Chemical Compositional Analysis of Catalytic Hydroconversion Products of Heishan Coal Liquefaction Residue.

ABSTRACT: Liquefaction residue of Heishan bituminous coal (HLR) was subject to two hydroconversion reactions under 5?MPa initial pressure of hydrogen at 300°C for 3?h, without catalyst and with acid supported catalyst (ASC), respectively. The reaction products were analyzed with gas chromatography/mass spectrometer (GC/MS). The results show that 222 organic compounds were detected totally in the products and they can be divided into alkanes, aromatic hydrocarbons (AHCs), phenols, ketones, ethers, and other species (OSs). The yield of hydroconversion over the ASC is much higher than that without catalyst. The most abundant products are aromatic hydrocarbons in the reaction products from both catalytic and noncatalytic reactions of HLR. The yield of aromatic hydrocarbons in the reaction product from hydroconversion with the ACS is considerably higher than that from hydroconversion without a catalyst.

SUBMITTER: Yue X

PROVIDER: S-EPMC5304314 | biostudies-literature | 2017

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Chemical Compositional Analysis of Catalytic Hydroconversion Products of Heishan Coal Liquefaction Residue.

Yue Xiaoming X Wu Yajun Y Zhang Shuangquan S Yang Xiaoqin X Wei Xianyong X

International journal of analytical chemistry 20170130

Liquefaction residue of Heishan bituminous coal (HLR) was subject to two hydroconversion reactions under 5 MPa initial pressure of hydrogen at 300°C for 3 h, without catalyst and with acid supported catalyst (ASC), respectively. The reaction products were analyzed with gas chromatography/mass spectrometer (GC/MS). The results show that 222 organic compounds were detected totally in the products and they can be divided into alkanes, aromatic hydrocarbons (AHCs), phenols, ketones, ethers, and othe ...[more]

PMID: 28250770

Similar Datasets

Preparation of Reusable Porous Carbon Nanofibers from Oxidized Coal Liquefaction Residue for Efficient Adsorption in Water Treatment.

Project description:Porous carbon nanofibers are commonly used for adsorption processes owing to their high specific surface area and rich pore structure. However, the poor mechanical properties of polyacrylonitrile (PAN)-based porous carbon nanofibers have limited their applications. Herein, we introduced solid waste-derived oxidized coal liquefaction residue (OCLR) into PAN-based nanofibers to obtain activated reinforced porous carbon nanofibers (ARCNF) with enhanced mechanical properties and regeneration for efficient adsorption of organic dyes in wastewater. This study examined the effects of contact time, concentration, temperature, pH, and salinity on the adsorption capacity. The adsorption processes of the dyes in ARCNF are appropriately described by the pseudo-second-order kinetic model. The maximum adsorption capacity for malachite green (MG) on ARCNF is 2712.84 mg g-1 according to the fitted parameters of the Langmuir model. Adsorption thermodynamics indicated that the adsorptions of the five dyes are spontaneous and endothermic processes. In addition, ARCNF have good regenerative performance, and the adsorption capacity of MG is still higher than 76% after 5 adsorption-desorption cycles. Our prepared ARCNF can efficiently adsorb organic dyes in wastewater, reducing the pollution to the environment and providing a new idea for solid waste recycling and water treatment.

| S-EPMC10222528 | biostudies-literature

Analysis of Coal Gasification Reactivity, Kinetics, and Mechanism with Iron-Based Catalyst from Coal Liquefaction.

Project description:In this work, the effect of an iron-based catalyst from coal liquefaction on coal gasification was studied. Two catalyst loading methods and three catalyst loading contents were taken into consideration. Besides, the carbon structure, surface morphology, and element distribution of coal char and gasified semi-char were investigated, and the interactions between the catalyst and internal minerals of coal were studied. The results showed that the coal char prepared by wet impregnation had higher reactivity than that prepared by a dry mixing method. From the perspective of improving the coal reactivity, the optimal addition method should be wet impregnation with a 2% catalyst. The model-free and model-fitting methods were applied to study the catalytic gasification kinetics. The iron-based catalyst would be broken during wet impregnation, and the catalyst fragments could stick to the surface of coal char, resulting in higher reactivity. The graphitization of char increased with the addition of the iron-based catalyst. This can imply that the carbon structure cannot effectively represent the gasification reactivity in the presence of the iron-based catalyst. The Iron-based catalyst can accelerate the gasification rate alone and can also provide higher catalytic activity with the internal minerals of coal.

| S-EPMC7818629 | biostudies-literature

Catalytic liquefaction of human feces over Ni-Tm/TiO2 catalyst and the influence of operating conditions on products.

