate of photodegradation. After efficient doping, the bandgap of titania reduced to 2.38 eV and caused the photodegradation of malachite green in visible light. The results of photocatalytic degradation were confirmed by using UV/Vis. spectroscopy and high-performance liquid chromatography coupled with a mass spectrophotometer (HPLC-ESI-MS) was used for the analysis of intermediates formed during photocatalytic utility of the work.

| S-EPMC9267965 | biostudies-literature

Agro-waste extracted cellulose supported silver phosphate nanostructures as a green photocatalyst for improved photodegradation of RhB dye and industrial fertilizer effluents.

Project description:The efficiency and reusability of photocatalysts are the dominant factors for their pragmatic use. The visible light induced semiconductor silver phosphate is a superior photocatalyst effective under visible light but its stability is still an undiscussed issue. To overcome this stability issue in this present manuscript, eco-friendly agro-waste extracted cellulose supported silver phosphate nanostructures have been designed for the first time through a simple chemical process. At first, silver phosphate nanostructures were synthesized by the co-precipitation method. Then, different weights of cellulose were added to the silver nitrate solution to form cellulose supported silver phosphate nanostructures. The photodegradation efficiency for each weight ratio was examined in which the photocatalyst Ag-8 nanostructures showed a high rate (0.024 min-1) for degradation of Rhodamine B (RhB) using a low intensity tungsten bulb. Real sample analysis has also been carried out using this photocatalyst for the degradation of industrial fertilizer effluents. The degradation rate of all the nanostructures was found to be high in comparison to pristine silver phosphate as well as the extracted bare cellulose. The photocatalytic activity is enhanced because of the participation of cellulose as a support which makes an interface for silver phosphate and assists it in delaying the charge recombination period under visible light. To understand the photochemical reaction of electrons and holes, scavenger studies were also performed.

| S-EPMC9417693 | biostudies-literature

Inorganic Photocatalytic Enhancement: Activated RhB Photodegradation by Surface Modification of SnO2 Nanocrystals with V2O5-like species.

Project description:SnO2 nanocrystals were prepared by precipitation in dodecylamine at 100 °C, then they were reacted with vanadium chloromethoxide in oleic acid at 250 °C. The resulting materials were heat-treated at various temperatures up to 650 °C for thermal stabilization, chemical purification and for studying the overall structural transformations. From the crossed use of various characterization techniques, it emerged that the as-prepared materials were constituted by cassiterite SnO2 nanocrystals with a surface modified by isolated V(IV) oxide species. After heat-treatment at 400 °C, the SnO2 nanocrystals were wrapped by layers composed of vanadium oxide (IV-V mixed oxidation state) and carbon residuals. After heating at 500 °C, only SnO2 cassiterite nanocrystals were obtained, with a mean size of 2.8 nm and wrapped by only V2O5-like species. The samples heat-treated at 500 °C were tested as RhB photodegradation catalysts. At 10-7 M concentration, all RhB was degraded within 1 h of reaction, at a much faster rate than all pure SnO2 materials reported until now.

| S-EPMC5353695 | biostudies-literature

Photosensitization of TiO2 nanofibers by Ag2S with the synergistic effect of excess surface Ti3+ states for enhanced photocatalytic activity under simulated sunlight.

Project description:TiO2 nanofibers, with mean diameter ~200 nm, were fabricated by electrospinning and successfully photosensitized with low bandgap Ag2S nanoparticles of 11, 17, 23 and 40 nm mean sizes, with corresponding loading of 4, 10, 18 and 29 wt.% Ag2S, respectively. 17 nm Ag2S@TiO2 nanofibers exhibited optimal activity in the photodegradation of methylene blue under simulated sunlight with pseudo-first order rate constant of 0.019 min-1 compared to 0.009 min-1 for pure TiO2 nanofibers. In spite of greater visible-light absorption and reduced bandgap, larger than 17 nm Ag2S nanoparticles exhibited sluggish photodegradation kinetics probably due to less photo-induced carriers generation in TiO2 and reduced electron injection rates from the larger sized Ag2S into TiO2. Furthermore, a UV-O3 surface treatment induced excess Ti3+ surface states and oxygen vacancies which synergistically enhanced the photodegradation rate constant to 0.030 min-1 for 17 nm Ag2S@TiO2 sample which is ~70% better than the previously reported for Ag2S/TiO2 hierarchical spheres. This was attributed to the efficient charge separation and transfer driven by increased visible-light absorption, bandgap narrowing and reduced electron-hole recombination rates. The present study demonstrate the potential utilization of Ag2S@TiO2 nanofibers in filtration membranes for removal of organic pollutants from wastewater.

| S-EPMC5428275 | biostudies-literature

Microwave-Assisted Synthesis of Zn2SnO4 Nanostructures for Photodegradation of Rhodamine B under UV and Sunlight.

