Robust and Elastic Lunar and Martian Structures from 3D-Printed Regolith Inks.

ABSTRACT: Here, we present a comprehensive approach for creating robust, elastic, designer Lunar and Martian regolith simulant (LRS and MRS, respectively) architectures using ambient condition, extrusion-based 3D-printing of regolith simulant inks. The LRS and MRS powders are characterized by distinct, highly inhomogeneous morphologies and sizes, where LRS powder particles are highly irregular and jagged and MRS powder particles are rough, but primarily rounded. The inks are synthesized via simple mixing of evaporant, surfactant, and plasticizer solvents, polylactic-co-glycolic acid (30% by solids volume), and regolith simulant powders (70% by solids volume). Both LRS and MRS inks exhibit similar rheological and 3D-printing characteristics, and can be 3D-printed at linear deposition rates of 1-150 mm/s using 300 μm to 1.4 cm-diameter nozzles. The resulting LRS and MRS 3D-printed materials exhibit similar, but distinct internal and external microstructures and material porosity (~20-40%). These microstructures contribute to the rubber-like quasi-static and cyclic mechanical properties of both materials, with young's moduli ranging from 1.8 to 13.2 MPa and extension to failure exceeding 250% over a range of strain rates (10^-1-10² min^-1). Finally, we discuss the potential for LRS and MRS ink components to be reclaimed and recycled, as well as be synthesized in resource-limited, extraterrestrial environments.

SUBMITTER: Jakus AE

PROVIDER: S-EPMC5357966 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thermal Weathering of 3D-Printed Lunar Regolith Simulant Composites.

Project description:The production of lunar regolith composites is a promising venture, especially when enabled by extrusion-based additive manufacturing techniques such as direct ink write. However, both three-dimensional (3D) printing production and usage of polymer composites containing regolish on the lunar surface are challenges due to harsh environmental conditions such as severe thermal cycling. While thermal degradation in polymer composites under thermal cycling has been studied, there is limited understanding of how polymer properties impact the mechanical performance of lunar regolith composites when both printing and usage are carried out under extreme thermal conditions. Here, we aim to bridge that gap through the creation of composites containing a lunar Highlands regolith simulant suspended in an ultraviolet (UV) curable binder, which were printed at -30 °C and thermally cycled between weekly lunar day (127 °C) and weekly night (-190 °C) temperatures. We validate that thermal stresses cause both physical and chemical degradation since the regolith simulant composites become stiffer, more porous, and show yellowing after exposure to thermal cycling. Moreover, we indicate that chemical degradation mechanisms seem to compete with residual polymerization in certain formulations. We attribute this phenomenon to partial crystallization of monomer species during printing at -30 °C, resulting in low vinyl bond conversion during initial curing. The results presented here shed light on the intricate interplay between thermal stresses, uncured polymer properties, and degradation mechanisms, which can help guide future use cases of regolith composites for lunar infrastructure needs.

| S-EPMC11348411 | biostudies-literature

Plants grow in lunar regolith

Project description:The extent to which plants can enhance human life support on other worlds depends on the ability of plants to thrive in extraterrestrial environments using in situ resources. Using samples from Apollo 11, 12 and 17, we show that the terrestrial plant Arabidopsis thaliana germinates and grows in diverse lunar regoliths. However, our results show that growth is challenging; the lunar regolith plants were slow to develop, expressed genes indicative of ionic stresses, and many showed severe stress morphologies. Therefore, although in situ lunar regolith can be useful for plant production in lunar habitats, they are not benign substrates. The interaction between plants and lunar regolith will need to be further elucidated, and likely mitigated, to enable efficient use of lunar regolith for life support.

2022-05-16 | GSE188852 | GEO

Plants grow in lunar regolith

Project description:Plants grow in lunar regolith

| PRJNA780518 | ENA

EAC-1A: A novel large-volume lunar regolith simulant.