Project description:In this study, human feces were hydrothermal liquefied and converted into biocrude over Ni-Tm/TiO2 catalyst. The influence of catalysts, reaction temperature, and holding time on the distribution of products and element content of biocrude was assessed. The biocrude yield increased to 53.16% with a reaction temperature of 330 °C, a holding time of 30 min, and adding Ni-Tm/TiO2 catalyst while the liquefaction conversion peaked at 89.61%. The biocrude had an HHV of 36.64 MJ/kg and was similar to heavy crude oil. The biocrude is rich in fatty acid amides, esters, and oxygen-containing-only heteroatom-ring compounds as well as some nitrogen-containing heteroatom-ring compounds. The main gaseous products were CO2, CH4, and C2H6. Hydrothermal liquefaction over Ni-Tm/TiO2 catalyst could be a potential method to handle human excrement treatment and produce biofuel.

| S-EPMC5806599 | biostudies-literature

Chemical Speciation and Leaching Behavior of Hazardous Trace Elements in Coal Combustion Products from Coal-Fired Power Stations in China.

Project description:This paper reports on the chemical speciation and leaching behavior of a selected group of hazardous trace pollutants in lignite and lignite-petcoke blend co-combustion products from three power stations in China. The evaluation of speciation results showed that, during combustion, oxidizable elements, mainly As and Mo, bound to organic matter and sulfides in coals were mostly transferred to easily water-soluble forms or to slightly acidic states in the ashes. This manner was the most readily bioavailable condition for such an environment. The evaluation of the leaching results shows that the use of petroleum coke as co-fuel has an impact on the ash composition and on the leaching behavior of some inorganic trace pollutants such as Mo and V. The leaching results compared to the European waste acceptance criteria for landfills reveal that the Mo and As' leaching yield brand the coal combustion products as materials that necessitate preventative measures to reduce their potential leaching. Future work will be focused on the application of our novel chemical stabilization method to these coal ashes to reduce the mobility of elements such as Mo and As, and other potentially leachable elements, and on the use of the resulting ash with aggregate products as a substitute for concrete production.

| S-EPMC9088907 | biostudies-literature

Preparation of Mn/Zn@PG Catalyst for Catalytic Oxidation Treatment of Coal Chemical Wastewater

Project description:In this study, Mn/Zn@palygorskite (PG) catalysts with developed pores and good salt tolerance were prepared and applied to the treatment of coal chemical wastewater. A doping ratio of metal elements, calcination temperature, and calcination time was used to optimize the preparation conditions and determine the optimal preparation conditions of the Mn/Zn@PG catalysts. The catalysts, obtained under various preparation conditions, were characterized and analyzed by XRD, SEM, EDS, BET, XRF, XPS, and other techniques. Results showed that the Zn and Mn elements in the Mn/Zn@PG catalyst existed as ZnO and MnO2, respectively. The optimal working conditions of the Mn/Zn@PG catalyst for catalytic oxidation treatment of coal chemical wastewater, obtained through the optimization of working conditions, are the following: reaction time 60 min, wastewater pH = 9.28, ozone ventilation rate 0.2 L/min, catalyst filling ratio 20%. The height-to-diameter ratio of the tower was 6:1. The abrasion resistance and catalytic performance of the Mn/Zn@PG catalyst after repeated use were investigated, and the mechanism of the loss of active components of the Mn/Zn@PG catalyst was explored. The coal chemical wastewater, before and after treatment, was analyzed by UV–vis spectroscopy and 3D fluorescence spectroscopy. The hierarchical–principal component comprehensive evaluation system (AHP–PCA) was established to evaluate the catalytic ozonation process of coal chemical wastewater, so that the overall evaluation of the process performance can be achieved.

| S-EPMC9518122 | biostudies-literature

Neutron crystallography and quantum chemical analysis of bilin reductase PcyA mutants reveal substrate and catalytic residue protonation states.

Project description:PcyA, a ferredoxin-dependent bilin pigment reductase, catalyzes the site-specific reduction of the two vinyl groups of biliverdin (BV), producing phycocyanobilin. Previous neutron crystallography detected both the neutral BV and its protonated form (BVH+) in the wildtype (WT) PcyA-BV complex, and a nearby catalytic residue Asp105 was found to have two conformations (protonated and deprotonated). Semiempirical calculations have suggested that the protonation states of BV are reflected in the absorption spectrum of the WT PcyA-BV complex. In the previously determined absorption spectra of the PcyA D105N and I86D mutants, complexed with BV, a peak at 730 nm, observed in the WT, disappeared and increased, respectively. Here, we performed neutron crystallography and quantum chemical analysis of the D105N-BV and I86D-BV complexes to determine the protonation states of BV and the surrounding residues and study the correlation between the absorption spectra and protonation states around BV. Neutron structures elucidated that BV in the D105N mutant is in a neutral state, whereas that in the I86D mutant is dominantly in a protonated state. Glu76 and His88 showed different hydrogen bonding with surrounding residues compared with WT PcyA, further explaining why D105N and I86D have much lower activities for phycocyanobilin synthesis than the WT PcyA. Our quantum mechanics/molecular mechanics calculations of the absorption spectra showed that the spectral change in D105N arises from Glu76 deprotonation, consistent with the neutron structure. Collectively, our findings reveal more mechanistic details of bilin pigment biosynthesis.

| S-EPMC9800206 | biostudies-literature

Catalytic liquefaction of sewage sludge to small molecular weight chemicals.