Project description:The contamination of water resources by pollutants resulting from human activities represents a major concern nowadays. One promising alternative to solve this problem is the photocatalytic process, which has demonstrated very promising and efficient results. Oxide nanostructures are interesting alternatives for these applications since they present wide band gaps and high surface areas. Among the photocatalytic oxide nanostructures, zinc tin oxide (ZTO) presents itself as an eco-friendly alternative since its composition includes abundant and non-toxic zinc and tin, instead of critical elements. Moreover, ZTO nanostructures have a multiplicity of structures and morphologies possible to be obtained through low-cost solution-based syntheses. In this context, the current work presents an optimization of ZTO nanostructures (polyhedrons, nanoplates, and nanoparticles) obtained by microwave irradiation-assisted hydrothermal synthesis, toward photocatalytic applications. The nanostructures’ photocatalytic activity in the degradation of rhodamine B under both ultraviolet (UV) irradiation and natural sunlight was evaluated. Among the various morphologies, ZTO nanoparticles revealed the best performance, with degradation > 90% being achieved in 60 min under UV irradiation and in 90 min under natural sunlight. The eco-friendly production process and the demonstrated ability of these nanostructures to be used in various water decontamination processes reinforces their sustainability and the role they can play in a circular economy.

| S-EPMC9231267 | biostudies-literature

Construction of Embedded Heterostructured SrZrO3/Flower-like MoS2 with Enhanced Dye Photodegradation under Solar-Simulated Light Illumination.

Project description:SrZrO3/flower-like MoS2 composites with an embedded heterostructure were synthesized via a simple two-step hydrothermal method and their performance was evaluated by photodegradation of methylene blue (MB) under solar-simulated light irradiation. The sandwiched flower-like MoS2 with a high Mo(VI) ratio was adopted as the matrix, and SrZrO3 was grown between the MoS2 layers, forming an intense contact interface, which promotes the efficient separation and transport of photoinduced carriers. The enhanced photocatalytic degradation of 99.7% after 80 min of irradiation is exhibited over the MS5 sample (5 wt % SrZrO3 loading amount on the MoS2 matrix). Moreover, the ratio of Mo(VI) and the superoxide radical plays a crucial role in the photodegradation of MB, and the higher the ratio the better the performance. This work provided a strategy to design a new kind of photocatalyst for photocatalysis and indicated that MoS2 is preferably adopted as a matrix rather than as a loading component.

| S-EPMC7191852 | biostudies-literature

Synergy of Au-Pt for Enhancing Ethylene Photodegradation Performance of Flower-like TiO2.

Project description:Efficient and low-cost degradation of ethylene has always been a difficult problem in the storage and transportation of fruits and vegetables. Although photocatalysis is considered to be a feasible and efficient solution for ethylene degradation, the low degradation ability of conventional catalysts for small non-polar molecules limits its application. TiO2 has the advantage of tunable microstructure, but it also has the defects of wide band gap and low utilization of sunlight. The surface plasmon resonance (SPR) effect of noble metals can effectively improve the visible light absorption range of catalysts, and the synergy of noble metals further enhances the photocatalytic ability. Herein, we developed a series of AuPt catalysts through the photo-deposition method. Benefited from the SPR effect and the synergy of Au and Pt, the efficiency of AuPt-TiO2 was 19.9, 4.64 and 2.42 times that of TiO2, Au-TiO2 and Pt-TiO2, and the photocatalytic degradation ability of AuPt-TiO2 was maintained in five cyclic stability tests. Meanwhile, the transient photocurrent spectra and PL spectra proved that the light absorption capacity and carrier separation efficiency of AuPt-TiO2 were enhanced. This work provides a new direction for enhancing non-polar small-molecule photodegradation of semiconductors.

| S-EPMC9505558 | biostudies-literature

Co-assembled MoS2-TiO2 Inverse Opal Photocatalysts for Visible Light-Activated Pharmaceutical Photodegradation.

Project description:Heterostructured photocatalytic materials in the form of photonic crystals have been attracting attention for their unique light harvesting ability that can be ideally combined with judicious compositional modifications toward the development of visible light-activated (VLA) photonic catalysts, though practical environmental applications, such as the degradation of pharmaceutical emerging contaminants, have been rarely reported. Herein, heterostructured MoS2-TiO2 inverse opal films are introduced as highly active immobilized photocatalysts for the VLA degradation of tetracycline and ciprofloxacin broad-spectrum antibiotics as well as salicylic acid. A single-step co-assembly method was implemented for the challenging incorporation of MoS2 nanosheets into the nanocrystalline inverse opal walls. Compositional tuning and photonic band gap engineering of the MoS2-TiO2 photonic films showed that integration of low amounts of MoS2 nanosheets in the inverse opal framework maintains intact the periodic macropore structure and enhances the available surface area, resulting in efficient VLA antibiotic degradation far beyond the performance of benchmark TiO2 films. The combination of broadband MoS2 visible light absorption and photonic-assisted light trapping together with the enhanced charge separation that enables the generation of reactive oxygen species via firm interfacial coupling between MoS2 nanosheets and TiO2 nanoparticles is concluded as a competent approach for pharmaceutical abatement in water bodies.

| S-EPMC10515384 | biostudies-literature