Project description:The European Astronaut Centre (EAC) is currently constructing the European Lunar Exploration Laboratory (LUNA), a large training and operations facility to be located adjacent to EAC at the DLR (German Aerospace Centre) campus in Cologne, Germany. With an estimated representative lunar testbed area of approximately 660 m2, a large volume of lunar regolith simulant material is needed for this purpose. In this study, a basanitic sandy silt from a quarry located in the Siebengebirge Volcanic Field is evaluated as a large-volume source of material. The focus of this project has been to conduct a physical and chemical characterisation of the fine-grained material to be used in LUNA; the European Astronaut Centre lunar regolith simulant 1 (EAC-1?A). The physical characterisation tests undertaken include sphericity, density measurements, cohesion and static angle of repose, with mineralogical investigations via petrographical analysis with optical microscope and SEM, XRF, XRD and DSC measurements. The results of the EAC-1A tests are compared to published data on existing widely used lunar regolith simulants, namely JSC-1A, JSC-2A, NU-LHT-3M, DNA and FJS-1.

| S-EPMC7096503 | biostudies-literature

Aqueous Inks of Pristine Graphene for 3D Printed Microsupercapacitors with High Capacitance.

Project description:Three-dimensional (3D) printing is gaining importance as a sustainable route for the fabrication of high-performance energy storage devices. It enables the streamlined manufacture of devices with programmable geometry at different length scales down to micron-sized dimensions. Miniaturized energy storage devices are fundamental components for on-chip technologies to enable energy autonomy. In this work, we demonstrate 3D printed microsupercapacitor electrodes from aqueous inks of pristine graphene without the need of high temperature processing and functional additives. With an intrinsic electrical conductivity of ∼1370 S m-1 and rationally designed architectures, the symmetric microsupercapacitors exhibit an exceptional areal capacitance of 1.57 F cm-2 at 2 mA cm-2 which is retained over 72% after repeated voltage holding tests. The areal power density (0.968 mW cm-2) and areal energy density (51.2 μWh cm-2) outperform the ones of previously reported carbon-based supercapacitors which have been either 3D or inkjet printed. Moreover, a current collector-free interdigitated microsupercapacitor combined with a gel electrolyte provides electrochemical performance approaching the one of devices with liquid-like ion transport properties. Our studies provide a sustainable and low-cost approach to fabricate efficient energy storage devices with programmable geometry.

| S-EPMC8482754 | biostudies-literature

Bioinspired reconfiguration of 3D printed microfluidic hydrogels via automated manipulation of magnetic inks.

Project description:One of the key components in controlling fluid streams in microfluidic devices is the valve and gating modules. In most situations, these components are fixed at specific locations, and a new reconfiguration of microchannels requires costly and laborious fabrication of new devices. In this study, inspired by the human vasculature microcapillary reconfiguration in response to blood transport requirements, the idea of reconfigurable gel microfluidic systems is presented for the first time. A simple approach is described to print microchannels in methacrylated gelatin (GelMA) hydrogels by using agarose fibers that are loaded with iron microparticles. The agarose fibers can then be used as valves, which are then manipulated using a permanent magnet, providing the reconfigurability of the system. The feasibility of agarose gels is tested with different iron microparticle loadings as well as their resistance to fluid flows. Further, it is shown that using this technique, multiple configurations, as well as reconfigurability, are possible from a single device. This work opens the framework to design more intricate and reconfigurable microfluidic devices, which will decrease the cost and size of the final product.

| S-EPMC7395927 | biostudies-literature

Martian biolith: A bioinspired regolith composite for closed-loop extraterrestrial manufacturing.

Project description:Given plans to revisit the lunar surface by the late 2020s and to take a crewed mission to Mars by the late 2030s, critical technologies must mature. In missions of extended duration, in situ resource utilization is necessary to both maximize scientific returns and minimize costs. While this present a significantly more complex challenge in the resource-starved environment of Mars, it is similar to the increasing need to develop resource-efficient and zero-waste ecosystems on Earth. Here, we make use of recent advances in the field of bioinspired chitinous manufacturing to develop a manufacturing technology to be used within the context of a minimal, artificial ecosystem that supports humans in a Martian environment.

| S-EPMC7494075 | biostudies-literature

Untangling the formation and liberation of water in the lunar regolith.