Project description:The catalytic hydrotreatment of sewage sludge, the wet solid byproducts from wastewater treatment plants, using supported Ir, Pt, Pd, Ru catalysts had been investigated with different solvent conditions. Reactions were carried out in a batch set-up at elevated temperatures (400 °C) using a hydrogen donor (formic acid (FA) in isopropanol (IPA) or hydrogen gas), with sewage sludge obtained from different sampling places. Sewage sludge conversions of up to 83.72% were achieved using Pt/C, whereas the performance for the others catalysts is different and solvent had a strong effect on the conversion rate and product constitution. The sewage sludge oils were characterised using a range of analytical techniques (GC, GC-MS, GCxGC, GPC) and were shown to consist of monomers, mainly alkanes and higher oligomers.

| S-EPMC7609695 | biostudies-literature

Effect of Soda Residue Addition and Its Chemical Composition on Physical Properties and Hydration Products of Soda Residue-Activated Slag Cementitious Materials.

Project description:Soda residue (SR), the solid waste of Na2CO3 produced by ammonia soda process, pollutes water and soil, increasing environmental pressure. SR has high alkalinity, and its main components are Ca(OH)2, NaCl, CaCl2, CaSO4, and CaCO3, which accords with the requirements of being an alkali activator. The aim of this research is to investigate the best proportion of SR addition and the contribution of individual chemical components in SR to SR- activated ground granulated blast furnace slag (GGBS) cementitious materials. In this paper, GGBS pastes activated by SR, Ca(OH)2, Ca(OH)2 + NaCl, Ca(OH)2 + CaCl2, Ca(OH)2 + CaSO4, and Ca(OH)2 + CaCO3 were studied regarding setting time, compressive strength (1 d, 3 d, 7 d, 14 d, 28 d), hydration products, and microstructure. The results demonstrate that SR (24%)-activated GGBS pastes possess acceptable setting time and compressive strength (29.6 MPa, 28 d), and its hydration products are calcium silicate hydrate (CSH) gel, calcium aluminum silicate hydrates (CASH) gel and Friedel's salt. CaCl2 in SR plays a main role in hydration products generation and high compressive strength of SR- activated GGBS pastes.

| S-EPMC7179023 | biostudies-literature

Organic solvent extraction-assisted catalytic hydrothermal liquefaction of algae to bio-oil.

Project description:In this paper, we report our investigation into a two-step method of transformation of algae to bio-oil. Elemental analysis, gas chromatography-mass spectrometry and Fourier transform infrared spectroscopy were used to analyze bio-oil. First, organic solvent Soxhlet extraction and reflux extraction were used in the algal extraction step. Ethanol was proven to be the best solvent, and the addition of MgSO4 could transform acids to esters. In MgSO4 extraction oil, the yield of hexadecanoic acid ethyl ester was as high as 48.40%. Then, the residual algae powders through the catalytic hydrothermal liquefaction process were converted to bio-oil. Commercialized noble metal catalysts Pd/C, Pt/C, Ru/C and Rh/C combined with Pd/HZSM-5 were used in the second step. Rh/C performed the best in the catalytic hydrothermal liquefaction process, and the highest bio-oil yield of 50.98% and HHV of 30.67 MJ kg-1 were achieved. The oil yield through two steps was higher than that by a direct decomposition step. Also, the two-step method could achieve a higher energy conversion ratio of 85.61% and total energy of 81.09 kJ.

| S-EPMC9085724 | biostudies-literature

Liquefaction of Lignin Using Chemical Decomposition and Its Application to Polyurethane Foam.

Project description:To utilize the chemical application of lignin (LN), a decomposition reaction was carried out to cleave chemical bonds. Indeed, a liquefaction process is essential for the chemical use of lignin to achieve a uniform reaction and maximize the chemical utility of lignin. To this end, hydroxyl radicals were adopted as a powerful oxidation agent, and FT-IR results confirmed the cleavage of the ether linkages. Additionally, the water solubility of LN significantly increased after decomposition, and dissolution levels up to 0.5 g·mL-1 were obtained. Using these high solubility properties in water, NMR and DLS analyses were performed. In particular, an average particle diameter of 300 ± 240 nm was found, corresponding to the size of polydisperse l-LN. By controlling size uniformity and using high water-solubility levels, polyurethane foams were manufactured using l-LN.

| S-EPMC8153736 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data