Project description:The source of water (H2O) and hydroxyl radicals (OH), identified on the lunar surface, represents a fundamental, unsolved puzzle. The interaction of solar-wind protons with silicates and oxides has been proposed as a key mechanism, but laboratory experiments yield conflicting results that suggest that proton implantation alone is insufficient to generate and liberate water. Here, we demonstrate in laboratory simulation experiments combined with imaging studies that water can be efficiently generated and released through rapid energetic heating like micrometeorite impacts into anhydrous silicates implanted with solar-wind protons. These synergistic effects of solar-wind protons and micrometeorites liberate water at mineral temperatures from 10 to 300 K via vesicles, thus providing evidence of a key mechanism to synthesize water in silicates and advancing our understanding on the origin of water as detected on the Moon and other airless bodies in our solar system such as Mercury and asteroids.

| S-EPMC6561281 | biostudies-literature

Nanocellulose-Based Inks-Effect of Alginate Content on the Water Absorption of 3D Printed Constructs.

Project description:2,2,6,6-tetramethylpyperidine-1-oxyl (TEMPO) oxidized cellulose nanofibrils (CNF) were used as ink for three-dimensional (3D) printing of porous structures with potential as wound dressings. Alginate (10, 20, 30 and 40 wt%) was incorporated into the formulation to facilitate the ionic cross-linking with calcium chloride (CaCl2). The effect of two different concentrations of CaCl2 (50 and 100 mM) was studied. The 3D printed hydrogels were freeze-dried to produce aerogels which were tested for water absorption. Scanning Electronic Microscopy (SEM) pictures demonstrated that the higher the concentration of the cross-linker the higher the definition of the printed tracks. CNF-based aerogels showed a remarkable water absorption capability. Although the incorporation of alginate and the cross-linking with CaCl2 led to shrinkage of the 3D printed constructs, the approach yielded suitable porous structures for water and moisture absorption. It is concluded that the 3D printed biocomposite structures developed in this study have characteristics that are promising for wound dressings devices.

| S-EPMC6784144 | biostudies-literature

Rapid Magnetic 3D Printing of Cellular Structures with MCF-7 Cell Inks.

Project description:A contactless label-free method using a diamagnetophoretic ink to rapidly print three-dimensional (3D) scaffold-free multicellular structures is described. The inks consist of MCF-7 cells that are suspended in a culture medium to which a paramagnetic salt, diethylenetriaminepentaacetic acid gadolinium (III) dihydrogen salt hydrate (Gd-DTPA), is added. When a magnetic field is applied, the host fluid containing the paramagnetic salt is attracted towards regions of high magnetic field gradient, displacing the ink towards regions with a low gradient. Using this method, 3D structures are printed on ultra-low attachment (ULA) surfaces. On a tissue culture treated (TCT) surface, a 3D printed spheroid coexists with a two-dimensional (2D) cell monolayer, where the composite is termed as a 2.5D structure. The 3D structures can be magnetically printed within 6 hours in a medium containing 25 mM Gd-DTPA. The influence of the paramagnetic salt on MCF-7 cell viability, cell morphology, and ability of cells to adhere to each other to stabilize the printed structures on both ULA and TCT surfaces is investigated. Gene expressions of hypoxia-inducible factor 1-alpha (HIF1α) and vascular endothelial growth factor (VEGF) allow comparison of the relative stresses for the printed 3D and 2.5D cell geometries with those for 3D spheroids formed without magnetic assistance. This magnetic printing method can be potentially scaled to a higher throughput to rapidly print cells into 3D heterogeneous cell structures with variable geometries with repeatable dimensions for applications such as tissue engineering and tumour formation for drug discovery.

| S-EPMC6750075 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data